CN108466465A - 一种临床护理垫及其制备方法 - Google Patents
一种临床护理垫及其制备方法 Download PDFInfo
- Publication number
- CN108466465A CN108466465A CN201810221526.0A CN201810221526A CN108466465A CN 108466465 A CN108466465 A CN 108466465A CN 201810221526 A CN201810221526 A CN 201810221526A CN 108466465 A CN108466465 A CN 108466465A
- Authority
- CN
- China
- Prior art keywords
- woven fabric
- conservancy diversion
- clinical care
- water conservancy
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种临床护理垫及其制备方法，所述的护理垫包括表层无纺布、导流透气层、吸水层以及底膜；所述的导流透气层为聚酯无纺布、玉米纤维无纺布与海绵复合而成，聚酯无纺布、玉米纤维无纺布与海绵上均匀分布有若干导流透气结构，所述的导流透气结构为贯穿聚酯无纺布、玉米纤维无纺布与海绵的导流孔，导流孔直径为85‑92微米，导流孔的密度为120‑140个/cm2。本发明特别适用于新生儿或生病婴儿的临床护理使用，本发明临床护理垫透气性好，可快速排出湿气，防止闷热。
Description
技术领域
本发明属于临床护理用品技术领域，尤其涉及一种临床护理垫及其制备方法。
背景技术
护理垫由PE膜、无纺布、绒毛浆、高分子等材质制成的一次性卫生用品，主要用于医院手术、妇科检查、产妇护理、幼儿看护、瘫痪病人大小便失禁、妇女经期时候使用。
护理垫可分为婴儿护理垫，产妇护理垫，成人护理垫。
婴儿临床护理垫主要用于新生儿，起到隔离尿液作用，以保证下面的褥子或床垫不被尿液浸湿，因此婴儿护理垫也被称为是隔尿垫。当护理垫湿了最好立即更换，保证宝宝的屁股干爽。特别是对于生病的婴儿，更要减少其尿液、汗液刺激。
新生儿皮肤非常娇嫩，特别不耐湿热。在新生儿的临床护理过程中，对排泄物的处理占据了整个护理过程的重要地位；婴儿大小便从体内排出时具有一定温度，导致婴儿皮肤和护理垫之间湿度、温度上升，加上新生儿大小便频繁，使其皮肤经常处于湿度和温度过高的环境中，因此，使用婴儿护理垫时，若尿湿后不及时更换，会十分闷热。
传统的婴儿临床护理垫，多关注其表层的柔软度、舒适度，以及吸水性等指标。但这些指标都无法解决护理垫吸收尿液导致的闷热问题，特别是夏季，热气无法快速排出，闷热更加严重，从而引起皮肤的湿疹和红屁股。对于有疾病的婴儿或新生儿，上述问题会更加严重。
因此，研发一种适合夏季使用的可以减轻闷热问题的婴儿临床护理垫，为新生儿或病儿轻松散出闷热湿气，解决湿疹、红屁股等问题，成为临床护理技术中广受专注的课题。
发明内容
本发明提供一种临床护理垫及其制备方法，以达到以下目的：使婴儿临床护理垫在柔软度好、吸水性高的基础上，提高其透气散湿性能，实现干爽、凉感、透气的效果。
为解决上述技术问题，本发明采取的技术方案如下：
一种临床护理垫及其制备方法，所述的护理垫包括表层无纺布、导流透气层、吸水层以及底膜。
所述的导流透气层为聚酯无纺布、玉米纤维无纺布与海绵复合而成，聚酯无纺布、玉米纤维无纺布与海绵上均匀分布有若干导流透气结构，所述的导流透气结构为贯穿聚酯无纺布、玉米纤维无纺布与海绵的导流孔，导流孔直径为85-92微米，导流孔的密度为120-140个/cm2。
所述的聚酯无纺布：由聚丙烯纤维制备而成，克重为1.5g/㎡，厚度为0.05mm；
