CN108541718A - A kind of negative ion air purifying material and preparation method thereof - Google Patents
A kind of negative ion air purifying material and preparation method thereof Download PDFInfo
- Publication number
- CN108541718A CN108541718A CN201810555555.0A CN201810555555A CN108541718A CN 108541718 A CN108541718 A CN 108541718A CN 201810555555 A CN201810555555 A CN 201810555555A CN 108541718 A CN108541718 A CN 108541718A
- Authority
- CN
- China
- Prior art keywords
- parts
- negative ion
- air purifying
- ion air
- tourmaline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of negative ion air purifying materials and preparation method thereof, negative ion air purifying material provided by the invention, existing tourmaline anion releasable material is improved and processed, on the basis of using tourmaline as base-material, add rare earth oxide, semiconductor catalysis material, Strange ice stone powder, graphene complex, sterilize Chinese herbal medicine powder, it is more thorough that above-mentioned each ingredient promotes the performance of tourmaline to play, the anion of release dramatically increases, simultaneously, sterilization Chinese herbal medicine powder is also added into formula to remove the harmful substances such as bacterium in air, finally so that indoor air is purified well.The anion release rate of the negative ion air purifying material of the present invention can reach 9000/cm3More than, substantially increase burst size.
Description
Technical field
The invention belongs to building material technical fields, and in particular, to a kind of negative ion air purifying material and its preparation
Method.
Background technology
Daily living environment is required with the improvement of people ' s living standards it is also higher and higher, but house decoration when
The largely building materials containing harmful substance are waited, the body of people has been arrived in pernicious gases, the thus grievous injury such as meeting release formaldehyde mostly
Body health；Therefore people need a kind of ep-type material for the environment that purifies the air of a room, and can discharge anion, purify air.
Existing artificial anion mainly use high-voltage electrostatic field, high-frequency electric field, ultraviolet light, radioactive ray and water the side such as shock
Method makes air ionization, generates anion, presently mainly uses anion generator, corona anion generator is in 3000V
Under above high pressure, makes air ionization and generate anion.The disadvantage of this method is to generate ozonation by-product, easily lure
Send out artery sclerosis and cancer etc..Excessively high negative ion concentration also has harmful effect to human body.There is also consumption electric energy, actual effects simultaneously
Property difference disadvantage.
Chinese patent CN1179754C disclose a kind of composition tourmaline powder body that can efficiently generate negative aeroion and its
Preparation method, the composite granule ingredient be polar mineral tourmaline, rare earth complex salt or rare earth oxide and photocatalysis half
Conductor material.The airion concentration that the composite granule generates only has 1000-1200/cm3Low yield.
Chinese patent CN1765802A discloses ultra-fine efficient anion powder material of one kind and preparation method thereof, the powder
Material includes natural negative ion releasable material, excitation material and energy transmission material.The preparation method of the powder body material is by day
It is added directly into ball mill and grinds with energy transmission material after right anion releasable material and the direct mechanical crushing of excitation material
Mill, then plus water is made into slurry, is ground again after adding dispersant, and dry, regrinding obtains.The air that the composite granule generates
Ion concentration also only has 2000/cm3Left and right.
To solve the above-mentioned problems, a kind of negative ion air purifying material of present invention offer and preparation method thereof.
Invention content
For the defects in the prior art, the object of the present invention is to provide a kind of negative ion air purifying material and preparation sides
Method.
According to a kind of negative ion air purifying material provided by the invention, the negative ion air purifying material includes such as
The raw material of lower parts by weight：26-43 parts of tourmaline, 7-12 parts of rare earth oxide, 2-11 parts of semiconductor catalysis material, Strange ice stone powder
5-13 parts 5-9 parts last, 7-15 parts of graphene complex, sterilization of Chinese herbal medicine powder.
