CN108547164A - The dichromatism one-bath process method of cationic terylene composite material - Google Patents
The dichromatism one-bath process method of cationic terylene composite material Download PDFInfo
- Publication number
- CN108547164A CN108547164A CN201810370244.7A CN201810370244A CN108547164A CN 108547164 A CN108547164 A CN 108547164A CN 201810370244 A CN201810370244 A CN 201810370244A CN 108547164 A CN108547164 A CN 108547164A
- Authority
- CN
- China
- Prior art keywords
- parts
- dichromatism
- composite material
- process method
- desizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of dichromatism one-bath process methods of cationic terylene composite material, by ordinary polyester and cationic terylene respectively through twisting, shape, lead the fabric blank that form inside and outside two sides structure different of the weaving after, then fabric blank is put into after refined, preshrunk, pre-setting and alkali number in mixed dye and is dyed.The present invention can have the characteristics that simultaneously it is time-consuming it is short, low energy consumption and coloring is good.
Description
Technical field
The present invention relates to a kind of colouring method of two-color fabric, especially a kind of dichromatism one of cationic terylene composite material
Bath dyeing method.
Background technology
Continuous pursuit with people to shade fabric effect, the fabric of conventional color and luster is since tone is single, aesthetic effect
The poor daily need that can no longer meet people, and the fabric with dual-sided two color effect compares traditional fabric with more
Color change and more preferably aesthetic feeling, then it is more and more extensive to be welcome by user.It is big to the colouring method of two-color fabric at present
Two one bath two-step methods or one bath two stage process are mostly used, two one bath two-step methods are first to contaminate different yarns two kinds of dyestuffs respectively
Color, then the yarn weaving after two groups of dyeing is molded;And one bath two stage process is then that the fabric after weaving is sequentially placed into two
It is dyed in the different dyestuff of kind, two kinds of dyestuffs is made to be dyed respectively to the yarn of unlike material in fabric.But both
Staining method has technique, and time-consuming, power consumption of polymer processing is high, to cause the raising of fabric production cost.And with skill
The development of art has a kind of colouring method of one step of a bath again, is to be dyed to fabric after being mixed by multiple dyestuffs, mixing is made to contaminate
Each dyestuff in material corresponds to the different yarns in fabric respectively;But this mode can lead to different dyes mutual shadow upon mixing
It rings, to cause the reduction of the aberration or color fastness of fabric after dyeing, coloring poor.Therefore, existing to two-color fabric
Colouring method have the shortcomings that can not to be provided simultaneously with it is time-consuming it is short, low energy consumption and coloring is good.
Invention content
The object of the present invention is to provide a kind of dichromatism one-bath process methods of cationic terylene composite material.It can
Simultaneously have the characteristics that it is time-consuming it is short, low energy consumption and coloring is good.
Technical scheme of the present invention:The dichromatism one-bath process method of cationic terylene composite material, by ordinary polyester and sun
Ion terylene respectively through twisting, shape, lead after weaving and form the different fabric blank of inside and outside two sides structure, then by fabric blank
It is put into mixed dye and is dyed after refined, preshrunk, pre-setting and alkali number.
In the dichromatism one-bath process method of cation terylene composite material above-mentioned, the mixed dye is by disperse dyes
It is formed with dye of positive ion mixed configuration, when dyeing, the bath raio of mixed dye is 1:5.
In the dichromatism one-bath process method of cation terylene composite material above-mentioned, the disperse dyes are in mixed dye
Account for 50%~60%.
In the dichromatism one-bath process method of cation terylene composite material above-mentioned, the disperse dyes by weight,
It is to be prepared from the following materials:100~920 parts of non-cationic dyestuff, 900~1500 parts of glacial acetic acid and levelling agent 400~600
Part.
In the dichromatism one-bath process method of cation terylene composite material above-mentioned, the refining includes carrying out successively
Desizing and neutralization, wherein temperature of the fabric blank in desizing are 95 DEG C~98 DEG C, and movement speed is 35~45 ms/min;It moves back
The desizing liquid for being added with 7~9g lye using every liter when slurry, the lye is to be prepared from the following materials by weight:
2500~3500 parts of sodium hydroxide liquid caustic soda, 1800~2200 parts of hydrogen peroxide, 800~1100 parts of degreaser, chelating agent 900~1000
Part and refining agent Nx900~1000 part;The bath raio of desizing liquid is 1 when desizing:5.
