CN108505351A - A kind of special artistic cloth of glass technology and its production method - Google Patents

A kind of special artistic cloth of glass technology and its production method Download PDF

Info

Publication number
CN108505351A
CN108505351A CN201810278366.3A CN201810278366A CN108505351A CN 108505351 A CN108505351 A CN 108505351A CN 201810278366 A CN201810278366 A CN 201810278366A CN 108505351 A CN108505351 A CN 108505351A
Authority
CN
China
Prior art keywords
parts
blotting
raw material
cloth
surface layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810278366.3A
Other languages
Chinese (zh)
Inventor
张洪彪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU AOLI ADVERTISEMENT MATERIAL CO Ltd
Original Assignee
JIANGSU AOLI ADVERTISEMENT MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU AOLI ADVERTISEMENT MATERIAL CO Ltd filed Critical JIANGSU AOLI ADVERTISEMENT MATERIAL CO Ltd
Priority to CN201810278366.3A priority Critical patent/CN108505351A/en
Publication of CN108505351A publication Critical patent/CN108505351A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of special artistic cloth of glass technology, it can solve that existing artistic cloth color is dim, saturation degree is low, air brushing effect is poor and poor waterproof properties, the low technical problem of service life.A kind of special artistic cloth of glass technology, it is characterised in that:It includes the blotting surface layer being arranged from top to bottom, blotting middle level, blotting internal layer, base material, blotting middle level and blotting surface layer, and blotting internal layer includes following raw material by weight, 32 parts of acrylic emulsion, 26 parts of natural stone-powder；Blotting middle level includes following raw material by weight, 35 parts of acetate emulsion, 25 parts of natural stone-powder, 3.8 parts of silica, 4 parts of polyvinyl alcohol, 4.3 parts of color fixing agent；Blotting surface layer includes following raw material by weight, 35 parts of acetate emulsion, 18 parts of natural stone-powder, 5.6 parts of silica, 6.5 parts of polyvinyl alcohol, 4.3 parts of color fixing agent.

Description

A kind of special artistic cloth of glass technology and its production method
Technical field
The present invention relates to artistic cloth fields, and in particular to a kind of special artistic cloth of glass technology and its production method.
Background technology
The special artistic cloth of existing glass technology includes base material and is coated on multiple ink-absorbed coated layers of substrate surface, and base material is Using natural polymers such as cellulose and protein as raw material, macromolecule concentrate is made through chemical process, then through spinning Textile fabric is made with post-processing in silk, then the base fabric being compiled into；Natural stone-powder, PVC are mixed by ink-absorbed coated layer Slurry is formed in coating in base fabric；It is fixed on glass surface after first thering is the one side air brushing of ink-absorbed coated layer to play picture base fabric when use. However this kind of traditional artistic cloth, not only color is dim, saturation degree is low, and air brushing effect is poor, and poor waterproof properties, service life It is low.
Invention content
In view of the above-mentioned problems, the present invention provides a kind of special artistic cloth of glass technology, existing artistic cloth can be solved Color is dim, saturation degree is low, and air brushing effect is poor and poor waterproof properties, the low technical problem of service life.
Its technical solution is a kind of such, special artistic cloth of glass technology, it is characterised in that:It includes setting from top to bottom Blotting surface layer, blotting middle level, blotting internal layer, base material, blotting middle level and the blotting surface layer set,
The blotting internal layer includes following raw material by weight, 32 parts of acrylic emulsion, 26 parts of natural stone-powder；
The blotting middle level includes following raw material by weight, 35 parts of acetate emulsion, 25 parts of natural stone-powder, titanium dioxide 3.8 parts of silicon, 4 parts of polyvinyl alcohol, 4.3 parts of color fixing agent；
The blotting surface layer includes following raw material by weight, 35 parts of acetate emulsion, 18 parts of natural stone-powder, titanium dioxide 5.6 parts of silicon, 6.5 parts of polyvinyl alcohol, 4.3 parts of color fixing agent.
Further, the color fixing agent is cation-type water-thinned polyurethane color fixing agent.
Further, the base material is waterproof chemical fiber woven cloth.
The present invention also provides the production methods of the special artistic cloth of above-mentioned glass technology, include the following steps：
S1, by each raw material of the blotting internal layer according to proportioning mixing after be warming up to 60 DEG C stir 5 minutes, the slurry of formation is with 35 g/m2-50 g/m2Dry glue grammes per square metre be uniformly coated on base material front, form blotting internal layer, and carry out drying and processing；
S2, by each raw material in the blotting middle level according to proportioning mixing after be warming up to 68 DEG C stir 5 minutes, the slurry of formation is with 35 g/m2-50 g/m2Dry glue grammes per square metre be uniformly coated on S1 treated base material positive and negative, form blotting middle level, and dried Dry-cure；
S3, by each raw material on the blotting surface layer according to proportioning mixing after be warming up to 60 DEG C stir 3 minutes, the slurry of formation is with 35 g/m2-50 g/m2Dry glue grammes per square metre be uniformly coated on S2 treated base material positive and negative, form blotting surface layer, and dried Dry-cure obtains finished product.
Further, step S1, in S2 and S3, the concrete operations of drying and processing are, with the speed of 25m/min-30m/min The baking oven for being 80 DEG C -110 DEG C by temperature.
The reasonable adjustment that the present invention passes through component selection and each group distribution ratio to each ink absorbing layer so that improved glass The special artistic cloth of glass technique, color is beautiful after air brushing, and saturation degree is high, and blotting effect is good, not fugitive color, and with waterproof effect Fruit, service life are long.
Description of the drawings
Fig. 1 is the structural diagram of the present invention.
Specific implementation mode
As shown in Figure 1, a kind of special artistic cloth of glass technology comprising in the blotting surface layer that is arranged from top to bottom, blotting Layer, blotting internal layer, base material, blotting middle level and blotting surface layer；
Base material is waterproof chemical fiber woven cloth；
Blotting internal layer includes following raw material by weight, 32 parts of acrylic emulsion, 26 parts of natural stone-powder；
Blotting middle level includes following raw material by weight, 35 parts of acetate emulsion, 25 parts of natural stone-powder, silica 3.8 parts, 4 parts of polyvinyl alcohol, 4.3 parts of cation-type water-thinned polyurethane color fixing agent；
Blotting surface layer includes following raw material by weight, 35 parts of acetate emulsion, 18 parts of natural stone-powder, silica 5.6 parts, 6.5 parts of polyvinyl alcohol, 4.3 parts of cation-type water-thinned polyurethane color fixing agent.
The present invention also provides the production methods of the special artistic cloth of above-mentioned glass technology, include the following steps：
S1, by each raw material of blotting internal layer according to proportioning mixing after be warming up to 60 DEG C stir 5 minutes, the slurry of formation is with 35 g/ m2-50 g/m2Dry glue grammes per square metre be uniformly coated on base material front, blotting internal layer is formed, and with the speed of 25m/min-30m/min Degree carries out drying and processing by the baking oven that temperature is 80 DEG C -110 DEG C；
S2, by each raw material in blotting middle level according to proportioning mixing after be warming up to 68 DEG C stir 5 minutes, the slurry of formation is with 35 g/ m2-50 g/m2Dry glue grammes per square metre be uniformly coated on S1 treated base material positive and negative, form blotting middle level, and with 25m/ The speed of min-30m/min carries out drying and processing by the baking oven that temperature is 80 DEG C -110 DEG C；
S3, by each raw material on blotting surface layer according to proportioning mixing after be warming up to 60 DEG C stir 3 minutes, the slurry of formation is with 35 g/ m2-50 g/m2Dry glue grammes per square metre be uniformly coated on S2 treated base material positive and negative, form blotting surface layer, and with 25m/ The speed of min-30m/min carries out drying and processing by the baking oven that temperature is 80 DEG C -110 DEG C, obtains finished product.
Wherein, in aforementioned production method, the dry glue grammes per square metre of slurry coating is bigger, and coating is thicker, and speed needs to drop when drying Low, temperature increases；When raw material mixes, 5 parts ~ 15 parts deionized waters can be according to circumstances added.
The special artistic cloth of glass technology produced by the invention, compared to market traditional art cloth, color is beautiful after air brushing, satisfies It is high with degree；And blotting effect is good, not fugitive color；And there is waterproof effect, easy to make, service life is long.