Tourmaline is due to the asymmetry on c-axis, and electrical operation makes there is electrode generation in itself, i.e., for good and all at one end
It generates " positive electrode ", " negative electrode " is generated in the other end.Positive electrode can absorb anion, and by tourmaline itself charge
" conveying " arrives negative electrode, and the anion that the anion and negative electrode itself that these charges generate generate releases, continually
Ground flies to positive electrode outside crystal along power line, forms the electric field to move in endless cycles.But simple tourmaline powder bear from
Sub- releasability is very weak, and the concentration for discharging anion is also not enough to eliminate the pollution of people's living environment.
Negative ion air purifying material provided by the invention improves existing tourmaline anion releasable material
And processing, on the basis of using tourmaline as base-material, addition rare earth oxide, semiconductor catalysis material, Strange ice stone powder, graphite
Alkene compound, sterilization Chinese herbal medicine powder, it is more thorough that above-mentioned each ingredient promotes the performance of tourmaline to play, and the anion of release is notable
Increase, meanwhile, it is also added into sterilization Chinese herbal medicine powder in formula, the harmful substances such as bacterium in air are removed, finally makes
Indoor air is obtained to be purified well.
Preferably, the negative ion air purifying material includes the raw material of following parts by weight：26-33 parts of tourmaline,
9-12 parts of rare earth oxide, 5-11 parts of semiconductor catalysis material, 6-9 parts of Strange ice stone powder, 9-15 parts of graphene complex, sterilization
7-13 parts of Chinese herbal medicine powder.
Preferably, the negative ion air purifying material includes the raw material of following parts by weight：31 parts of tourmaline, rare earth
9 parts 11 parts of oxide, 7 parts of semiconductor catalysis material, 8 parts of Strange ice stone powder, 13 parts of graphene complex, sterilization of Chinese herbal medicine powder.
After proportioning between above-mentioned each ingredient by above-mentioned amount, anion air purifying material that the formula of composition is prepared
Expect that anion release is most, and bactericidal effect is best, wherein 31 parts of tourmaline, 11 parts of rare earth oxide, semiconductor catalysis material
7 parts, 13 parts of graphene complex, 9 parts of Chinese herbal medicine powder of sterilization mutually synergistic effect play crucial effect.
Preferably, the rare earth oxide is one kind or two in cerium oxide, lanthana, niobium oxide and erbium oxide
Kind.
Preferably, the semiconductor catalysis material is titanium dioxide, zinc oxide, silver oxide, vanadic anhydride, three oxidations
It is one or two kinds of in two boron and tin oxide.
After rare earth oxide is combined with the other compositions in raw material, tourmaline release anion is promoted.
Preferably, the graphene complex is calcium ferrite graphene complex.
Calcium ferrite under visible light can effective photocatalytic degradation pernicious gas.And it can be between graphene and calcium ferrite
Chemical bond is formed, the photocatalytic activity of calcium ferrite can be enhanced, promotes the decomposition to air pernicious gas, plays air purification
Effect.
Preferably, the preparation method of the calcium ferrite graphene complex is as follows：
（1）The graphene oxide for weighing 0.06 gram, is added the EtOH Sonicate 20min of 40ml, 5 grams of calcium ferrites is added to and have been surpassed
In the graphene oxide solution of sound, stir 15 minutes；
（2）Above-mentioned solution is moved in reaction kettle 150 DEG C, is reacted 2 hours, is washed with water to neutrality, dried at 50 DEG C, i.e.,
It can.
The quality for the calcium ferrite graphene complex being prepared by above-mentioned operation and specific parameter is best.
Preferably, the sterilization Chinese herbal medicine powder ingredient includes：Radix Glycyrrhizae, kuh-seng, myrobalan.