In the dichromatism one-bath process method of cation terylene composite material above-mentioned, the neutralization is by the face after desizing
Material blank is put into neutralization pond, so that the pH value of fabric blank is reached 7 by being slowly added to neutralizer;Contain in every liter of neutralizer
There is the acid solution of 7~9g, which is prepared from the following materials by weight:900~1000 parts of glacial acetic acid and peregal
45~60 parts.
In the dichromatism one-bath process method of cation terylene composite material above-mentioned, the preshrunk is the face after refining
Blank is expected after the cleaning of preshrunk liquid, is put into steam box decatize 30 minutes at 100 DEG C~105 DEG C, is contained in every liter of preshrunk liquid
There is the lye of 7~9g.
In the dichromatism one-bath process method of cation terylene composite material above-mentioned, the lye in the preshrunk liquid is by weight
Part meter, is to be prepared from the following materials:9000~10000 parts of sodium hydroxide liquid caustic soda, 1800~2100 parts of olive oil and WA are refined
1~2 part of agent.
In the dichromatism one-bath process method of cation terylene composite material above-mentioned, the alkali number is will be after pre-setting
Fabric blank, which is put into lye, to be impregnated 30 minutes, and the temperature of lye is 90 DEG C~96 DEG C, concentration of lye 8g/L.
In the dichromatism one-bath process method of cation terylene composite material above-mentioned, the technological parameter when sizing is temperature
60 DEG C~70 DEG C of degree, setting time 100~120 minutes;The technological parameter when weaving is 540 revs/min of speed;It is described pre-
Technological parameter when sizing is 180 DEG C~195 DEG C of pre-setting temperature, movement speed of the fabric in pre-setting be 40~50 meters/
Minute.
Compared with prior art, the present invention dyes fabric blank after mixing disperse dyes and the dye of positive ion,
Make disperse dyes and the dye of positive ion that can complete to dye to corresponding terylene respectively in primary dip dyeing, and coordinates two layers inside and outside
The different fabric blank of structure, to realize the dual-sided two color effect of fabric after dyeing, compared to two one bath two-step methods or a bath two
Footwork can effectively increase the processing efficiency of fabric and reduce its processing cost;Present invention is alternatively directed to the compositions of the dye of positive ion
With the formula of featured configuration disperse dyes, disperse dyes is enable to reduce the shadow caused by the dye of positive ion when dyed blended
Ring and improve the coloring to ordinary polyester, to make fabric after being dyed through mixed dye have good coloring and
Color fastness;The technological parameter and cleaning solution being arranged through the invention in the refining of fabric blank, preshrunk and alkali number, can improve
It is influenced caused by effectively reducing characteristic of each treatment process ordinary polyester and cationic terylene while fabric treatment effect,
To improve dye-uptake of each terylene to the anti-interference ability of different dyes and to corresponding dyestuff in dyed blended, further
Improve coloring of the present invention to fabric.In addition, featured configuration of the present invention also according to ordinary polyester and cationic terylene
The parameter of respective handling technique makes the present invention maximumlly improve while realizing treatment effect adding for terylene and fabric
Work efficiency rate further reduced the time-consuming and energy consumption of flow of the present invention;The concentration of lye and bath raio being arranged through the invention can also
The present invention is enough set to reach highest to the utilization rate of lye, to further decrease this under conditions of not influencing fabric treatment effect
The energy consumption and production cost of invention.So the present invention can have the characteristics that simultaneously it is time-consuming it is short, low energy consumption and coloring is good.