所述的玉米纤维无纺布：克重为8.5 g/㎡，厚度为0.25mm，含水量为2.3-2.8%；
所述的海绵：克重为2.5 g/㎡，厚度为0.15mm，含水量为4.2-4.5%。
所述的吸水层由木浆与高分子混合而成，并由无尘纸包覆，吸水层厚度为1.9-2.3mm；木浆与高分子的质量配比为1：7。
所述的木浆为：针叶长纤维木浆，机械粉碎至纤维长度为3.8-4.2mm的绒毛浆；
所述的高分子为：日本住友高分子，其比重为1.70g/cm3，收缩率为0.1%，吸水率为0.02%，洛氏硬度为91，抗张强度为150MPa，泊松比为0.49，导热系数为0.57W/m/K，极限氧指数为48%。
所述的表层无纺布为水刺无纺布，由竹纤维、锦纶、薄荷纤维、醋酸纤维以及草珊瑚纤维按照7：2：3：1：5的质量比混合制备而成。
所述的底膜为防水透气底膜，由壳聚糖纤维无纺布、PE高分子透气膜和PP纺粘无纺布复合而成，所述壳聚糖纤维无纺布、PE高分子透气膜和PP纺粘无纺布的厚度比为1：2：1，构成的底膜厚度为0.01-0.015mm，底膜透气量为2680g/平方/24小时。
所述的一种临床护理垫的制备方法，包括以下步骤：
步骤1、制备表层无纺布
（1）将竹纤维、锦纶、薄荷纤维、醋酸纤维以及草珊瑚纤维按照配方比例预混，加经过开松、梳理，得到纤维网，纤网的MD:CD为 2.8-3.3:1；
（2）排出纤维网中的空气，使纤维网进入水刺区后能有效地吸收水射流的能量，最后得到湿纤维网，射流时间为20-25min；
（3）将得到的湿纤维网低温烘干至含水量为6.5-6.8%，所述的烘干温度为58-64℃，得到的表层无纺布收卷备用。
步骤2、制备导流透气层
（1）将聚酯无纺布、玉米纤维无纺布与海绵依次铺设，牵引至热压辊，经热压辊压合，热压温度为87-89℃，热压强度为23-24MPa，线速度为16-18m/s。
（2）热压后经激光打孔，打孔密度为120-140个/cm2，孔径85-92微米，形成导流孔，导流孔依次贯穿聚酯无纺布、玉米纤维无纺布与海绵。
（3）打孔后采用超声波处理，超声波频率为28kHz，超声波处理时间为4-5s，温度为75-78℃；处理后，得到导流透气层，收卷备用。
步骤3、制备吸水芯体
选用针叶长纤维木浆，机械粉碎至纤维长度为3.8-4.2mm的绒毛浆，与高分子均匀混合并铺设成型，经无尘纸包覆，得到吸水芯体；木浆与高分子的质量配比为1：7。
所述的高分子为：日本住友高分子，其比重为1.70g/cm3，收缩率为0.1%，吸水率为0.02%，洛氏硬度为91，抗张强度为150MPa，泊松比为0.49，导热系数为0.57W/m/K，极限氧指数为48%。
步骤4、复合成型
步骤3得到的吸水芯体经压辊压实，形成吸水层，吸水层厚度为1.9-2.3mm；随着制备护理垫的设备的运行，吸水层依次与导流透气层、表层无纺布、底膜复合在一起，经热压花纹和封边，得到成品；成品自上而下依次为：表层无纺布、导流透气层、吸水层以及底膜，所述的吸水层与底膜之间以及护理垫周边通过喷涂热敏胶复合在一起，其他位置均不喷胶。
与现有技术相比，本发明的有益效果为：
1、本发明特别适用于新生儿或生病婴儿的临床护理使用，本发明临床护理垫采用特殊结构和制备方法，透气性好，100℃蒸汽透气量≥166g/㎡/小时，婴儿排尿后，可快速排出湿气，防止闷热。
2、本发明临床护理垫，使用特殊导流透气层，通过特殊的制备工艺，吸水速度快，可快速吸干尿液，婴儿使用时，0.5s内可完全吸收尿液，反渗率低于0.2%，表层干爽，有效防止尿液刺激婴儿肌肤，即使吸尿后未及时更换护理垫，也不会反渗出尿液；防止婴儿排尿后湿热引起湿疹、红屁股等问题；
3、本发明临床护理垫，采用特殊的表层无纺布，柔软、干爽，且夏天具有明显的凉感，温度可降低2-2.5℃，明显减轻婴儿排尿后因温度高透气差引起湿疹、起痱子等问题。
