CN108384579A - A kind of gasification of biomass and direct reduced iron coproduction additive and its application - Google Patents
A kind of gasification of biomass and direct reduced iron coproduction additive and its application Download PDFInfo
- Publication number
- CN108384579A CN108384579A CN201810269309.9A CN201810269309A CN108384579A CN 108384579 A CN108384579 A CN 108384579A CN 201810269309 A CN201810269309 A CN 201810269309A CN 108384579 A CN108384579 A CN 108384579A
- Authority
- CN
- China
- Prior art keywords
- biomass
- iron
- additive
- gasification
- direct reduced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of gasification of biomass of the present invention and direct reduced iron coproduction additive and its application, belong to ironmaking technology field.The additive of the present invention includes sodium carbonate, lateritic nickel ore, dolomite and plant ash.Iron content agglomerate is obtained after iron-bearing material, biomass and additive are mixed, iron content agglomerate is put into elevated temperature vessel and is heated, biomass generates imflammable gas by gasification, and ferriferous oxide is reduced generation direct reduced iron；The iron-bearing material includes iron ore concentrate, blast furnace ash and sinter return fine.The additive of the present invention reduces biomass and its decomposition product thermal stability, biomass is as the reducing agent of ferriferous oxide and the sources C of imflammable gas and the sources H, ferriferous oxide serves as the standby source of iron of steel and carbon reaction generates the oxygen source of CO, the catalytic pyrolysis for promoting other decomposition products of tar and biomass improves the degree of metalization of direct reduced iron while improving gasification of biomass yield.
Description
Present patent application is for application No. is 2017101469513 divisional applications, and the applying date of original application is：
2016-03-13, invention and created name are：A kind of gasification of biomass and direct reduced iron co-production and additive therefor.
Technical field
The present invention relates to ironmaking technology fields, more specifically to a kind of gasification of biomass and direct reduced iron coproduction
Method and additive therefor.
Background technology
Biomass energy (biomass energy) is the form of energy that solar energy is stored in the form of chemical energy in biomass,
I.e. using biomass as the energy of carrier.It directly or indirectly derives from the photosynthesis of green plants, is a kind of renewable energy
Source.Biomass energy has many advantages, such as renewable, low stain, widely distributed.Biomass energy is rationally utilized, can be effectively reduced to mine
The dependence of the object energy, by mitigating energy-consuming to pollution caused by environment.Nowadays the development and utilization of biomass energy at
For the focus of international concern, Biomass Energy Technology has suitable vast potential for future development.Process of the existing biomass in application
In, often gasify to biomass, gasification of biomass be under certain thermodynamic condition, by means of air part (or
Oxygen), the effect of vapor, make the high polymer of biomass that pyrolysis, oxidation, reduction reforming reaction occur, be eventually converted into an oxygen
Change carbon, the process of the fuel gas such as hydrogen and low molecular hydrocarbon.
Steel and iron industry means the industry of the production pig iron, steel, steel, ingot iron and ferroalloy, is all industrialization in the world
One of the basic industries of country.At the same time, steel and iron industry is also resource, energy intensive industry, and typical high material-consumption,
High energy consumption, high pollutive industries consume the limited resources such as a large amount of iron ore, coal, water in process of production, while discharge is big again
The waste of amount causes serious pollution to environment.Iron and Steel Enterprises in China energy consumption about occupies the 10% of national total energy consumption, gives up
Water, solid waste, discharge amount of exhaust gas account for the 14% of national emission of industrial pollutants total amount respectively, and 17%, 16%.Currently, I
The development of state's steel and iron industry faces the dual restriction of the energy and environment, the energy and environment oneself become and influence steel and iron industry existence and hair
The significant problem of exhibition.The energy-saving and emission-reduction policy of steel and iron industry is promoted, energy-saving and emission-reduction dynamics is increased, improves efficiency of energy utilization, hair
" low-carbon economy " based on low energy consumption, low stain is opened up, the sustainable development of steel and iron industry could be promoted.Therefore, it can incite somebody to action
Biomass is applied in steel and iron industry, and the coal and coke of traditional iron-smelting process are replaced using biomass.
Through retrieval, have the research of relevant technical staff's development in this respect, such as：Qingdao Technological University carries out relevant
Research, and applied for patent：A kind of direct reduction iron making device and method (number of patent application based on biomass
201110408416.3 the applying date：2011-12-09) and a kind of direct reduction iron making device based on biomass pyrolytic tar and
Method (number of patent application 201310107214.4, applying date 2013-03-29), use biomass pyrolytic tar substitute coal and
Natural gas carries out direct reduction iron making, to reduce dependence of the iron-smelting process to fossil energy, improves direct-reduction iron product
The harm to environment can also be reduced while quality.But this method is often using biomass as the substitute of fuel, still
Biomass is during restoring ore, the cracking of simultaneous biomass, and cracking easily occurs for biomass incomplete during this
And a large amount of tar is generated, the waste of biomass energy is not only caused, but also cause serious environmental pollution, there is an urgent need for solutions for this problem
Certainly.
