CN108455917A - A kind of novel glass brick and preparation method thereof - Google Patents
A kind of novel glass brick and preparation method thereof Download PDFInfo
- Publication number
- CN108455917A CN108455917A CN201810125641.8A CN201810125641A CN108455917A CN 108455917 A CN108455917 A CN 108455917A CN 201810125641 A CN201810125641 A CN 201810125641A CN 108455917 A CN108455917 A CN 108455917A
- Authority
- CN
- China
- Prior art keywords
- parts
- kaolin
- dispersant
- novel glass
- cordierite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of novel glass bricks, include the raw material of following parts by weight：20~30 parts of discarded glass, 13~22 parts of quartz, 4~8 parts of lime stone, 13~19 parts of cordierite, 6~12 parts of mullite, 7~15 parts of kaolin, 7~11 parts of yellow ground, 15~25 parts of cement, 3~6 parts of modified coal ash, 2~5 parts of calcium phosphate, 1~4 part of magnesium sulfate, 2~3 parts of sodium tetraborate, 1~3 part of silver oxide, 2~4 parts of aluminium oxide, 2~4 parts of dispersant, 3~6 parts of binder.The novel glass brick anti-pressure ability is strong, and not easy to crack, service life is long, and preparation process is simple, efficient and at low cost, is suitble to promote.
Description
Technical field
The invention belongs to glassware technical fields, and in particular to a kind of novel glass brick and preparation method thereof.
Background technology
Glass block is with transparent or coloured glass material compression moulding bulk or hollow box-like, the larger glass system of the bodily form
Product.Its kind mainly has glass hollow block, glass solid brick, mosaic to be not included.In most cases, glass block is not done
It is used for finishing material, but as structural material, it is used as similar functions such as wall, screen, partitions.
But glass block anti-pressure ability in the prior art is weak, easy to crack, service life is short, of high cost, is not suitable for promoting.
Invention content
The present invention provides a kind of novel glass bricks and preparation method thereof, solve problems of the prior art, institute
It is strong to state novel glass brick anti-pressure ability, not easy to crack, service life is long, and preparation process is simple, efficient and at low cost, is suitble to
It promotes.
It is of the existing technology in order to solve the problems, such as, it adopts the following technical scheme that：
A kind of novel glass brick includes the raw material of following parts by weight：20~30 parts of discarded glass, 13~22 parts of quartz, lime
4~8 parts of stone, 13~19 parts of cordierite, 6~12 parts of mullite, 7~15 parts of kaolin, 7~11 parts of yellow ground, 15~25 parts of cement,
3~6 parts of modified coal ash, 2~5 parts of calcium phosphate, 1~4 part of magnesium sulfate, 2~3 parts of sodium tetraborate, 1~3 part of silver oxide, aluminium oxide
2~4 parts, 2~4 parts of dispersant, 3~6 parts of binder.
Preferably, the novel glass brick includes the raw material of following parts by weight：23~28 parts of discarded glass, quartz 15
~20 parts, 5~7 parts of lime stone, 15~18 parts of cordierite, 8~10 parts of mullite, 9~13 parts of kaolin, 8~10 parts of yellow ground, water
17~22 parts of mud, 4~5 parts of modified coal ash, 3~4 parts of calcium phosphate, 2~3 parts of magnesium sulfate, 2.1~2.8 parts of sodium tetraborate, oxidation
1.5~2.6 parts of silver, 2.3~3.6 parts of aluminium oxide, 2.4~3.7 parts of dispersant, 4~5 parts of binder.
Preferably, the novel glass brick includes the raw material of following parts by weight：25 parts of discarded glass, 18 parts of quartz, stone
6 parts of lime stone, 17 parts of cordierite, 9 parts of mullite, 11 parts of kaolin, 9 parts of yellow ground, 20 parts of cement, 4.5 parts of modified coal ash, phosphoric acid
3.4 parts of calcium, 2.3 parts of magnesium sulfate, 2.7 parts of sodium tetraborate, 2 parts of silver oxide, 2.9 parts of aluminium oxide, 3 parts of dispersant, binder 4.5
Part.
