CN108528006A - The production method of moisture absorbing and sweat releasing shirt fabric - Google Patents

The production method of moisture absorbing and sweat releasing shirt fabric Download PDF

Info

Publication number
CN108528006A
CN108528006A CN201810242744.2A CN201810242744A CN108528006A CN 108528006 A CN108528006 A CN 108528006A CN 201810242744 A CN201810242744 A CN 201810242744A CN 108528006 A CN108528006 A CN 108528006A
Authority
CN
China
Prior art keywords
production method
sweat releasing
moisture absorbing
shirt fabric
crease
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810242744.2A
Other languages
Chinese (zh)
Inventor
顾红娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Red Dress Technology Development Co Ltd
Original Assignee
Jiangyin Red Dress Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Red Dress Technology Development Co Ltd filed Critical Jiangyin Red Dress Technology Development Co Ltd
Priority to CN201810242744.2A priority Critical patent/CN108528006A/en
Publication of CN108528006A publication Critical patent/CN108528006A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of production methods of moisture absorbing and sweat releasing shirt fabric, including：（1）The step of making base；（2）The step of moisture absorption layer is made by polyester fiber and coolplus fiber blends；（3）The step of making crease-resistant layer；（4）The step of moisture absorption layer and crease-resistant layer are bonded in the both sides of base respectively；（5）The step of being dyed using disperse dyes；（6）The step of final finishing.The base of the present invention is formed using cotton ramie blended spinning, salubrious ventilative, and can greatly improve the ventilative effect of moisture absorption using coolplus fibers in moisture absorption layer, makes comfortable and easy to wear, and in addition crease-resistant layer can also play crease-resistant effect.And since elder generation in the surface spraying of coolplus fibers carries silver-colored oyster shell whiting antiseptic, there is no need to immerse monoblock cloth to carry out antimicrobial treatment in antiseptic, the time of cloth processing is shortened, and the heavy feeling caused by mass-impregnation is also avoided while ensure that antibacterial action, make comfortable and easy to wear.

Description

The production method of moisture absorbing and sweat releasing shirt fabric
Technical field
The present invention relates to a kind of production methods of moisture absorbing and sweat releasing shirt fabric.
Background technology
Shirt is the necessity of people's life, and the fabrics such as common cotton, yarn or silk are made, although when temperature is relatively low It is comfortable and easy to wear, but when hot weather is worn since perspiring is more, shirt be sticked to people can be allowed not feel well.Therefore Need it is a kind of can to the greatest extent moisture absorbing and sweat releasing, keep skin clean, dry and comfortable shirt fabric.
Invention content
The present invention is above-mentioned in order to overcome the shortcomings of, provides a kind of moisture absorbing and sweat releasing shirt fabric that skin can be kept dry and comfortable Production method, including：
（1）The step of making base；
（2）The step of moisture absorption layer is made by polyester fiber and coolplus fiber blends；
（3）The step of making crease-resistant layer；
（4）The step of moisture absorption layer and crease-resistant layer are bonded in the both sides of base respectively；
（5）The step of being dyed using disperse dyes；
（6）The step of final finishing.
The production method of moisture absorbing and sweat releasing shirt fabric of the present invention, the step（1）Middle base is 50%-70% by weight fraction Cotton fiber and 30%-50% Sheng-bast fibers are blended forms.
The production method of moisture absorbing and sweat releasing shirt fabric of the present invention, the step（2）The weight fraction of middle polyester fiber is 50%-70%, coolplus fiber are 30%-50%, and coolplus fibers spray the silver-colored oyster shell whiting antiseptic of load before blended.
The production method of moisture absorbing and sweat releasing shirt fabric of the present invention, step（3）Moderate resistance rennet is 20%-30%'s by weight fraction The blend polyester of silk and 70%-80% form.
The production method of moisture absorbing and sweat releasing shirt fabric of the present invention, step（5）Middle dyeing includes：Disperse dyes, dispersant, 20min → be warming up to 115 DEG C with the speed of 1 DEG C/min and keep the temperature 40min → flushing is washed in the mixed solution of sodium acetate and water To room temperature → addition reactive dye, anhydrous sodium sulphate and soda ash and be warming up to 60 DEG C, keep the temperature soap after 1h → cooled to room temperature → Be heated to 85 DEG C → be cooled to room temperature.
The production method of moisture absorbing and sweat releasing shirt fabric of the present invention, step（5）It is adjusted with acetic acid in the mixed solution of washing PH to 4-4.5.
The production method of moisture absorbing and sweat releasing shirt fabric of the present invention, step（5）Middle dispersant concentration is 1g/L, sodium acetate is 1.5g/L, anhydrous sodium sulphate 40g/L, soda ash 15g/L.
The production method of moisture absorbing and sweat releasing shirt fabric of the present invention, step（6）Hydrophilic softener is added when final finishing and passes through Stentering forming is carried out after loose-drying on stenter.
The production method of moisture absorbing and sweat releasing shirt fabric of the present invention, setting temperature are 170 DEG C -190 DEG C.
The beneficial effects of the invention are as follows：
The base of the present invention is formed using cotton ramie blended spinning, salubrious ventilative, and can be significantly using coolplus fibers in moisture absorption layer Improve the ventilative effect of moisture absorption, make comfortable and easy to wear, in addition crease-resistant layer can also play crease-resistant effect.And since elder generation exists The surface spraying of coolplus fibers carries silver-colored oyster shell whiting antiseptic, and there is no need to immerse monoblock cloth to carry out in antiseptic Antimicrobial treatment has shortened the time of cloth processing, and has only adhered on the surface of coolplus fibers and carry silver-colored oyster shell whiting antiseptic, The heavy feeling caused by mass-impregnation is also avoided while ensure that antibacterial action, is made comfortable and easy to wear.
Specific implementation mode
The present invention is described in further detail now.
A kind of production method of moisture absorbing and sweat releasing shirt fabric, including：
（1）By weight fraction be 50%-70% cotton fiber and 30%-50% Sheng-bast fibers it is blended form base the step of；
（2）The step of moisture absorption layer is made of polyester fiber and 30%-50%coolplus fiber blends that weight fraction is 50%-70% Suddenly；（3）The step of crease-resistant layer is formed by the blend polyester of silk and 70%-80% that weight fraction is 20%-30%；
（4）The step of moisture absorption layer and crease-resistant layer are bonded in the both sides of base respectively by aqueous polyurethane adhesive；
（5）The step of being dyed using disperse dyes；
（6）The step of final finishing.
Above-mentioned steps（5）Middle dyeing includes：It is washed in the mixed solution of disperse dyes, dispersant, sodium acetate and water 20min → be warming up to 115 DEG C with the speed of 1 DEG C/min and keep the temperature 40min → flushing to room temperature → addition reactive dye, anhydrous sodium sulphate With soda ash and be warming up to 60 DEG C, heat preservation 1h → soaping after cooled to room temperature → be heated to 85 DEG C → be cooled to room temperature.Step （6）Hydrophilic softener is added when final finishing and carries out stentering forming, setting temperature 170 on stenter after loose-drying ℃-190℃。
The base of the present invention is formed using cotton ramie blended spinning, salubrious ventilative, and can using coolplus fibers in moisture absorption layer The ventilative effect of moisture absorption is greatly improved, makes comfortable and easy to wear, in addition crease-resistant layer can also play crease-resistant effect.And since elder generation exists The surface spraying of coolplus fibers carries silver-colored oyster shell whiting antiseptic, and there is no need to immerse monoblock cloth to carry out in antiseptic Antimicrobial treatment has shortened the time of cloth processing, and has only adhered on the surface of coolplus fibers and carry silver-colored oyster shell whiting antiseptic, The heavy feeling caused by mass-impregnation is also avoided while ensure that antibacterial action, is made comfortable and easy to wear.
It is above-mentioned according to the present invention be enlightenment, through the above description, relevant staff completely can without departing from In the range of this invention technological thought, various changes and amendments are carried out.The technical scope of this invention is not limited to In the content on specification, it is necessary to determine its technical scope according to right.

