CN108485435A - 一种微胶囊技术制备的多功能内墙荧光负离子涂料 - Google Patents

一种微胶囊技术制备的多功能内墙荧光负离子涂料 Download PDF

Info

Publication number
CN108485435A
CN108485435A CN201810353939.4A CN201810353939A CN108485435A CN 108485435 A CN108485435 A CN 108485435A CN 201810353939 A CN201810353939 A CN 201810353939A CN 108485435 A CN108485435 A CN 108485435A
Authority
CN
China
Prior art keywords
parts
negative ion
interior wall
paint prepared
microcapsules technology
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810353939.4A
Other languages
English (en)
Inventor
邓雪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Foshan Kang Dong Lighting Technology Co Ltd
Original Assignee
Foshan Kang Dong Lighting Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Foshan Kang Dong Lighting Technology Co Ltd filed Critical Foshan Kang Dong Lighting Technology Co Ltd
Priority to CN201810353939.4A priority Critical patent/CN108485435A/zh
Publication of CN108485435A publication Critical patent/CN108485435A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种微胶囊技术制备的多功能内墙荧光负离子涂料，其原料按重量份包括以下组分：有机硅改性丙烯酸乳液30‑50 份、荧光颜料5‑10份、负离子粉3‑8份，纳米二氧化钛8‑12份、硅藻泥10‑20份、云母粉5‑10份、钛白粉3‑6份、高岭土3‑8份、碳酸钙10‑20份、羟乙基纤维素溶液3‑6份、pH 调节剂0.1‑0.3份、分散剂0.5‑1.0 份、消泡剂0.2‑0.5 份、成膜助剂1.0‑2.5 份、增稠剂0.5‑0.8 份、防沉剂1‑3 份、去离子水20‑30 份。

