CN108395851A - Adhesive tape and preparation method thereof with anti-skidding and light-accumulated luminous performance - Google Patents
Adhesive tape and preparation method thereof with anti-skidding and light-accumulated luminous performance Download PDFInfo
- Publication number
- CN108395851A CN108395851A CN201810490931.2A CN201810490931A CN108395851A CN 108395851 A CN108395851 A CN 108395851A CN 201810490931 A CN201810490931 A CN 201810490931A CN 108395851 A CN108395851 A CN 108395851A
- Authority
- CN
- China
- Prior art keywords
- light
- accumulated luminous
- adhesive tape
- film layer
- skidding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods with anti-skidding and light-accumulated luminous performance adhesive tape, include the following steps, (1) takes rare earth element, titanium dioxide, alkaline earth aluminate, alkaline-earth silicate, it is put into reaction kettle and stirs, crosslinking agent is added after reaction, obtain semi liquid state colloidal sol；(2) colloidal sol is uniformly coated on adhesive band base surface, the adhesive band base with light-accumulated luminous film layer is made in drying；(3) it takes acrylic glue glue and resin cross-linking agent to be sufficiently stirred in a reservoir, obtains liquid glue；(4) by liquid glue be uniformly coated in double plastic single silicon release paper, after sizing obtain with adhesive linkage release paper；(5) adhesive band base with light-accumulated luminous film layer is compounded on the adhesive linkage of release paper, obtains the adhesive tape with light-accumulated luminous function；(6) diamond particles are adsorbed in light-accumulated luminous film layer, obtain the adhesive tape with anti-skidding and light-accumulated luminous performance.The adhesive tape of preparation has excellent durability, weatherability, light emission luminance and skid resistance.
Description
Technical field
The present invention relates to a kind of adhesive tapes and preparation method thereof with anti-skidding and light-accumulated luminous performance.
Background technology
Anti-skid adhesive tape has been widely used in industry, business, food and restaurant service industry, hospital, swimming pool, sports place
And family activity range；But we can usually encounter some fields that can not be covered in upgrade service, such as：Work as burst
Situation powers off or some light environments are not in very perfect environment, and how to promote our product makes its significantly more efficient be
Consumer provides the direction that help is industry effort always.
Invention content
The technical problem to be solved in the present invention is to provide a kind of durability and light emission luminance are excellent, and bright color is fresh
Bright, readily discernible anti-skidding, Luminous adhesive tape preparation method.
In order to solve the above technical problem, the present invention provides a kind of preparations with anti-skidding and light-accumulated luminous performance adhesive tape
Method includes the following steps,
(1) it counts in parts by weight, takes 8~15 parts of rare earth element, 2~6 parts of titanium dioxide, 12~25 parts of alkaline earth aluminate, alkali
20~35 parts of native silicate, is put into reaction kettle and is sufficiently stirred, and crosslinking agent is added after reacting 20~30min, is dispersed with stirring reaction
48~52 hours, obtain flowable semi liquid state colloidal sol；
(2) colloidal sol in step (1) is uniformly coated on adhesive band base surface, drying is made with light-accumulated luminous film layer
Adhesive band base；
(3) it takes acrylic glue glue and resin cross-linking agent to be sufficiently stirred in a reservoir, obtains liquid glue；
(4) the liquid glue obtained in step (3) is uniformly coated in double plastic single silicon release paper, is carried after sizing
The release paper of adhesive linkage；
(5) adhesive band base with light-accumulated luminous film layer obtained in step (2) is compounded on the adhesive linkage of release paper,
Obtain the adhesive tape with light-accumulated luminous function；
(6) storage light that the diamond particles that fineness is 40~80 mesh are adsorbed on to the adhesive band base in step step (2) is sent out
In light film layer；Or be adsorbed in the light-accumulated luminous film layer of the adhesive tape in step (5), obtaining has anti-skidding and light-accumulated luminous performance
Adhesive tape.
In a preferred embodiment of the present invention, further comprise diamond particles uniform adsorption through Electrostatic Absorption equipment
In the light-accumulated luminous film layer.
In a preferred embodiment of the present invention, further comprise the even spread acrylate glue in the light-accumulated luminous film layer
Water, by diamond particles uniform adsorption on being coated with the light-accumulated luminous film layer of acrylic acid glue, under certain temperature environment
One-step solidification is dried.
In a preferred embodiment of the present invention, after further comprising that diamond particles are adsorbed on light-accumulated luminous film layer, inhaling
It is coated with acrylic acid glue again in light-accumulated luminous film layer with diamond particles, second of solidification is dry under certain temperature environment
It is dry.
In a preferred embodiment of the present invention, further comprise that it is 60 DEG C to cure dry temperature for the first time, hardening time
For 10~15min.
