CN1084834A - Gold star glass making method from tail sand of gold mine - Google Patents
Gold star glass making method from tail sand of gold mine Download PDFInfo
- Publication number
- CN1084834A CN1084834A CN 92108580 CN92108580A CN1084834A CN 1084834 A CN1084834 A CN 1084834A CN 92108580 CN92108580 CN 92108580 CN 92108580 A CN92108580 A CN 92108580A CN 1084834 A CN1084834 A CN 1084834A
- Authority
- CN
- China
- Prior art keywords
- gold
- glass
- raw material
- making method
- tail sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Gold star glass making method from tail sand of gold mine, adopt gold ore tailing as main raw material and glass industry with the additive of common cheap raw material and a spot of formation Venus pedestal through founding after abundant the mixing, making after the moulding, annealing.Finished product is of fine quality, and is attractive in appearance, magnificent and cost is reduced significantly, and alternative natural marble, grouan are made the surface lining of buildings, also can make practical vessel, artwork and other ornaments.
Description
The present invention belongs to the aventurine(glass) field about the manufacturing and the method for aventurine(glass).
Aventurine(glass) not only has the good physics of general glass, chemistry, mechanical property, and glass inside has the charming some point Venus that flashes, and has high decorative effect.But because the cost of aventurine(glass) costliness, so only in order to make a spot of artwork and pendulum decorations.
The objective of the invention is to utilize the exploitation gold mine after ore dressing depleted tailings is made aventurine(glass) of fine quality, attractive in appearance, magnificent, wide application, the cost of producing aventurine(glass) is descended significantly, so that can replace marble, lithotomes such as granite, face decoration material as all kinds of senior constructure interior walls, exterior wall and ground, in addition, also can make practical vessel, artwork and table top are decorated.Utilize gold ore tailing to turn waste into wealth, be of value to environment protection, therefore have high economic benefit and social benefit.
Formation of the present invention at first is to utilize the raw material of the common, inexpensive that gold ore tailing uses for main raw material(s) and general glass industry, and forms the additive of Venus pedestal on a small quantity and implement by following aspects;
The chemical ingredients of gold sand tailings (%):
SiO
270～83 Al
2O
30.1～1.0 CaO 0.01～0.2
MgO 0.02～0.15 Fe
2O
30.12～0.41
And contain trace ingredientss such as Au, Ag, Cu, Zn, Pb, F.
The consisting of of glass (%)
SiO
260～70, Al
2O
32～6, CaO6～10, MgO2～5,
Na
2O6～14, B
2O
30～5, Fe
2O
30.1～0.2
So glass still belongs to silicon, aluminium, calcium, magnesium, sodium system.The consumption of preparing the gold ore tailing of this glass can reach 60% or more.
Characteristics of the present invention according to the composition of glass, need to add a certain amount of alkaline earth except gold ore tailing, and alkalimetal oxide is as simple glass raw materials such as rhombspar, Wingdale, feldspar, borax and soda ash.In addition, need to add a small amount of additive that forms the Venus pedestal.
The glass melting temperature of glass is 1350～1450 ℃, soaking time 2～4 hours, and the glass metal that melts has processability preferably, is applicable to casting, kinds of processes such as compacting.
Glass after the moulding promptly gets the aventurine(glass) finished product in 650～680 ℃ of annealing.
The present invention is owing to made full use of the main raw material of gold ore tailing as aventurine(glass); because cost of material is cheap; it is abundant to originate; can reduce the cost of aventurine(glass) significantly; can turn waste into wealth again; not only be of value to environment protection but also opened up a new raw material source, have good economic benefits and social benefit for material of construction.
Embodiment:
20 parts of 5 parts of feldspars of 20 parts of Wingdales of 80 parts of rhombspars of gold ore tailing
1.5 parts of 15 parts of additives of 5 parts of soda ash of borax
Above material mixing is even, found at 1350～1450 ℃, be incubated 2-4 hour, promptly get aventurine(glass) 650～680 ℃ of annealing after the cast molding.
Embodiment two:
20 parts in 20 parts of Wingdales of 100 parts of rhombspars of gold ore tailing
1.5 parts of 2 parts of additives of 20 parts of fluorites of soda ash
Above material mixing is even, found at 1350～1450 ℃, be incubated 2-4 hour, promptly get aventurine(glass) 650～680 ℃ of annealing after the cast molding.
Claims (1)
- Adopt gold star glass making method from tail sand of gold mine, it is characterized in that with the gold ore tailing being the common raw material of main raw material and glass industry and the additive of a spot of formation Venus pedestal, through mixing, found at 1350～1450 ℃, be incubated 2-4 hour, the glass after the moulding promptly gets the aventurine(glass) finished product in 650～680 ℃ of annealing.