CN108489324A - Technique is not taken over and its is realized in the stretching of expansion-joint type clip to one kind - Google Patents
Technique is not taken over and its is realized in the stretching of expansion-joint type clip to one kind Download PDFInfo
- Publication number
- CN108489324A CN108489324A CN201810330647.9A CN201810330647A CN108489324A CN 108489324 A CN108489324 A CN 108489324A CN 201810330647 A CN201810330647 A CN 201810330647A CN 108489324 A CN108489324 A CN 108489324A
- Authority
- CN
- China
- Prior art keywords
- over
- bottom end
- take over
- boss
- taken
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
It is taken over the invention discloses a kind of not expansion-joint type clip stretching and its two kinds of stretch forming process.Using stainless steel materials stretch forming process include stock, continuous stretching die stretch plank, top is taken in edger trimming, finish-milling takes over bottom end, rough mill take over top, flange die flange takes over bottom end, bottom end is taken in edger trimming, cleaning pipe ends weld, soldering, quality inspection process.Using stainless steel pipe stretch forming process includes stock, flange die flange takes over top, top is taken in edger trimming, flange die flange takes over bottom end, bottom end is taken in edger trimming, cleans pipe ends weld, soldering, quality inspection process.The present invention, which has many advantages, such as to simplify, to be taken over more particularly to the processing technology with the stainless joint of clip butt welding, and raw material and mach cost are significantly reduced.
Description
Technical field
The present invention is taken over by what new process was processed, more particularly to the stainless joint with clip butt welding, is applied to soldering
On plate heat exchanger, main feature is a simplified the processing technology taken over, and significantly reduces raw material and mach cost.
Background technology
Plate heat exchanger is that liquid-liquid, liquid-vapour carry out the ideal equipment of heat exchange, high with heat exchanger effectiveness,
The series of advantages such as heat loss is small, advantages of compact and light structure, small, the service life length of floor space, thus be widely used in it is metallurgical,
The departments such as mine, oil, chemical industry, electric power, medicine, food, chemical fibre, papermaking, light textile, ship, heat supply.Also, it can be used for adding
The various situations such as heat, cooling, evaporation, condensation, sterilizing, waste heat recovery.Plate heat exchanger mainly has detachable and welding
Formula two major classes, in comparison, welding type heat exchanger have many advantages, such as to hold that temperature, bearing capacity are strong, and resistance to corrosion is good, thus weld
Formula heat exchanger use scope is more extensive.
Welding type heat exchanger can be divided into half welding type heat exchanger, full welding type heat exchanger, plate visitor's formula heat exchanger, brazing sheet again
Formula heat exchanger.Since soldering has, heating temperature is relatively low, connector is smooth, tissue and mechanical performance change small, workpiece size
The advantages that accurate, brazing plate type heat exchanger can be used as condenser and evaporator in refrigeration industry, can be used as alcohol in chemical industry
The operating temperature range of cooler ... the pricker welded type heat exchanger of fermentation etc. is -160 DEG C~+225 DEG C, and working pressure range is
0.01MPa~3.2MPa.
Have inlet and outlet on pricker welded type heat exchanger, frequently with welding or expanded joint mode by its with take over one end phase
Connection, the take over other end is with external water inlet pipe, outlet pipe frequently with welding or clamp connection.It is used on existing brazing plate type heat exchanger
Take over and be mostly processed on numerically controlled lathe by tubing or solid round steel, and clip is all and welding take over butt welding
Together；For bigbore welded pipe, a large amount of material can not only be wasted using above-mentioned traditional processing method, processed
Cost is also special height.Therefore, a kind of in the case where ensureing that the normal uses such as take over intensity require there is an urgent need for proposing, what is more simplified connects
Pipe processing technique, to reduce raw material and mach cost.
