CN108441036A - PVC waterproof coatings with anti-aging effect - Google Patents
PVC waterproof coatings with anti-aging effect Download PDFInfo
- Publication number
- CN108441036A CN108441036A CN201810111637.6A CN201810111637A CN108441036A CN 108441036 A CN108441036 A CN 108441036A CN 201810111637 A CN201810111637 A CN 201810111637A CN 108441036 A CN108441036 A CN 108441036A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof coatings
- pvc waterproof
- pvc
- aging effect
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses the PVC waterproof coatings with anti-aging effect, the raw material composition of the PVC waterproof coatings is by weight ratio:Polyvinyl chloride resin, 80~100 parts, cycloaliphatic epoxy resin, 20~35 parts, di-n-octyl phthalate, 10~25 parts, calcium carbonate, 15~30 parts, haloflex, 10~20 parts, zinc borate, 8~15 parts, magnesium stearate, 5~15 parts, phosphorous vinegar, 15~25 parts.The present invention need to only coat 0.1~0.3mm thickness by optimizing component formula, the PVC waterproof coatings provided, when use, with good water resistance, anti-ultraviolet aging performance, and not occurring coating shedding situation after 120 DEG C of heat ageing 240h, adhesive force is good, and service life is long.
Description
Technical field
The present invention relates to a kind of PVC waterproof materials, and in particular to a kind of PVC waterproof coatings with anti-aging effect.
Background technology
Polyvinyl chloride (PVC) is most important in man-made polymer and uses most common one kind, and being primarily due to it has
Prodigious variability can coordinate different purposes and needs during manufacturing PVC products, various plasticizers and addition is added
Agent changes its physics and chemical property.After the maximum of PVC is characterized as addition liquid plasticizer, glass transition temperature will be opened
Begin to decline, because semi-rigid can be prepared to the soft material with extensive spring rate in plasticization, this is soft PVC tool
The reason of practicability.Existing PVC water-proof air-inflateds fabric is widely used in inflatable life jacket, biochemical defence suit, oxygen bag, inflation
The fields such as pad, airbed, air dome, air bag, aircushion vehicle and Waterproof Breathable top grade dress material, and it is generally by base fabric and patch
The PVC film in base fabric side is closed to form.In particular for air dome in use, needing that there is good antioxidation, but
One layer of PVC film is only arranged in existing air dome fabric, and antioxidant effect is poor.
Invention content
The technical problem to be solved by the present invention is to:One layer of PVC film is only arranged in existing air dome fabric, anti-oxidant
Effect is poor, and the present invention provides the PVC waterproof coatings with anti-aging effect to solve the above problems.
The present invention is achieved through the following technical solutions:
PVC waterproof coatings with anti-aging effect, the raw material of the PVC waterproof coatings forms is by weight ratio:
Polyvinyl chloride resin, 80~100 parts,
Cycloaliphatic epoxy resin, 20~35 parts,
Di-n-octyl phthalate, 10~25 parts,
Calcium carbonate, 15~30 parts,
Haloflex, 10~20 parts,
Zinc borate, 8~15 parts,
Magnesium stearate, 5~15 parts,
Phosphorous vinegar, 15~25 parts.
Preferably, the raw material composition of the PVC waterproof coatings is by weight ratio:
Polyvinyl chloride resin, 85~95 parts,
Cycloaliphatic epoxy resin, 25~32 parts,
Di-n-octyl phthalate, 12~20 parts,
Calcium carbonate, 18~25 parts,
Haloflex, 12~18 parts,
Zinc borate, 10~13 parts,
Magnesium stearate, 6~12 parts,
Phosphorous vinegar, 18~22 parts.
Preferably, the raw material composition of the PVC waterproof coatings is by weight ratio:
Polyvinyl chloride resin, 90 parts,
Cycloaliphatic epoxy resin, 28 parts,
Di-n-octyl phthalate, 18 parts,
Calcium carbonate, 20 parts,
Haloflex, 16 parts,
Zinc borate, 12 parts,
Magnesium stearate, 10 parts,
Phosphorous vinegar, 20 parts.
Preferably, the raw material composition of the PVC waterproof coatings further includes diisooctyl phthalate, the O-phthalic
The mass values of sour di-n-octyl and diisooctyl phthalate are 1~3.5.
Preferably, the mass values of the di-n-octyl phthalate and diisooctyl phthalate are 2.
The present invention has the advantage that and advantageous effect:
The present invention need to only coat 0.1~0.3mm thickness by optimizing component formula, the PVC waterproof coatings provided, when use
Degree has good water resistance, anti-ultraviolet aging performance, and does not occur coating shedding situation after 120 DEG C of heat ageing 240h,
Adhesive force is good, and service life is long.
Specific implementation mode
To make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiment, the present invention is made
Further to be described in detail, exemplary embodiment of the invention and its explanation are only used for explaining the present invention, are not intended as to this
The restriction of invention.