Invention content
1. technical problems to be solved by the inivention
It is an object of the invention to overcome in the prior art, tar yield is higher, the lower deficiency of gasifyin g yield, provides one
Kind gasification of biomass and direct reduced iron co-production and additive therefor；
A kind of gasification of biomass wherein provided and direct reduced iron co-production, iron content roll into a ball biomass in the block and are gasified
Imflammable gas is generated, ferriferous oxide is reduced generation direct reduced iron, can reduce tar content, while improving gasification production
Rate；Degree of metalization can further be improved；
A kind of gasification of biomass wherein provided and direct reduced iron coproduction additive, by each component with cooperation
With can promote the decomposition of larger molecular organics, reduce tar content, while improving gasifyin g yield；It can further carry
High metal rate.
2. technical solution
In order to achieve the above objectives, technical solution provided by the invention is：
A kind of gasification of biomass and the direct reduced iron co-production of the present invention, by iron-bearing material, biomass, additive and
Binder mixing agglomeration obtains iron content agglomerate, and iron content agglomerate is put into elevated temperature vessel and is heated, and biomass is generated by gasification can
Combustion property gas, ferriferous oxide are reduced generation direct reduced iron, and the additive includes sodium carbonate, lateritic nickel ore, dolomite
And plant ash.
Preferably, it is as follows：
(1) iron-bearing material, biomass, additive and binder are mixed, it is standby in 80-120 DEG C of hot pressing by cuber
Obtain iron content agglomerate；
(2) the iron content agglomerate after drying is put into 800-900 DEG C of elevated temperature vessel, keeps 5-10min, then be warming up to
1150-1250 DEG C, and keep the temperature 30-60min.
Preferably, the iron-bearing material, biomass, additive and binder are formed by following mass fraction：
Preferably, the sodium carbonate, lateritic nickel ore, dolomite and 200 mesh percent of pass of vegetation ash particle are more than 90%.
Preferably, the mass percent of additive each component is：Sodium carbonate：20%, lateritic nickel ore：45%, dolomite：
30%, plant ash：5%.
Preferably, the wherein described iron-bearing material includes iron ore concentrate, blast furnace ash and sinter return fine.
Preferably, the granularity of the biomass is less than 40 mesh.
Preferably, Yang Di, Tu Balang powder, Canadian fine powder, Kazakhstan mixes powder and Jin Buba powder forms by breathing out for the iron ore concentrate.
A kind of gasification of biomass of the present invention and direct reduced iron coproduction additive, the additive includes carbonic acid
Sodium, lateritic nickel ore, dolomite and plant ash.
Preferably, the additive further includes chromium slag.
3. advantageous effect
Using technical solution provided by the invention, compared with existing known technology, there is following remarkable result：
(1) a kind of gasification of biomass of the invention and direct reduced iron co-production, iron content roll into a ball biomass in the block by gas
For metaplasia at imflammable gas, ferriferous oxide is reduced generation direct reduced iron, can reduce tar content, while improving gasification production
Rate；Degree of metalization can further be improved；
(2) a kind of gasification of biomass of the invention and direct reduced iron co-production, biomass are gone back as ferriferous oxide
The sources C and the sources H of former agent and imflammable gas, ferriferous oxide serves as the standby source of iron of steel and carbon reaction generates the oxygen source of CO,
Improve the degree of metalization of direct reduced iron；On the other hand the catalytic pyrolysis of other decomposition products of tar and biomass is promoted；
(3) a kind of gasification of biomass of the invention and direct reduced iron co-production, complex oxide strengthen its focusing
The ion deviation effect of the pyrolysis products such as oil at high temperature, promotes the electron cloud in tar to be destroyed and loss of stability, promotes
Coke tar cracking generates small organic molecule, and the imflammable gas being cracked to form enhances ferriferous oxide goes back ferriferous oxide
Former process improves the degree of metalization of direct reduced iron obtained by the reaction；
(3) a kind of gasification of biomass of the invention and direct reduced iron coproduction additive, metal ion are being heated at high temperature
Process be adsorbed on the surface of biomass and its decomposition product, promoted that the offset of C-C and C-O bond angles, bond distance be elongated, carbocyclic ring is not advised
Then deformation etc., and bond energy is caused to reduce, tar and biomass other decomposition product thermal stability reduction can promote macromolecular
The decomposition of organic matter reduces tar content, while improving gasifyin g yield.