Preferably, the modified coal ash is made using following methods：
Flyash is dried in 100~110 DEG C of baking ovens first, then the flyash after drying is put into high-speed kneading machine, is added
Enter to be equivalent to the aluminate coupling agent of flyash weight 4%, 3% wooden sodium sulfonate, 3% triethyl citrate, 1%
Atoleine and 4% talcum powder, after mixed at high speed, drying, attrition grinding is at superfines.
Preferably, the kaolin is the kaolin after 1000~1200 DEG C of high-temperature calcinations.
Preferably, the dispersant is selected from boric acid.
A method of the novel glass brick is prepared, is included the following steps：
（1）Discarded glass is weighed by above-mentioned formula, quartz, lime stone, cordierite, mullite, kaolin, yellow ground, cement, is changed
Property flyash, calcium phosphate, magnesium sulfate, sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder, it is spare；
（2）By discarded glass removal of impurities, cleaning, air-dry be placed on ball milling 10~20 minutes in ball mill；
（3）By step（2）The discarded glass powder of gained is uniformly mixed with quartz, cordierite, mullite, is subsequently placed in earthenware
In crucible, 1400 DEG C are warming up to, keeps the temperature 100 minutes after firing, Water Quenching；
（4）By step（3）The product of gained and lime stone, kaolin, yellow ground, cement, modified coal ash, calcium phosphate, magnesium sulfate,
Sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder are placed in ball milling 1~2 hour in ball mill together, then cross 100~
200 mesh, obtain mixed material；
（5）It is 30~40% that material moisture is added water into mixed material, is uniformly mixed, pours into mold, then by mold
It moves into mo(u)ldenpress, cold moudling obtains adobe；
（6）Above-mentioned gained adobe is moved into tunnel oven, after firing 1 hour, moves into annealing kiln annealing 50 minutes, discharging to get
The novel glass brick.
Preferably, the step（6）Middle firing temperature is 600~800 DEG C.
Compared with prior art, the present invention it has the advantages that：
Novel glass brick anti-pressure ability of the present invention is strong, and not easy to crack, service life is long, and preparation process is simple, efficient
And it is at low cost, it is suitble to promote, it is specific as follows：
（1）Novel glass brick of the present invention is using discarded glass, quartz, lime stone, cordierite, mullite, kaolin etc.
It as raw material, mutually acts synergistically between raw material, in sintering process, long column shape tissue can be formed in intrinsic silicon, and be in nothing
Regular distribution state, such microscopic structure is conducive to improve the thermal shock resistance of product, to avoid leading because the temperature difference is larger
Product stripping, cracking are caused, its service life is improved；
（2）Novel glass brick of the present invention uses discarded glass for raw material, while cost is reduced, also reduces discarded glass
Harm of the glass to environment and people, and a kind of new side of obsolete material recycling has been createed, it not only solves useless
The garbage disposal problem for abandoning glass, can also save natural resources, reduce a large amount of energy expenditure.
Specific implementation mode
Present invention will be further explained below with reference to specific examples.These embodiments are merely to illustrate the present invention and do not have to
In limiting the scope of the invention.
Embodiment 1
The present embodiment is related to a kind of novel glass brick, includes the raw material of following parts by weight：20 parts of discarded glass, 13 parts of quartz,
4 parts of lime stone, 13 parts of cordierite, 6 parts of mullite, 7 parts of kaolin, 7 parts of yellow ground, 15 parts of cement, 3 parts of modified coal ash, phosphoric acid
2 parts of calcium, 1 part of magnesium sulfate, 2 parts of sodium tetraborate, 1 part of silver oxide, 2 parts of aluminium oxide, 2 parts of dispersant, 3 parts of binder.