Embodiment 1
The present invention provides a kind of PVC waterproof coatings with anti-aging effect, and the raw material composition of the PVC waterproof coatings is pressed
Weight is:
80~100 parts of polyvinyl chloride resin, 20~35 parts of cycloaliphatic epoxy resin, 10~25 parts of di-n-octyl phthalate, carbon
15~30 parts of sour calcium, 10~20 parts of haloflex, 8~15 parts of zinc borate, 5~15 parts of magnesium stearate, phosphorous vinegar 15~25
Part.The mass values of di-n-octyl phthalate and diisooctyl phthalate are 1~3.5.
Embodiment 2
The present invention provides a kind of PVC waterproof coatings with anti-aging effect, and the raw material composition of the PVC waterproof coatings is pressed
Weight is:
80~100 parts of polyvinyl chloride resin, 20~35 parts of cycloaliphatic epoxy resin, 10~25 parts of di-n-octyl phthalate, carbon
15~30 parts of sour calcium, 10~20 parts of haloflex, 8~15 parts of zinc borate, 5~15 parts of magnesium stearate, phosphorous vinegar 15~25
Part.The mass values of di-n-octyl phthalate and diisooctyl phthalate are 1~3.5.
Embodiment 3
The present invention provides a kind of PVC waterproof coatings with anti-aging effect, and the raw material composition of the PVC waterproof coatings is pressed
Weight is:
85~95 parts of polyvinyl chloride resin, 25~32 parts of cycloaliphatic epoxy resin, 12~20 parts of di-n-octyl phthalate, carbon
18~25 parts of sour calcium, 12~18 parts of haloflex, 10~13 parts of zinc borate, 6~12 parts of magnesium stearate, phosphorous vinegar 18~
22 parts.The mass values of di-n-octyl phthalate and diisooctyl phthalate are 1~3.5.
Embodiment 4
The present invention provides a kind of PVC waterproof coatings with anti-aging effect, and the raw material composition of the PVC waterproof coatings is pressed
Weight is:
85~95 parts of polyvinyl chloride resin, 25~32 parts of cycloaliphatic epoxy resin, 12~20 parts of di-n-octyl phthalate, carbon
18~25 parts of sour calcium, 12~18 parts of haloflex, 10~13 parts of zinc borate, 6~12 parts of magnesium stearate, phosphorous vinegar 18~
22 parts.The mass values of di-n-octyl phthalate and diisooctyl phthalate are 1~3.5.
Embodiment 5
The present invention provides a kind of PVC waterproof coatings with anti-aging effect, and the raw material composition of the PVC waterproof coatings is pressed
Weight is:
90 parts of polyvinyl chloride resin, 28 parts of cycloaliphatic epoxy resin, 18 parts of di-n-octyl phthalate, 20 parts of calcium carbonate, chlorination
16 parts of polyethylene, 12 parts of zinc borate, 10 parts of magnesium stearate, phosphorous acid, 20 parts.Di-n-octyl phthalate and phthalic acid
The mass values of di-isooctyl are 2.
Above-described specific implementation mode has carried out further the purpose of the present invention, technical solution and advantageous effect
It is described in detail, it should be understood that the foregoing is merely the specific implementation mode of the present invention, is not intended to limit the present invention
Protection domain, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should all include
Within protection scope of the present invention.
Claims (5)
1. the PVC waterproof coatings with anti-aging effect, which is characterized in that the raw material composition of the PVC waterproof coatings is by weight
Part matches:
Polyvinyl chloride resin, 80~100 parts,
Cycloaliphatic epoxy resin, 20~35 parts,
Di-n-octyl phthalate, 10~25 parts,
Calcium carbonate, 15~30 parts,
Haloflex, 10~20 parts,
Zinc borate, 8~15 parts,
Magnesium stearate, 5~15 parts,
Phosphorous vinegar, 15~25 parts.
2. the PVC waterproof coatings according to claim 1 with anti-aging effect, which is characterized in that the PVC waterproofs apply
The raw material of layer forms:
Polyvinyl chloride resin, 85~95 parts,
Cycloaliphatic epoxy resin, 25~32 parts,
Di-n-octyl phthalate, 12~20 parts,
Calcium carbonate, 18~25 parts,
Haloflex, 12~18 parts,
Zinc borate, 10~13 parts,
Magnesium stearate, 6~12 parts,
Phosphorous vinegar, 18~22 parts.
3. the PVC waterproof coatings according to claim 2 with anti-aging effect, which is characterized in that the PVC waterproofs apply
The raw material of layer forms:
Polyvinyl chloride resin, 90 parts,
Cycloaliphatic epoxy resin, 28 parts,
Di-n-octyl phthalate, 18 parts,
Calcium carbonate, 20 parts,
Haloflex, 16 parts,
Zinc borate, 12 parts,
Magnesium stearate, 10 parts,
Phosphorous vinegar, 20 parts.
4. the PVC waterproof coatings according to claim 1 with anti-aging effect, which is characterized in that the PVC waterproofs apply
The raw material composition of layer further includes diisooctyl phthalate, and the di-n-octyl phthalate and phthalic acid two are different pungent
The mass values of ester are 1~3.5.
5. the PVC waterproof coatings according to claim 4 with anti-aging effect, which is characterized in that the O-phthalic
The mass values of sour di-n-octyl and diisooctyl phthalate are 2.