Invention content
The technical problem to be solved in the present invention is, for taking over using tubing on traditional brazing plate type heat exchanger
Or solid round steel is processed on numerically controlled lathe, and due to clip all with take over to being welded together, for heavy caliber
Welded pipe processing when can waste a large amount of material, the shortcomings of processing cost is also special height, and processing technology is cumbersome, carries
Go out two kinds of take over stretch forming process for more simplifying and greatly reducing processing cost.
The present invention solves the above problems designed take over material as stainless steel, and take over endoporus is got through.Taken over top and
Bottom end is distinguished, and the ruler of the outer diameter of take over bottom boss and depth dimensions and counterbore at brazing plate type heat exchanger water-in and water-out nozzle
Very little equal, the two is connected using brazing mode.
Preferably, above-mentioned take over bottom boss outside diameter size range of taking over is：20~40mm, thickness range be 1~
3mm；
Preferably, above-mentioned stage casing wall thickness of taking over is 1~3mm；
Preferably, above-mentioned connecting pipe length size range is：20~40mm；
Preferably, above-mentioned take over diameter of bore size range is：12~30mm.
Above-mentioned top of taking over is machined with boss structure.When external water pipe with take over connect using clamping hoop type when, take over top
Boss is linked together with clip by way of butt welding, take over the outer diameter of top boss, thickness should be with selected card
Hoop standard size matches.
Preferably, it is 1~3mm to take over top boss thickness, takes over a diameter of 20~60mm of top boss.
The present invention also proposes above-mentioned two taken over kind manufacturing process comprising step in detail below：
(1) stainless steel materials stretch forming process is used：
Stock：Prepare the stainless steel materials of corresponding size；
Continuous stretching die stretches plank：Using stretching die by stainless steel materials by continuously elongated to diameter of bore and taking over
Stage casing wall thickness is respectively 12~30mm and 1~3mm；
Top is taken in edger trimming：The above-mentioned tubing that is obtained after continuously elongated is subjected to edger trimming to taking over
A diameter of 20~the 60mm of top boss；
Finish-milling takes over bottom end：Finish-milling takes over top until it is 1~3mm to take over top boss thickness；
It rough mills and takes over top：By finish-milling cross take over bottom end on the basis of, butt tube bottom end rough mill until meet takes over
Length is bigger 2~5mm plus the poor value of bottom end internal-and external diameter is taken over than target connecting pipe length；
Flange die flange takes over bottom end：Use flange die by above-mentioned stainless steel pipe bottom end by flange to connecting pipe length for
20~40mm, take over bottom boss thickness are 1~3mm；
Bottom end is taken in edger trimming：Edger trimming will be carried out to taking over bottom by the take over bottom boss after above-mentioned processing
Hold a diameter of 20~40mm of boss；
Clean pipe ends weld：Bottom end weld, removal grease, oxide, ash are taken over using organic solvent cleaning
Dirt etc.；
Soldering：It is evenly heated soldered pipe fitting, dipping suitable fine agent (welding powder) with the solder of heating is uniformly put on gap
Place, solder is sent into when temperature reaches 650 DEG C -750 DEG C.Lead to low speed nitrogen in by welded tube when welding, prevents from aoxidizing, work as solder
All stop heating when fusing, when soldering will take over the counterbore that bottom end circle deck is put on matched brazing plate type heat exchanger
At limiting slot, compressed using briquetting taking over top, it is cooling after welding, clear up pipe inner oxide with drying nitrogen
And welding slag；
Quality inspection：By national standard or professional standard or company standard to above-mentioned take over carry out quality examination.Quality inspection links are worn
It is inserted in each manufacturing process.
