CN108456840A - A kind of handware high-strength wear-resistant alloy stick - Google Patents
A kind of handware high-strength wear-resistant alloy stick Download PDFInfo
- Publication number
- CN108456840A CN108456840A CN201810179625.7A CN201810179625A CN108456840A CN 108456840 A CN108456840 A CN 108456840A CN 201810179625 A CN201810179625 A CN 201810179625A CN 108456840 A CN108456840 A CN 108456840A
- Authority
- CN
- China
- Prior art keywords
- content
- accounts
- alloy
- pellet
- account
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of handware high-strength wear-resistant alloy sticks, including：Alloy pellet and alloy surface, alloy surface are fixed on the outer surface of alloy pellet by way of founding；Alloy pellet specifically includes the ingredient of following mass percentage：The content of C accounts for 0.6 0.8%, the content of Si accounts for 1.2 2.2%, the content of Mn accounts for 0.7 1.1%, the content of Co accounts for 0.2 0.6%, and the content of Zn accounts for 0.7 1.1%, and the content of Al accounts for 2.2 2.5%, the content of Ti accounts for 1.8 2.4%, the content of Ni accounts for 0.8 1.2%, and the content of Mo accounts for 0.4 1.6%, and surplus is Fe and inevitable impurity；Alloy surface specifically includes the ingredient of following mass percentage：The content of Mg accounts for 15 25%, and the content of titanium accounts for 1 3%, and the content of Co accounts for 1 5%, the content of Ni accounts for 8 16%, the content of Mn accounts for 11 16%, and the content of W accounts for 3 7%, and the content of V accounts for 1 5%, the content of lubricant accounts for 1 9%, remaining is melt polypropylene, by the above-mentioned means, the present invention can not only improve the surface abrasion resistance and core strength of alloy bar, and cost can also be reduced, improve use value.
Description
Technical field
The present invention relates to a kind of handware, more particularly to a kind of handware high-strength wear-resistant alloy stick.
Background technology
Handware refers to metals such as gold, silver, copper, iron, tin by processing, and the tool cast is used for fixed east
West, processing thing, decoration etc., are mainly used for the industries such as automobile, space flight, building, and the hardware used in automobile industry at present
Part is based on stick class, axis class, and such handware is in material used, mostly uses conventional alloys block greatly and is made, not only needed for
Production it is larger, and its physical characteristic can not be carried out compared with quantum jump, and be showed in terms of intensity and wear-resisting property especially prominent.
Invention content
The invention mainly solves the technical problem of providing a kind of handware high-strength wear-resistant alloy sticks, can not only carry
The surface abrasion resistance and core strength of high alloy stick, and cost can also be reduced, improve use value.
In order to solve the above technical problems, one aspect of the present invention is：A kind of handware high intensity is provided
Wear-proof alloy stick, including：Alloy pellet and alloy surface, the alloy surface are fixed on the alloy core by way of founding
The outer surface of block；
The alloy pellet specifically includes the ingredient of following mass percentage：
The content of C accounts for 0.6-0.8%, and the content of Si accounts for 1.2-2.2%, and the content of Mn accounts for 0.7-1.1%, and the content of Co accounts for 0.2-
The content of 0.6%, Zn account for 0.7-1.1%, and the content of Al accounts for 2.2-2.5%, and the content of Ti accounts for 1.8-2.4%, and the content of Ni accounts for 0.8-
The content of 1.2%, Mo account for 0.4-1.6%, and surplus is Fe and inevitable impurity；
The alloy surface specifically includes the ingredient of following mass percentage：The content of Mg accounts for 15-25%, and the content of titanium accounts for 1-
The content of 3%, Co account for 1-5%, and the content of Ni accounts for 8-16%, and the content of Mn accounts for 11-16%, and the content of W accounts for 3-7%, and the content of V accounts for 1-
5%, the content of lubricant accounts for 1-9%, remaining is melt polypropylene.
In a preferred embodiment of the present invention, the inevitable impurity is mixed for any one or more of P, S, N
It closes.
In a preferred embodiment of the present invention, the inevitable total impurities are no more than 0.02%.