本发明临床护理垫，可用于新生儿日常护理使用和婴儿的临床护理使用，对于因疾病在医院治疗的婴儿，本发明临床护理垫的效果和重要性更加突出，在婴儿或病儿无法正常翻身的情况下，本发明可很好的解决因湿热带来的一系列问题。
具体实施例
下面结合实施例对本发明做进一步说明：
实施例1 一种临床护理垫及其制备方法
一种临床护理垫及其制备方法，所述的护理垫包括表层无纺布、导流透气层、吸水层以及底膜。
所述的导流透气层为聚酯无纺布、玉米纤维无纺布与海绵复合而成，聚酯无纺布、玉米纤维无纺布与海绵上均匀分布有若干导流透气结构，所述的导流透气结构为贯穿聚酯无纺布、玉米纤维无纺布与海绵的导流孔，导流孔直径为85微米，导流孔的密度为120个/cm2。
所述的聚酯无纺布：由聚丙烯纤维制备而成，克重为1.5g/㎡，厚度为0.05mm；
所述的玉米纤维无纺布：克重为8.5 g/㎡，厚度为0.25mm，含水量为2.3-2.8%；
所述的海绵：克重为2.5 g/㎡，厚度为0.15mm，含水量为4.2-4.5%。
所述的吸水层由木浆与高分子混合而成，并由无尘纸包覆，吸水层厚度为1.9mm；木浆与高分子的质量配比为1：7。
所述的木浆为：针叶长纤维木浆，机械粉碎至纤维长度为3.8-4.2mm的绒毛浆；
所述的高分子为：日本住友高分子，其比重为1.70g/cm3，收缩率为0.1%，吸水率为0.02%，洛氏硬度为91，抗张强度为150MPa，泊松比为0.49，导热系数为0.57W/m/K，极限氧指数为48%。
所述的表层无纺布为水刺无纺布，由竹纤维、锦纶、薄荷纤维、醋酸纤维以及草珊瑚纤维按照7：2：3：1：5的质量比混合制备而成。
所述的底膜为防水透气底膜，由壳聚糖纤维无纺布、PE高分子透气膜和PP纺粘无纺布复合而成，所述壳聚糖纤维无纺布、PE高分子透气膜和PP纺粘无纺布的厚度比为1：2：1，构成的底膜厚度为0.015mm，底膜透气量为2680g/平方/24小时。
所述的一种临床护理垫的制备方法，包括以下步骤：
步骤1、制备表层无纺布
（4）将竹纤维、锦纶、薄荷纤维、醋酸纤维以及草珊瑚纤维按照配方比例预混，加经过开松、梳理，得到纤维网，纤网的MD:CD为 2.8:1；
（5）排出纤维网中的空气，使纤维网进入水刺区后能有效地吸收水射流的能量，最后得到湿纤维网，射流时间为20min；
（6）将得到的湿纤维网低温烘干至含水量为6.5%，所述的烘干温度为58℃，得到的表层无纺布收卷备用。
步骤2、制备导流透气层
（1）将聚酯无纺布、玉米纤维无纺布与海绵依次铺设，牵引至热压辊，经热压辊压合，热压温度为87℃，热压强度为23MPa，线速度为16m/s。
（2）热压后经激光打孔，打孔密度为120个/cm2，孔径85微米，形成导流孔，导流孔依次贯穿聚酯无纺布、玉米纤维无纺布与海绵。
（3）打孔后采用超声波处理，超声波频率为28kHz，超声波处理时间为4s，温度为75℃；处理后，得到导流透气层，收卷备用。
步骤3、制备吸水芯体
选用针叶长纤维木浆，机械粉碎至纤维长度为3.8-4.2mm的绒毛浆，与高分子均匀混合并铺设成型，经无尘纸包覆，得到吸水芯体；木浆与高分子的质量配比为1：7。
所述的高分子为：日本住友高分子，其比重为1.70g/cm3，收缩率为0.1%，吸水率为0.02%，洛氏硬度为91，抗张强度为150MPa，泊松比为0.49，导热系数为0.57W/m/K，极限氧指数为48%。
步骤4、复合成型
步骤3得到的吸水芯体经压辊压实，形成吸水层吸，水层厚度为1.9mm；随着制备护理垫的设备的运行，吸水层依次与导流透气层、表层无纺布、底膜复合在一起，经热压花纹和封边，得到成品；成品自上而下依次为：表层无纺布、导流透气层、吸水层以及底膜，所述的吸水层与底膜之间以及护理垫周边通过喷涂热敏胶复合在一起，其他位置均不喷胶。
