CN108409224A - A kind of building concrete formula - Google Patents
A kind of building concrete formula Download PDFInfo
- Publication number
- CN108409224A CN108409224A CN201810370095.4A CN201810370095A CN108409224A CN 108409224 A CN108409224 A CN 108409224A CN 201810370095 A CN201810370095 A CN 201810370095A CN 108409224 A CN108409224 A CN 108409224A
- Authority
- CN
- China
- Prior art keywords
- parts
- auxiliary agent
- brick
- building
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of building concrete formula, each raw material component is remembered by weight：Include 95 128 parts of cement, 48 53 parts of water, 37 52 parts of stone, 53 62 parts of sand, 38 parts of iron filings, 8 14 parts of brick powder and 36 parts of auxiliary agent, the brick powder is discarded fine powder of the building brick after drying and crushing.The auxiliary agent includes 23 parts of polyacrylic acid and 23 parts of carboxymethyl cellulose.It applies the technical scheme of the present invention, concrete is directly used in finishing and uses, and corrugationless after drying, surface smoothness is high, improves using effect；And it is smoothed out repeatedly without construction personnel, construction efficiency greatly improves.
Description
Technical field
The invention belongs to construction engineering technical fields, in particular to a kind of building concrete formula.
Background technology
Concrete is the current maximum construction material of dosage in the world, because its is cheap, bearing capacity is strong and durability is good
And it is widely used in various fields.In the prior art, in most cases, it is by concrete casting to the skeleton being made of reinforcing bar
In, the armored concrete of rock-steady structure is formed, the flatness of appearance is not taken into account that and whether has the appearance of fold.And also have
For the concrete in finishing, it is desirable that it not only has higher intensity, also requires it with higher smoothness, and prevent out
Existing fold, but existing universal concrete formulation cannot be satisfied the requirement directly used.Therefore, a kind of corrugationless, smooth is developed
High concrete formulation is spent to have broad application prospects.
Invention content
The main purpose of the present invention is to provide a kind of building concrete formulas, it is intended to solve skill existing in the prior art
Art problem.
In order to achieve the above purpose, the present invention provides a kind of building concrete formula, each raw material component is by weight
Note：Include 95-128 parts of cement, 48-53 parts of water, 37-52 parts of stone, 53-62 parts of sand, 3-8 parts of iron filings, 8-
The auxiliary agent of 14 parts of brick powder and 3-6 part, the brick powder is discarded fine powder of the building brick after drying and crushing.
Preferably, the auxiliary agent includes 2-3 parts of polyacrylic acid and 2-3 parts of carboxymethyl cellulose.
Preferably, each raw material component is remembered by weight：Include 95-115 parts of cement, 49-52 parts of water, 41-51 parts
Stone, 54-58 parts of sand, 4-7 parts of iron filings, 10-13 parts of brick powder and 5 parts of auxiliary agent, the auxiliary agent are poly- by 2.5 parts
Acrylic acid and 2.5 parts of carboxymethyl cellulose coordinate.
Preferably, each raw material component is remembered by weight：Include 100 parts of cement, 50 parts of water, 46 parts of stone, 55 parts
Sand, 5 parts of iron filings, 10 parts of brick powder and 5 parts of auxiliary agent, the auxiliary agent is by 2.5 parts of polyacrylic acid and 2.5 parts of carboxylic
Methylcellulose coordinates.
It applies the technical scheme of the present invention, concrete is directly used in finishing and uses, corrugationless after drying, surface smoothness
Height improves using effect；And it is smoothed out repeatedly without construction personnel, construction efficiency greatly improves.
Specific implementation mode
It should be noted that in the absence of conflict, the features in the embodiments and the embodiments of the present application can phase
Mutually combination.
It is noted that described further below be all exemplary, it is intended to provide further instruction to the application.Unless another
It indicates, all technical and scientific terms used herein has usual with the application person of an ordinary skill in the technical field
The identical meanings of understanding.
It should be noted that term used herein above is merely to describe specific implementation mode, and be not intended to restricted root
According to the illustrative embodiments of the application.As used herein, unless the context clearly indicates otherwise, otherwise singulative
It is also intended to include plural form, additionally, it should be understood that, when in the present specification using term "comprising" and/or " packet
Include " when, indicate existing characteristics, step, operation, device, component and/or combination thereof.
It should be noted that the term " first ", " second " etc. in the description and claims of this application are to be used for
Similar object is distinguished, without being used to describe specific sequence or precedence.It should be appreciated that the data used in this way are suitable
It can be interchanged in the case of, so that presently filed embodiment described herein for example can be in addition to those of being described herein
Sequence in addition is implemented.
In addition, belonging to " comprising " and " having " and their any deformation, it is intended that it includes example to cover non-exclusive
Such as, process, method, system, product or the equipment for containing series of steps or unit those of are not necessarily limited to clearly to list
Step or unit, but may include not listing clearly or for intrinsic other of these processes, method, product or equipment
Step or unit.