Wherein, the modified coal ash is made using following methods：
Flyash is dried in 100 DEG C of baking ovens first, then the flyash after drying is put into high-speed kneading machine, phase is added
When in the aluminate coupling agent of flyash weight 4%, 3% wooden sodium sulfonate, 3% triethyl citrate, 1% liquid
Paraffin and 4% talcum powder, after mixed at high speed, drying, attrition grinding is at superfines.
Wherein, the kaolin is the kaolin after 1000 DEG C of high-temperature calcinations.
Wherein, the dispersant is selected from boric acid.
A method of the novel glass brick is prepared, is included the following steps：
（1）Discarded glass is weighed by above-mentioned formula, quartz, lime stone, cordierite, mullite, kaolin, yellow ground, cement, is changed
Property flyash, calcium phosphate, magnesium sulfate, sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder, it is spare；
（2）By discarded glass removal of impurities, cleaning, air-dry be placed on ball milling 10 minutes in ball mill；
（3）By step（2）The discarded glass powder of gained is uniformly mixed with quartz, cordierite, mullite, is subsequently placed in earthenware
In crucible, 1400 DEG C are warming up to, keeps the temperature 100 minutes after firing, Water Quenching；
（4）By step（3）The product of gained and lime stone, kaolin, yellow ground, cement, modified coal ash, calcium phosphate, magnesium sulfate,
Sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder are placed in ball milling 1 hour in ball mill together, then cross 100~200
Mesh obtains mixed material；
（5）It is 30% that material moisture is added water into mixed material, is uniformly mixed, pours into mold, then mold is moved into
In mo(u)ldenpress, cold moudling obtains adobe；
（6）Above-mentioned gained adobe is moved into tunnel oven, after firing 1 hour, moves into annealing kiln annealing 50 minutes, discharging to get
The novel glass brick.
Wherein, the step（6）Middle firing temperature is 600 DEG C.
Embodiment 2
The present embodiment is related to a kind of novel glass brick, includes the raw material of following parts by weight：30 parts of discarded glass, 22 parts of quartz,
8 parts of lime stone, 19 parts of cordierite, 12 parts of mullite, 15 parts of kaolin, 11 parts of yellow ground, 25 parts of cement, 6 parts of modified coal ash, phosphorus
5 parts of sour calcium, 4 parts of magnesium sulfate, 3 parts of sodium tetraborate, 3 parts of silver oxide, 4 parts of aluminium oxide, 4 parts of dispersant, 6 parts of binder.
Wherein, the modified coal ash is made using following methods：
Flyash is dried in 110 DEG C of baking ovens first, then the flyash after drying is put into high-speed kneading machine, is added suitable
In the aluminate coupling agent of flyash weight 4%, 3% wooden sodium sulfonate, 3% triethyl citrate, 1% liquid stone
Wax and 4% talcum powder, after mixed at high speed, drying, attrition grinding is at superfines.
Wherein, the kaolin is the kaolin after 1200 DEG C of high-temperature calcinations.
Wherein, the dispersant is selected from boric acid.
A method of the novel glass brick is prepared, is included the following steps：
（1）Discarded glass is weighed by above-mentioned formula, quartz, lime stone, cordierite, mullite, kaolin, yellow ground, cement, is changed
Property flyash, calcium phosphate, magnesium sulfate, sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder, it is spare；
（2）By discarded glass removal of impurities, cleaning, air-dry be placed on ball milling 20 minutes in ball mill；
（3）By step（2）The discarded glass powder of gained is uniformly mixed with quartz, cordierite, mullite, is subsequently placed in earthenware
In crucible, 1400 DEG C are warming up to, keeps the temperature 100 minutes after firing, Water Quenching；
（4）By step（3）The product of gained and lime stone, kaolin, yellow ground, cement, modified coal ash, calcium phosphate, magnesium sulfate,
Sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder are placed in ball milling 2 hours in ball mill together, then cross 100~200
Mesh obtains mixed material；
（5）It is 40% that material moisture is added water into mixed material, is uniformly mixed, pours into mold, then mold is moved into
In mo(u)ldenpress, cold moudling obtains adobe；
（6）Above-mentioned gained adobe is moved into tunnel oven, after firing 1 hour, moves into annealing kiln annealing 50 minutes, discharging to get
The novel glass brick.