Specific implementation mode
With reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
Embodiment 1.The dichromatism one-bath process method (red blue two-color fabric) of cationic terylene composite material, including it is following
Step:
1. being twisted respectively to ordinary polyester and cationic terylene;
2. being carried out shaping respectively with cationic terylene to the ordinary polyester after twisting, setting temperature is 60 DEG C, setting time
It is 120 minutes;
It is weaved after into the different face of inside and outside two sides structure 3. passing through with cationic terylene the ordinary polyester after sizing leading
Expect that blank, the ordinary polyester content of fabric blank wherein one side are more than cationic terylene, the cationic terylene content of another side is big
In ordinary polyester, (surface layer of fabric blank is interwoven using five pieces of Warp Satins, the inner layer of fabric blank using eight pieces through face
Satin weave is interwoven) fabric blank weaving when loom speed be 540 revs/min;
4. carrying out desizing to fabric blank, temperature of the fabric blank in desizing is 95 DEG C, and movement speed is 45 ms/min
Clock, the desizing liquid for being added with 7g lye using every liter when desizing, the lye by weight, be prepared by following raw material and
At:2500 parts of the sodium hydroxide liquid caustic soda of 30% concentration, 2200 parts of hydrogen peroxide, (906) 800 parts of degreaser, chelating agent (M-175)
1000 parts and Nx900 parts of refining agent;Bath raio (weight ratio) of the desizing liquid in desizing is 1:5;
5. being put into neutralization pond to the fabric blank after desizing, the pH value of fabric blank is set to reach by being slowly added to neutralizer
To 7;Acid solution containing 9g in every liter of neutralizer, acid solution are prepared from the following materials by weight:Glacial acetic acid
(HAC) 900 parts and 60 parts of peregal;
6. preshrunk:By the fabric blank after neutralization after the cleaning of preshrunk liquid, decatize 30 minutes in 100 DEG C of steam box are put into,
Lye containing 7~9g in every liter of preshrunk liquid, the lye are prepared from the following materials by weight:32% concentration
10000 parts of sodium hydroxide liquid caustic soda, 2 parts of olive oil 1800 parts of (TF-106B) and WA refining agents;
7. carrying out pre-setting to the fabric blank after preshrunk, pre-setting temperature is 180 DEG C, and fabric blank is in pre-setting
It is 40 ms/min to move speed;
8. alkali number:Fabric blank after pre-setting is put into 90 DEG C of lye and is impregnated 30 minutes, which is 8g/
L;
It is dyed 9. the fabric blank after alkali number is put into mixed dye, the mixed dye is by disperse dyes and sun
Ionic dye mixed configuration forms, and disperse dyes account for 50% in mixed dye, fabric hair when dyeing
The bath raio of embryo and mixed dye is 1:5;The disperse dyes are to be prepared from the following materials by weight:Divide S-5BL red
It is 84 parts beautiful, divide GS bright red 619 parts, divides red 169 parts of (Ya Bang) FB, 900 parts of glacial acetic acid (HAC), 600 parts of levelling agent (NL) and chelating
950 parts of agent (M-175);The dye of positive ion is to be prepared from the following materials by weight:SD-BL cationic blues 134
630 parts of part, 85 parts of SD-RL cationic blues, bright blue 385 parts of SD-GB cations, 1100 parts of glacial acetic acid (HAC) and urea.
Real-time example 2.The dichromatism one-bath process method (dark brown/yellow fabric) of cationic terylene composite material, including with
Lower step:
1. being twisted respectively to ordinary polyester and cationic terylene;
2. being carried out shaping respectively with cationic terylene to the ordinary polyester after twisting, setting temperature is 70 DEG C, setting time
It is 100 minutes;
It is weaved after into the different face of inside and outside two sides structure 3. passing through with cationic terylene the ordinary polyester after sizing leading
Expect that blank, the ordinary polyester content of fabric blank wherein one side are more than cationic terylene, the cationic terylene content of another side is big
In ordinary polyester, (surface layer of fabric blank is interwoven using five pieces of Warp Satins, the inner layer of fabric blank is using 12 pieces of warps
Face satin weave is interwoven) fabric blank weaving when loom speed be 540 revs/min;
4. carrying out desizing to fabric blank, temperature of the fabric blank in desizing is 98 DEG C, and movement speed is 35 ms/min
Clock, the desizing liquid for being added with 9g lye using every liter when desizing, the lye by weight, be prepared by following raw material and
At:3500 parts of a concentration of 30% sodium hydroxide liquid caustic soda, 1800 parts of hydrogen peroxide, (906) 1100 parts of degreaser, chelating agent (M-
175) 900 parts and Nx1000 parts of refining agent;Bath raio (weight ratio) of the desizing liquid in desizing is 1:5;
5. being put into neutralization pond to the fabric blank after desizing, the pH value of fabric blank is set to reach by being slowly added to neutralizer