本实施例制备的临床护理垫，适用于婴儿夏季使用，特别是新生儿；本发明临床护理垫透气性好，100℃蒸汽透气量为166g/㎡/小时，婴儿排尿后，可快速排出湿气，防止闷热。使用特殊导流透气层，通过特殊的制备工艺，吸水速度快，可快速吸干尿液，婴儿使用时，0.5s内可完全吸收尿液，反渗率低于0.2%，表层干爽，有效防止尿液刺激婴儿肌肤，即使吸尿后未及时更换护理垫，也不会反渗出尿液；防止婴儿排尿后湿热引起湿疹、红屁股等问题；采用特殊的表层无纺布，柔软、干爽，且夏天具有明显的凉感，温度可降低2℃，防止婴儿排尿后因温度高透气差引起湿疹、起痱子等问题。
实施例2一种临床护理垫及其制备方法
一种临床护理垫及其制备方法，所述的护理垫包括表层无纺布、导流透气层、吸水层以及底膜。
所述的导流透气层为聚酯无纺布、玉米纤维无纺布与海绵复合而成，聚酯无纺布、玉米纤维无纺布与海绵上均匀分布有若干导流透气结构，所述的导流透气结构为贯穿聚酯无纺布、玉米纤维无纺布与海绵的导流孔，导流孔直径为92微米，导流孔的密度为140个/cm2。
所述的聚酯无纺布：由聚丙烯纤维制备而成，克重为1.5g/㎡，厚度为0.05mm；
所述的玉米纤维无纺布：克重为8.5 g/㎡，厚度为0.25mm，含水量为2.3-2.8%；
所述的海绵：克重为2.5 g/㎡，厚度为0.15mm，含水量为4.2-4.5%。
所述的吸水层由木浆与高分子混合而成，并由无尘纸包覆，吸水层厚度为2.3mm；木浆与高分子的质量配比为1：7。
所述的木浆为：针叶长纤维木浆，机械粉碎至纤维长度为3.8-4.2mm的绒毛浆；
所述的高分子为：日本住友高分子，其比重为1.70g/cm3，收缩率为0.1%，吸水率为0.02%，洛氏硬度为91，抗张强度为150MPa，泊松比为0.49，导热系数为0.57W/m/K，极限氧指数为48%。
所述的表层无纺布为水刺无纺布，由竹纤维、锦纶、薄荷纤维、醋酸纤维以及草珊瑚纤维按照7：2：3：1：5的质量比混合制备而成。
所述的底膜为防水透气底膜，由壳聚糖纤维无纺布、PE高分子透气膜和PP纺粘无纺布复合而成，所述壳聚糖纤维无纺布、PE高分子透气膜和PP纺粘无纺布的厚度比为1：2：1，构成的底膜厚度为0.01mm，底膜透气量为2680g/平方/24小时。
所述的一种临床护理垫的制备方法，包括以下步骤：
步骤1、制备表层无纺布
（7）将竹纤维、锦纶、薄荷纤维、醋酸纤维以及草珊瑚纤维按照配方比例预混，加经过开松、梳理，得到纤维网，纤网的MD:CD为 3.3:1；
（8）排出纤维网中的空气，使纤维网进入水刺区后能有效地吸收水射流的能量，最后得到湿纤维网，射流时间为25min；
（9）将得到的湿纤维网低温烘干至含水量为6.8%，所述的烘干温度为64℃，得到的表层无纺布收卷备用。
步骤2、制备导流透气层
（1）将聚酯无纺布、玉米纤维无纺布与海绵依次铺设，牵引至热压辊，经热压辊压合，热压温度为89℃，热压强度为24MPa，线速度为18m/s。
（2）热压后经激光打孔，打孔密度为140个/cm2，孔径92微米，形成导流孔，导流孔依次贯穿聚酯无纺布、玉米纤维无纺布与海绵。
（3）打孔后采用超声波处理，超声波频率为28kHz，超声波处理时间为5s，温度为78℃；处理后，得到导流透气层，收卷备用。
步骤3、制备吸水芯体
选用针叶长纤维木浆，机械粉碎至纤维长度为3.8-4.2mm的绒毛浆，与高分子均匀混合并铺设成型，经无尘纸包覆，得到吸水芯体；木浆与高分子的质量配比为1：7。
所述的高分子为：日本住友高分子，其比重为1.70g/cm3，收缩率为0.1%，吸水率为0.02%，洛氏硬度为91，抗张强度为150MPa，泊松比为0.49，导热系数为0.57W/m/K，极限氧指数为48%。
步骤4、复合成型
步骤3得到的吸水芯体经压辊压实，形成吸水层吸，水层厚度为2.3mm；随着制备护理垫的设备的运行，吸水层依次与导流透气层、表层无纺布、底膜复合在一起，经热压花纹和封边，得到成品；成品自上而下依次为：表层无纺布、导流透气层、吸水层以及底膜，所述的吸水层与底膜之间以及护理垫周边通过喷涂热敏胶复合在一起，其他位置均不喷胶。
