CN108485545A - The preparation method of house ornamentation PVC wallpaper - Google Patents

The preparation method of house ornamentation PVC wallpaper Download PDF

Info

Publication number
CN108485545A
CN108485545A CN201810205546.9A CN201810205546A CN108485545A CN 108485545 A CN108485545 A CN 108485545A CN 201810205546 A CN201810205546 A CN 201810205546A CN 108485545 A CN108485545 A CN 108485545A
Authority
CN
China
Prior art keywords
layer
pvc
preparation
wallpaper
pvc plastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810205546.9A
Other languages
Chinese (zh)
Inventor
孙宗林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kunshan City Spotlight Decoration Materials Co Ltd
Original Assignee
Kunshan City Spotlight Decoration Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kunshan City Spotlight Decoration Materials Co Ltd filed Critical Kunshan City Spotlight Decoration Materials Co Ltd
Priority to CN201810205546.9A priority Critical patent/CN108485545A/en
Publication of CN108485545A publication Critical patent/CN108485545A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of preparation method of house ornamentation PVC wallpaper, the preparation method of PVC wallpaper includes the following steps：Step 1：One layer of decoration paste layers are coated in any surface of the PVC plastic bed of material, then one layer of crack resistence coating is coated in the another side of the PVC plastic bed of material, form crack resistence layer；Step 2：The semi-finished product that step 1 is obtained have the one side of decoration thickener after pressure roller is suppressed, and form pattern decorative layer；Step 3：One layer of oil-proof paint is coated in the another side for the pattern decorative layer that step 2 obtains, forms anti-oil reservoir；Step 4：One layer of adhesive sticker is coated in the another side for the crack resistence layer that step 1 obtains, forms non-drying glue layer；Step 5：It is bonded an off-style paper layer in the another side for the non-drying glue layer that step 4 obtains.The present invention can prepare the wallpaper of different decorative layers, adapt to the demand of various clients；And the wallpaper surface smoothness of the present invention is high, and oil resistivity is good, free from extraneous odour, can avoid the problem that wallpaper cracks caused by long-time use.

