CN108558219A - 一种夜光水晶珠胚及其制备方法 - Google Patents
一种夜光水晶珠胚及其制备方法 Download PDFInfo
- Publication number
- CN108558219A CN108558219A CN201810347593.7A CN201810347593A CN108558219A CN 108558219 A CN108558219 A CN 108558219A CN 201810347593 A CN201810347593 A CN 201810347593A CN 108558219 A CN108558219 A CN 108558219A
- Authority
- CN
- China
- Prior art keywords
- parts
- bead blank
- crystal bead
- crystal
- noctilucence
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种夜光水晶珠胚及其制备方法，所述的夜光水晶珠胚是由下列重量份配比成份组成：石英砂80‑160份、氧化锌2‑15.5份、氧化铈0.5‑5份、纯碱27‑51份、碳酸钾16‑30份、硼酸7‑16份、碳酸钙2.5‑5.5份、氢氧化铝0.8‑3.5份、食盐0.5‑2份、硝酸钾12‑27份和含铽铝酸盐2‑32份。所述夜光水晶珠胚制备时采用含铽铝酸盐产生光致长余辉磷光，用氧化锌和氧化铈调整氧化还原气氛，使工艺更稳定；所制备的夜光水晶珠胚在白天或光照条件下无色透明或呈白色，在夜晚或黑暗条件下能发出绿色磷光，具有光泽度好，整齐、无色差，无花纹，产量高，生产效益好的优点。
Description
(一)技术领域
本发明涉及一种夜光水晶珠胚及其制备方法。
(二)背景技术
夜光水晶珠胚是用来制备夜光水晶产品的半成品。目前现有的有色水晶珠胚和水晶珠只适合于在白天或照明条件好的情况下观赏，在夜晚或照明条件不好的情况观赏效果较差。胡健敏公开了一种夜光水晶球(专利申请号：CN201310525731.3)，在水晶球底端增设一个光控底座，光控底座的LED灯在光线弱时自动点亮和光线强时自动关闭，水晶球在黑暗中被照射发亮。宋吉成公开了超长余辉夜光水晶影像(专利申请号：CN00216357.8)，其特征在于基体上涂超长余辉夜光层，字画颜色层粘在夜光层上，再在夜光层上配上透明材料的表层。但以上公开的两种工艺生产效率低，不耐高温，显然不适合连续大批量生产水晶珠胚。
(三)发明内容
本发明所要解决的技术问题是提供一种再现性好，颜色一致无色差、无花纹，产品质量稳定，生产效率高，可适合连续池窑的生产作业，生产成本低，无污染的夜光水晶珠胚。
为解决上述问题，本发明是通过以下技术方案来实现的：
一种夜光水晶珠胚，所述的夜光水晶珠胚是由下列重量份配比成份制成：石英砂80-160份、氧化锌2-15.5份、氧化铈0.5-5份、纯碱27-51份、碳酸钾16-30份、硼酸7-16份、碳酸钙2.5-5.5份、氢氧化铝0.8-3.5份、食盐0.5-2份、硝酸钾12-27份以及含铽铝酸盐2-32份。
本发明所要解决的另一技术问题是提供一种夜光水晶珠胚的制备方法，本发明是通过以下技术方案来实现的：所述夜光水晶珠胚的制备过程如下：
(1)按重量份配比提取石英砂80-160份、氧化锌7-15.5份、氧化铈0.5-5份、纯碱27-51份、碳酸钾16-30份、硼酸7-16份、碳酸钙2.5-5.5份、氢氧化铝0.8-3.5份、食盐1-2份、硝酸钾12-27份、混合均匀得到水晶珠胚原料；
(2)将步骤(1)所得混合均匀的水晶珠胚原料通过造粒机进行造粒制成颗粒状的水晶珠胚原料；
(3)将步骤(2)所得颗粒状的水晶珠胚原料放入玻璃水晶池炉中在强氧化气氛下进行熔制，熔制时保持溶液液面稳定，得到水晶溶液；
(4)向步骤(3)所得水晶溶液中加入2-32份含铽铝酸盐并混合均匀，将所得混合溶液经料道均化冷却后模压制得成型珠胚；
(5)将成型珠胚匀速进入火抛炉的不锈钢管道中，管道温度控制在800℃-900℃，转速180r/s，在管道内停留5分钟，抛光、整型得到整型、颜色一致、无色差、无花纹的夜光水晶珠胚。
进一步，步骤(3)中，所述的熔制过程中，温度控制在1380℃-1450℃。
进一步，步骤(4)中，所述的冷却过程中，温度控制在800℃-1000℃。
与现有技术相比，本发明夜光水晶珠胚的有益效果是：
所述夜光水晶珠胚制备时采用含铽铝酸盐产生光致长余辉磷光，用氧化锌和氧化铈调整氧化还原气氛，使工艺更稳定；所制备的夜光水晶珠胚在白天或光照条件下无色透明或呈白色，在夜晚或黑暗条件下能发出绿色磷光，具有光泽度好，整齐、无色差，无花纹，产量高，生产效益好的优点。
(四)具体实施方式
下面通过具体实施例对本发明进行进一步描述，但本发明的保护范围并不仅限于此。
