CN108559180A - A kind of corrosion-resistant plastic electric wire skin - Google Patents
A kind of corrosion-resistant plastic electric wire skin Download PDFInfo
- Publication number
- CN108559180A CN108559180A CN201810439919.9A CN201810439919A CN108559180A CN 108559180 A CN108559180 A CN 108559180A CN 201810439919 A CN201810439919 A CN 201810439919A CN 108559180 A CN108559180 A CN 108559180A
- Authority
- CN
- China
- Prior art keywords
- parts
- electric wire
- corrosion
- wire skin
- resistant plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of corrosion-resistant plastic electric wire skin, and the corrosion-resistant plastic electric wire skin ingredient and consumption proportion are：36 parts of phthalic acid ester, 47 parts of makrolon, 38 parts of odium stearate, 25 parts of stabilizer, by 58 parts of polypropylene, 38 parts of melamine, 47 parts of antioxidant, 12 parts of triethylene diamine, 37 parts of paraffin oil, 25 parts of polyvinyl chloride, 36 parts of asbestos.Beneficial effects of the present invention：The present invention provides a kind of corrosion-resistant plastic electric wire skins, wherein, this electric wire skin raw material is by obtaining corrosion-resistant electric wire skin after extruding machine composing type, have excellent flame retardant property and corrosion resistance, it is not easily susceptible to extraneous factor damage, and is not easy on fire when short circuit, considerably increases the security performance of electric wire, meanwhile the method that is used to prepare the electric wire skin is simple, raw material is easy to get.
Description
Technical field
The present invention relates to plastic products technology field more particularly to a kind of ambroins.
Background technology
With the development of science and technology, people’s lives are more and more convenient, especially in terms of office, easily done with various
Utility occurs, and such as computer, fax, phone, printer, staff can handle a large amount of things in office, thus
The time that staff contacts these office appliances is also increasingly longer, and the safety of electronic product is also increasingly by the weight of people
Depending on.Ambroin as substantially all electronic products is that sheathing material is increasingly valued by people, and insulation performance
Quality determines the security feature of product.
Invention content
To reach the insulation purpose of the above electronic product or circuit, the present invention provides a kind of ambroin.
The used technical solution is as follows：
A kind of corrosion-resistant plastic electric wire skin,
The corrosion-resistant plastic electric wire skin ingredient and consumption proportion are：3-6 parts of phthalic acid ester, 4-7 parts of makrolon,
3-8 parts of odium stearate, 2-5 parts of stabilizer, by 5-8 parts of polypropylene, 3-8 parts of melamine, 4-7 parts of antioxidant, triethylene diamine
1-2 parts, 3-7 parts of paraffin oil, 2-5 parts of polyvinyl chloride, 3-6 parts of asbestos.
As further explanation,
The corrosion-resistant plastic electric wire skin ingredient and consumption proportion are：3 parts of phthalic acid ester, 4 parts of makrolon, tristearin
3 parts of sour sodium, 2 parts of stabilizer, by 5 parts of polypropylene, 3 parts of melamine, 4 parts of antioxidant, 1 part of triethylene diamine, 3 parts of paraffin oil,
2 parts of polyvinyl chloride, 3 parts of asbestos.
As further explanation,
The corrosion-resistant plastic electric wire skin ingredient and consumption proportion are：6 parts of phthalic acid ester, 7 parts of makrolon, tristearin
8 parts of sour sodium, 5 parts of stabilizer, by 8 parts of polypropylene, 8 parts of melamine, 7 parts of antioxidant, 2 parts of triethylene diamine, 7 parts of paraffin oil,
5 parts of polyvinyl chloride, 6 parts of asbestos.
As further explanation,
The electric wire skin production process is as follows：
After raw material is thoroughly mixed, melting operation is carried out, the melting time is 20-30 minutes, and temperature is maintained at 200-
250 degree.
Beneficial effects of the present invention：
Invention provides a kind of corrosion-resistant plastic electric wire skin, wherein this electric wire skin raw material after extruding machine composing type by obtaining
To corrosion-resistant electric wire skin, have excellent flame retardant property and corrosion resistance, is not easily susceptible to extraneous factor damage, and short circuit
Shi Buyi is on fire, considerably increases the security performance of electric wire, meanwhile, the method that is used to prepare the electric wire skin is simple, raw material is easy to get.
