CN108531765A - A kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of brown and its technique - Google Patents
A kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of brown and its technique Download PDFInfo
- Publication number
- CN108531765A CN108531765A CN201810820107.9A CN201810820107A CN108531765A CN 108531765 A CN108531765 A CN 108531765A CN 201810820107 A CN201810820107 A CN 201810820107A CN 108531765 A CN108531765 A CN 108531765A
- Authority
- CN
- China
- Prior art keywords
- corrosion
- temperature
- billons
- brown
- high intensity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of brown and its techniques.According to weight percent, the ingredient of the alloy is:Sr:0.3‑0.5wt.%,P:0.2‑0.4wt.%,Rh:1.5‑1.8wt.%,V:1.2‑1.6wt.%,Cu:15.0‑18.0wt.%,Co:20.0‑22.0wt.%,Au:41.0 42.0wt.%, surplus are silver.The patent solves the insufficient present situation of the reddish brown golden performances of current K, and effectively breaches the development bottleneck in field of jewelry.It is contemplated that the implementation and industrialization of the material can obtain plentiful and substantial economic gain and social benefit.
Description
Technical field
The present invention relates to technical field of alloy, specifically, being related to a kind of billon.
Background technology
Gold has high erosion-resisting stability, good electric conductivity and thermal conductivity.Gold also has good craftsmanship,
Easily it is processed into ultra-thin goldleaf, micron spun gold and bronze.Gold is easy on the surface for being plated to other metals and pottery and glass,
Gold is easy by melting welding and smithwelding under certain pressure.These numerous functional characteristics make gold or billon use modern height extensively
In new technological industry, such as electronic technology, mechanics of communication, aerospace flight technology, Chemical Engineering Technology, medical technology.
Golden initial functions as jewellery and decorative material material and obtains the attention of people.With the development of the times and people
People's improvement of living standard, the aesthetic idea of people are also constantly promoted, and noble metal jewelry is more and more by vast consumption
The favor of person.Proof gold due to too soft, it is recent be no longer most popular breeding in the market.Due to controlling different add
Added elements and content can control the performance color of billon, thus the jewellery of billon preparation or ornament materials are on the market
It is more favourable.International K of generally use is made to weigh the content of gold, thus billon is also referred to as karat gold.
The technology that karat gold jewellery are born with its unique essence, has won the heart of people, it will be filled with mysterious, illusion color
Natural gemstone dexterously combines together with karat gold, shows charming elegance.Although the history that karat gold jewellery produce in China is not grown,
But between from it after generation, sweep the country immediately.Karat gold can produce the ornaments of more multi-configuration item, meet the heart that modern follows the fashion
Reason, meets the aesthetic requirement of modern.Currently, traditional gold ornaments has been subjected to the impact of colourful karat gold jewelry, by
It is more in karat gold ornaments color, it is handsome in appearance, it is cheap, it will to be increasingly accepted by people and like.
Why welcome karat gold jewellery are, this is because its many aspect is better than proof gold jewellery.Proof gold jewellery are softer, are easy
Deformation and abrasion.And karat gold jewellery are due to adding other metals into billon, it is corrosion-resistant at both wear-resisting, and be unlikely to deform
Alloying metal.Since the raising of golden hardness promotes the fast development of jewellery industry, traditional-handwork processing for thousands of years is broken
The custom of jewellery also changes originally backward processing technology.Present processing of ornament not only plates, also nail edge, pawl edge etc..
This, which is proof gold jewellery, to accomplish.Karat gold various colors, and proof gold jewellery are a kind of color, i.e. golden true qualities.Karat gold
Occur, people are brought in a multicoloured world.When proof gold is cleverly combined with other metals, just will present different
Color.In addition, karat gold style is modish, and proof gold jewellery style is more dull, stiff.The style of K jewellery in the market, can be up to several
Ten thousand kinds, ten tens of thousands of kinds, its novelty, aesthetic feeling completely can be with times.
As the drawback of the differentiation in market, the aggravation of competition, the promotion of consumers' aesthetic grade, industry homogeneity highlights.K
Golden market is developing.Market more needs the karat gold product that personalized, fashion is graceful, and originality is full, design processing is first-class,
To meet brand personality demand.On the one hand the addition of karat gold ornaments alloy element improves the hardness of gold ornaments, to be suitble to make
On the other hand various gemmy jewellery can also change the color of karat gold ornaments by changing the ratio of the type of its ingredient.
The color of karat gold also has the type of brownish red in addition to yellow, white with outside red.Traditionally, it is formed when Pd is added in gold
Billon just have reddish brown color and luster.But regrettably, the addition of Pd can form intermetallic compound.And such is closed
Gold is passing through the phenomenon that often changing colour, the serious perception for affecting jewellery after using some months.