In a preferred embodiment of the present invention, further comprise that the temperature of second of solidification drying is 60 DEG C, hardening time
For 30~50min.
In a preferred embodiment of the present invention, further comprise in step (2), is coated with the adhesive band base of melten gel closed
60 DEG C of constant temperature bakings are kept in formula drying box, are stored with the at the uniform velocity speed of 5m/min by obtaining to carry after 60 meters of drying channel
The adhesive band base of the luminous film layer of light.
In a preferred embodiment of the present invention, further comprise that the adhesive band base is PET base material.
In order to solve the above-mentioned technical problem, the present invention also provides a kind of adhesive tape with anti-skidding and light-accumulated luminous performance,
Including adhesive band base, the Buddha's warrior attendant for being coated on the light-accumulated luminous film layer compared with adhesive band base surface and being adsorbed in light-accumulated luminous film layer
Sand skid resistant course, the adhesive band base are compounded in the double plastic single silicon release paper with adhesive linkage.
In a preferred embodiment of the present invention, further comprise being additionally provided with waterproof layer or anti-on the diamond dust skid resistant course
Oil reservoir.
A kind of adhesive tape preparation method with anti-skidding and light-accumulated luminous performance of the present invention, is made using titanium dioxide as fluorescer
The bright color that generates of light-accumulated luminous film layer is vivid, readily discernible, have excellent durability, weatherability, light emission luminance and
Skid resistance, can be widely used in the emergency access of skyscraper, frozen storehouse, school, hospital, fire symbol, ship reference and
The fields such as underground work.
Description of the drawings
Fig. 1 is the schematic diagram of a layer structure of anti-skidding and light-accumulated luminous performance adhesive tape in second embodiment of the invention.
Wherein：2- adhesive band bases, the light-accumulated luminous film layers of 4-, 6- diamond dust skid resistant courses, 8- double plastic single silicon release papers.
Specific implementation mode
The invention will be further described in the following with reference to the drawings and specific embodiments, so that those skilled in the art can be with
It more fully understands the present invention and can be practiced, but illustrated embodiment is not as a limitation of the invention.
Embodiment one
(1) it counts in parts by weight, takes 8 parts of rare earth element, 2 parts of titanium dioxide, 12 parts of alkaline earth aluminate, alkaline-earth silicate 35
Part, it is put into reaction kettle to be sufficiently stirred under the stirring condition of 700~800 turns/min, crosslinking is added after reacting 20~30min
Agent is dispersed with stirring reaction 48~52 hours, and it is spare to obtain flowable semi liquid state colloidal sol.
(2) PET adhesive tape base material is taken, the adhesive tape sample of 50mm × 10mm × 100um is made, the colloidal sol prepared is uniformly applied
Cloth keeps 60 DEG C of constant temperature bakings on the surface of adhesive tape sample, by closed drying box, is passed through with the speed of at the uniform velocity 5 meters/min
The adhesive band base with light-accumulated luminous film layer is made in 60 meters of drying equipment, drying.
(3) it takes acrylic glue glue and resin cross-linking agent to be sufficiently stirred in a reservoir, obtains liquid glue.
(4) double plastic single silicon release paper is taken, liquid glue is uniformly coated in double plastic single silicon release paper, band is obtained after sizing
There is the release paper of adhesive linkage.
(5) adhesive band base with light-accumulated luminous film layer is compounded on the adhesive linkage of release paper, obtains and is sent out with storage light
The adhesive tape of light film layer.
(6) the even spread acrylic acid glue in light-accumulated luminous film layer will pass through the thin of screening by Electrostatic Absorption equipment
Degree is that the diamond particles of 40~80 mesh are adsorbed in the light-accumulated luminous film layer for being coated with acrylic acid glue, passes through 20 meters of drying
Channel carries out baking and curing with 60 DEG C of temperature of constant temperature, and hardening time is 10~15min；Then, diamond particles are being adsorbed with
Light-accumulated luminous film layer on be coated with acrylic acid glue again, by 50 meters of drying channel, dried with 60 DEG C of temperature of constant temperature
Solidization, hardening time are 30~50min, obtain the adhesive tape with anti-skidding and light-accumulated luminous performance, wherein are adsorbed on storage light hair
Diamond particles form the skid resistant course of adhesive tape in light film layer.
In addition, preparing skid resistant course in light-accumulated luminous film layer, can be executed after step (2), it can also be in step (5)
After execute.
Embodiment two
(1) it counts in parts by weight, takes 12 parts of rare earth element, 4 parts of titanium dioxide, 18 parts of alkaline earth aluminate, alkaline-earth silicate 28
Part, it is put into reaction kettle to be sufficiently stirred under the stirring condition of 700~800 turns/min, crosslinking is added after reacting 20~30min
Agent is dispersed with stirring reaction 48~52 hours, and it is spare to obtain flowable semi liquid state colloidal sol.
