CN108468144A - A kind of washable woollen fabric and its preparation process - Google Patents
A kind of washable woollen fabric and its preparation process Download PDFInfo
- Publication number
- CN108468144A CN108468144A CN201810401127.2A CN201810401127A CN108468144A CN 108468144 A CN108468144 A CN 108468144A CN 201810401127 A CN201810401127 A CN 201810401127A CN 108468144 A CN108468144 A CN 108468144A
- Authority
- CN
- China
- Prior art keywords
- wool
- yarn
- washable
- cam system
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of washable woollen fabric and its preparation processes, belong to textile production field.In order to reach the washable purpose of wool knitting fabrics, and change of the reduction to this body structure of wool fiber to the greatest extent, this research is weaved using the wool that non-anti-shrinking is crossed with polyester filament, using 1+1 interlock constructions, four tunnels weave, wherein the first cam system feeds wool yarn, the second cam system feeds polyester filament, third cam system feeds polyester filament, and the 4th cam system feeds wool yarn.The structure that this special coil mutually covers, the performance of polyester filament stabilization is utilized, wool yarn has been restrained to deform caused by shrink, felting etc., fabric overall structure is set to stablize, shrink-proof, in conjunction with the postfinishing process for discharging fabric internal stress to greatest extent, gained fabric is while with higher wool content, realize washing it is indeformable, every dimensional stability is more outstanding.
Description
Technical field
The present invention relates to textile production fields, and in particular to a kind of washable woollen fabric and its preparation process.
Background technology
Wool knitting fabrics since warmth retention property is strong, feel slides the advantages that glutinous, elasticity is good, dress is fit comfortable, quality sense is strong,
It is deep always to be liked by consumers in general.As the wool fabric of high-grade clothing first choice, especially wool knitting fabrics, on the one hand
Due to the felting property of wool itself, on the other hand due to the unstability of the size of knitting fabric, wool knitting fabrics develop mesh
It is preceding to tend not to reach normal ready-made clothes and take requirement there are the washing shrinkage that a big restricting reason is fabric.At present to wool needle
The means that knitted fabric washing shrinkage control effectively are the methods using anti-shrinking, and summary and induction is divided into two major classes：It is a kind of
Using subtraction, wool appearance scale is removed using auxiliary agent or biological enzyme；It is another kind of to use addition, by high polymer to wool table
The covering of face scale layer reduces the direction friction effect of wool, to achieve the purpose that felt proofing.Such as：Chinese patent
CN105544200B describes a kind of wool top chlorination shrinkproof mercerization method, by grilling shredding treated wool hair
Item is placed in bleeding agent aqueous solution, is added into aqueous solution and is shelled squama agent containing chlorine, reacted under room temperature, to reach the mesh of wool desquamation
's.For another example：Chinese patent CN105506952B describes a kind of preparation method of polylactic acid shiinkproof finish wool fabric, uses
Polylactic acid dressing liquid forms protective effect to wool fabric, forms the scale layer that stable three-dimensional network is covered in fiber surface
Outside.These two kinds of methods are required to addition other materials at present, on the one hand easy to produce the residual of chemical substance, on the one hand can change
Wool fabric original feel or style.And the washable woollen fabric obtained with above method, most wool content compared with
It is low, general only more than ten to twenties percent, which also limits the applications of high-grade wool spinning fabric.
Invention content
For the above prior art and its there are the problem of, the present invention is quasi- provide it is a kind of need not addition chemical assistant, and
The high washable woollen fabric of wool content.In order to subtract to the greatest extent under the premise of reaching wool knitting fabrics washable purpose
The small change to this body structure of wool fiber, this research are weaved using the wool that non-anti-shrinking is crossed with polyester filament, are led to
Specific institutional framework is crossed, the washing stability of wool knitting fabrics is reached in the method for physics.
A kind of washable woollen fabric, using 1+1 interlock constructions, the braiding of four tunnels, by wool worsted yarn and
The different configuration yarn feedings of terylene.Wherein the first cam system feeds wool yarn, and the second cam system feeds polyester filament, third lopping
System feeds polyester filament, and the 4th cam system feeds wool yarn.
From the first cam system to the second cam system, the complete double rib row of upper and lower needle knitting one, in cross
A wool yarn coil and the spaced structure of a polyester filament coil are presented on row；From third cam system to the 4th lopping
A polyester filament coil and one is presented in system, another complete double rib row of upper and lower needle knitting in row
The spaced structure of a wool yarn coil.
In the identical faces of fabric, along wale direction, wool yarn coil and polyester filament coil are also in alternate row
Column-shaped state.
On arbitrary vertical plane material plane normal, fabric positive and negative is respectively opposite wool yarn coil and polyester filament line
Circle.