Although China's bullion industry, especially first jewelry alloy is quickly grown, and due to starting evening, starting point is low, one
Also there is a big difference compared with world level on a little sport technique segments.Industry problems do not solve for a long time, not only affect related production
The market sales volume and usage experience of product, also it is serious limit such product international scope market occupancy volume.Exploitation is simultaneously
It has been the inevitable problem of field of jewelry that industrialization, which has the brownish red karat gold of advanced feature, and domestic for a long time is very much
Research institution and enterprise have carried out multi-faceted trial, but regrettably, any substance is not yet obtained so far
Progress.Alloy material can be carried out by the thermodynamics and kinetics means of bottom by advanced design of material technology
Innovation, and prodigious market value is had to the problem solution and industrialization of developing and develop karat gold.In face of what is be growing more intense
Domestic and international market competes, it is necessary to and paces of accelerating restructuring, this is not only the needs of China's jewellery industry survival and development,
It is the development trend of world today's related field.
Invention content
The purpose of the present invention is to overcome the deficiency in the prior art, provides a kind of corrosion-resistant resistance to brittle failure high intensity 10K gold of brown
Alloy and its technique.
To achieve the goals above, the present invention adopts the following technical scheme that:
A kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of brown and its technique.By weight percentage, the group of alloy becomes
Sr:0.3-0.5wt.%,P:0.2-0.4wt.%,Rh:1.5-1.8wt.%,V:1.2-1.6wt.%,Cu:15.0-18.0wt.%,
Co:20.0-22.0wt.%,Au:41.0-42.0wt.%, surplus are silver.
The preparation method of a kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of above-mentioned brown and its technique, including walk as follows
Suddenly:As above the raw material matched is added in the electric induction furnace of argon gas protection, and uses graphite crucible;Using low after metal molten
The argon gas of flow is protected, and big air-flow is avoided to make the serious scaling loss of alloying element;10 minutes are kept the temperature at 1200 degree when melting, leans on high frequency
Induction furnace electromagnetic agitation is uniform;1 minute being kept the temperature at 1200 degree after stirring evenly and being cast come out of the stove;Billon casting uses diameter
The punching block of 50-100mm, and cooled down by the way of water cooling.The ingot casting of gained is rolled at room temperature, every time rolls lower amount
For 30-40%;It is 380 degree per intermediate anneal temperature after rolling twice, keeps the temperature 0.5 hour;Material, which is finally rolled into thickness, is
The golden plate of 10-20mm;In jewellery forming process, needs to carry out intermediate annealing process, eliminate the stress in process;Its
In, homogenization temperature is 350 degree, and the time is 1-2 hours.
Compared with prior art, the present invention has the advantages that:
(1)Traditionally, the billon formed when Pd is added in gold just has reddish brown color and luster.But regrettably,
The addition of Pd can form intermetallic compound.And such alloy is passing through the phenomenon that often changing colour after using some months, it is serious
Affect the perception of jewellery.This patent has carried out karat gold multi-faceted innovation and raising by advanced materialogy technology.Also
It is to say, it solves the colors that the reddish brown coloured gold materials of field of jewelry K are difficult to take into account, and corrosion resistance and processing performance cannot
The present situation obtained simultaneously.
(2)Traditional brownish red karat gold material composition is also uncomplicated, but dendritic segregation is serious after pouring into a mould, and is unfavorable for it and adds
Work performance and corrosion resistance.Homogenization Treatments must be carried out before processing, corrosion resistant when causing the cumbersome of process and using
Corrosion can be insufficient.The alloy of present patent application protection has close to eutectic structure, possesses best etch resistant properties and machining deformation
Performance.The generation of primary phase, and thinning microstructure can be efficiently controlled after casting.Meanwhile the alloy due to liquidus curve it is relatively low,
Thus it is suitable for casting.
(3)For the alloy of this patent when carrying out alloying component and performance optimizes, the screening of alloying component is first from electricity
From the point of view of chemical attack mechanisms, selection, which is added to the alloying element in billon, to form passivating film on surface, to right
Ambient enviroment corrosion plays a protective role.Alloying element be added is harmless, with skin contact without the effect of paying, inexpensive, money
Source is abundant.By the test of prolonged marine environment and desert Environment, the karat gold of present patent application protection can use 8-10
It remains to keep original brownish red quality in year, show to the extremely huge corrosion resistance of environment.