(2) stainless steel pipe stretch forming process is used：
Stock：Prepare the stainless steel pipe of corresponding size；
Flange die flange takes over top：Use flange die by stainless steel pipe by flange to take over top boss thickness for
1~3mm, it is 1~3mm to take over stage casing wall thickness；
Top is taken in edger trimming：The above-mentioned tubing that is obtained after flange die flange is subjected to edger trimming to connecing
The tube top end a diameter of 20~60mm of boss；
Flange die flange takes over bottom end：Using flange die to carrying out flange to take over length by the bottom end of taking over after above-mentioned processing
Degree is 20~40mm, and take over bottom boss thickness is 1~3mm；
Bottom end is taken in edger trimming：Edger trimming will be carried out to taking over bottom by the take over bottom boss after above-mentioned processing
Hold a diameter of 20~40mm of boss；
Clean pipe ends weld：Bottom end weld, removal grease, oxide, ash are taken over using organic solvent cleaning
Dirt etc.；
Soldering：It is evenly heated soldered pipe fitting, dipping suitable fine agent (welding powder) with the solder of heating is uniformly put on gap
Place, solder is sent into when temperature reaches 650 DEG C -750 DEG C.Lead to low speed nitrogen in by welded tube when welding, prevents from aoxidizing, work as solder
All stop heating when fusing, when soldering will take over the counterbore that bottom end circle deck is put on matched brazing plate type heat exchanger
At limiting slot, compressed using briquetting taking over top, it is cooling after welding, clear up pipe inner oxide with drying nitrogen
And welding slag；
Quality inspection：By national standard or professional standard or company standard to above-mentioned take over carry out quality examination.Quality inspection links are worn
It is inserted in each manufacturing process.
Compared with the prior art, the advantages of the present invention are as follows：
1. the stretching of expansion-joint type clip is not taken over and functionally be will take over clip collection together in one, compared to tradition in the present invention
Joint pipe structure greatly simplify, thus material cost substantially reduces.
2. the stretching of expansion-joint type clip does not take over and butt welding mode can be used connect clip with taking in the present invention, two take over pair
For postwelding again by clip sealed clamping, system stability is good, and easy to maintenance.
3. expansion-joint type clip stretching tube can not realize that process is relatively simple by plate stretch technique in the present invention, batch
Production cost is low.
4. expansion-joint type clip stretching tube can not also realize that process is few by tubing flanging process in the present invention, batch
Production efficiency is high.
5. expansion-joint type clip stretching tube in vibration frequency is not 30HZ in the present invention, acceleration 10G, amplitude is 5mm
Under the conditions of continue 500h No leakages, thus product strength machine Fatigue Vibration performance is high.
Description of the drawings
Fig. 1 is the structural schematic diagram of the present invention, and wherein A is brazing plate type heat exchanger, B is to stretch to take over.
Fig. 2 is that the half sectional view taken over is stretched in the present invention.
Fig. 3 is with sheet fabrication in the present invention into technical process schematic diagram when taking over.
Fig. 4 is with tubular object extruding in the present invention into technical process schematic diagram when taking over.
Fig. 5 is that the assembling schematic diagram taken over brazing plate type heat exchanger during the brazing process is stretched in the present invention.
Fig. 6 is that take over vibration-testing tests schematic diagram in the present invention.
Specific embodiment
Below in conjunction with attached drawing, present invention is further described in detail.
The present invention proposes that a kind of not expansion-joint type clip stretching is taken over, and the specific technical solution taken is：
It is respectively brazing plate type heat exchanger A and take over B from left to right, as shown in Figure 1.It is described to take over as using not expanded joint
The stainless steel tubulation that formula stretch forming process is manufactured into.Top and the bottom end taken over is distinguished, and both ends are all flanging type pedestal
It is welded and with clip with brazing plate type heat exchanger entery and delivery port counterbore to being welded together respectively, size is as shown in Figure 2：
The a diameter of b=25mm of take over inner via hole；It is d=29mm to take over stage casing outer diameter；Location A is to take over top, with card
For hoop to being welded together, outer diameter is to be matched with selected clip standard size, takes over top flanging type pedestal outside diameter
For a=50.5mm, thickness c=2mm；B location is to take over bottom end, outside diameter f=50.5mm, thickness g=1mm,
It is heavy with the bottom end flanging type pedestal corresponding size of institute connecting tubes to be machined at brazing plate type heat exchanger water-in and water-out nozzle
Hole, counter bore hole diameters 50.5mm, counterbore depth are 1mm；Connecting pipe length is e=21.5mm.