Description

一种微胶囊技术制备的多功能内墙荧光负离子涂料
技术领域
本发明涉及内墙涂料，具体涉及一种微胶囊技术制备的多功能内墙荧光负离子涂料。
背景技术
随着经济的迅速发展，人们越来越重视自身的健康，拥有一个健康环境是保持自身健康的首要前提。目前，大部分涂料为溶剂型涂料，溶剂型涂料中含有约50%的有机溶齐IJ，这些涂料喷涂后会释放大量的VOC气体，不仅严重危害到使用人的身体健康，还会对大气造成污染，损坏生态环境。据统计，人类的生活和生产活动向大气中排放的VOC占全球大气污染量的15%，而涂料加工和生产释放出来的VOC量占其排放总量的20°/Γ30%，仅次于汽车尾气的排放而位居污染量第二位。因此，控制涂料VOC的排放越来越受到人们的重视。水性涂料作为溶剂型涂料的理想替代品，以其安全、无毒、无污染等优点，备受各界研发学者的关注。许多公共场所在失去光源的时候，就会产生极大的安全隐患，如地下通道、楼梯走廊等。这时候，就亟需在这些地方涂有荧光涂料，来减少安全隐患。其他地方，如各种安全应急启动标志、高压电等危险标志,也需要这种涂料。负离子被誉为空气维生素，具有环保、健康、灭菌三大功能，不仅能净化空气，还能增强人们的抵抗力，促进新陈代谢，现有医学研究表明维持人们健康的负离子数为1000-2000个/cm3，而现在住宅、办公室的负离子数只有40-50个/cm3，远远少于维持健康的标准要求，涂料种类繁多，在许多领域都得到广泛的应用。在现有涂料中大部分都是单一功效的涂料比较多，还没有一款合格的、安全性能高的、含有负离子荧光内墙装饰涂料的销售。 所以研制出一种微胶囊技术制备的多功能内墙荧光负离子涂料是涂料领域亟需解决的问题。
发明内容
本发明的目的就是针对现有问题，提供一种微胶囊技术制备的多功能内墙荧光负离子涂料，该一种微胶囊技术制备的多功能内墙荧光负离子涂料以有机硅改性丙烯酸乳液为成膜物质，添加的荧光颜料乳液、负离子粉，纳米二氧化钛、硅藻泥、云母粉、钛白粉、高岭土、碳酸钙等多种多功能性的颜、填料，并加入部分助剂，通过微胶囊技术制备得到的一种微胶囊技术制备的多功能内墙荧光负离子涂料。该一种微胶囊技术制备的多功能内墙荧光负离子涂料不但具有良好的芳香性、耐水性、耐碱性、耐洗刷性、耐粘污性和抗老化性，而且还具有静态持续释放负离子、祛除甲醛、氨、苯等有害气体、抗菌抑菌、无污染、绿色环保、高装饰性能和较好的荧光性能等优点。
为实现上述目的本发明所采用的技术方案如下：一种微胶囊技术制备的多功能内墙荧光负离子涂料，其原料按重量份包括以下组分：有机硅改性丙烯酸乳液30-50 份、荧光颜料5-10份、负离子粉3-8份，纳米二氧化钛8-12份、硅藻泥10-20份、云母粉5-10份、钛白粉3-6份、高岭土3-8份、碳酸钙10-20份、羟乙基纤维素溶液3-6份、pH 调节剂0.1-0.3份、分散剂0.5-1.0 份、消泡剂0.2-0.5 份、成膜助剂1.0-2.5 份、增稠剂0.5-0.8 份、防沉剂1-3份、去离子水20-30 份。
进一步地，所述的荧光颜料为无机颜料铝粉。
进一步地，所述的所述的负离子粉为粒度为80-150nm 的电气石粉末。
进一步地，所述的钛白粉金红石型钛白粉，粒径为100 ～ 150μm。
进一步地，所述的PH调节剂为氨水。
进一步地，所述的分散剂为焦磷酸钠。
进一步地，所述的消泡剂为为非离子型表面活性剂。
进一步地，所述的成膜助剂为丙二醇。
与现有技术对比，本发明具有如下优点：
1、本发明的一种微胶囊技术制备的多功能内墙荧光负离子涂料以有机硅改性丙烯酸乳液为成膜材料，以水为容剂，无污染，绿色环保；
2、本发明中加入的负离子粉在太阳光（尤其是紫外线）照射下生成OH-，能有效除去室内外的苯、甲醛、硫化物、氨和臭味物质，并具有杀菌功能，为绿色环保涂料。并且能每分钟持续释放负离子，能有效改善室内空气质量，祛除室内空气中甲醛、甲苯，氨等有害污染物质；该涂料还能迅速消除室内香烟、油烟雾、家用电器所产生的空气污染和电子污染；大大降低电磁辐射强度等多功能于一体，其24 小时杀菌、灭菌率达90% 以上，其健康性表现为通过改善了空气质量，达到增强人体免疫力、预防多种疾病的辅助作用，符合人们对环保和健康的双重要求；
3、本发明采用硅藻泥为填料，硅藻泥（英文：Diatom mud）是一种以硅藻土为主要原材料的内墙环保装饰壁材。其具有消除甲醛、净化空气、调节湿度、释放负氧离子、防火阻燃、墙面自洁、杀菌除臭等功能。硅藻泥健康环保，不仅有很好装饰性，还具有功能性，是替代壁纸和乳胶漆的新一代室内装饰材料，是优良的环保型室内外装修材料；
4、本发明的一种多功能醋酸乙烯酯内墙装饰涂料乳液合成过程中采用了先进的微胶囊技术，涂料制备过程中添加了具有高效光催作用的纳米二氧化钛，使得该涂料具有良好的芳香性、耐擦洗性和杀菌等功能；并且该内墙装饰涂料的制备工艺简单，并且具备水性及多功能化的多重特点，符合现代涂料发展的要求，环境效益显著，具有很大的市场潜力；
5、本发明的一种微胶囊技术制备的多功能内墙荧光负离子涂料不但具有良好的芳香性、耐水性、耐碱性、耐洗刷性、耐粘污性和抗老化性，而且还具有静态持续释放负离子、祛除甲醛、氨、苯等有害气体、抗菌抑菌、无污染、绿色环保、高装饰性能和较好的荧光性能等优点。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步详细说明。此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
实施例1
一种微胶囊技术制备的多功能内墙荧光负离子涂料，其原料按重量份包括以下组分：有机硅改性丙烯酸乳液30份、荧光颜料5份、负离子粉3份，纳米二氧化钛8份、硅藻泥10份、云母粉5份、钛白粉3份、高岭土3份、碳酸钙10份、羟乙基纤维素溶液3份、pH 调节剂0.1份、分散剂0.5份、消泡剂0.2份、成膜助剂1.0份、增稠剂0.5份、防沉剂1份、去离子水20份。
所述的荧光颜料为无机颜料铝粉。
所述的所述的负离子粉为粒度为80nm 的电气石粉末。
所述的钛白粉金红石型钛白粉，粒径为100 μm。
所述的PH调节剂为氨水。
所述的分散剂为焦磷酸钠。
所述的消泡剂为为非离子型表面活性剂。
所述的成膜助剂为丙二醇。
实施例2
一种微胶囊技术制备的多功能内墙荧光负离子涂料，其原料按重量份包括以下组分：有机硅改性丙烯酸乳液50 份、荧光颜料10份、负离子粉8份，纳米二氧化钛12份、硅藻泥20份、云母粉10份、钛白粉6份、高岭土8份、碳酸钙20份、羟乙基纤维素溶液6份、pH 调节剂0.3份、分散剂1.0 份、消泡剂0.5 份、成膜助剂2.5 份、增稠剂0.8 份、防沉剂3 份、去离子水30 份。
所述的荧光颜料为无机颜料铝粉。
所述的所述的负离子粉为粒度为150nm 的电气石粉末。
所述的钛白粉金红石型钛白粉，粒径为150μm。
所述的PH调节剂为氨水。
所述的分散剂为焦磷酸钠。
所述的消泡剂为为非离子型表面活性剂。
所述的成膜助剂为丙二醇。
实施例3
一种微胶囊技术制备的多功能内墙荧光负离子涂料，其原料按重量份包括以下组分：有机硅改性丙烯酸乳液35份、荧光颜料8份、负离子粉5份，纳米二氧化钛10份、硅藻泥15份、云母粉8份、钛白粉5份、高岭土6份、碳酸钙15份、羟乙基纤维素溶液5份、pH 调节剂0.2份、分散剂0.8份、消泡剂0.4份、成膜助剂1..5 份、增稠剂0.6份、防沉剂2 份、去离子水25份。
所述的荧光颜料为无机颜料铝粉。
所述的所述的负离子粉为粒度为100nm 的电气石粉末。
所述的钛白粉金红石型钛白粉，粒径为120μm。
所述的PH调节剂为氨水。
所述的分散剂为焦磷酸钠。
所述的消泡剂为为非离子型表面活性剂。
所述的成膜助剂为丙二醇。
上述实施方式仅为本发明的优选实施方式，不能以此来限定本发明保护的范围，本领域的技术人员在本发明的基础上所做的任何非实质性的变化及替换均属于本发明所要求保护的范围。