Radix Glycyrrhizae：Alias state is old, Herba Hedyotis cantonensis, has the effects that clearing heat and detoxicating, sterilization；
Myrobalan：In vitro test shows：Myrobalan's water decoction（100%）Have inhibiting effect to various shigella dysenteriaes, to Pseudomonas aeruginosa,
The effect of corynebacterium diphtheriae is stronger, to staphylococcus aureus, Escherichia coli, pneumococcus, hemolytic streptococcus, proteus,
Bacillus typhi murium also has inhibiting effect（Flat band method）, to staphylococcus aureus, the sense of green pus bar, shigella dysenteriae effective concentration
Respectively 1:128、1:64、1:32（Test tube method）, in addition, myrobalan in vitro also has typhoid bacillus good antibacterial action.
Kuh-seng：Bitter；It is cold in nature, hot eliminating dampness；Wind dispelling insecticide.
The bacterium harmful substance in air can will be purged after above-mentioned three kinds of Chinese herbal medicine compatibilities, has purified air.
Preferably, the Radix Glycyrrhizae, kuh-seng, myrobalan mass ratio be 1:2-5:3-7.
Bactericidal effect after the proportioning of above-mentioned three kinds of Chinese herbal medicines is preferable.
A kind of preparation method of negative ion air purifying material, the preparation method include the following steps：
Step 1: tourmaline powder is broken to 300-500 mesh, and 0.5-2h is roasted at 500-600 DEG C；
Ultra-fine grinding is carried out Step 2: the tourmaline after roasting is added in milling apparatus, until particle diameter distribution is 400-
600nm；
Step 3: when grinding closes to an end, surface conditioning agent is added and is surface-treated；
Step 4: by rare earth oxide, semiconductor catalysis material, Strange ice stone powder, graphene complex, sterilization Chinese herbal medicine powder,
It is ground to particle diameter distribution and is less than 1 μm；
Step 5: putting into high speed dispersor and disperseing step 3 and step 4 product according to the ratio, it is sieved, is drying to obtain.
The negative ion air purifying material preparation method is simple, and the product anion release being prepared is more.
Compared with prior art, the present invention has following advantageous effect：
A kind of negative ion air purifying material provided by the invention, negative ion air purifying material provided by the invention, to existing
Tourmaline anion releasable material improved and processed, on the basis of using tourmaline as base-material, add rare-earth oxidation
Object, semiconductor catalysis material, Strange ice stone powder, graphene complex, sterilization Chinese herbal medicine powder, above-mentioned each ingredient promote tourmaline
Performance performance is more thorough, and the anion of release dramatically increases, meanwhile, sterilization Chinese herbal medicine powder is also added into formula in air
The harmful substances such as bacterium removed, finally so that indoor air is purified well.The anion of the present invention is empty
The anion release rate of gas scavenging material can reach 9000/cm3More than, substantially increase burst size.
Specific implementation mode
Present invention will be further explained below with reference to specific examples.It should be understood that these embodiments are merely to illustrate the present invention
Rather than it limits the scope of the invention.
Embodiment 1
A kind of negative ion air purifying material provided in this embodiment, the negative ion air purifying material include following weight
The raw material of number：43 parts of tourmaline, 7 parts of rare earth oxide, 11 parts of semiconductor catalysis material, 5 parts of Strange ice stone powder, graphene are multiple
Close 5 parts 15 parts of object, sterilization of Chinese herbal medicine powder.
Preferably, the rare earth oxide be cerium oxide, lanthana, niobium oxide and erbium oxide in one kind or
Two kinds of person.
Preferably, the semiconductor catalysis material be titanium dioxide, zinc oxide, silver oxide, vanadic anhydride,
It is one or two kinds of in diboron trioxide and tin oxide.
Preferably, the graphene complex is calcium ferrite graphene complex.
Preferably, the preparation method of the calcium ferrite graphene complex is as follows：
（1）The graphene oxide for weighing 0.06 gram, is added the EtOH Sonicate 20min of 40ml, 5 grams of calcium ferrites is added to and have been surpassed
In the graphene oxide solution of sound, stir 15 minutes；
（2）Above-mentioned solution is moved in reaction kettle 150 DEG C, is reacted 2 hours, is washed with water to neutrality, dried at 50 DEG C, i.e.,
It can.