Wherein, the step（6）Middle firing temperature is 800 DEG C.
Embodiment 3
The present embodiment is related to a kind of novel glass brick, includes the raw material of following parts by weight：23 parts of discarded glass, 15 parts of quartz,
5 parts of lime stone, 15 parts of cordierite, 8 parts of mullite, 9 parts of kaolin, 8 parts of yellow ground, 17 parts of cement, 4 parts of modified coal ash, phosphoric acid
3 parts of calcium, 2 parts of magnesium sulfate, 2.1 parts of sodium tetraborate, 1.5 parts of silver oxide, 2.3 parts of aluminium oxide, 2.4 parts of dispersant, 4 parts of binder.
Wherein, the modified coal ash is made using following methods：
Flyash is dried in 103 DEG C of baking ovens first, then the flyash after drying is put into high-speed kneading machine, is added suitable
In the aluminate coupling agent of flyash weight 4%, 3% wooden sodium sulfonate, 3% triethyl citrate, 1% liquid stone
Wax and 4% talcum powder, after mixed at high speed, drying, attrition grinding is at superfines.
Wherein, the kaolin is the kaolin after 1000 DEG C of high-temperature calcinations.
Wherein, the dispersant is selected from boric acid.
A method of the novel glass brick is prepared, is included the following steps：
（1）Discarded glass is weighed by above-mentioned formula, quartz, lime stone, cordierite, mullite, kaolin, yellow ground, cement, is changed
Property flyash, calcium phosphate, magnesium sulfate, sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder, it is spare；
（2）By discarded glass removal of impurities, cleaning, air-dry be placed on ball milling 13 minutes in ball mill；
（3）By step（2）The discarded glass powder of gained is uniformly mixed with quartz, cordierite, mullite, is subsequently placed in earthenware
In crucible, 1400 DEG C are warming up to, keeps the temperature 100 minutes after firing, Water Quenching；
（4）By step（3）The product of gained and lime stone, kaolin, yellow ground, cement, modified coal ash, calcium phosphate, magnesium sulfate,
Sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder are placed in ball milling 1.2 hours in ball mill together, then cross 100~
200 mesh, obtain mixed material；
（5）It is 33% that material moisture is added water into mixed material, is uniformly mixed, pours into mold, then mold is moved into
In mo(u)ldenpress, cold moudling obtains adobe；
（6）Above-mentioned gained adobe is moved into tunnel oven, after firing 1 hour, moves into annealing kiln annealing 50 minutes, discharging to get
The novel glass brick.
Wherein, the step（6）Middle firing temperature is 650 DEG C.
Embodiment 4
The present embodiment is related to a kind of novel glass brick, includes the raw material of following parts by weight：28 parts of discarded glass, 20 parts of quartz,
7 parts of lime stone, 18 parts of cordierite, 10 parts of mullite, 13 parts of kaolin, 10 parts of yellow ground, 22 parts of cement, 5 parts of modified coal ash, phosphorus
4 parts of sour calcium, 3 parts of magnesium sulfate, 2.8 parts of sodium tetraborate, 2.6 parts of silver oxide, 3.6 parts of aluminium oxide, 3.7 parts of dispersant, binder 5
Part.
Wherein, the modified coal ash is made using following methods：
Flyash is dried in 105 DEG C of baking ovens first, then the flyash after drying is put into high-speed kneading machine, is added suitable
In the aluminate coupling agent of flyash weight 4%, 3% wooden sodium sulfonate, 3% triethyl citrate, 1% liquid stone
Wax and 4% talcum powder, after mixed at high speed, drying, attrition grinding is at superfines.
Wherein, the kaolin is the kaolin after 1100 DEG C of high-temperature calcinations.
Wherein, the dispersant is selected from boric acid.