实施例1
本发明的一种夜光水晶珠胚，该夜光水晶珠胚是由下列重量份配比成份组成:石英砂160份、氧化锌7份、氧化铈0.5份、纯碱27份、碳酸钾30份、硼酸16份、碳酸钙5.5份、硝酸钾27份、氢氧化铝0.8份、食盐2份、含铽铝酸盐32份。
所述夜光水晶珠胚的制备过程如下：
1)按重量份配比提取石英砂160份、氧化锌7份、氧化铈0.5份、纯碱27份、碳酸钾30份、硼酸16份、碳酸钙5.5份、氢氧化铝0.8份、食盐1份混合均匀；
2)将混合均匀的水晶珠胚原料通过造粒机进行造粒；
3)将制成颗粒状的水晶珠胚原料放入玻璃水晶池炉中熔制，熔制时保持强氧化气氛和溶液液面稳定，熔制温度控制在1380℃-1450℃；
4)在水晶溶液中加入32份含铽铝酸盐并混合均匀；
5)将水晶溶液经料道均化冷却后模压成夜光水晶珠胚，冷却温度控制在800℃-1000℃；
6)将成型珠胚放入火抛炉抛光、整型，让成型珠胚匀速进入不锈钢管道，管道温度控制在800℃-900℃，转速180转/秒，在管道内5分钟后，管道出来就是经过整型、颜色一致、无色差、无花纹的夜光水晶珠胚。
实施例2
其与实施例1不同之处在于，该夜光水晶珠胚是由下列重量份配比成份组成:石英砂80份、氧化锌7份、氧化铈0.5份、纯碱27份、碳酸钾16份、硼酸7份、碳酸钙2.5份、氢氧化铝0.8份、食盐0.5份、含铽铝酸盐2份。
实施例3
其与实施例1不同之处在于，该夜光水晶珠胚是由下列重量份配比成份组成:石英砂150份、氧化锌15.5份、氧化铈5份、纯碱51份、碳酸钾30份、硼酸16份、碳酸钙5.5份、氢氧化铝3.5份、食盐2份、硝酸钾27份和含铽铝酸盐20份。
实施例4
其与实施例1不同之处在于，该夜光水晶珠胚是由下列重量份配比成份组成:石英砂100份、氧化锌2份、氧化铈1.5份、纯碱31份、碳酸钾20份、硼酸13份、碳酸钙3.5份、氢氧化铝1.5份、食盐1.0份、硝酸钾15份和含铽铝酸盐15份。
实施例5
其与实施例1不同之处在于，该夜光水晶珠胚是由下列重量份配比成份组成:石英砂155份、氧化锌14份、氧化铈2.1份、纯碱47份、碳酸钾28份、硼酸14份、碳酸钙5.1份、氢氧化铝3.1份、食盐1.8份、硝酸钾25份、含铽铝酸盐28份。
实施例6
其与实施例1不同之处在于，该夜光水晶珠胚是由下列重量份配比成份组成:石英砂125份、氧化锌11份、氧化铈3.1份、纯碱33份、碳酸钾23份、硼酸12份、碳酸钙3.5份、氢氧化铝2.5份、食盐1.5份和含铽铝酸盐25份。
实施例7
其与实施例1不同之处在于，该夜光水晶珠胚是由下列重量份配比成份组成:石英砂100份、氧化锌9.5份、氧化铈2份、纯碱40份、碳酸钾21份、硼酸13份、碳酸钙4份、氢氧化铝2份、食盐1份和和含铽铝酸盐19份。
实施例8
其与实施例1不同之处在于，该夜光水晶珠胚是由下列重量份配比成份组成:石英砂115份、氧化锌13.5份、氧化铈1.5份、纯碱39份、碳酸钾25份、硼酸13份、碳酸钙4.3份、氢氧化铝2.9份、食盐1.7份和含铽铝酸盐29份。
本发明不局限于上述最佳实施方式，任何人在本发明的启示下得出的其他任何与本发明相同或相近似的产品，均落在本发明的保护范围之内。
Claims (4)
1.一种夜光水晶珠胚，其特征在于：所述的夜光水晶珠胚由下列重量份配比成份制成：石英砂80-160份、氧化锌2-15.5份、氧化铈0.5-5份、纯碱27-51份、碳酸钾16-30份、硼酸7-16份、碳酸钙2.5-5.5份、氢氧化铝0.8-3.5份、食盐0.5-2份、硝酸钾12-27份以及含铽铝酸盐2-32份。
2.如权利要求1所述的所述夜光水晶珠胚的制备方法，其特征在于：所述的方法具体按照如下步骤进行：
(1)按重量份配比提取石英砂80-160份、氧化锌7-15.5份、氧化铈0.5-5份、纯碱27-51份、碳酸钾16-30份、硼酸7-16份、碳酸钙2.5-5.5份、氢氧化铝0.8-3.5份、食盐1-2份、硝酸钾12-27份、混合均匀得到水晶珠胚原料；
(2)将步骤(1)所得混合均匀的水晶珠胚原料通过造粒机进行造粒制成颗粒状的水晶珠胚原料；
(3)将步骤(2)所得颗粒状的水晶珠胚原料放入玻璃水晶池炉中在强氧化气氛下进行熔制，熔制时保持溶液液面稳定，得到水晶溶液；
(4)向步骤(3)所得水晶溶液中加入2-32份含铽铝酸盐并混合均匀，将所得混合溶液经料道均化冷却后模压制得成型珠胚；
(5)将成型珠胚匀速进入火抛炉的不锈钢管道中，管道温度控制在800℃-900℃，转速180r/s，在管道内停留5分钟，抛光、整型得到整型、颜色一致、无色差、无花纹的夜光水晶珠胚。
3.如权利要求2所述的方法，其特征在于：步骤(3)中，熔制时温度控制在1380℃-1450℃。
4.如权利要求2所述的方法，其特征在于：步骤(4)中，所述的冷却温度控制在800℃-1000℃。