Preferably, the sterilization Chinese herbal medicine powder ingredient includes：Radix Glycyrrhizae, kuh-seng, myrobalan.
Preferably, the Radix Glycyrrhizae, kuh-seng, myrobalan mass ratio be 1:2-5:3-7.
The building materials obtained after resting under these conditions, quality higher.
A kind of preparation method of negative ion air purifying material, the preparation method include the following steps：
Step 1: tourmaline powder is broken to 500 mesh, and 2h is roasted at 500 DEG C；
Ultra-fine grinding is carried out Step 2: the tourmaline after roasting is added in milling apparatus, until particle diameter distribution is 600nm；
Step 3: when grinding closes to an end, surface conditioning agent is added and is surface-treated；
Step 4: by rare earth oxide, semiconductor catalysis material, Strange ice stone powder, graphene complex, sterilization Chinese herbal medicine powder,
It is ground to particle diameter distribution and is less than 1 μm；
Step 5: putting into high speed dispersor and disperseing step 3 and step 4 product according to the ratio, it is sieved, is drying to obtain.
Embodiment 2
A kind of negative ion air purifying material provided in this embodiment, the negative ion air purifying material include following weight
The raw material of number：26 parts of tourmaline, 12 parts of rare earth oxide, 5 parts of semiconductor catalysis material, 9 parts of Strange ice stone powder, graphene are multiple
Close 13 parts 9 parts of object, sterilization of Chinese herbal medicine powder.
Preferably, the rare earth oxide be cerium oxide, lanthana, niobium oxide and erbium oxide in one kind or
Two kinds of person.
Preferably, the semiconductor catalysis material be titanium dioxide, zinc oxide, silver oxide, vanadic anhydride,
It is one or two kinds of in diboron trioxide and tin oxide.
Preferably, the graphene complex is calcium ferrite graphene complex.
Preferably, the preparation method of the calcium ferrite graphene complex is as follows：
（1）The graphene oxide for weighing 0.06 gram, is added the EtOH Sonicate 20min of 40ml, 5 grams of calcium ferrites is added to and have been surpassed
In the graphene oxide solution of sound, stir 15 minutes；
（2）Above-mentioned solution is moved in reaction kettle 150 DEG C, is reacted 2 hours, is washed with water to neutrality, dried at 50 DEG C, i.e.,
It can.
Preferably, the sterilization Chinese herbal medicine powder ingredient includes：Radix Glycyrrhizae, kuh-seng, myrobalan.
Preferably, the Radix Glycyrrhizae, kuh-seng, myrobalan mass ratio be 1:2:7.
The building materials obtained after resting under these conditions, quality higher.
A kind of preparation method of negative ion air purifying material, the preparation method include the following steps：
Step 1: tourmaline powder is broken to 300 mesh, and 0.5h is roasted at 600 DEG C；
Ultra-fine grinding is carried out Step 2: the tourmaline after roasting is added in milling apparatus, until particle diameter distribution is 400nm；
Step 3: when grinding closes to an end, surface conditioning agent is added and is surface-treated；
Step 4: by rare earth oxide, semiconductor catalysis material, Strange ice stone powder, graphene complex, sterilization Chinese herbal medicine powder,
It is ground to particle diameter distribution and is less than 1 μm；
Step 5: putting into high speed dispersor and disperseing step 3 and step 4 product according to the ratio, it is sieved, is drying to obtain.
Embodiment 3
A kind of negative ion air purifying material provided in this embodiment, the negative ion air purifying material include following weight
The raw material of number：31 parts of tourmaline, 11 parts of rare earth oxide, 7 parts of semiconductor catalysis material, 8 parts of Strange ice stone powder, graphene are multiple
Close 9 parts 13 parts of object, sterilization of Chinese herbal medicine powder.
Preferably, the rare earth oxide be cerium oxide, lanthana, niobium oxide and erbium oxide in one kind or
Two kinds of person.
