CN108559367A - A kind of pearl point coating - Google Patents
A kind of pearl point coating Download PDFInfo
- Publication number
- CN108559367A CN108559367A CN201611246331.9A CN201611246331A CN108559367A CN 108559367 A CN108559367 A CN 108559367A CN 201611246331 A CN201611246331 A CN 201611246331A CN 108559367 A CN108559367 A CN 108559367A
- Authority
- CN
- China
- Prior art keywords
- pearl point
- pearl
- coating
- point coating
- ink material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of pearl point coating, the pearl point coating includes construction, cured gloss oil material and ink material successively, wherein, according to mass percentage, the gloss oil material includes macromolecule polyester resin 45%~78%, higher boiling environmentally friendly solvent 16%~49%, isocyanates 0.6%~2.3% and pearl point initiator A 2%~7%；The ink material includes high concentration alkyd resin 80%~90%, low boiling point solvent 5%~22% and pearl point initiator B 0.3%~4.3%.The suitable offset printing of the pearl point coating or roller coating, easy for construction, loss is low, can increase substantially production efficiency；Can be presented pearl point decorative pattern after solidification, appearance is beautiful, it is decorative it is strong, the shallower mechanical scar in coated article body surface face and rough whole surface defect can be covered up.
Description
Technical field
The present invention relates to artistic coating field more particularly to a kind of pearl point coating.
Background technology
Artistic coating is called novelty finish, fine arts paint；Artistic coating is that have special efficiency by what sapecial coating was constituted
Coating variety is a kind of industrial finish, and as other coating, this coating, which is coated in body surface, can play to various objects
Protective effect, unlike after its coating film forming, coating surface self-assembling formation and naturally various beautiful patterns can occur, such as
Mallear stria, wrinkle, tangerine line, stone pattern, speckle, crystallized, crackle, wood grain etc.；Appearance is beautiful, decorative strong, can cover up coated article body surface
The shallower mechanical scar in face and rough whole surface defect.In the prior art, the decorative pattern of pearl dot shape is mainly by spraying skill
It being formed, when coating decoration, will generally spray repeatedly, first uniformly construct according to conventional spraying process, after it is completely dried, choosing
The paint solution of stiff is sprayed into sparse raindrop shape varnish stain and is sprinkled upon workpiece surface under lower air pressure with the nozzle being relatively large in diameter
On, paint solution point has little time levelling, and solvent has volatilized, to formed it is uniform in size, ask away from almost the same droplet shape.
However, this construction technology is to the more demanding of construction personnel and nozzle, not stable in performance, repeatability is not high,
Therefore, it is necessary to provide a kind of pearl point coating, by way of offset printing or roller coating also can natural shape beading point decorative pattern, it is right
Construction technology does not require, with overcome the deficiencies in the prior art.
Invention content
The purpose of the present invention is to provide a kind of pearl point coating, are suitble to offset printing or roller coating, easy for construction, presentation naturally
Pearl point decorative pattern, appearance be beautiful, it is decorative it is strong, the shallower mechanical scar in coated article body surface face can be covered up and rough whole surface lacks
It falls into.
To realize that the purpose, the present invention provide a kind of pearl point coating, which is characterized in that the pearl point coating includes applying successively
Work, cured gloss oil material and ink material, wherein according to mass percentage, the gloss oil material includes macromolecule polyester
Resin 45%~78%, higher boiling environmentally friendly solvent 16%~49%, isocyanates 0.6%~2.3% and pearl point initiator A
2%~7%；The ink material includes high concentration alkyd resin 80%~90%, low boiling point solvent 5%~22% and pearl point
Initiator B 0.3%~4.3%.