I.e. gained is knitted fabric, and horizontal, Zong Xiangshang, wool yarn coil and polyester filament are alternately arranged braiding in identical faces,
Opposite coil in different sides, also respectively wool yarn coil and terylene coil.
Further, the wool yarn is the 100% wool worsted yarn without anti-shrinking, yarn count 70S/2-100S/2.
Further, the terylene is FDY polyester filaments, and fineness is 100D/36F or 120D/48F.
Further, the wool content of the washable woollen fabric is 50% or more.
A kind of preparation process of washable woollen fabric, includes the following steps：
S1：Standby yarn, using 100% wool worsted yarn and 100% polyester filament；
S2：Weaving, using 1+1 interlock constructions, four tunnels braiding, wherein the first cam system feeds wool yarn, the second lopping
System feeds polyester filament, and third cam system feeds polyester filament, and the 4th cam system feeds wool yarn；
S3：Thermal finalization, upper machine thermal finalization after overboard, warp-wise overfeeding, broadwise tentering, sizing end low speed, low-tension clot；
S4：Preshrunk, damp and hot blanket preshrunk, preshrunk terminate low speed, low-tension clot.
Further, wool yarn described in step 1 is the 100% wool worsted yarn without anti-shrinking, and yarn count is 70S/2-
100S/2；The terylene is FDY polyester filaments, and fineness is 100D/36F or 120D/48F.
Further, in step S3, warp-wise overfeeding 6% -8%, broadwise tentering is more than Fabric width 1-2cm, heat setting temperature
200—220℃。
Further, in step S3 and S4, clot speed is 20-30m/min, and clot tension is 0.2Mpa-0.3Mpa.
By above technical scheme, the present invention can reach following advantageous effects：
1. woollen fabric provided by the present invention is between wool yarn coil and terylene coil in horizontal, vertical, positive and negative direction
Every being alternately arranged.The performance of polyester filament stabilization is utilized in the structure that this special coil mutually covers, and has restrained wool yarn because of contracting
It is deformed caused by water, felting etc., fabric overall structure is made to stablize, it is shrink-proof.The washable knitting woollen reached by physical form
Fabric avoids various other substances that the shrinkproof mode of chemistry is added, and can retain the original natural feel of wool and product to the greatest extent
Texture, health environment-friendly.
2. wool yarn and polyester filament yarn knit specification mutual cooperation, while ensure that wool content, polyester filament can be right
Wool yarn plays enough restraining functions.
3. the damp and hot sizing of higher temperature is used after overboard, warp-wise overfeeding, the light tentering of broadwise, by overboard, high temperature and overfeeding,
Reduce fabric internal stress to the greatest extent, terylene is shaped complete, further increase the washing stability of woollen fabric, it is fixed
Low speed, low-tension clot after type and preshrunk, the low internal stress state that fabric can be maintained to stablize to the full extent.
4. the washable woollen fabric hair content of non-anti-shrinking is relatively low mostly at present, hair content is more than ten percent
To between twenties, knitting fabric hair content of the invention is up to 50% or more.
Description of the drawings
Fig. 1 is the weave diagram of the washable woollen fabric of the present invention
Fig. 2 is the A upper thread loop graphs of the washable woollen fabric of the present invention
Fig. 3 is the B upper thread loop graphs of the washable woollen fabric of the present invention
Wherein the face A, B is the opposite different sides of fabric
1, first cam system in figure, the 2, second cam system, 3, third cam system, the 4, the 4th cam system, 5, wool yarn line
Circle, 6, polyester filament coil.
Specific implementation mode
Below in conjunction with the drawings and specific embodiments, the invention will be further described, it should be noted that following embodiment
It is only used as explanation of the invention rather than limiting the scope of the invention, protection scope of the present invention is with claims
Subject to the range showed, in the case where not departing from the scope of the invention defined by claims, to reality as described below
Many alterations and modifications can be carried out by applying mode and embodiment.
A kind of washable woollen fabric, as shown in Figure 1, using 1+1 interlock constructions, the braiding of four tunnels passes through sheep
The different configuration yarn feedings of wool worsted yarn and polyester filament.Wherein the first cam system 1 feeds wool yarn, the feeding of the second cam system 2
Polyester filament, third cam system 3 feed polyester filament, and the 4th cam system 4 feeds wool yarn.The wool yarn is without shrinkproof place
100% wool worsted yarn of reason, yarn count is between 70S/2-100S/2, such as can be 70S/2,80S/2,90S/2,100S/2
Deng.The terylene is FDY polyester filaments, and fineness is 100D/36F or 120D/48F.