(4)Alloy optimization is carried out due to not having in traditional brown karat gold, a large amount of gold is produced in the tissue of alloy
Compound between category.The appearance of these compounds not only reduces the toughness of alloy, causes brittle fracture.Also serious to reduce
The processing performance and production cost of alloy.Thus commercial is limited, and the market sales volume is also little.This patent is due to carrying out
The innovation of materialogy, fundamentally reduces the forming amount of intermetallic compound.As alloy content is in the change of optimization range
Dynamic, the mechanical performance of the alloy can be adjusted significantly.Meanwhile the alloy due to liquidus curve it is relatively low, 850 degree are left
The right side, thus be suitable for casting.Since crystal grain is refined, hot cracking tendency is big when solving solution casting, and casting is empty and loose
Apparent product yield rate is low to wait technical barriers, thus has a vast market foreground.
Specific implementation mode
Embodiment 1
A kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of brown and its technique.By weight percentage, the group of alloy becomes
Sr:0.3wt.%,P:0.2wt.%,Rh:1.5wt.%,V:1.2wt.%,Cu:15.0wt.%,Co:20.0wt.%,Au:
41.0wt.%, surplus are silver.A kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of above-mentioned brown and its technique, including walk as follows
Suddenly:As above the raw material matched is added in the electric induction furnace of argon gas protection, and uses graphite crucible;Using low after metal molten
The argon gas of flow is protected, and big air-flow is avoided to make the serious scaling loss of alloying element;10 minutes are kept the temperature at 1200 degree when melting, leans on high frequency
Induction furnace electromagnetic agitation is uniform;1 minute being kept the temperature at 1200 degree after stirring evenly and being cast come out of the stove;Billon casting uses diameter
The punching block of 50-100mm, and cooled down by the way of water cooling.The ingot casting of gained is rolled at room temperature, every time rolls lower amount
For 30-40%;It is 380 degree per intermediate anneal temperature after rolling twice, keeps the temperature 0.5 hour;Material, which is finally rolled into thickness, is
The golden plate of 10-20mm;In jewellery forming process, needs to carry out intermediate annealing process, eliminate the stress in process;Its
In, homogenization temperature is 350 degree, and the time is 1-2 hours.
The alloy has close to eutectic structure, possesses best etch resistant properties and Deformation Properties of Al.Can have after casting
The generation of effect ground control primary phase, and thinning microstructure.Meanwhile the alloy due to liquidus curve it is relatively low, thus be suitable for casting.It closes
The screening of golden ingredient selects the alloying element being added in billon can be in table first from the point of view of Electrochemical Corrosion Mechanism
Face forms passivating film, to play a protective role to ambient enviroment corrosion.Alloying element be added is harmless, is connect with skin
It is tactile without side-effects, it is inexpensive, it is resourceful.By the test of prolonged marine environment and desert Environment, present patent application protection
Karat gold can remain to keep original brownish red quality in using 8-10, show extremely huge corrosion-resistant to environment
Ability.As alloy content is in the variation of optimization range, the mechanical performance of the alloy can be adjusted significantly.Together
When, the alloy is since liquidus curve is relatively low, 850 degree or so, thus is suitable for casting.Since crystal grain is refined, solve to understand
Hot cracking tendency is big when certainly casting, and casting cavity is low with loose apparent product yield rate to wait technical barriers.
Embodiment 2
A kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of brown and its technique.By weight percentage, the group of alloy becomes
Sr:0.5wt.%,P:0.4wt.%,Rh:1.8wt.%,V:1.6wt.%,Cu:18.0wt.%,Co:22.0wt.%,Au:
42.0wt.%, surplus are silver.A kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of above-mentioned brown and its technique, including walk as follows
Suddenly:As above the raw material matched is added in the electric induction furnace of argon gas protection, and uses graphite crucible;Using low after metal molten
The argon gas of flow is protected, and big air-flow is avoided to make the serious scaling loss of alloying element;10 minutes are kept the temperature at 1200 degree when melting, leans on high frequency
Induction furnace electromagnetic agitation is uniform;1 minute being kept the temperature at 1200 degree after stirring evenly and being cast come out of the stove;Billon casting uses diameter
The punching block of 50-100mm, and cooled down by the way of water cooling.The ingot casting of gained is rolled at room temperature, every time rolls lower amount
For 30-40%;It is 380 degree per intermediate anneal temperature after rolling twice, keeps the temperature 0.5 hour;Material, which is finally rolled into thickness, is
The golden plate of 10-20mm;In jewellery forming process, needs to carry out intermediate annealing process, eliminate the stress in process;Its
In, homogenization temperature is 350 degree, and the time is 1-2 hours.