Above-mentioned take over uses soldering connection with brazing plate type heat exchanger, as shown in figure 5, will take over the bottom ends B deck when assembly
It stretches at brazing plate type heat exchanger C interface in counterbore, carries out Welding, pressed using briquetting A taking over top when soldering
Tightly.
The present invention also proposes above-mentioned two taken over kind manufacturing process comprising step in detail below：
(1) plate processing technology process
Stock：Prepare the stainless steel materials of 3mm thickness；
Continuous stretching die stretches plank：It will be passed through shown in stainless steel materials such as Fig. 3 (a), (b), (c) using stretching die continuous
It is b=25mm to be stretched to hole size, and it is d=29mm to take over stage casing outer diameter；
Top is taken in edger trimming：The above-mentioned tubing obtained after continuously elongated cut as shown in Fig. 3 (d)
In cross cutting to taking over a diameter of a=24mm of top boss；
Finish-milling takes over bottom end：Finish-milling takes over top until it is c=2mm to take over top boss thickness；
It rough mills and takes over top：By finish-milling cross take over bottom end on the basis of, butt tube bottom end rough mill until meet takes over
Length is 35mm, as shown in Fig. 3 (e)；
Flange die flange takes over bottom end：Flange will be passed through using flange die shown in above-mentioned stainless steel pipe bottom end such as Fig. 3 (f)
It is e=21.5mm to connecting pipe length, take over bottom boss thickness is g=1mm；
Bottom end is taken in edger trimming：Edger trimming will be carried out to taking over bottom by the take over bottom boss after above-mentioned processing
The a diameter of f=50.5mm of boss is held, obtains taking over as shown in Fig. 3 (g)；
Clean pipe ends weld：Bottom end weld, removal grease, oxide, ash are taken over using organic solvent cleaning
Dirt etc.；
Soldering：It is evenly heated soldered pipe fitting, dipping suitable fine agent (welding powder) with the solder of heating is uniformly put on gap
Place, solder is sent into when temperature reaches 650 DEG C -750 DEG C.Lead to low speed nitrogen in by welded tube when welding, prevents from aoxidizing.Work as solder
All stop heating when fusing, when soldering will take over bottom end circle deck and is put into matched brazing-sheet type heat exchange as shown in Figure 5
At counterbore limiting slot C on device, compressed using briquetting A at the top of take over B.It is cooling after welding, it is clear with drying nitrogen
Manage pipe inner oxide and welding slag；
Quality inspection：By national standard or professional standard or company standard to above-mentioned take over carry out quality examination.Quality inspection links are worn
It is inserted in each manufacturing process.