In a preferred embodiment of the present invention, the single content of the inevitable impurity is no more than 0.005%.
In a preferred embodiment of the present invention, a diameter of 12-20mm of the alloy pellet.
In a preferred embodiment of the present invention, the thickness of the alloy surface is 1.5-3.5mm.
The beneficial effects of the invention are as follows：
1）A kind of handware high-strength wear-resistant alloy stick of the present invention, by the alloy pellet to alloy bar inside center at
Divide, match and reasonably improved, the intensity of alloy pellet greatly improved, so that the core strength of alloy bar obtains greatly
Width is promoted；
2）A kind of handware high-strength wear-resistant alloy stick of the present invention by ingredient to the alloy surface outside alloy bar, is matched
Than reasonably being improved, the wear-resisting property of alloy surface greatly improved, to strengthen the surface abrasion resistance of alloy bar；
3）A kind of handware high-strength wear-resistant alloy stick of the present invention, by way of by the alloy surface of high abrasion by founding
The content of metal component can be reduced compared to traditional single alloy material by being fixed on the alloy pellet surface of high intensity, to
Reduce production cost.
Specific implementation mode
The preferred embodiments of the present invention will be described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that so as to make a clearer definition of the protection scope of the present invention.
Embodiment 1：
A kind of handware high-strength wear-resistant alloy stick, including：Alloy pellet and alloy surface, the alloy surface pass through founding
Mode be fixed on the outer surface of the alloy pellet；
The alloy pellet specifically includes the ingredient of following mass percentage：
The content that the content of C accounts for 0.6%, Si accounts for the content of 2.2%, Mn and accounts for the content of 0.7%, Co and account for the content of 0.6%, Zn and account for
The content that the content of 0.7%, Al account for 2.5%, Ti accounts for the content of 1.8%, Ni and accounts for the content of 1.2%, Mo and account for 0.4%, surplus be Fe and
Inevitable impurity；
The alloy surface specifically includes the ingredient of following mass percentage：The content of Mg accounts for 25%, and the content of titanium accounts for 1%, Co
Content account for the content of 5%, Ni and account for the content of 8%, Mn and account for the content of 16%, W and account for the content of 3%, V and account for 5%, the content of lubricant accounts for
1%, remaining is melt polypropylene.
Embodiment 2：
A kind of handware high-strength wear-resistant alloy stick, including：Alloy pellet and alloy surface, the alloy surface pass through founding
Mode be fixed on the outer surface of the alloy pellet；
The alloy pellet specifically includes the ingredient of following mass percentage：
The content that the content of C accounts for 0.8%, Si accounts for the content of 1.2%, Mn and accounts for the content of 1.1%, Co and account for the content of 0.2%, Zn and account for
The content that the content of 1.1%, Al account for 2.2%, Ti accounts for the content of 2.4%, Ni and accounts for the content of 0.8%, Mo and account for 1.6%, surplus be Fe and
Inevitable impurity；
The alloy surface specifically includes the ingredient of following mass percentage：The content of Mg accounts for 15%, and the content of titanium accounts for 3%, Co
Content account for the content of 1%, Ni and account for the content of 16%, Mn and account for the content of 11%, W and account for the content of 7%, V and account for 1%, the content of lubricant accounts for
9%, remaining is melt polypropylene.
Embodiment 3：
A kind of handware high-strength wear-resistant alloy stick, including：Alloy pellet and alloy surface, the alloy surface pass through founding
Mode be fixed on the outer surface of the alloy pellet；
The alloy pellet specifically includes the ingredient of following mass percentage：
The content that the content of C accounts for 0.7%, Si accounts for the content of 1.7%, Mn and accounts for the content of 0.9%, Co and account for the content of 0.4%, Zn and account for
The content that the content of 0.9%, Al account for 2.35%, Ti accounts for the content of 2.1%, Ni and accounts for the content of 1.0%, Mo and account for 1.0%, surplus be Fe with
And inevitable impurity；
The alloy surface specifically includes the ingredient of following mass percentage：The content of Mg accounts for 20%, and the content of titanium accounts for 2%, Co
Content account for the content of 3%, Ni and account for the content of 12%, Mn and account for the content of 13.5%, W and account for the content of 5%, V and account for 3%, the content of lubricant
5% is accounted for, remaining is melt polypropylene.