Preferably, the semiconductor catalysis material be titanium dioxide, zinc oxide, silver oxide, vanadic anhydride,
It is one or two kinds of in diboron trioxide and tin oxide.
Preferably, the graphene complex is calcium ferrite graphene complex.
Preferably, the preparation method of the calcium ferrite graphene complex is as follows：
（1）The graphene oxide for weighing 0.06 gram, is added the EtOH Sonicate 20min of 40ml, 5 grams of calcium ferrites is added to and have been surpassed
In the graphene oxide solution of sound, stir 15 minutes；
（2）Above-mentioned solution is moved in reaction kettle 150 DEG C, is reacted 2 hours, is washed with water to neutrality, dried at 50 DEG C, i.e.,
It can.
Preferably, the sterilization Chinese herbal medicine powder ingredient includes：Radix Glycyrrhizae, kuh-seng, myrobalan.
Preferably, the Radix Glycyrrhizae, kuh-seng, myrobalan mass ratio be 1:3:5.
The building materials obtained after resting under these conditions, quality higher.
A kind of preparation method of negative ion air purifying material, the preparation method include the following steps：
Step 1: tourmaline powder is broken to 400 mesh, and 1h is roasted at 550 DEG C；
Ultra-fine grinding is carried out Step 2: the tourmaline after roasting is added in milling apparatus, until particle diameter distribution is 500nm；
Step 3: when grinding closes to an end, surface conditioning agent is added and is surface-treated；
Step 4: by rare earth oxide, semiconductor catalysis material, Strange ice stone powder, graphene complex, sterilization Chinese herbal medicine powder,
It is ground to particle diameter distribution and is less than 1 μm；
Step 5: putting into high speed dispersor and disperseing step 3 and step 4 product according to the ratio, it is sieved, is drying to obtain.
Performance test：
Each raw material is weighed according to the proportional quantity of embodiment 1,2,3：
Embodiment 1：43 parts of tourmaline, 7 parts of rare earth oxide, 11 parts of semiconductor catalysis material, 5 parts of Strange ice stone powder, graphene
5 parts 15 parts of compound, sterilization of Chinese herbal medicine powder.
Embodiment 2：26 parts of tourmaline, 12 parts of rare earth oxide, 5 parts of semiconductor catalysis material, 9 parts of Strange ice stone powder, stone
13 parts 9 parts of black alkene compound, sterilization of Chinese herbal medicine powder.
Embodiment 3：31 parts of tourmaline, 11 parts of rare earth oxide, 7 parts of semiconductor catalysis material, 8 parts of Strange ice stone powder, stone
9 parts 13 parts of black alkene compound, sterilization of Chinese herbal medicine powder.
The above-mentioned corresponding embodiment of the numeric reference of other raw materials or parameter.
Preparation method according to the invention is prepared the corresponding negative ion air purifying material of each embodiment, takes simultaneously
As a comparison case, acetylene powder is with grain through the grain with embodiment 1 or embodiment 2 or embodiment 3 for powder after acetylene crushing
Through suitable, the powder of embodiment 2, embodiment 1, embodiment 3 and comparative example is respectively placed in seal box, powder body material is uniform
Spread out, it is closed for 24 hours, detected with the AIC-1000 that Alphalab companies of the U.S. produce, as a result such as following table
| Index | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example |
| Negative ion concentration（A/cm3） | 9812 | 9760 | 9832 | 2300 |
| Negative ion concentration increment rate（%） | 326 | 324 | 327 | - |
Upper table analysis can obtain：
Negative ion concentration is discharged in table（A/cm3）Sequence from more to less is followed successively by embodiment 3, embodiment 1, embodiment 2, and
And it is all higher than the release negative ion concentration of comparative example（A/cm3）.The release negative ion concentration of embodiment 3（A/cm3）At most, by
The formula composition of this visible embodiment 3 and mutual weight proportion are relative optimizations, in formula, wherein tourmaline
31 parts, 11 parts of rare earth oxide, 7 parts of semiconductor catalysis material, 13 parts of graphene complex, 9 parts of Chinese herbal medicine powder of sterilization mutually association
Same-action plays crucial effect.
