CN108485404A - 一种高流平、耐沾污pva内墙抗菌涂料 - Google Patents

一种高流平、耐沾污pva内墙抗菌涂料 Download PDF

Info

Publication number
CN108485404A
CN108485404A CN201810344399.3A CN201810344399A CN108485404A CN 108485404 A CN108485404 A CN 108485404A CN 201810344399 A CN201810344399 A CN 201810344399A CN 108485404 A CN108485404 A CN 108485404A
Authority
CN
China
Prior art keywords
parts
stain resistant
high levelling
wall
antibacterial coatings
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810344399.3A
Other languages
English (en)
Inventor
邹奇峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810344399.3A priority Critical patent/CN108485404A/zh
Publication of CN108485404A publication Critical patent/CN108485404A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种高流平、耐沾污PVA内墙抗菌涂料，其原料按重量份包括以下组分：聚乙烯醇10‑20 份、纳米二氧化钛浆料10‑20份、抗菌纳米二氧化钛4‑6份、钛白粉10‑20份、重质碳酸钙10‑20份、轻质碳酸钙3‑6份、滑石粉8‑10份、硅灰石粉3‑6份、蜡乳液3‑6份、羟乙基纤维素0.2‑0.5 份、分散剂0.5‑1.0 份、消泡剂0.2‑0.5 份、成膜助剂1.0‑2.5 份、防冻剂1‑3份、去离子水40‑60 份。该种高流平、耐沾污PVA内墙抗菌涂料不但具有良好的流平性、涂膜具有憎水性、而且具有抗菌抑菌、高流平、耐沾污性、高装饰性、呼吸调湿性能、绿色环保和成本低等优点。