(2) PET adhesive tape base material is taken, the adhesive tape sample of 50mm × 10mm × 100um is made, the colloidal sol prepared is uniformly applied
Cloth keeps 60 DEG C of constant temperature bakings on the surface of adhesive tape sample, by closed drying box, is passed through with the speed of at the uniform velocity 5 meters/min
The adhesive band base with light-accumulated luminous film layer is made in 60 meters of drying equipment, drying.
(3) it takes acrylic glue glue and resin cross-linking agent to be sufficiently stirred in a reservoir, obtains liquid glue.
(4) double plastic single silicon release paper is taken, liquid glue is uniformly coated in double plastic single silicon release paper, band is obtained after sizing
There is the release paper of adhesive linkage.
(5) adhesive band base with light-accumulated luminous film layer is compounded on the adhesive linkage of release paper, obtains and is sent out with storage light
The adhesive tape of light film layer.
(6) the even spread acrylic acid glue in light-accumulated luminous film layer will pass through the thin of screening by Electrostatic Absorption equipment
Degree is that the diamond particles of 40~80 mesh are adsorbed in the light-accumulated luminous film layer for being coated with acrylic acid glue, passes through 20 meters of drying
Channel carries out baking and curing with 60 DEG C of temperature of constant temperature, and hardening time is 10~15min；Then, diamond particles are being adsorbed with
Light-accumulated luminous film layer on be coated with acrylic acid glue again, by 50 meters of drying channel, dried with 60 DEG C of temperature of constant temperature
Solidization, hardening time are 30~50min, obtain the adhesive tape with anti-skidding and light-accumulated luminous performance, wherein are adsorbed on storage light hair
Diamond particles form the skid resistant course of adhesive tape in light film layer.
In addition, preparing skid resistant course in light-accumulated luminous film layer, can be executed after step (2), it can also be in step (5)
After execute.
Embodiment three
(1) it counts in parts by weight, takes 15 parts of rare earth element, 6 parts of titanium dioxide, 25 parts of alkaline earth aluminate, alkaline-earth silicate 20
Part, it is put into reaction kettle to be sufficiently stirred under the stirring condition of 700~800 turns/min, crosslinking is added after reacting 20~30min
Agent is dispersed with stirring reaction 48~52 hours, and it is spare to obtain flowable semi liquid state colloidal sol.
(2) PET adhesive tape base material is taken, the adhesive tape sample of 50mm × 10mm × 100um is made, the colloidal sol prepared is uniformly applied
Cloth keeps 60 DEG C of constant temperature bakings on the surface of adhesive tape sample, by closed drying box, is passed through with the speed of at the uniform velocity 5 meters/min
The adhesive band base with light-accumulated luminous film layer is made in 60 meters of drying equipment, drying.
(3) it takes acrylic glue glue and resin cross-linking agent to be sufficiently stirred in a reservoir, obtains liquid glue.
(4) double plastic single silicon release paper is taken, liquid glue is uniformly coated in double plastic single silicon release paper, band is obtained after sizing
There is the release paper of adhesive linkage.
(5) adhesive band base with light-accumulated luminous film layer is compounded on the adhesive linkage of release paper, obtains and is sent out with storage light
The adhesive tape of light film layer.
(6) the even spread acrylic acid glue in light-accumulated luminous film layer will pass through the thin of screening by Electrostatic Absorption equipment
Degree is that the diamond particles of 40~80 mesh are adsorbed in the light-accumulated luminous film layer for being coated with acrylic acid glue, passes through 20 meters of drying
Channel carries out baking and curing with 60 DEG C of temperature of constant temperature, and hardening time is 10~15min；Then, diamond particles are being adsorbed with
Light-accumulated luminous film layer on be coated with acrylic acid glue again, by 50 meters of drying channel, dried with 60 DEG C of temperature of constant temperature
Solidization, hardening time are 30~50min, obtain the adhesive tape with anti-skidding and light-accumulated luminous performance, wherein are adsorbed on storage light hair
Diamond particles form the skid resistant course of adhesive tape in light film layer.
In addition, preparing skid resistant course in light-accumulated luminous film layer, can be executed after step (2), it can also be in step (5)
After execute.
Example IV
As shown in Figure 1, present embodiment discloses a kind of adhesive tape with anti-skidding and light-accumulated luminous performance, including PET adhesive tape
Base material 2, to be coated on the light-accumulated luminous film layer 4 compared with 2 surface of adhesive band base and the diamond dust being adsorbed in light-accumulated luminous film layer 4 anti-
Slip layer 6, above-mentioned adhesive band base 2 are compounded in the double plastic single silicon release paper 8 with adhesive linkage, on above-mentioned diamond dust skid resistant course 6 also
Equipped with waterproof layer or anti-oil reservoir.