Claims (8)

1.一种微胶囊技术制备的多功能内墙荧光负离子涂料，其特征在于，其原料按重量份包括以下组分：有机硅改性丙烯酸乳液30-50 份、荧光颜料5-10份、负离子粉3-8份，纳米二氧化钛8-12份、硅藻泥10-20份、云母粉5-10份、钛白粉3-6份、高岭土3-8份、碳酸钙10-20份、羟乙基纤维素溶液3-6份、pH 调节剂0.1-0.3份、分散剂0.5-1.0 份、消泡剂0.2-0.5份、成膜助剂1.0-2.5 份、增稠剂0.5-0.8 份、防沉剂1-3 份、去离子水20-30 份。
2.根据权利要求1 所述的一种微胶囊技术制备的多功能内墙荧光负离子涂料，其特征在于：所述的荧光颜料为无机颜料铝粉。
3.根据权利要求1 所述的一种微胶囊技术制备的多功能内墙荧光负离子涂料，其特征在于：所述的所述的负离子粉为粒度为80-150nm 的电气石粉末。
4.根据权利要求1 所述的一种微胶囊技术制备的多功能内墙荧光负离子涂料，其特征在于：所述的钛白粉金红石型钛白粉，粒径为100 ～ 150μm。
5.根据权利要求1 所述的一种微胶囊技术制备的多功能内墙荧光负离子涂料，其特征在于：所述的PH调节剂为氨水。
6.根据权利要求1 所述的一种微胶囊技术制备的多功能内墙荧光负离子涂料，其特征在于：所述的分散剂为焦磷酸钠。
7.根据权利要求1 所述的一种微胶囊技术制备的多功能内墙荧光负离子涂料，其特征在于：所述的消泡剂为为非离子型表面活性剂。
8.根据权利要求1 所述的一种微胶囊技术制备的多功能内墙荧光负离子涂料，其特征在于：所述的成膜助剂为丙二醇。
CN201810353939.4A 2018-04-19 2018-04-19 一种微胶囊技术制备的多功能内墙荧光负离子涂料 Pending CN108485435A (zh)