The pearl point coating of the present invention is suitable on roller coating or printing to metal base, such as iron-based material or aluminium base, first
It by the roller coating of gloss oil material or is printed on metal base, baking removal higher boiling environmentally friendly solvent, macromolecule at 150 DEG C~170 DEG C
Polyester resin is crosslinked with isocyanates reacts film forming.Then roller coating or printing ink material on the gloss oil material after film forming
Expect, high-temperature baking cures at 150 DEG C~160 DEG C, and pearl point decorative pattern is formed on ink material surface after solidification.Specifically, pearl point is spent
The formation basic theory of line is：Ink material is constructed when the film surface that gloss oil material is formed, and surface tension makes ink material as possible
Film is shrunk to the shape of surface area minimum, having the surface levelling of wrinkle, groove mark, streak or ridge into even curface, still,
When film surface is there are when pearl point initiator B, pearl point initiator B has lower surface tension, and surface tension can be caused uneven,
Generating shrinkage cavity so that the surface of ink material forms protuberance and low ebb, and bump pad is faster than the low boiling point solvent volatilization at low ebb place, this
Meaning that the cooling velocity of bump pad is fast, viscosity is high, has larger surface tension, and ink material film is pulled up from low ebb is past,
Low ebb is correspondingly set to become deeper, to form shrinkage cavity.In addition, being added in gloss oil material has pearl point initiator A, pearl point initiator
A reduces the surface tension of gloss oil material, and the film forming for being not only conducive to gloss oil material is smooth, smooth and uniform, and gloss oil after film forming
There is non-infiltration phenomenon between material and the ink material of liquid, keep the shrinkage cavity of above-mentioned formation until ink material is solidified into
Shape, to form pearl point decorative pattern.
Wherein, high concentration alkyd resin is from thermosetting resin, and very fast to the release of solvent, drying property is good, and low boiling point is molten
Agent is quickly volatilized under 150 DEG C~160 DEG C high temperature.
In the present invention, it can dissolve macromolecule polyester resin and boiling point can be used as this hair in 150 DEG C~170 DEG C of solvent
Bright higher boiling environmentally friendly solvent, can dissolve high concentration alkyd resin and solvent of the boiling point less than 150 DEG C can be used as the present invention's
Low boiling point solvent.
Preferably, the high concentration alkyd resin is polymerized by polyalcohol, vegetable oil and binary acid, the high concentration
The oil content of alkyd resin is 45%~55%.
Preferably, the polyalcohol be glycerine, trimethylolpropane, trimethylolethane, pentaerythrite, ethylene glycol,
At least one of 1,2-PD and 1,3-PD, the vegetable oil are linseed oil or dehydrated castor oil, the binary acid
For phthalic anhydride or M-phthalic acid.
Preferably, according to mass percentage, the gloss oil material further includes levelling agent 0.1%~3%, drawing oil
0.2%~2% and wax liquor 2%~6%.
Preferably, according to mass percentage, the ink material further includes drier 0.04%~2.1%.
Preferably, according to mass percentage, the drier includes manganese dry oily 0.03%~2% or/and the dry oil of cobalt
0.01~0.1%.
Preferably, the ink material further includes having pigment.
Preferably, the pearl point initiator A is anticrater agent, including isophorone, diacetone alcohol or butyl cellulose.
Preferably, the pearl point initiator B is spheric granules object.
Preferably, the pearl point initiator B in nano silicon dioxide, carbon black, nano-magnetic powder, nano mica at least
It is a kind of.
The prior art is compared, and the present invention has the advantages that：
Suitable offset printing or roller coating, easy for construction, loss is low, can increase substantially production efficiency；Can be in after solidification
Existing pearl point decorative pattern, appearance is beautiful, it is decorative it is strong, the shallower mechanical scar in coated article body surface face and rough whole surface can be covered up
Defect.
Figure of description
Fig. 1 is the design sketch after pearl point coating of the present invention cures on metal base, has pearl point decorative pattern.
Fig. 2 be pearl point coating of the present invention cure on metal base after another design sketch, with yellow uitramarine pattern with
Pearl point decorative pattern.
Specific implementation mode
The technical solution further illustrated the present invention below by specific implementation mode.
Embodiment 1
A kind of pearl point coating is provided, including is constructed successively, cured gloss oil material and ink material, according to mass percent
Meter, the gloss oil material include：
The ink material includes：
Embodiment 2
A kind of pearl point coating is provided, including is constructed successively, cured gloss oil material and ink material, according to mass percent
Meter, the gloss oil material include：
The ink material includes：
Embodiment 3
A kind of pearl point coating is provided, including is constructed successively, cured gloss oil material and ink material, according to mass percent
Meter, the gloss oil material include：
The ink material includes：
Embodiment 4
A kind of pearl point coating is provided, including is constructed successively, cured gloss oil material and ink material, according to mass percent
Meter, the gloss oil material include：
The ink material includes：
Comparative example 1
A kind of coating is provided, including is constructed successively, cured gloss oil material and ink material, according to mass percentage,
The gloss oil material includes：
The ink material includes：
The pearly coating of above-described embodiment 1~4 and the coating of comparative example 1 are constructed using identical method in metal base
On, it is specific as follows：
By the gloss oil material roller coating of each embodiment and comparative example on iron substrate, toasted 10 minutes at 170 DEG C, gloss oil material
Expect that film-forming, the roller coating ink material on the gloss oil material of film forming toast 10 minutes at 155 DEG C, ink material is solid
Change.