A method of the novel glass brick is prepared, is included the following steps：
（1）Discarded glass is weighed by above-mentioned formula, quartz, lime stone, cordierite, mullite, kaolin, yellow ground, cement, is changed
Property flyash, calcium phosphate, magnesium sulfate, sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder, it is spare；
（2）By discarded glass removal of impurities, cleaning, air-dry be placed on ball milling 15 minutes in ball mill；
（3）By step（2）The discarded glass powder of gained is uniformly mixed with quartz, cordierite, mullite, is subsequently placed in earthenware
In crucible, 1400 DEG C are warming up to, keeps the temperature 100 minutes after firing, Water Quenching；
（4）By step（3）The product of gained and lime stone, kaolin, yellow ground, cement, modified coal ash, calcium phosphate, magnesium sulfate,
Sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder are placed in ball milling 1.5 hours in ball mill together, then cross 100~
200 mesh, obtain mixed material；
（5）It is 35% that material moisture is added water into mixed material, is uniformly mixed, pours into mold, then mold is moved into
In mo(u)ldenpress, cold moudling obtains adobe；
（6）Above-mentioned gained adobe is moved into tunnel oven, after firing 1 hour, moves into annealing kiln annealing 50 minutes, discharging to get
The novel glass brick.
Wherein, the step（6）Middle firing temperature is 700 DEG C.
Embodiment 5
The present embodiment is related to a kind of novel glass brick, includes the raw material of following parts by weight：25 parts of discarded glass, 18 parts of quartz,
6 parts of lime stone, 17 parts of cordierite, 9 parts of mullite, 11 parts of kaolin, 9 parts of yellow ground, 20 parts of cement, 4.5 parts of modified coal ash, phosphorus
3.4 parts of sour calcium, 2.3 parts of magnesium sulfate, 2.7 parts of sodium tetraborate, 2 parts of silver oxide, 2.9 parts of aluminium oxide, 3 parts of dispersant, binder 4.5
Part.
Wherein, the modified coal ash is made using following methods：
Flyash is dried in 108 DEG C of baking ovens first, then the flyash after drying is put into high-speed kneading machine, phase is added
When in the aluminate coupling agent of flyash weight 4%, 3% wooden sodium sulfonate, 3% triethyl citrate, 1% liquid
Paraffin and 4% talcum powder, after mixed at high speed, drying, attrition grinding is at superfines.
Wherein, the kaolin is the kaolin after 1150 DEG C of high-temperature calcinations.
Wherein, the dispersant is selected from boric acid.
A method of the novel glass brick is prepared, is included the following steps：
（1）Discarded glass is weighed by above-mentioned formula, quartz, lime stone, cordierite, mullite, kaolin, yellow ground, cement, is changed
Property flyash, calcium phosphate, magnesium sulfate, sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder, it is spare；
（2）By discarded glass removal of impurities, cleaning, air-dry be placed on ball milling 18 minutes in ball mill；
（3）By step（2）The discarded glass powder of gained is uniformly mixed with quartz, cordierite, mullite, is subsequently placed in earthenware
In crucible, 1400 DEG C are warming up to, keeps the temperature 100 minutes after firing, Water Quenching；
（4）By step（3）The product of gained and lime stone, kaolin, yellow ground, cement, modified coal ash, calcium phosphate, magnesium sulfate,
Sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder are placed in ball milling 1.8 hours in ball mill together, then cross 100~
200 mesh, obtain mixed material；
（5）It is 38% that material moisture is added water into mixed material, is uniformly mixed, pours into mold, then mold is moved into
In mo(u)ldenpress, cold moudling obtains adobe；
（6）Above-mentioned gained adobe is moved into tunnel oven, after firing 1 hour, moves into annealing kiln annealing 50 minutes, discharging to get
The novel glass brick.
Wherein, the step（6）Middle firing temperature is 750 DEG C.