As shown in Figure 1, from the first cam system to the second cam system, the complete double rib coil of upper and lower needle knitting one
A wool yarn coil 5 and the spaced knot of a polyester filament coil 6 is presented as shown in Figure 2 or Figure 3 in row in row
Structure；From third cam system to the 4th cam system, another complete double rib row of upper and lower needle knitting, such as Fig. 2
Or shown in Fig. 3, a polyester filament coil 6 and the spaced structure of a wool yarn coil 5 are presented in row.
In the identical faces of fabric, as shown in Figure 2 or Figure 3, along wale direction, wool yarn coil 5 and polyester filament
Coil 6 is also in spaced state；On arbitrary vertical plane material plane normal, fabric positive and negative is respectively opposite wool yarn line
Circle 5 and polyester filament coil 6.I.e. gained is knitted fabric, in identical faces cross, Zong Xiangshang, wool yarn coil 5 and polyester filament coil 6
It is alternately arranged braiding, opposite coil in different sides, also respectively wool yarn coil and terylene coil.The washable knitting woollen
The wool content of fabric is 50% or more.
Those skilled in the art can make a change the present invention according to the above specific implementation mode, such as by 1+1
Double rib structure replaces with other similar structures, but equally uses forward and backward, horizontal, the vertical alternately arranged form of coil, to be formed
Stable fabric structure；Polyester filament is for another example replaced with into other yarns with stability, inhibits hair to reach same
The purpose of yarn deformation；For another example the specification such as yarn count etc. of raw material of the present invention is changed.These changes are to do on the basis of the present invention
Change that is going out, being readily apparent that and not having creativeness.
The preparation process of washable woollen fabric provided by the present invention is made below by way of specific embodiment further
Explanation.
Embodiment 1
A kind of preparation process of washable woollen fabric, includes the following steps：
S1：Standby yarn, using the wool worsted yarn of 100% of 70S/2 without anti-shrinking, fineness is that the polyester FDY of 100D/36F is long
Silk；
S2：Weaving, using 1+1 interlock constructions, four tunnels braiding, wherein the first cam system feeds wool yarn, the second lopping
System feeds polyester FDY long filament, and third cam system feeds polyester FDY long filament, and the 4th cam system feeds wool yarn；
S3：Thermal finalization, upper machine thermal finalization, 200 DEG C of thermal finalizations, warp-wise overfeeding 6%, broadwise tentering to more than finished product 1cm after overboard,
Sizing terminates clot, clot speed 20m/min, clot tension 0.2Mpa；
S4：Preshrunk, damp and hot blanket preshrunk, preshrunk terminate clot, clot speed 20m/min, clot tension 0.2Mpa.
Embodiment 2
A kind of preparation process of washable woollen fabric, includes the following steps：
S1：Standby yarn, using the wool worsted yarn of 100% of 80S/2 without anti-shrinking, fineness is that the polyester FDY of 100D/36F is long
Silk；
S2：Weaving, using 1+1 interlock constructions, four tunnels braiding, wherein the first cam system feeds wool yarn, the second lopping
System feeds polyester FDY long filament, and third cam system feeds polyester FDY long filament, and the 4th cam system feeds wool yarn；
S3：Thermal finalization, upper machine thermal finalization, 210 DEG C of thermal finalizations, warp-wise overfeeding 7%, broadwise tentering to more than finished product 1cm after overboard,
Sizing terminates clot, clot speed 20m/s, clot tension 0.2Mpa；
S4：Preshrunk, damp and hot blanket preshrunk, preshrunk terminate clot, clot speed 20m/s, clot tension 0.2Mpa.
Embodiment 3
A kind of preparation process of washable woollen fabric, includes the following steps：
S1：Standby yarn, using the wool worsted yarn of 100% of 90S/2 without anti-shrinking, fineness is that the polyester FDY of 120D/48F is long
Silk；
S2：Weaving, using 1+1 interlock constructions, four tunnels braiding, wherein the first cam system feeds wool yarn, the second lopping
System feeds polyester FDY long filament, and third cam system feeds polyester FDY long filament, and the 4th cam system feeds wool yarn；
S3：Thermal finalization, upper machine thermal finalization, 220 DEG C of thermal finalizations, warp-wise overfeeding 7%, broadwise tentering to more than finished product 2cm after overboard,
Sizing terminates clot, clot speed 25m/s, clot tension 0.3Mpa；
S4：Preshrunk, damp and hot blanket preshrunk, preshrunk terminate clot, clot speed 25m/s, clot tension 0.3Mpa.