The results show that comparative example 1 can only form plane pattern, no pearl point is formed.
As shown in Figure 1, being formed with pearl point decorative pattern on the ink material of each embodiment, it is notable that in ink material
Pigment be distributed evenly on gloss oil material, shrinkage cavity phenomenon does not occur with the other components of ink material, Fig. 2 illustrates ink
Material is printed in spider reticulation on gloss oil material, and after baking, pigment is distributed evenly on gloss oil material, shape on ink material
Cheng Youzhu point decorative patterns so that pearl point coating of the invention has the effect of that characteristic, pigment can be random color.
The prior art is compared, and the present invention has the advantages that：
Suitable offset printing or roller coating, easy for construction, loss is low, can increase substantially production efficiency；Can be in after solidification
Existing pearl point decorative pattern, appearance is beautiful, it is decorative it is strong, the shallower mechanical scar in coated article body surface face and rough whole surface can be covered up
Defect.
More than, only presently preferred embodiments of the present invention for those of ordinary skill in the art can be according to this hair
Bright technical solution and technical concept makes other various corresponding change and deformations, and all these change and distortions should all belong to
In the range of the claims in the present invention.
The present invention illustrates the method detailed of the present invention by above-described embodiment, but the invention is not limited in above-mentioned detailed
Method does not mean that the present invention has to rely on above-mentioned method detailed and could implement.Person of ordinary skill in the field should
It is illustrated, any improvement in the present invention, addition, the concrete mode of equivalence replacement and auxiliary element to each raw material of product of the present invention
Selection etc., all fall within protection scope of the present invention and the open scope.
Claims (10)
1. a kind of pearl point coating, which is characterized in that the pearl point coating includes construction, cured gloss oil material and ink material successively
Material,
Wherein, according to mass percentage, the gloss oil material includes：
The ink material includes：
High concentration alkyd resin 80%~90%；
Low boiling point solvent 5%~22%；And
Pearl point initiator B 0.3%~4.3%.
2. epoxy resin as described in claim 1, which is characterized in that the high concentration alkyd resin is by polyalcohol, plant
Oil and binary acid are polymerized, and the oil content of the high concentration alkyd resin is 45%~55%.
3. pearl point coating as claimed in claim 2, which is characterized in that the polyalcohol is glycerine, trimethylolpropane, three
At least one of hydroxymethyl ethane, pentaerythrite, ethylene glycol, 1,2-PD and 1,3-PD, the vegetable oil are Asia
Sesame oil or dehydrated castor oil, the binary acid are phthalic anhydride or M-phthalic acid.
4. pearl point coating as described in claim 1, which is characterized in that according to mass percentage, the gloss oil material also wraps
It includes：
Levelling agent 0.1%~3%；
Drawing oil 0.2%~2%；And
Wax liquor 2%~6%.
5. pearl point coating as described in claim 1, which is characterized in that according to mass percentage, the ink material also wraps
Include drier 0.04%~2.1%.
6. pearl point coating as claimed in claim 5, which is characterized in that according to mass percentage, the drier includes manganese
Dry oily 0.03%~2% or/and cobalt dry oily 0.01~0.1%.
7. pearl point coating as described in claim 1, which is characterized in that the ink material further includes having pigment.
8. pearl point coating as described in claim 1, which is characterized in that the pearl point initiator A is anticrater agent, including different Buddhist
That ketone, diacetone alcohol or butyl cellulose.
9. pearl point coating as described in claim 1, which is characterized in that the pearl point initiator B is spheric granules object.
10. pearl point coating as claimed in claim 9, which is characterized in that the pearl point initiator B be selected from nano silicon dioxide,
At least one of carbon black, nano-magnetic powder, nano mica.