Description

一种高流平、耐沾污PVA内墙抗菌涂料
技术领域
本发明涉及一种内墙涂料，具体涉及一种高流平、耐沾污PVA内墙抗菌涂料。
背景技术
内墙涂料就是一般装修用的乳胶漆。乳胶漆即是乳液性涂料，按照基材的不同，分为聚醋酸乙烯乳液和丙烯酸乳液两大类。乳胶漆以水为稀释剂，是一种施工方便、安全、耐水洗、透气性好的的涂料，它可根据不同的配色方案调配出不同的色泽。种类：水性内墙漆、油性内墙漆、干粉型内墙漆，属水性涂料，主要由水，乳液，颜料，填料，添加剂五种成分构成。涂料业的发展也带来室内环境污染问题，由于室内涂料含有挥发性有机溶剂成分，在施工以及使用过程中主要会产生挥发性有机化合物、游离甲醛、可溶性铅、镉、铬和汞等重金属，以及苯、甲苯、二甲苯等有害物质，能够造成室内空气质量下降以及有可能影响人体健康。涂料所挥发出的有机物经呼吸道吸入能使人出现眩晕、头痛和恶心等症状，对眼、鼻有一定的刺激作用，严重时可引起气喘、神志不清、呕吐和支气管炎等。甲醛对皮肤、眼睛及呼吸道具有很强的刺激性，使人体发生致敏反应，国际癌症研究中心已将其列为人类可疑致癌物质。
目前建筑装饰材料特别是房屋内墙的装饰材料，主要起到美化室内外的作用，使人感觉舒适温暖，房屋更加牢固，使用的材料一般是高岭土、硅石灰粉、滑石粉、云母粉、钛白粉等原料加入分散剂、润湿剂、丙二醇、乳液、水调和而成，起到了美化效果和保护墙体的作用但是人们对环保的要求越来越高，对墙面装饰材料提出来新的希望——装饰材料对人体健康的保护作用。但一般不具有杀死细菌、防霉、耐虫蛀、耐冲刷和高装饰性功能。建筑装饰材料虽然能够使室内墙面美观整洁，从而使居住和生活环境更舒适，但是很多现有的建筑装饰材料在使用中易在墙体表层滋生霉菌和虫卵，尤其是沿海等潮湿地区，霉菌能在20-38℃、相对湿度85％左右的适宜条件下大量繁殖，侵蚀建筑物表面，破坏底材，同时建筑内墙涂料表面由于暴露面积大，也是真菌、细菌、虫卵滋生的主要位置。这些霉菌、细菌、真菌、虫卵一方面破坏了涂料表面的美观和冲刷性，另一方面还严重影响人们的健康。功能涂料种类繁多，在许多领域都得到广泛的应用。
发明内容
本发明的目的就是提供一种高流平、耐沾污PVA内墙抗菌涂料，该一种高流平、耐沾污PVA内墙抗菌涂料不但具有良好的流平性、涂膜具有憎水性、而且具有抗菌抑菌、高流平、耐沾污性、高装饰性、呼吸调湿性能、绿色环保和成本低等优点。
为实现上述目的本发明所采用的技术方案如下：一种高流平、耐沾污PVA内墙抗菌涂料，其原料按重量份包括以下组分：聚乙烯醇10-20 份、纳米二氧化钛浆料10-20份、抗菌纳米二氧化钛4-6份、钛白粉10-20份、重质碳酸钙10-20份、轻质碳酸钙3-6份、滑石粉8-10份、硅灰石粉3-6份、蜡乳液3-6份、羟乙基纤维素0.2-0.5 份、分散剂0.5-1.0 份、消泡剂0.2-0.5 份、成膜助剂1.0-2.5 份、防冻剂1-3份、去离子水40-60 份。
进一步地，所述的聚乙烯醇为浓度为10%的聚乙烯醇。
进一步地，所述的钛白粉金红石型钛白粉，粒径为100 ～ 150μm。
进一步地，所述的滑石粉为过500-1000目筛的粉剂。
进一步地，所述的分散剂三聚磷酸钠。
进一步地，所述的消泡剂为AMP-19。
进一步地，所述的成膜助剂为Texanol酯醇。
进一步地，所述的防冻剂为乙二醇。
本发明优点：
1、本发明中的一种高流平、耐沾污PVA内墙抗菌涂料以聚乙烯醇作增稠流平剂，使涂料具有较好的流平性；将高分子蜡乳液应用于高流平性乳胶漆中，涂膜具有较好的憎水性，当涂膜受到沾污时其憎水性可以阻止粘污源随着水分向涂膜中渗透，同时，使涂膜具有荷叶效应；在保持较好的开罐效果，涂装饰性能能满足国家标准要求的情况下，可减少各种贵材料的用量，并且进行优化配合，保持较低的成本。该种涂料经过1-2年的存储，各项指标均无明显变化；
2、本发明一种高流平、耐沾污PVA内墙抗菌涂料中加入了纳米二氧化钛屏蔽紫外线作用强，防止紫外线的侵害，提高了涂料的使用寿命。同时，其较高的硬度、密度、介电常数及折射率，有助于提高涂料的遮盖力，遮盖力增长率约为27.61%，改善了涂料的施工性能和环保节能性能，具有相应的高装饰性、呼吸调湿性能；
3、本发明一种高流平、耐沾污PVA内墙抗菌涂料中添加复合纳米TiO2的水性建筑涂料具有杀菌功能，含纳米TiO2的涂料在紫外线照射30min后，对金黄色葡萄球菌，大肠杆菌杀菌效果均较好，抑菌率分别为79．07%、78．70%，但在无紫外线照射下，无明显的杀菌效果；
4、本发明的一种高流平、耐沾污PVA内墙抗菌涂料，该一种高流平、耐沾污PVA内墙抗菌涂料不但具有良好的流平性、涂膜具有憎水性、而且具有抗菌抑菌、高流平、耐沾污性、高装饰性、呼吸调湿性能、绿色环保和成本低等优点。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步详细说明。此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
实施例1
一种高流平、耐沾污PVA内墙抗菌涂料，其原料按重量份包括以下组分：聚乙烯醇10份、纳米二氧化钛浆料10份、抗菌纳米二氧化钛4份、钛白粉10份、重质碳酸钙10份、轻质碳酸钙3份、滑石粉8份、硅灰石粉3份、蜡乳液3份、羟乙基纤维素0.2份、分散剂0.5份、消泡剂0.2份、成膜助剂1.0份、防冻剂1份、去离子水40份。
所述的聚乙烯醇为浓度为10%的聚乙烯醇。
所述的钛白粉金红石型钛白粉，粒径为100 μm。
所述的滑石粉为过500目筛的粉剂。
所述的分散剂三聚磷酸钠。
所述的消泡剂为AMP-19。
所述的成膜助剂为Texanol酯醇。
所述的防冻剂为乙二醇。
实施例2
一种高流平、耐沾污PVA内墙抗菌涂料，其原料按重量份包括以下组分：聚乙烯醇20份、纳米二氧化钛浆料20份、抗菌纳米二氧化钛6份、钛白粉20份、重质碳酸钙20份、轻质碳酸钙6份、滑石粉10份、硅灰石粉6份、蜡乳液6份、羟乙基纤维素0.5 份、分散剂1.0 份、消泡剂0.5 份、成膜助剂2.5 份、防冻剂3份、去离子水60 份。
所述的聚乙烯醇为浓度为10%的聚乙烯醇。
所述的钛白粉金红石型钛白粉，粒径为150μm。
所述的滑石粉为过1000目筛的粉剂。
所述的分散剂三聚磷酸钠。
所述的消泡剂为AMP-19。
所述的成膜助剂为Texanol酯醇。
所述的防冻剂为乙二醇。
实施例3
一种高流平、耐沾污PVA内墙抗菌涂料，其原料按重量份包括以下组分：聚乙烯醇15份、纳米二氧化钛浆料15份、抗菌纳米二氧化钛5份、钛白粉15份、重质碳酸钙15份、轻质碳酸钙4份、滑石粉9份、硅灰石粉4份、蜡乳液4份、羟乙基纤维素0.4份、分散剂0.9 份、消泡剂0.4份、成膜助剂1.5 份、防冻剂2份、去离子水45份。
所述的聚乙烯醇为浓度为10%的聚乙烯醇。
所述的钛白粉金红石型钛白粉，粒径为130 μm。
所述的滑石粉为过900目筛的粉剂。
所述的分散剂三聚磷酸钠。
所述的消泡剂为AMP-19。
所述的成膜助剂为Texanol酯醇。
所述的防冻剂为乙二醇。
上述实施例仅仅是为清楚地说明本申请所作的举例，而并非对实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。而由此所引申出的显而易见的变化或变动仍处于本申请型的保护范围之中。