The alloy has close to eutectic structure, possesses best etch resistant properties and Deformation Properties of Al.Can have after casting
The generation of effect ground control primary phase, and thinning microstructure.Meanwhile the alloy due to liquidus curve it is relatively low, thus be suitable for casting.It closes
The screening of golden ingredient selects the alloying element being added in billon can be in table first from the point of view of Electrochemical Corrosion Mechanism
Face forms passivating film, to play a protective role to ambient enviroment corrosion.Alloying element be added is harmless, is connect with skin
It is tactile without side-effects, it is inexpensive, it is resourceful.By the test of prolonged marine environment and desert Environment, present patent application protection
Karat gold can remain to keep original brownish red quality in using 8-10, show extremely huge corrosion-resistant to environment
Ability.As alloy content is in the variation of optimization range, the mechanical performance of the alloy can be adjusted significantly.Together
When, the alloy is since liquidus curve is relatively low, 850 degree or so, thus is suitable for casting.Since crystal grain is refined, solve to understand
Hot cracking tendency is big when certainly casting, and casting cavity is low with loose apparent product yield rate to wait technical barriers.
Embodiment 3
A kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of brown and its technique.By weight percentage, the group of alloy becomes
Sr:0.4wt.%,P:0.3wt.%,Rh:1.6wt.%,V:1.5wt.%,Cu:16.0wt.%,Co:21.0wt.%,Au:
41.0wt.%, surplus are silver.A kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of above-mentioned brown and its technique, including walk as follows
Suddenly:As above the raw material matched is added in the electric induction furnace of argon gas protection, and uses graphite crucible;Using low after metal molten
The argon gas of flow is protected, and big air-flow is avoided to make the serious scaling loss of alloying element;10 minutes are kept the temperature at 1200 degree when melting, leans on high frequency
Induction furnace electromagnetic agitation is uniform;1 minute being kept the temperature at 1200 degree after stirring evenly and being cast come out of the stove;Billon casting uses diameter
The punching block of 50-100mm, and cooled down by the way of water cooling.The ingot casting of gained is rolled at room temperature, every time rolls lower amount
For 30-40%;It is 380 degree per intermediate anneal temperature after rolling twice, keeps the temperature 0.5 hour;Material, which is finally rolled into thickness, is
The golden plate of 10-20mm;In jewellery forming process, needs to carry out intermediate annealing process, eliminate the stress in process;Its
In, homogenization temperature is 350 degree, and the time is 1-2 hours.
The alloy has close to eutectic structure, possesses best etch resistant properties and Deformation Properties of Al.Can have after casting
The generation of effect ground control primary phase, and thinning microstructure.Meanwhile the alloy due to liquidus curve it is relatively low, thus be suitable for casting.It closes
The screening of golden ingredient selects the alloying element being added in billon can be in table first from the point of view of Electrochemical Corrosion Mechanism
Face forms passivating film, to play a protective role to ambient enviroment corrosion.Alloying element be added is harmless, is connect with skin
It is tactile without side-effects, it is inexpensive, it is resourceful.By the test of prolonged marine environment and desert Environment, present patent application protection
Karat gold can remain to keep original brownish red quality in using 8-10, show extremely huge corrosion-resistant to environment
Ability.As alloy content is in the variation of optimization range, the mechanical performance of the alloy can be adjusted significantly.Together
When, the alloy is since liquidus curve is relatively low, 850 degree or so, thus is suitable for casting.Since crystal grain is refined, solve to understand
Hot cracking tendency is big when certainly casting, and casting cavity is low with loose apparent product yield rate to wait technical barriers.
Claims (3)
1. a kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of brown and its technique;According to weight percent, the ingredient of the alloy
For:Sr:0.3-0.5wt.%,P:0.2-0.4wt.%,Rh:1.5-1.8wt.%,V:1.2-1.6wt.%,Cu:15.0-
18.0wt.%,Co:20.0-22.0wt.%,Au:41.0-42.0wt.%, surplus are silver.
2. a kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of brown described in claim 1 and its technique, it is characterised in that including
Following smelting step:As above the raw material matched is added in the electric induction furnace of argon gas protection, and uses graphite crucible;Metal is molten
It is protected using the argon gas of low discharge after change, big air-flow is avoided to make the serious scaling loss of alloying element;10 are kept the temperature when melting at 1200 degree
Minute, it is uniform by Efco-Northrup furnace electromagnetic agitation;1 minute being kept the temperature at 1200 degree after stirring evenly and being cast come out of the stove;Billon pours
Casting uses the punching block of diameter 50-100mm, and is cooled down by the way of water cooling.
3. according to a kind of corrosion-resistant resistance to brittle failure high intensity 10K billons of brown described in claim 1 and its technique, it is characterised in that packet
Step is used containing following:The ingot casting of gained is rolled at room temperature, it is 30-40% that every time, which rolls lower amount,;After rolling twice
Intermediate anneal temperature is 380 degree, keeps the temperature 0.5 hour;Material is finally rolled into the golden plate that thickness is 10-20mm;Jewellery at
During type, needs to carry out intermediate annealing process, eliminate the stress in process;Wherein, homogenization temperature is 350 degree, when
Between be 1-2 hours.