To 7;Acid solution containing 7g in every liter of neutralizer, acid solution are prepared from the following materials by weight:Glacial acetic acid
(HAC) 1000 parts and 45 parts of peregal;
6. preshrunk:By the fabric blank after neutralization after the cleaning of preshrunk liquid, decatize 30 minutes in 105 DEG C of steam box are put into,
Lye containing 7~9g in every liter of preshrunk liquid, the lye are prepared from the following materials by weight:32% concentration
9000 parts of sodium hydroxide liquid caustic soda, 1 part of olive oil 2100 parts of (TF-106B) and WA refining agents;
7. carrying out pre-setting to the fabric blank after preshrunk, pre-setting temperature is 195 DEG C, and fabric blank is in pre-setting
It is 50 ms/min to move speed;
8. alkali number:Fabric blank after pre-setting is put into 96 DEG C of lye and is impregnated 30 minutes, which is 8g/
L;
It is dyed 9. the fabric blank after alkali number is put into mixed dye, the mixed dye is by disperse dyes and sun
Ionic dye mixed configuration forms, and disperse dyes account for 60% in mixed dye, fabric hair when dyeing
The bath raio of embryo and mixed dye is 1:5;The disperse dyes are to be prepared from the following materials by weight:Divide F-2G blue
84 parts, divide 165 parts of 165%S-2G carbunclies, yellowish-brown 116 parts of 200% point of S-2R, 1100 parts of glacial acetic acid (HAC) and levelling agent (NL)
400 parts;The dye of positive ion is to be prepared from the following materials by weight:34 parts of SD-2RL cationic yellows, SD-2GL
700 parts of 375 parts of cationic golden yellow, 1000 parts of glacial acetic acid (HAC) and urea.
Real-time example 3.The dichromatism one-bath process method (black/blue fabric) of cationic terylene composite material, including it is following
Step:
1. being twisted respectively to ordinary polyester and cationic terylene;
2. being carried out shaping respectively with cationic terylene to the ordinary polyester after twisting, setting temperature is 65 DEG C, setting time
It is 100 minutes;
It is weaved after into the different face of inside and outside two sides structure 3. passing through with cationic terylene the ordinary polyester after sizing leading
Expect that blank, the ordinary polyester content of fabric blank wherein one side are more than cationic terylene, the cationic terylene content of another side is big
In ordinary polyester, (surface layer of fabric blank is interwoven using five pieces of Warp Satins, the inner layer of fabric blank is using 15 pieces of warps
Face satin weave is interwoven) fabric blank weaving when loom speed be 540 revs/min;
4. carrying out desizing to fabric blank, temperature of the fabric blank in desizing is 98 DEG C, and movement speed is 40 ms/min
Clock, the desizing liquid for being added with 8g lye using every liter when desizing, the lye by weight, be prepared by following raw material and
At:3000 parts of a concentration of 30% sodium hydroxide liquid caustic soda, 2000 parts of hydrogen peroxide, (906) 1000 parts of degreaser, chelating agent (M-
175) 1000 parts and Nx1000 parts of refining agent;Bath raio (weight ratio) of the lye in desizing is 1:5;
5. being put into neutralization pond to the fabric blank after desizing, the pH value of fabric blank is set to reach by being slowly added to neutralizer
To 7;Acid solution containing 8g in every liter of neutralizer, acid solution are prepared from the following materials by weight:Glacial acetic acid
(HAC) 1000 parts and 50 parts of peregal;
6. preshrunk:By the fabric blank after neutralization after the cleaning of preshrunk liquid, decatize 30 minutes in 105 DEG C of steam box are put into,
Lye containing 7~9g in every liter of preshrunk liquid, the lye are prepared from the following materials by weight:32% concentration
10000 parts of sodium hydroxide liquid caustic soda, olive oil 2000 parts of (TF-106B), 2 parts of WA refining agents, 3000 parts of chelating agent (M-175) and essence
Refine 200 parts of agent (Q-2C);
7. carrying out pre-setting to the fabric blank after preshrunk, pre-setting temperature is 190 DEG C, and fabric blank is in pre-setting
It is 40 ms/min to move speed;
8. alkali number:Fabric blank after pre-setting is put into 95 DEG C of lye and is impregnated 30 minutes, which is 8g/
L;
It is dyed 9. the fabric blank after alkali number is put into mixed dye, the mixed dye is by disperse dyes and sun
Ionic dye mixed configuration forms, and disperse dyes account for 60% in mixed dye, fabric hair when dyeing
The bath raio of embryo and mixed dye is 1:5;The disperse dyes are to be prepared from the following materials by weight:400% point
Black 804 parts of SE-DB divides 20 parts of 165%S-2G carbunclies, yellowish-brown 100 parts of 200% point of S-2R, 1500 parts of glacial acetic acid (HAC), level dyeing
1000 parts of 500 parts of agent (NL) and chelating agent (M-175);The dye of positive ion by weight, be prepared by following raw material and
At:32 parts of SD-GSL cationic blues, bright blue 36 parts of SD-GB cations, SD-BRL cations are deep 22 parts green, glacial acetic acid (HAC) 900
600 parts of part and urea.