Claims (9)

1. a kind of production method of moisture absorbing and sweat releasing shirt fabric, which is characterized in that including：
（1）The step of making base；
（2）The step of moisture absorption layer is made by polyester fiber and coolplus fiber blends；
（3）The step of making crease-resistant layer；
（4）The step of moisture absorption layer and crease-resistant layer are bonded in the both sides of base respectively；
（5）The step of being dyed using disperse dyes；
（6）The step of final finishing.
2. the production method of moisture absorbing and sweat releasing shirt fabric according to claim 1, which is characterized in that the step（1）In Base is by the cotton fiber that weight fraction is 50%-70% and 30%-50% Sheng-bast fibers are blended forms.
3. the production method of moisture absorbing and sweat releasing shirt fabric according to claim 1, which is characterized in that the step（2）In The weight fraction of polyester fiber is 50%-70%, and coolplus fibers are 30%-50%, and coolplus fibers spray before blended Carry silver-colored oyster shell whiting antiseptic.
4. the production method of moisture absorbing and sweat releasing shirt fabric according to claim 1, which is characterized in that step（3）In it is crease-resistant Layer is formed by the blend polyester of silk and 70%-80% that weight fraction is 20%-30%.
5. the production method of moisture absorbing and sweat releasing shirt fabric according to claim 1, which is characterized in that step（5）Middle dyeing Including：20min → be warming up to the speed of 1 DEG C/min is washed in the mixed solution of disperse dyes, dispersant, sodium acetate and water 115 DEG C and 40min → flushing is kept the temperature to room temperature → addition reactive dye, anhydrous sodium sulphate and soda ash and is warming up to 60 DEG C, heat preservation 1h → Soap after cooled to room temperature → being heated to 85 DEG C → be cooled to room temperature.
6. the production method of moisture absorbing and sweat releasing shirt fabric according to claim 5, which is characterized in that step（5）It is washing Mixed solution in vinegar acid for adjusting pH to 4-4.5.
7. the production method of moisture absorbing and sweat releasing shirt fabric according to claim 6, which is characterized in that step（5）Middle dispersion Agent concentration is 1g/L, sodium acetate 1.5g/L, anhydrous sodium sulphate 40g/L, soda ash 15g/L.
8. the production method of moisture absorbing and sweat releasing shirt fabric according to claim 1, which is characterized in that step（6）Final finishing When be added and hydrophilic softener and carry out stentering forming on stenter after loose-drying.
9. the production method of moisture absorbing and sweat releasing shirt fabric according to claim 8, which is characterized in that setting temperature 170 ℃-190℃。
CN201810242744.2A 2018-03-23 2018-03-23 The production method of moisture absorbing and sweat releasing shirt fabric Pending CN108528006A (en)