本实施例制备的临床护理垫，适用于婴儿夏季使用，特别是新生儿；本发明临床护理垫透气性好，100℃蒸汽透气量为186g/㎡/小时，婴儿排尿后，可快速排出湿气，防止闷热。使用特殊导流透气层，通过特殊的制备工艺，吸水速度快，可快速吸干尿液，婴儿使用时，0.5s内可完全吸收尿液，反渗率低于0.2%，表层干爽，有效防止尿液刺激婴儿肌肤，即使吸尿后未及时更换护理垫，也不会反渗出尿液；防止婴儿排尿后湿热引起湿疹、红屁股等问题；采用特殊的表层无纺布，柔软、干爽，且夏天具有明显的凉感，温度可降低2.5℃，防止婴儿排尿后因温度高透气差引起湿疹、起痱子等问题。
在上述实施例中，对本发明的最佳实施方式做了描述，很显然，在本发明的发明构思下，仍可做出很多变化。在此，在本发明的发明构思下所做出的任何改变都将落入本发明的保护范围内。
Claims (8)
1.一种临床护理垫，其特征在于：所述的护理垫包括表层无纺布、导流透气层、吸水层以及底膜；
所述的导流透气层为聚酯无纺布、玉米纤维无纺布与海绵复合而成，聚酯无纺布、玉米纤维无纺布与海绵上均匀分布有若干导流透气结构，所述的导流透气结构为贯穿聚酯无纺布、玉米纤维无纺布与海绵的导流孔，导流孔直径为85-92微米，导流孔的密度为120-140个/cm2。
2.根据权利要求1所述的一种临床护理垫，其特征在于：所述的聚酯无纺布：由聚丙烯纤维制备而成；
所述的玉米纤维无纺布：克重为8.5 g/㎡，厚度为0.25mm，含水量为2.3-2.8%。
3.根据权利要求1所述的一种临床护理垫，其特征在于：所述的吸水层由木浆与高分子混合而成，并由无尘纸包覆，吸水层厚度为1.9-2.3mm；木浆与高分子的质量配比为1：7；
所述的木浆为：针叶长纤维木浆，机械粉碎至纤维长度为3.8-4.2mm的绒毛浆；
所述的高分子为：日本住友高分子，其比重为1.70g/cm3，收缩率为0.1%，吸水率为0.02%，洛氏硬度为91，抗张强度为150MPa，泊松比为0.49，导热系数为0.57W/m/K，极限氧指数为48%。
4.根据权利要求1所述的一种临床护理垫，其特征在于：所述的表层无纺布为水刺无纺布，由竹纤维、锦纶、薄荷纤维、醋酸纤维以及草珊瑚纤维按照7：2：3：1：5的质量比混合制备而成。
5.根据权利要求1所述的一种临床护理垫，其特征在于：所述的底膜为防水透气底膜，由壳聚糖纤维无纺布、PE高分子透气膜和PP纺粘无纺布复合而成。
6.根据权利要求1所述的一种临床护理垫，其特征在于：所述壳聚糖纤维无纺布、PE高分子透气膜和PP纺粘无纺布的厚度比为1：2：1，构成的底膜厚度为0.01-0.015mm，底膜透气量≥2680g/平方/24小时。
7.根据权利要求1所述的一种临床护理垫的制备方法，其特征在于：包括制备表层无纺布步骤；所述的制备表层无纺布：
将竹纤维、锦纶、薄荷纤维、醋酸纤维以及草珊瑚纤维按照配方比例预混，加经过开松、梳理，得到纤维网，纤网的MD:CD为 2.8-3.3:1；
排出纤维网中的空气，使纤维网进入水刺区后能有效地吸收水射流的能量，最后得到湿纤维网，射流时间为20-25min；
将得到的湿纤维网低温烘干至含水量为6.5-6.8%，所述的烘干温度为58-64℃，得到的表层无纺布。
8.根据权利要求1所述的一种临床护理垫的制备方法，其特征在于：还包括制备导流透气层步骤；所述的制备导流透气层：
（1）将聚酯无纺布、玉米纤维无纺布与海绵依次铺设，牵引至热压辊，经热压辊压合，热压温度为87-89℃，热压强度为23-24MPa，线速度为16-18m/s；
（2）热压后经激光打孔，打孔密度为120-140个/cm2，孔径85-92微米，形成导流孔，导流孔依次贯穿聚酯无纺布、玉米纤维无纺布与海绵；
（3）打孔后采用超声波处理，超声波频率为28kHz，超声波处理时间为4-5s，温度为75-78℃；处理后，得到导流透气层。