Claims (10)
1. the dichromatism one-bath process method of cationic terylene composite material, it is characterised in that:By ordinary polyester and cationic terylene
Respectively through twisting, shape, lead after weaving and form the different fabric blank of inside and outside two sides structure, then fabric blank is refined,
It is put into mixed dye and is dyed after preshrunk, pre-setting and alkali number.
2. the dichromatism one-bath process method of cation terylene composite material according to claim 1, it is characterised in that:It is described
Mixed dye is formed by disperse dyes and dye of positive ion mixed configuration, and when dyeing, the bath raio of mixed dye is 1:5.
3. the dichromatism one-bath process method of cation terylene composite material according to claim 2, it is characterised in that:It is described
Disperse dyes account for 50%~60% in mixed dye.
4. the dichromatism one-bath process method of cation terylene composite material according to claim 2, it is characterised in that:It is described
Disperse dyes are to be prepared from the following materials by weight:100~920 parts of non-cationic dyestuff, glacial acetic acid 900~
1500 parts and 400~600 parts of levelling agent.
5. the dichromatism one-bath process method of cation terylene composite material according to claim 1, it is characterised in that:It is described
Refining include the desizing and neutralization that carry out successively, wherein temperature of the fabric blank in desizing is 95 DEG C~98 DEG C, mobile speed
Degree is 35~45 ms/min;The desizing liquid for being added with 7~9g lye using every liter when desizing, the lye by weight, are
It is prepared from the following materials:2500~3500 parts of sodium hydroxide liquid caustic soda, 1800~2200 parts of hydrogen peroxide, degreaser 800~
1100 parts, 900~1000 parts of chelating agent and refining agent Nx900~1000 part;The bath raio of desizing liquid is 1 when desizing:5.
6. the dichromatism one-bath process method of cation terylene composite material according to claim 5, it is characterised in that:It is described
Neutralization be that the fabric blank after desizing is put into neutralization pond, so that the pH value of fabric blank is reached by being slowly added to desizing liquid
7;Acid solution containing 7~9g in every liter of neutralizer, the acid solution are prepared from the following materials by weight:Glacial acetic acid
900~1000 parts and 45~60 parts of peregal.
7. the dichromatism one-bath process method of cation terylene composite material according to claim 1, it is characterised in that:It is described
Preshrunk be fabric blank after refining after the cleaning of preshrunk liquid, be put into steam box that decatize 30 is divided at 100 DEG C~105 DEG C
Clock, the lye containing 7~9g in every liter of preshrunk liquid.
8. the dichromatism one-bath process method of cation terylene composite material according to claim 7, it is characterised in that:It is described
Lye in preshrunk liquid is to be prepared from the following materials by weight:9000~10000 parts of sodium hydroxide liquid caustic soda, olive oil
1800~2100 parts and 1~2 part of WA refining agents.
9. the dichromatism one-bath process method of cation terylene composite material according to claim 1, it is characterised in that:It is described
Alkali number be that the fabric blank after pre-setting is put into lye to impregnate 30 minutes, the temperature of lye is 90 DEG C~96 DEG C, lye
A concentration of 8g/L.
10. the dichromatism one-bath process method of cation terylene composite material according to claim 1, it is characterised in that:Institute
It is temperature 60 C~70 DEG C, setting time 100~120 minutes to state technological parameter when sizing;The technological parameter when weaving
For 540 revs/min of speed;The technological parameter when pre-setting is 180 DEG C~195 DEG C of pre-setting temperature, and fabric is in pre-setting
When movement speed be 40~50 ms/min.