Claims (5)

1. a kind of special artistic cloth of glass technology, it is characterised in that:It includes in the blotting surface layer being arranged from top to bottom, blotting Layer, blotting internal layer, base material, blotting middle level and blotting surface layer；
The blotting internal layer includes following raw material by weight, 32 parts of acrylic emulsion, 26 parts of natural stone-powder；
The blotting middle level includes following raw material by weight, 35 parts of acetate emulsion, 25 parts of natural stone-powder, titanium dioxide 3.8 parts of silicon, 4 parts of polyvinyl alcohol, 4.3 parts of color fixing agent；
The blotting surface layer includes following raw material by weight, 35 parts of acetate emulsion, 18 parts of natural stone-powder, titanium dioxide 5.6 parts of silicon, 6.5 parts of polyvinyl alcohol, 4.3 parts of color fixing agent.
2. a kind of special artistic cloth of glass technology according to claim 1, it is characterised in that：The color fixing agent is cation Type water-borne polyurethane color fixing agent.
3. a kind of special artistic cloth of glass technology according to claim 1, it is characterised in that：The base material is waterproof chemical fiber Woven cloth.
4. the production method of the special artistic cloth of glass technology as described in claim 1, includes the following steps：
S1, by each raw material of the blotting internal layer according to proportioning mixing after be warming up to 60 DEG C stir 5 minutes, the slurry of formation is with 35 g/m2-50 g/m2Dry glue grammes per square metre be uniformly coated on base material front, form blotting internal layer, and carry out drying and processing；
S2, by each raw material in the blotting middle level according to proportioning mixing after be warming up to 68 DEG C stir 5 minutes, the slurry of formation is with 35 g/m2-50 g/m2Dry glue grammes per square metre be uniformly coated on S1 treated base material positive and negative, form blotting middle level, and dried Dry-cure；
S3, by each raw material on the blotting surface layer according to proportioning mixing after be warming up to 60 DEG C stir 3 minutes, the slurry of formation is with 35 g/m2-50 g/m2Dry glue grammes per square metre be uniformly coated on S2 treated base material positive and negative, form blotting surface layer, and dried Dry-cure obtains finished product.
5. the production method of the special artistic cloth of glass technology according to claim 4, it is characterised in that：Step S1, S2 and In S3, the concrete operations of drying and processing are the baking oven for being 80 DEG C -110 DEG C by temperature with the speed of 25m/min-30m/min.
CN201810278366.3A 2018-03-31 2018-03-31 A kind of special artistic cloth of glass technology and its production method Pending CN108505351A (en)