The present invention provides a kind of building concrete formulas, improve existing concrete formulation, can be suitable for room
The finishing of inner wall surface, makes metope corrugationless and smoothness is high.And multiple formulations are provided with, it is specific as follows：
Formula 1
A kind of building concrete formula, each raw material component are remembered by weight：Include 95 parts of cement, 48 parts of water, 52 parts of stone
Son, 62 parts of sand, 8 parts of iron filings, 8 parts of brick powder and 6 parts of auxiliary agent, the brick powder are discarded building brick through xeraphium
Fine powder after broken.
Preferably, the auxiliary agent includes 3 parts of polyacrylic acid and 3 parts of carboxymethyl cellulose.
Formula 2
A kind of building concrete formula, each raw material component are remembered by weight：Include 100 parts of cement, 49 parts of water, 51 parts of stone
Son, 54 parts of sand, 3 parts of iron filings, 14 parts of brick powder and 3 parts of auxiliary agent, the brick powder are discarded building brick through drying
Fine powder after crushing.
Preferably, the auxiliary agent includes 1.5 parts of polyacrylic acid and 1.5 parts of carboxymethyl cellulose.
Formula 3
A kind of building concrete formula, each raw material component are remembered by weight：Include 100 parts of cement, 50 parts of water, 46 parts of stone
Son, 55 parts of sand, 5 parts of iron filings, 10 parts of brick powder and 5 parts of auxiliary agent, the brick powder are discarded building brick through drying
Fine powder after crushing.
Preferably, the auxiliary agent includes 2.5 parts of polyacrylic acid and 2.5 parts of carboxymethyl cellulose.
Formula 4
A kind of building concrete formula, each raw material component are remembered by weight：Include 115 parts of cement, 52 parts of water, 41 parts of stone
Son, 58 parts of sand, 4 parts of iron filings, 10 parts of brick powder and 5 parts of auxiliary agent, the brick powder are discarded building brick through drying
Fine powder after crushing.
Preferably, the auxiliary agent includes 2.5 parts of polyacrylic acid and 2.5 parts of carboxymethyl cellulose.
Formula 5
A kind of building concrete formula, each raw material component are remembered by weight：Include 128 parts of cement, 53 parts of water, 37 parts of stone
Son, 53 parts of sand, 7 parts of iron filings, 13 parts of brick powder and 6 parts of auxiliary agent, the brick powder are discarded building brick through drying
Fine powder after crushing.
Preferably, the auxiliary agent includes 3 parts of polyacrylic acid and 3 parts of carboxymethyl cellulose.
5 kinds of concrete formulations use rear effect comparison sheet
| Formula 1 | Formula 2 | Formula 3 | Formula 4 | Formula 5 | |
| Cement（Part） | 95 | 100 | 100 | 115 | 128 |
| Water（Part） | 48 | 49 | 50 | 52 | 53 |
| Stone（Part） | 52 | 51 | 46 | 41 | 37 |
| Sand（Part） | 62 | 54 | 55 | 58 | 53 |
| Iron filings（Part） | 8 | 3 | 5 | 4 | 7 |
| Brick powder（Part） | 8 | 14 | 10 | 10 | 13 |
| Auxiliary agent（Part） | 6 | 3 | 5 | 5 | 6 |
| Effect | There is iron filings exposure, hardness is slightly lower, slightly fold | There are stone exposure, slightly fold | Flatness is high, and corrugationless | Flatness is high, and corrugationless | There are numb eye, flatness slightly poor |
In summary, above-mentioned 5 formulas can realize the problem of adjusting more existing concrete metope fold, out-of-flatness substantially,
And formula 3 and 4 realizes good technique effect, corrugationless and flatness are high.
It applies the technical scheme of the present invention, concrete is directly used in finishing and uses, corrugationless after drying, surface smoothness
Height improves using effect；And it is smoothed out repeatedly without construction personnel, construction efficiency greatly improves.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, any made by repair
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (4)
1. a kind of building concrete formula, it is characterised in that：Each raw material component is remembered by weight：Include 95-128 parts of cement,
48-53 parts of water, 37-52 parts of stone, 53-62 parts of sand, 3-8 parts of iron filings, 8-14 parts of brick powder and 3-6 part help
Agent, the brick powder are discarded fine powder of the building brick after drying and crushing.
2. building concrete formula as described in claim 1, it is characterised in that：The auxiliary agent includes 2-3 parts of polyacrylic acid
With 2-3 parts of carboxymethyl cellulose.
3. building concrete formula as claimed in claim 2, it is characterised in that：Each raw material component is remembered by weight：Including 95-
115 parts of cement, 49-52 parts of water, 41-51 parts of stone, 54-58 parts of sand, 4-7 parts of iron filings, 10-13 parts of brick powder
And 5 parts of auxiliary agent, the auxiliary agent form with 2.5 parts of polyacrylic acid and 2.5 parts of carboxymethyl cellulose.
4. building concrete formula as claimed in claim 3, it is characterised in that：Each raw material component is remembered by weight：Including 100
The cement of part, 50 parts of water, 46 parts of stone, 55 parts of sand, 5 parts of iron filings, 10 parts of brick powder and 5 parts of auxiliary agent, institute
Auxiliary agent is stated to form with 2.5 parts of polyacrylic acid and 2.5 parts of carboxymethyl cellulose.