(2) tubular object extruding technical process
Stock：Preparation internal diameter is 25mm, and thickness 4mm, length is the stainless steel pipe of 50mm；
Flange die flange takes over top：Using flange die will shown in stainless steel pipe such as Fig. 4 (a), (b) by flange to connecing
Tube top end boss thickness is c=2mm, and it is d=29mm to take over stage casing outer diameter；
Top is taken in edger trimming：The above-mentioned tubing obtained after flange die flange is carried out as shown in Fig. 4 (c)
Edger trimming is to taking over top boss diameter a=50.5mm；
Flange die flange takes over bottom end：Using flange die to carrying out flange to take over length by the bottom end of taking over after above-mentioned processing
Degree is e=21.5mm, and take over bottom boss thickness is g=1mm, as shown in Fig. 4 (d)；
Bottom end is taken in edger trimming：Edger trimming will be carried out to taking over bottom by the take over bottom boss after above-mentioned processing
The a diameter of f=50.5mm of boss is held, obtains taking over as shown in Fig. 4 (e)；
Clean pipe ends weld：Bottom end weld, removal grease, oxide, ash are taken over using organic solvent cleaning
Dirt etc.；
Soldering：It is evenly heated soldered pipe fitting, dipping suitable fine agent (welding powder) with the solder of heating is uniformly put on gap
Place, solder is sent into when temperature reaches 650 DEG C -750 DEG C.Lead to low speed nitrogen in by welded tube when welding, prevents from aoxidizing.Work as solder
All stop heating when fusing, when soldering will take over bottom end circle deck and is put into matched brazing-sheet type heat exchange as shown in Figure 5
At counterbore limiting slot C on device, compressed using briquetting A at the top of take over B.It is cooling after welding, it is clear with drying nitrogen
Manage pipe inner oxide and welding slag；
Quality inspection：By national standard or professional standard or company standard to above-mentioned take over carry out quality examination.Quality inspection links are worn
It is inserted in each manufacturing process.
For taking the above-mentioned stretching manufactured by present invention process to take over, vibration-testing experiment has been carried out.As shown in Figure 6
Schematic diagram is tested for vibration-testing, A is pricker welded type heat exchanger, and B takes over to be above-mentioned, and C is clip, and D is external water pipe, and E is vibration
Testing stand, F are water pipe fixture, and when experiment will take over is welded with copper pipe, and fill 20kg compressed airs and carry out pressurize, then will
Heat exchanger pedestal is bolted fixed on vibration mechine, while copper pipe being fixed on fixture.Test condition：Vibration
Frequency is 30HZ, acceleration 10G, amplitude 5mm.After test result display vibration continues 500 hours, take over No leakage shakes
Show that intensity and Fatigue Vibration fully meet requirement after dynamic test.
The foregoing is merely illustrative of the preferred embodiments of the present invention, and those skilled in the art know, is not departing from the present invention
Spirit and scope in the case of, various changes or equivalent replacement can be carried out to these features and embodiment.In addition, in this hair
Under bright introduction, it can modify to these features and embodiment to adapt to particular situation and material without departing from this hair
Bright spirit and scope.Therefore, the present invention is not limited to the particular embodiment disclosed, the power of fallen with the application
Embodiment in sharp claimed range belongs to protection scope of the present invention.
Claims (5)
1. a kind of not expansion-joint type clip stretching is taken over, it is characterised in that：It is described take over using stainless steel materials or drawing pipe at
Type technique；Above-mentioned top boss of taking over is connected with clip by butt welding mode；Above-mentioned take over bottom boss exchanges heat with brazing-sheet type
Device is connected using not expansion-joint type brazing mode.
2. a kind of not expansion-joint type clip stretching according to claim 1 is taken over, it is characterised in that：Top and bottom end are taken over
It distinguishes, both ends are machined with boss structure respectively, and top is linked together with clip by butt welding, and it is straight to take over top boss outer circle
Diameter ranging from 20~60mm, thickness ranging from 1~3mm；Take over bottom boss outside diameter ranging from 20~40mm, thickness
Size range is 1~3mm, and the bottom boss phase with institute connecting tubes is machined at brazing plate type heat exchanger water-in and water-out nozzle
Answer the counterbore of size；Connecting pipe length size range is 20~40mm；Take over diameter of bore size range is 12~30mm；In taking over
Section wall thickness dimension ranging from 1~3mm.
3. a kind of not expansion-joint type clip stretching according to claim 1 is taken over, it is characterised in that：It is logical with clip to take over top
It crosses butt welding to link together, takes over the outer diameter of top boss, thickness should be matched with selected clip standard size.