Description

The preparation method of house ornamentation PVC wallpaper
Technical field
The invention belongs to house decorative material technical fields, more particularly to a kind of preparation method of house ornamentation PVC wallpaper.
Background technology
Wallpaper be for house, office, hotel interior decoration a kind of speciality paper, be generally divided into PVC (polychlorostyrene second Alkene) plastic wall paper, pure paper wallpaper and non-woven fabrics wallpaper etc..Wherein, non-woven fabrics wallpaper uses natural plant fibre without spinning process system At having many advantages, such as strong, environmentally friendly, the not mouldy jaundice of pulling force, good permeability；Pure paper wallpaper processed using high-quality natural wood pulp and At, have many advantages, such as good permeability, water suction the moisture absorption.
Chinese patent CN 102605679B disclose " a kind of wallpaper ", are made of adhesive, base material and metope inorganic agent, Even if it is a kind of environment protection type wallpaper that can repeatedly paste will not damage metope in the wallpaper more renewed, it will not There are residue glues on metope, are widely used in the use of the interior decorations such as household, hotel and public place of entertainment.
Though PVC wallpaper has the characteristics that pattern grace, good hand touch, there is also poor air permeability, have the shortcomings that remain smell, It is difficult to meet people the substance, environmental protection etc. the needs of.
Invention content
The invention mainly solves the technical problem of providing a kind of preparation methods of house ornamentation PVC wallpaper, can prepare difference The wallpaper of decorative layer adapts to the demand of various clients；And the wallpaper surface smoothness of the present invention is high, and oil resistivity is good, free from extraneous odour, It can avoid the problem that wallpaper cracks caused by long-time use.
In order to solve the above technical problems, one aspect of the present invention is：A kind of house ornamentation PVC wallpaper is provided Preparation method, the PVC wallpaper are followed successively by anti-oil reservoir, pattern decorative layer, the PVC plastic bed of material, crack resistence layer, adhesive sticker from outside to inside Layer and off-style paper layer；
The preparation method of the PVC wallpaper includes the following steps：
Step 1：The PVC plastic bed of material is subjected to sided corona treatment, and one layer of decoration thickener is coated in any surface of the PVC plastic bed of material The coating thickness of layer, the decoration paste layers is 0.1-0.2mm, and the PVC plastic bed of material is dried 1- at a temperature of 30-40 DEG C After 1.5h, then in another side one layer of crack resistence coating of coating of the PVC plastic bed of material, crack resistence layer is formed, the coating of crack resistence layer is thick Degree is 0.02-0.05mm；
Step 2：The semi-finished product that step 1 is obtained have the one side of decoration thickener after pressure roller is suppressed, and form figure Case decorative layer；
Step 3：One layer of oil-proof paint is coated in the another side for the pattern decorative layer that step 2 obtains, anti-oil reservoir is formed, prevents The coating thickness of oil reservoir is 0.05-0.07mm；
Step 4：One layer of adhesive sticker is coated in the another side for the crack resistence layer that step 1 obtains, non-drying glue layer is formed, does not do The coating thickness of glue-line is 0.01-0.02mm；
Step 5：It is bonded an off-style paper layer in the another side for the non-drying glue layer that step 4 obtains, pressing rolling after cooling is It can.
It further says, the main component of the decoration paste layers in the step 1 includes (counting in parts by weight)：50-70 Part emulsion acrylic resin, 50-70 parts of hydroxyethyl lotions, 30-40 parts of organosilicons, 10-20 parts of haloflexes and 5- 15 parts of talcum powder.
It further says, the main component of the crack resistence coating in the step 1 includes (by weight percentage)：10- 40% rosin resin, 20-60% polytetrafluoroethylene (PTFE), 15-60% nano-titanium dioxides and 5-10% toughener.
It further says, the main component of the oil-proof paint layer in the step 3 includes (by weight percentage)：20- 40% acrylic resin, 10-40% epoxy phenolics, 8-20% polytetrafluoroethylene (PTFE) and 15-30% dimethicones.
It further says, the pattern decorative layer of the step 2 is to pass through to be carved with specific pattern at a high temperature of 150-170 DEG C The pressure roller of case carries out compacting formation.
It further says, the PVC plastic bed of material is the electrostatic PVC plastic bed of material, transparent PVC plastic layer, has the white PVC plastic bed of material of light Or the unglazed white PVC plastic bed of material.
Further say, the off-style paper layer in the step 5 be PET fluorine mould off-style paper layer, PET silicate-containing oils off-style paper layer, PET matts off-style paper layer, PE off-style paper layers or PE lamination paper layers.
Beneficial effects of the present invention at least have the following：
1, the formula of the anti-oil reservoir of the present invention, decorative layer and crack resistence layer is reasonable and safe and non-toxic, and free from extraneous odour is a kind of ring Guarantor's type wallpaper；
2, the outermost layer of wallpaper of the present invention is anti-oil reservoir, and the substances such as water, the soda acid in external environment can be avoided to wallpaper The erosion on surface ensures the cleanliness factor on wallpaper surface；
3, wallpaper of the present invention is additionally provided with one layer of crack resistence layer, toughener and rosin resin, polytetrafluoroethylene (PTFE) and nano-silica Change being used cooperatively for titanium, can avoid the problem that wallpaper cracks caused by long-time use.
Description of the drawings
Fig. 1 is the structural schematic diagram of the present invention；
Each section label is as follows in attached drawing：
Anti- oil reservoir 1, pattern decorative layer 2, the PVC plastic bed of material 3, crack resistence layer 4, non-drying glue layer 5 and off-style paper layer 6.
Specific implementation mode
The preferred embodiments of the present invention will be described in detail below in conjunction with the accompanying drawings, so that advantages and features of the invention energy It is easier to be readily appreciated by one skilled in the art, so as to make a clearer definition of the protection scope of the present invention.
Embodiment：A kind of preparation method of house ornamentation PVC wallpaper, as shown in Figure 1, the PVC wallpaper is from outside to inside successively For anti-oil reservoir 1, pattern decorative layer 2, the PVC plastic bed of material 3, crack resistence layer 4, non-drying glue layer 5 and off-style paper layer 6；
The preparation method of the PVC wallpaper includes the following steps：
Step 1：The PVC plastic bed of material is subjected to sided corona treatment, and one layer of decoration thickener is coated in any surface of the PVC plastic bed of material The coating thickness of layer, the decoration paste layers is 0.1-0.2mm, and the PVC plastic bed of material is dried 1- at a temperature of 30-40 DEG C After 1.5h, then in another side one layer of crack resistence coating of coating of the PVC plastic bed of material, crack resistence layer is formed, the coating of crack resistence layer is thick Degree is 0.02-0.05mm；
Step 2：The semi-finished product that step 1 is obtained have the one side of decoration thickener after pressure roller is suppressed, and form figure Case decorative layer；
Step 3：One layer of oil-proof paint is coated in the another side for the pattern decorative layer that step 2 obtains, anti-oil reservoir is formed, prevents The coating thickness of oil reservoir is 0.05-0.07mm；
Step 4：One layer of adhesive sticker is coated in the another side for the crack resistence layer that step 1 obtains, non-drying glue layer is formed, does not do The coating thickness of glue-line is 0.01-0.02mm；
Step 5：It is bonded an off-style paper layer in the another side for the non-drying glue layer that step 4 obtains, pressing rolling after cooling is It can.
The main component of decoration paste layers in the step 1 includes (counting in parts by weight)：50-70 parts of acrylic acid trees Fat liquor, 50-70 parts of hydroxyethyl lotions, 30-40 parts of organosilicons, 10-20 parts of haloflexes and 5-15 parts of talcum powder.
The main component of crack resistence coating in the step 1 includes (by weight percentage)：10-40% rosin trees Fat, 20-60% polytetrafluoroethylene (PTFE), 15-60% nano-titanium dioxides and 5-10% toughener.
The main component of oil-proof paint layer in the step 3 includes (by weight percentage)：20-40% acrylic acid Resin, 10-40% epoxy phenolics, 8-20% polytetrafluoroethylene (PTFE) and 15-30% dimethicones.
The pattern decorative layer of the step 2 is to be carried out at a high temperature of 150-170 DEG C by being carved with the pressure roller of specific pattern Compacting is formed.
The PVC plastic bed of material is the electrostatic PVC plastic bed of material, transparent PVC plastic layer, has the white PVC plastic bed of material of light or unglazed white PVC Plastic layer.
Off-style paper layer in the step 5 is release for PET fluorine modeling off-style paper layer, PET silicate-containing oils off-style paper layer, PET matts Paper layer, PE off-style paper layers or PE lamination paper layers.
Example the above is only the implementation of the present invention is not intended to limit the scope of the invention, every to utilize this hair Equivalent structure transformation made by bright specification and accompanying drawing content is applied directly or indirectly in other relevant technical fields, Similarly it is included within the scope of the present invention.