Negative ion concentration increment rate in table（%）Descending sequence is followed successively by embodiment 3, embodiment 1, embodiment 2, most
Big increases by 327%.
In conclusion a kind of negative ion air purifying material provided by the invention, anion discharges more, air purification effect
It is good, it is worthy of popularization.
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (10)
1. a kind of negative ion air purifying material, it is characterised in that：The negative ion air purifying material includes following weight
The raw material of number：26-43 parts of tourmaline, 7-12 parts of rare earth oxide, 2-11 parts of semiconductor catalysis material, Strange ice stone powder 5-9
5-13 parts part, 7-15 parts of graphene complex, sterilization of Chinese herbal medicine powder.
2. a kind of negative ion air purifying material according to claim 1, it is characterised in that：The anion air is net
Change the raw material that material includes following parts by weight：26-33 parts of tourmaline, 9-12 parts of rare earth oxide, semiconductor catalysis material 5-
11 parts, 6-9 parts of Strange ice stone powder, 9-15 parts of graphene complex, sterilization 7-13 parts of Chinese herbal medicine powder.
3. a kind of negative ion air purifying material according to claim 1, it is characterised in that：The anion air is net
Change the raw material that material includes following parts by weight：31 parts of tourmaline, 11 parts of rare earth oxide, 7 parts of semiconductor catalysis material, strange ice
9 parts 8 parts of stone powder, 13 parts of graphene complex, sterilization of Chinese herbal medicine powder.
4. a kind of negative ion air purifying material according to claim 1, it is characterised in that：The rare earth oxide is oxygen
Change one or two kinds of in cerium, lanthana, niobium oxide and erbium oxide.
5. a kind of negative ion air purifying material according to claim 1, it is characterised in that：The semiconductor is catalyzed material
Material is one or two kinds of in titanium dioxide, zinc oxide, silver oxide, vanadic anhydride, diboron trioxide and tin oxide.
6. a kind of negative ion air purifying material according to claim 1, it is characterised in that：The graphene complex is
Calcium ferrite graphene complex.
7. a kind of negative ion air purifying material according to claim 6, it is characterised in that：The calcium ferrite graphene is multiple
The preparation method for closing object is as follows：
（1）The graphene oxide for weighing 0.06 gram, is added the EtOH Sonicate 20min of 40ml, 5 grams of calcium ferrites is added to and have been surpassed
In the graphene oxide solution of sound, stir 15 minutes；
（2）Above-mentioned solution is moved in reaction kettle 150 DEG C, is reacted 2 hours, is washed with water to neutrality, dried at 50 DEG C, i.e.,
It can.
8. a kind of negative ion air purifying material according to claim 7, it is characterised in that：The sterilization Chinese herbal medicine powder at
Divide and includes：Radix Glycyrrhizae, kuh-seng, myrobalan.
9. a kind of negative ion air purifying material according to claim 8, it is characterised in that：The Radix Glycyrrhizae, kuh-seng, myrobalan
Mass ratio be 1:2-5:3-7.
10. a kind of preparation method of negative ion air purifying material according to claim 1, it is characterised in that：The system
Preparation Method includes the following steps：
Step 1: tourmaline powder is broken to 300-500 mesh, and 0.5-2h is roasted at 500-600 DEG C；
Ultra-fine grinding is carried out Step 2: the tourmaline after roasting is added in milling apparatus, until particle diameter distribution is 400-
600nm；
Step 3: when grinding closes to an end, surface conditioning agent is added and is surface-treated；
Step 4: by rare earth oxide, semiconductor catalysis material, Strange ice stone powder, graphene complex, sterilization Chinese herbal medicine powder,
It is ground to particle diameter distribution and is less than 1 μm；
Step 5: putting into high speed dispersor and disperseing step 3 and step 4 product according to the ratio, it is sieved, is drying to obtain.