4. a kind of not expansion-joint type clip as described in claim 1 stretches the manufacturing method taken over, it is characterised in that：The method
Include the following steps：
(1) it stocks up：Prepare the stainless steel materials of corresponding size；
(2) continuous stretching die stretches plank：Using stretching die by stainless steel materials by continuously elongated to diameter of bore and taking over
Stage casing wall thickness is respectively 12~30mm and 1~3mm；
(3) top is taken in edger trimming：The above-mentioned tubing that is obtained after continuously elongated is subjected to edger trimming to taking over
A diameter of 20~the 60mm of top boss；
(4) finish-milling takes over bottom end：Finish-milling takes over top until it is 1~3mm to take over top boss thickness；
(5) it rough mills and takes over top：By finish-milling cross take over bottom end on the basis of, butt tube bottom end rough mill until meet take over length
Degree is bigger 2~5mm plus the poor value of bottom end internal-and external diameter is taken over than target connecting pipe length；
(6) flange die flange takes over bottom end：Use flange die by above-mentioned stainless steel pipe bottom end by flange to connecting pipe length for
20~40mm, take over bottom boss thickness are 1~3mm；
(7) bottom end is taken in edger trimming：Edger trimming will be carried out to taking over bottom by the take over bottom boss after above-mentioned processing
Hold a diameter of 20~40mm of boss；
(8) pipe ends weld is cleaned：Bottom end weld, removal grease, oxide, dust are taken over using organic solvent cleaning
Deng；
(9) it is brazed：It is evenly heated soldered pipe fitting, dipping suitable fine agent (welding powder) with the solder of heating is uniformly put on gap
Place, is sent into solder when temperature reaches 650 DEG C -750 DEG C, and when welding leads to low speed nitrogen in by welded tube, prevents from aoxidizing, works as solder
All stop heating when fusing, when soldering will take over the counterbore that bottom end circle deck is put on matched brazing plate type heat exchanger
At limiting slot, compressed using briquetting taking over top, it is cooling after welding, clear up pipe inner oxide with drying nitrogen
And welding slag；
(10) quality inspection：By national standard or professional standard or company standard to above-mentioned take over carry out quality examination, quality inspection links are worn
It is inserted in each manufacturing process.
5. a kind of not expansion-joint type clip as described in claim 1 stretches the manufacturing method taken over, it is characterised in that：The method
Include the following steps：
(1) it stocks up：Prepare the stainless steel pipe of corresponding size；
(2) flange die flange takes over top：Use flange die by stainless steel pipe by flange to taking over top boss thickness as 1
~3mm, it is 1~3mm to take over stage casing wall thickness；
(3) top is taken in edger trimming：The above-mentioned tubing that is obtained after flange die flange is subjected to edger trimming to connecing
The tube top end a diameter of 20~60mm of boss；
(4) flange die flange takes over bottom end：Using flange die to carrying out flange to take over length by the bottom end of taking over after above-mentioned processing
Degree is 20~40mm, and take over bottom boss thickness is 1~3mm；
(5) bottom end is taken in edger trimming：Edger trimming will be carried out to taking over bottom by the take over bottom boss after above-mentioned processing
Hold a diameter of 20~40mm of boss；
(6) pipe ends weld is cleaned：Bottom end weld, removal grease, oxide, dust are taken over using organic solvent cleaning
Deng；
(7) it is brazed：It is evenly heated soldered pipe fitting, dipping suitable fine agent with the solder of heating is uniformly put at gap, works as temperature
Degree is sent into solder when reaching 650 DEG C -750 DEG C, and when welding leads to low speed nitrogen in by welded tube, prevents from aoxidizing, when solder is all molten
Stop heating when change, when soldering will take over the counterbore limiting slot that bottom end circle deck is put on matched brazing plate type heat exchanger
Place is compressed taking over top using briquetting, cooling after welding, and pipe inner oxide and welding slag are cleared up with drying nitrogen；
(8) quality inspection：By national standard or professional standard or company standard to above-mentioned take over carry out quality examination, quality inspection links are interspersed
In each manufacturing process.