Claims (7)

1. a kind of preparation method of house ornamentation PVC wallpaper, it is characterised in that：The PVC wallpaper be followed successively by from outside to inside anti-oil reservoir, Pattern decorative layer, the PVC plastic bed of material, crack resistence layer, non-drying glue layer and off-style paper layer；
The preparation method of the PVC wallpaper includes the following steps：
Step 1：The PVC plastic bed of material is subjected to sided corona treatment, and one layer of decoration paste layers, institute are coated in any surface of the PVC plastic bed of material The coating thickness for stating decoration paste layers is 0.1-0.2mm, and after the PVC plastic bed of material is dried 1-1.5h at a temperature of 30-40 DEG C, One layer of crack resistence coating is coated in the another side of the PVC plastic bed of material again, forms crack resistence layer, the coating thickness of crack resistence layer is 0.02-0.05mm；
Step 2：The semi-finished product that step 1 is obtained have the one side of decoration thickener after pressure roller is suppressed, and form pattern dress Adorn layer；
Step 3：One layer of oil-proof paint is coated in the another side for the pattern decorative layer that step 2 obtains, forms anti-oil reservoir, anti-oil reservoir Coating thickness be 0.05-0.07mm；
Step 4：One layer of adhesive sticker is coated in the another side for the crack resistence layer that step 1 obtains, forms non-drying glue layer, non-drying glue layer Coating thickness be 0.01-0.02mm；
Step 5：It is bonded an off-style paper layer in the another side for the non-drying glue layer that step 4 obtains, presses rolling after cooling.
2. the preparation method of house ornamentation PVC wallpaper according to claim 1, it is characterised in that：Dress in the step 1 The main component for adoring paste layers includes (counting in parts by weight)：50-70 parts of emulsion acrylic resins, 50-70 parts of hydroxylethyls Yogurt liquid, 30-40 part organosilicon, 10-20 parts of haloflexes and 5-15 parts of talcum powder.
3. the preparation method of house ornamentation PVC wallpaper according to claim 1, it is characterised in that：It is anti-in the step 1 The main component of cracking coating includes (by weight percentage)：10-40% rosin resins, 20-60% polytetrafluoroethylene (PTFE), 15- 60% nano-titanium dioxide and 5-10% toughener.
4. the preparation method of house ornamentation PVC wallpaper according to claim 1, it is characterised in that：It is anti-in the step 3 The main component of oil paint layer includes (by weight percentage)：20-40% acrylic resins, 10-40% epoxy phenolics, 8-20% polytetrafluoroethylene (PTFE) and 15-30% dimethicones.
5. the preparation method of house ornamentation PVC wallpaper according to claim 1, it is characterised in that：The pattern of the step 2 Decorative layer is to carry out compacting formation by being carved with the pressure roller of specific pattern at a high temperature of 150-170 DEG C.
6. the preparation method of house ornamentation PVC wallpaper according to claim 1, it is characterised in that：The PVC plastic bed of material is quiet The electric PVC plastic bed of material, transparent PVC plastic layer have the white PVC plastic bed of material of light or the unglazed white PVC plastic bed of material.
7. the preparation method of house ornamentation PVC wallpaper according to claim 1, it is characterised in that：In the step 5 from Type paper layer is that PET fluorine moulds off-style paper layer, PET silicate-containing oils off-style paper layer, PET matts off-style paper layer, PE off-style paper layers or PE laminations Paper layer.
CN201810205546.9A 2018-03-13 2018-03-13 The preparation method of house ornamentation PVC wallpaper Pending CN108485545A (en)