Based on the preparation method that one~embodiment of above example three is recorded, it is 20 degree in room temperature, system is measured under D65 light sources
Standby adhesive tape out, sunset glow parameter is 19mcd/m to extinction after twenty minutes3, the sunset glow time is 4.5 hours, and composite long-acting sunset glow is certainly
The standard of illuminator, and its non-skid property reaches SGS international standards.
Embodiment described above is only to absolutely prove preferred embodiment that is of the invention and being lifted, protection model of the invention
It encloses without being limited thereto.Those skilled in the art on the basis of the present invention made by equivalent substitute or transformation, in the present invention
Protection domain within.Protection scope of the present invention is subject to claims.
Claims (10)
1. a kind of preparation method with anti-skidding and light-accumulated luminous performance adhesive tape, it is characterised in that：Include the following steps,
(1) it counts in parts by weight, takes 8~15 parts of rare earth element, 2~6 parts of titanium dioxide, 12~25 parts of alkaline earth aluminate, alkaline earth silicon
20~35 parts of hydrochlorate, is put into reaction kettle and is sufficiently stirred, react 20~30min after crosslinking agent is added, be dispersed with stirring reaction 48~
52 hours, obtain flowable semi liquid state colloidal sol；
(2) colloidal sol in step (1) is uniformly coated on adhesive band base surface, the adhesive tape with light-accumulated luminous film layer is made in drying
Base material；
(3) it takes acrylic glue glue and resin cross-linking agent to be sufficiently stirred in a reservoir, obtains liquid glue；
(4) the liquid glue obtained in step (3) is uniformly coated in double plastic single silicon release paper, is obtained with bonding after sizing
The release paper of layer；
(5) adhesive band base with light-accumulated luminous film layer obtained in step (2) is compounded on the adhesive linkage of release paper, is obtained
Adhesive tape with light-accumulated luminous function；
(6) diamond particles that fineness is 40~80 mesh are adsorbed on to the light-accumulated luminous film of the adhesive band base in step step (2)
On layer；Or be adsorbed in the light-accumulated luminous film layer of the adhesive tape in step (5), obtain the glue with anti-skidding and light-accumulated luminous performance
Band.
2. the preparation method with anti-skidding and light-accumulated luminous performance adhesive tape as described in claim 1, it is characterised in that：By quiet
Electro-adhesion device is by diamond particles uniform adsorption in the light-accumulated luminous film layer.
3. the preparation method with anti-skidding and light-accumulated luminous performance adhesive tape as claimed in claim 2, it is characterised in that：Described
Even spread acrylic acid glue in light-accumulated luminous film layer, by diamond particles uniform adsorption in the storage light for being coated with acrylic acid glue
In the film layer that shines, cure drying for the first time under certain temperature environment.
4. the preparation method with anti-skidding and light-accumulated luminous performance adhesive tape as claimed in claim 3, it is characterised in that：Diamond
Granular absorption is coated with acrylate glue again after light-accumulated luminous film layer in the light-accumulated luminous film layer for being adsorbed with diamond particles
Water, second of solidification drying under certain temperature environment.
5. the preparation method with anti-skidding and light-accumulated luminous performance adhesive tape as claimed in claim 3, it is characterised in that：For the first time
The dry temperature of solidification is 60 DEG C, and hardening time is 10~15min.
6. the preparation method with anti-skidding and light-accumulated luminous performance adhesive tape as claimed in claim 4, it is characterised in that：Second
The dry temperature of solidification is 60 DEG C, and hardening time is 30~50min.
7. the preparation method with anti-skidding and light-accumulated luminous performance adhesive tape as described in claim 1, it is characterised in that：Step
(2) in, the adhesive band base for being coated with melten gel keeps 60 DEG C of constant temperature bakings in closed drying box, with the at the uniform velocity speed of 5m/min
Degree after 60 meters of drying channel by obtaining the adhesive band base with light-accumulated luminous film layer.
8. the preparation method with anti-skidding and light-accumulated luminous performance adhesive tape as described in claim 1, it is characterised in that：The glue
Band base material is PET base material.
9. a kind of adhesive tape with anti-skidding and light-accumulated luminous performance, it is characterised in that：According to claim 1-8 any one of them
Prepared by method comprising adhesive band base is coated on the light-accumulated luminous film layer compared with adhesive band base surface and is adsorbed on light-accumulated luminous film
Diamond dust skid resistant course on layer, the adhesive band base are compounded in the double plastic single silicon release paper with adhesive linkage.
10. the adhesive tape with anti-skidding and light-accumulated luminous performance as claimed in claim 9, it is characterised in that：The diamond dust is anti-
Waterproof layer or anti-oil reservoir are additionally provided in slip layer.