Specific implementation mode
Below to technical scheme of the present invention make specifically, complete explanation.
Embodiment,
A kind of corrosion-resistant plastic electric wire skin,
The corrosion-resistant plastic electric wire skin ingredient and consumption proportion are：3-6 parts of phthalic acid ester, 4-7 parts of makrolon,
3-8 parts of odium stearate, 2-5 parts of stabilizer, by 5-8 parts of polypropylene, 3-8 parts of melamine, 4-7 parts of antioxidant, triethylene diamine
1-2 parts, 3-7 parts of paraffin oil, 2-5 parts of polyvinyl chloride, 3-6 parts of asbestos.
The corrosion-resistant plastic electric wire skin ingredient and consumption proportion are：3 parts of phthalic acid ester, 4 parts of makrolon, tristearin
3 parts of sour sodium, 2 parts of stabilizer, by 5 parts of polypropylene, 3 parts of melamine, 4 parts of antioxidant, 1 part of triethylene diamine, 3 parts of paraffin oil,
2 parts of polyvinyl chloride, 3 parts of asbestos.
The corrosion-resistant plastic electric wire skin ingredient and consumption proportion are：6 parts of phthalic acid ester, 7 parts of makrolon, tristearin
8 parts of sour sodium, 5 parts of stabilizer, by 8 parts of polypropylene, 8 parts of melamine, 7 parts of antioxidant, 2 parts of triethylene diamine, 7 parts of paraffin oil,
5 parts of polyvinyl chloride, 6 parts of asbestos.
The electric wire skin production process is as follows：
After raw material is thoroughly mixed, melting operation is carried out, the melting time is 20-30 minutes, and temperature is maintained at 200-
250 degree.
Invention provides a kind of corrosion-resistant plastic electric wire skin, wherein this electric wire skin raw material after extruding machine composing type by obtaining
To corrosion-resistant electric wire skin, have excellent flame retardant property and corrosion resistance, is not easily susceptible to extraneous factor damage, and short circuit
Shi Buyi is on fire, considerably increases the security performance of electric wire, meanwhile, the method that is used to prepare the electric wire skin is simple, raw material is easy to get.
Obviously, described embodiment is only a part of the embodiment of the present invention, rather than whole embodiments.Based on this
The embodiment of invention, all other reality obtained by those of ordinary skill in the art without making creative efforts
It applies, belongs to protection scope of the present invention.
Claims (4)
1. a kind of corrosion-resistant plastic electric wire skin, which is characterized in that
The corrosion-resistant plastic electric wire skin ingredient and consumption proportion are：3-6 parts of phthalic acid ester, 4-7 parts of makrolon, tristearin
Sour sodium 3-8 parts, 2-5 parts of stabilizer, by 5-8 parts of polypropylene, 3-8 parts of melamine, 4-7 parts of antioxidant, triethylene diamine 1-2
Part, 3-7 parts of paraffin oil, 2-5 parts of polyvinyl chloride, 3-6 parts of asbestos.
2. a kind of corrosion-resistant plastic electric wire skin according to claim 1, which is characterized in that
The corrosion-resistant plastic electric wire skin ingredient and consumption proportion are：3 parts of phthalic acid ester, 4 parts of makrolon, odium stearate
3 parts, 2 parts of stabilizer, by 5 parts of polypropylene, 3 parts of melamine, 4 parts of antioxidant, 1 part of triethylene diamine, 3 parts of paraffin oil, polychlorostyrene
2 parts of ethylene, 3 parts of asbestos.
3. a kind of corrosion-resistant plastic electric wire skin according to claim 1, which is characterized in that
The corrosion-resistant plastic electric wire skin ingredient and consumption proportion are：6 parts of phthalic acid ester, 7 parts of makrolon, odium stearate
8 parts, 5 parts of stabilizer, by 8 parts of polypropylene, 8 parts of melamine, 7 parts of antioxidant, 2 parts of triethylene diamine, 7 parts of paraffin oil, polychlorostyrene
5 parts of ethylene, 6 parts of asbestos.
4. a kind of corrosion-resistant plastic electric wire skin according to claim 1, which is characterized in that the electric wire skin production process is such as
Under：
After raw material is thoroughly mixed, melting operation is carried out, the melting time is 20-30 minutes, and temperature is maintained at 200-250
Degree.