Specific implementation mode
Hereafter to the detailed description of exemplary embodiment of the present invention, although these exemplary embodiments are by fully in detail
Description is so that those skilled in the art can implement the present invention, it is to be understood that can realize other embodiment and can not depart from
To the present invention, various changes can be made in the case of the spirit and scope of the present invention.Hereafter the more detailed of the embodiment of the present invention is retouched
It states and is not limited to required the scope of the present invention, and just to be illustrated and do not limit the spy to the present invention
The description of point and feature to propose to execute the best mode of the present invention, and is sufficient to make those skilled in the art that can implement this
Invention.Therefore, the scope of the invention is only defined by the appended claims.
Embodiment 1
A kind of gasification of biomass of the present invention and direct reduced iron co-production, specific steps are as follows：
S1：Step (1) mixes iron-bearing material, biomass, additive and binder, by cuber in 80-120 DEG C of heat
Iron content agglomerate is prepared in pressure, and the pressure of iron content agglomerate is 20MPa, then keeps the temperature agglomerate as under conditions of 105 ± 5 DEG C
3h is to being completely dried；Iron-bearing material, biomass, additive and the binder is formed by following mass fraction：Biomass 50-
60 parts, preferably 52g；Iron-bearing material 100-200g, preferably 150g；Additive 5-10g, preferably 8g；Binder 3-5g, preferably 4g.
Wherein the iron-bearing material includes blast furnace ash, sinter return fine and iron ore concentrate, and the mass percent of each component is：Blast furnace ash：
5%, sinter return fine：10%, iron ore concentrate：85%.It is worth noting that the binder is bentonite.
It is worth noting that：The source of wherein biomass includes the straw in addition to grain fruit in agriculture and forestry production process
The lignocellulosics such as stalk, trees, farming industry leftover bits and pieces, agriculture and forestry organic waste material, industrial bio matter waste；It can certainly
It is fowl and animal excrement and the waste etc. during Animal husbandry production.Biomass is dried and is crushed before the use, is dried
Dry temperature is 105 DEG C, and granularity need to be crushed to when broken and is less than 40 mesh, and the ash content of biomass is required to be less than 3%.
Sinter return fine is：It returns mine for the particulate in sintering process, blast furnace gas ash composition is：Blast furnace dust is blast furnace
The raw material dust that coal gas carries out, contains biological cycle, K2The mass percentage of O is：1.0~2.0%；Na2The quality hundred of O
Point content is：5.0%~9.0%.
S2：Iron content agglomerate after drying is put into 800-900 DEG C of closed elevated temperature vessel by step (2), and in closed item
It is heated under part, keeps 5-10min, be warming up to 1150-1250 DEG C with the heating rate of 2-3 DEG C/min, and keep the temperature 30-
60min.Biomass generates H by gasification2、CO、CH4Equal imflammable gas, ferriferous oxide are reduced generation direct reduced iron；
Wherein, additive is made of sodium carbonate, lateritic nickel ore, dolomite and plant ash, and the mass percent of each component is：
Sodium carbonate：20%, lateritic nickel ore：45%, dolomite：30%, plant ash：5%.Be worth further illustrate be：Lateritic nickel ore,
Dolomite and 200 mesh percent of pass of vegetation ash particle are more than 90%.
The lateritic nickel ore chemical composition mass percent is：Ni：1.8%, TFe：24%, SiO2：35%, CaO：
1.3%, MgO：16%, Al2O3：3.5%, Cr：0.5%, remaining is impurity.
Dolomitized ingredient percent is：TFe：0.28%, SiO2：0.66%, Al2O3：0.31%, CaO：
52.12%, MgO：31.03%.Degree of metalization, gas yield and the tar yield for being prepared into direct reduced iron are as shown in table 1；No
Gasification of biomass yield is only substantially increased, and improves the degree of metalization of direct reduced iron.
Comparative example 1
The substance of this comparative example with embodiment 1, the difference is that：Additive, detection reaction is not added wherein
The degree of metalization of direct reduced iron afterwards, gasification of biomass yield, tar yield.Experimental result record is as shown in table 1.
Comparative example 2
The substance of this comparative example with embodiment 1, the difference is that：Do not include sinter return fine in iron-bearing material,
It is only made of iron ore concentrate and blast furnace ash in iron-bearing material, the degree of metalization of direct reduced iron, gasification of biomass after detection reaction
Yield, tar yield.Experimental result record is as shown in table 1.