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of novel glass brick, which is characterized in that include the raw material of following parts by weight：20~30 parts of discarded glass, quartz
13~22 parts, 4~8 parts of lime stone, 13~19 parts of cordierite, 6~12 parts of mullite, 7~15 parts of kaolin, 7~11 parts of yellow ground,
15~25 parts of cement, 3~6 parts of modified coal ash, 2~5 parts of calcium phosphate, 1~4 part of magnesium sulfate, 2~3 parts of sodium tetraborate, silver oxide
1~3 part, 2~4 parts of aluminium oxide, 2~4 parts of dispersant, 3~6 parts of binder.
2. novel glass brick according to claim 1, which is characterized in that include the raw material of following parts by weight：Discarded glass
23~28 parts, 15~20 parts of quartz, 5~7 parts of lime stone, 15~18 parts of cordierite, 8~10 parts of mullite, kaolin 9~13
Part, 8~10 parts of yellow ground, 17~22 parts of cement, 4~5 parts of modified coal ash, 3~4 parts of calcium phosphate, 2~3 parts of magnesium sulfate, tetraboric acid
2.1~2.8 parts of sodium, 1.5~2.6 parts of silver oxide, 2.3~3.6 parts of aluminium oxide, 2.4~3.7 parts of dispersant, 4~5 parts of binder.
3. novel glass brick according to claim 1, which is characterized in that include the raw material of following parts by weight：Discarded glass
25 parts, 18 parts of quartz, 6 parts of lime stone, 17 parts of cordierite, 9 parts of mullite, 11 parts of kaolin, 9 parts of yellow ground, 20 parts of cement, change
4.5 parts of flyash of property, 3.4 parts of calcium phosphate, 2.3 parts of magnesium sulfate, 2.7 parts of sodium tetraborate, 2 parts of silver oxide, aluminium oxide 2.9 part, point
3 parts of powder, 4.5 parts of binder.
4. novel glass brick according to claim 1, which is characterized in that the modified coal ash uses following methods system
：
Flyash is dried in 100~110 DEG C of baking ovens first, then the flyash after drying is put into high-speed kneading machine, is added
Enter to be equivalent to the aluminate coupling agent of flyash weight 4%, 3% wooden sodium sulfonate, 3% triethyl citrate, 1%
Atoleine and 4% talcum powder, after mixed at high speed, drying, attrition grinding is at superfines.
5. novel glass brick according to claim 1, which is characterized in that the kaolin is through 1000~1200 DEG C of high temperature
Kaolin after calcining.
6. novel glass brick according to claim 1, which is characterized in that the dispersant is selected from boric acid.
7. a kind of method preparing any one of claim 1~6 novel glass brick, which is characterized in that include the following steps：
（1）Discarded glass is weighed by above-mentioned formula, quartz, lime stone, cordierite, mullite, kaolin, yellow ground, cement, is changed
Property flyash, calcium phosphate, magnesium sulfate, sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder, it is spare；
（2）By discarded glass removal of impurities, cleaning, air-dry be placed on ball milling 10~20 minutes in ball mill；
（3）By step（2）The discarded glass powder of gained is uniformly mixed with quartz, cordierite, mullite, is subsequently placed in earthenware
In crucible, 1400 DEG C are warming up to, keeps the temperature 100 minutes after firing, Water Quenching；
（4）By step（3）The product of gained and lime stone, kaolin, yellow ground, cement, modified coal ash, calcium phosphate, magnesium sulfate,
Sodium tetraborate, silver oxide, aluminium oxide, dispersant, binder are placed in ball milling 1~2 hour in ball mill together, then cross 100~
200 mesh, obtain mixed material；
（5）It is 30~40% that material moisture is added water into mixed material, is uniformly mixed, pours into mold, then by mold
It moves into mo(u)ldenpress, cold moudling obtains adobe；
（6）Above-mentioned gained adobe is moved into tunnel oven, after firing 1 hour, moves into annealing kiln annealing 50 minutes, discharging to get
The novel glass brick.
8. preparation method according to claim 7, which is characterized in that the step（6）Middle firing temperature is 600~800
℃。