Claims (8)

1.一种高流平、耐沾污PVA内墙抗菌涂料，其特征在于，其原料按重量份包括以下组分：聚乙烯醇10-20 份、纳米二氧化钛浆料10-20份、抗菌纳米二氧化钛4-6份、钛白粉10-20份、重质碳酸钙10-20份、轻质碳酸钙3-6份、滑石粉8-10份、硅灰石粉3-6份、蜡乳液3-6份、羟乙基纤维素0.2-0.5 份、分散剂0.5-1.0 份、消泡剂0.2-0.5 份、成膜助剂1.0-2.5 份、防冻剂1-3份、去离子水40-60 份。
2.根据权利要求1 所述的一种高流平、耐沾污PVA内墙抗菌涂料，其特征在于：所述的聚乙烯醇为浓度为10%的聚乙烯醇。
3.根据权利要求1 所述的一种高流平、耐沾污PVA内墙抗菌涂料，其特征在于：所述的钛白粉金红石型钛白粉，粒径为100 ～ 150μm。
4.根据权利要求1 所述的一种高流平、耐沾污PVA内墙抗菌涂料，其特征在于：所述的滑石粉为过500-1000目筛的粉剂。
5.根据权利要求1 所述的一种高流平、耐沾污PVA内墙抗菌涂料，其特征在于：所述的分散剂三聚磷酸钠。
6.根据权利要求1 所述的一种高流平、耐沾污PVA内墙抗菌涂料，其特征在于：所述的消泡剂为AMP-19。
7.根据权利要求1 所述的一种高流平、耐沾污PVA内墙抗菌涂料，其特征在于：所述的成膜助剂为Texanol酯醇。
8.根据权利要求1 所述的一种纳米改性丙烯酸酯抗菌除甲醛内墙涂料，其特征在于：所述的防冻剂为乙二醇。
CN201810344399.3A 2018-04-17 2018-04-17 一种高流平、耐沾污pva内墙抗菌涂料 Pending CN108485404A (zh)