It further illustrates, the inevitable impurity is any one or more mixing of P, S, N；It is described inevitable
Total impurities be no more than 0.02%；The single content of the inevitable impurity is no more than 0.005%.
It further illustrates, a diameter of 12-20mm of the alloy pellet；The thickness of the alloy surface is 1.5-3.5mm.
Further illustrate, a kind of handware of the present invention is specific as follows with the preparation method of high-strength wear-resistant alloy stick：
1）Each component materials of alloy pellet are chosen according to said ratio, and are mixed in input high-temperature smelting pot and are carried out high-temperature molten
It closes, then in casting to specified mold, alloy pellet is obtained after cooling；
2）Above-mentioned alloy pellet is put into the center of casting box chamber so that exist between the periphery and cavity of alloy pellet certain
Alloy pellet is then fixed in gap；
3）Each component materials of alloy surface are chosen according to said ratio, and are mixed in input high-temperature smelting pot and are carried out high-temperature molten
It closes, obtains high temperature alloy liquid；
4）High temperature alloy liquid is poured into the casting box chamber for being fixed with alloy pellet so that high temperature alloy liquid wraps alloy
Pellet obtains handware high-strength wear-resistant alloy stick after final cooling.
It is different from the prior art, a kind of handware high-strength wear-resistant alloy stick of the present invention, on the one hand, by alloy bar
The ingredient of the alloy pellet of inside center, proportioning are reasonably improved, and the intensity of alloy pellet greatly improved, so that
The core strength of alloy bar is increased dramatically；On the other hand, by ingredient to the alloy surface outside alloy bar, match into
Row is rational to be improved, and the wear-resisting property of alloy surface greatly improved, to strengthen the surface abrasion resistance of alloy bar；In addition,
A kind of handware high-strength wear-resistant alloy stick of the present invention, by the alloy surface of high abrasion by founding by way of be fixed on
The alloy pellet surface of high intensity can reduce the content of metal component compared to traditional single alloy material, to reduce life
Produce cost.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, any made by repair
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (6)
1. a kind of handware high-strength wear-resistant alloy stick, which is characterized in that including：Alloy pellet and alloy surface, the conjunction
Golden watch layer is fixed on the outer surface of the alloy pellet by way of founding；
The alloy pellet specifically includes the ingredient of following mass percentage：
The content of C accounts for 0.6-0.8%, and the content of Si accounts for 1.2-2.2%, and the content of Mn accounts for 0.7-1.1%, and the content of Co accounts for 0.2-
The content of 0.6%, Zn account for 0.7-1.1%, and the content of Al accounts for 2.2-2.5%, and the content of Ti accounts for 1.8-2.4%, and the content of Ni accounts for 0.8-
The content of 1.2%, Mo account for 0.4-1.6%, and surplus is Fe and inevitable impurity；
The alloy surface specifically includes the ingredient of following mass percentage：The content of Mg accounts for 15-25%, and the content of titanium accounts for 1-
The content of 3%, Co account for 1-5%, and the content of Ni accounts for 8-16%, and the content of Mn accounts for 11-16%, and the content of W accounts for 3-7%, and the content of V accounts for 1-
5%, the content of lubricant accounts for 1-9%, remaining is melt polypropylene.
2. handware according to claim 1 high-strength wear-resistant alloy stick, which is characterized in that described inevitably miscellaneous
Matter is any one or more mixing of P, S, N.
3. handware according to claim 1 high-strength wear-resistant alloy stick, which is characterized in that described inevitably miscellaneous
Matter total amount is no more than 0.02%.
4. handware according to claim 1 high-strength wear-resistant alloy stick, which is characterized in that described inevitably miscellaneous
The single content of matter is no more than 0.005%.
5. handware according to claim 1 high-strength wear-resistant alloy stick, which is characterized in that the alloy pellet it is straight
Diameter is 12-20mm.
6. handware according to claim 1 high-strength wear-resistant alloy stick, which is characterized in that the thickness of the alloy surface
Degree is 1.5-3.5mm.