Embodiment 4
A kind of preparation process of washable woollen fabric, includes the following steps：
S1：Standby yarn, using the wool worsted yarn of 100% of 100S/2 without anti-shrinking, fineness is that the polyester FDY of 120D/48F is long
Silk；
S2：Weaving, using 1+1 interlock constructions, four tunnels braiding, wherein the first cam system feeds wool yarn, the second lopping
System feeds polyester FDY long filament, and third cam system feeds polyester FDY long filament, and the 4th cam system feeds wool yarn；
S3：Thermal finalization, upper machine thermal finalization, 220 DEG C of thermal finalizations, warp-wise overfeeding 8%, broadwise tentering to more than finished product 2cm after overboard,
Sizing terminates clot, clot speed 30m/s, clot tension 0.3Mpa；
S4：Preshrunk, damp and hot blanket preshrunk, preshrunk terminate clot, clot speed 30m/s, clot tension 0.3Mpa.
To the washable fabric of knitting woollen obtained by the preparation process using embodiment 1-4, various physicochemical property surveys are carried out
Examination, test result is as follows：
Test example 1
Composition test：
| Test event | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 |
| GB/T 2910-2009 | 53% mao 47% is washed | 61% mao 39% is washed | 59% mao 41% is washed | 65% mao 35% is washed |
Size changing rate is tested：
Quantitative measurement：
It is real by the above test example it is found that there is higher wool content by the washable woollen fabric obtained by present invention process
It applies example 1-4 to be averaged wool content 59.5%, compared to the existing washable wool fabric without feld proofing, wool content has
Larger promotion, fabric have stronger quality sense, washable simultaneously in guarantee, do not lose the texture of wool fabric itself
And characteristic.In terms of washing, dry-cleaning, cold perm size changing rate, the performance of this fabric is good, more common wool knitting fabrics have compared with
Big promotion, the especially fabric of embodiment 2, not only wool content is high, but also the equal very little of every shrinkage.Pilling performance exists
3-4 grades or more, meet the requirement of national standard.
Claims (10)
1. a kind of washable woollen fabric, using 1+1 interlock constructions, four tunnels braiding, wherein the first cam system is fed
Enter wool yarn, the second cam system feeds polyester filament, and third cam system feeds polyester filament, and the 4th cam system feeds hair
Yarn；From the first cam system to the second cam system, the complete double rib row of upper and lower needle knitting one is in row
An existing wool yarn coil and the spaced structure of a polyester filament coil；From third cam system to the 4th cam system,
Another complete double rib row of upper and lower needle knitting, is presented a polyester filament coil and a wool yarn in row
The spaced structure of coil；In the identical faces of fabric, along wale direction, wool yarn coil and polyester filament coil are in
Spaced state；On arbitrary vertical plane material plane normal, fabric positive and negative is respectively that opposite wool yarn coil and terylene are long
Wire coil.
2. a kind of washable woollen fabric according to claim 1, it is characterised in that：The wool yarn is without shrinkproof place
100% wool worsted yarn of reason.
3. a kind of washable woollen fabric according to claim 1, it is characterised in that：The wool yarn yarn count is 70S/
2—100S/2。
4. a kind of washable woollen fabric according to claim 1, it is characterised in that：The polyester filament is washed for FDY
Synthetic fibre long filament, fineness are 100D/36F or 120D/48F.
5. according to a kind of any washable woollen fabric of claim 1-4, it is characterised in that：The washable hair
The wool content of fabric is knitted 50% or more.
6. a kind of preparation process of washable woollen fabric, includes the following steps：
S1：Standby yarn, using 100% wool worsted yarn and 100% polyester filament；
S2：Weaving, using 1+1 interlock constructions, four tunnels braiding, wherein the first cam system feeds wool yarn, the second lopping
System feeds polyester FDY long filament, and third cam system feeds polyester FDY long filament, and the 4th cam system feeds wool yarn；
S3：Thermal finalization, upper machine thermal finalization, warp-wise overfeeding, broadwise tentering, clot after sizing after overboard；
S4：Preshrunk, damp and hot blanket preshrunk, clot after preshrunk.
7. a kind of preparation process of washable woollen fabric according to claim 7, it is characterised in that：In step S1,
The wool yarn is the 100% wool worsted yarn without anti-shrinking, and yarn count is 70S/2-100S/2, and the terylene is washed for FDY
Synthetic fibre long filament, fineness are 100D/36F or 120D/48F.
8. a kind of preparation process of washable woollen fabric according to claim 7, it is characterised in that：In step S3,
Warp-wise overfeeding 6%-8%, broadwise tentering are more than Fabric width 1-2cm, and heat setting temperature is 200-220 DEG C.
9. a kind of preparation process of washable woollen fabric according to claim 7, it is characterised in that：Step S3 and S4
In, the clot speed is 20-30m/min.
10. a kind of preparation process of washable woollen fabric according to claim 7, it is characterised in that：Step S3 and
In S4, the clot tension is 0.2Mpa -0.3Mpa.