Comparative example 3
The substance of this comparative example with embodiment 1, the difference is that：Do not include lateritic nickel ore in iron-bearing material,
It is only made of iron ore concentrate and sinter return fine in iron-bearing material, the degree of metalization of direct reduced iron, biogas after detection reaction
Change yield, tar yield.Experimental result record is as shown in table 1.
Comparative example 4
The substance of this comparative example with embodiment 1, the difference is that：Iron content agglomerate after drying is put into reaction
900 DEG C are gradually heating to by room temperature in device, then 1150-1250 DEG C is warming up to the heating rate of 2-3 DEG C/min, and keeps the temperature 30-
60min.The degree of metalization of direct reduced iron, gasification of biomass yield, tar yield after detection reaction.Experimental result record such as table
Shown in 1.
1 experimental data of table
| Degree of metalization | Gasifyin g yield | Tar yield | |
| Embodiment 1 | 85.8% | 93.5% | 6.1% |
| Comparative example 1 | 83.3% | 89.2% | 10.1% |
| Comparative example 2 | 78.9% | 81.8% | 16.8% |
| Comparative example 3 | 82.4% | 89.0% | 10.5% |
| Comparative example 4 | 79.8% | 85.9% | 12.5% |
| Embodiment 2 | 86.3% | 92.5% | 7.2% |
| Embodiment 3 | 85.9% | 93.8% | 7.7% |
| Embodiment 4 | 84.8% | 93.1% | 6.2% |
| Embodiment 5 | 85.7% | 92.3% | 7.1% |
Above-mentioned conclusion is compared, it can be deduced that draw a conclusion：
(1) it is found by comparative example 1 and the comparison of embodiment 1, under the same conditions, when additive is not added, gasification production
Measure relatively low, and tar yield is higher, and a large amount of metal ion is contained in additive；
(2) it is found by comparative example 2 and the comparison of embodiment 1, under the same conditions, when not adding sinter return fine, tar
Conversion ratio and gasification efficiency decrease, reason may be the complex oxide containing part in sinter return fine, the complexity
Oxide may generate oxides or the complexity such as iron-nickel-magnesium with the metallic element of additive under the high temperature conditions heating
Oxide, and these oxides react on metal ion, strengthen its ion to pyrolysis products such as tar at high temperature
Deviation effect promotes the electron cloud in tar to be destroyed and loss of stability, and C-C keys, c h bond is made to be easy to happen fracture, to
Coke tar cracking has been promoted to generate small organic molecule, the H being cracked to form2、CH4Equal imflammable gas enhance pair ferriferous oxide
The reduction process of ferriferous oxide improves the degree of metalization of direct reduced iron obtained by the reaction.
(3) it is found by comparative example 3 and the comparison of embodiment 1, under the same conditions, when not adding blast furnace ash, biomass
Gasification efficiency reduce, reason is still unintelligible, but may be due in blast furnace ash contain a large amount of Na, K, Pb, Zn, these
Metal ion on the one hand enhance the attraction to larger molecular organics electronics, offset, on the other hand may under the high temperature conditions with
Ferriferous oxide or nickel iron compound combine, and improve the catalytic activity of ferriferous oxide, nickel iron compound, so as to improve catalysis effect
Fruit；Above-mentioned element not only promotes the decomposition of larger molecular organics, at the same improve improve ferriferous oxide, nickel iron compound it is anti-
Activity is answered, and promotes the reduction of ferriferous oxide, to improve degree of metalization.
(4) comparative example 4 is found with the comparison of embodiment 1, under the conditions of identical raw material proportioning, when slow heating, tar
Yield increases, wherein may be to generate relatively large number of tar during slowly heating up due to early period, and tar is in generation
In the process just by volatilizing in container, and the oxides such as iron-nickel-magnesium or complex oxide are not yet effective during low temperature
Formed, another aspect metal ion be difficult in chilling process the larger molecular organics being effectively facilitated in tar occur cracking,
It reforms, to the yield of incrementss tar.
Certainly, in order to realize recycling application of the biomass in steel industry, the sustainable development of steel and iron industry is realized,
Have relevant technical staff, has carried out the technical research of related fields.For example, innovation and creation is entitled：Joint Production is given birth to
The method and apparatus of iron and high quality synthesis gas, number of patent application：201180048198.5 patent application day is：2011-08-
03.The patent application is aoxidized by the way that by iron ore and gas co-production, although this method is realized using biomass reduction iron
Object prepares direct reduced iron, and at the same time production imflammable gas, but due to the larger molecular organics such as tar in gasification
It cannot effectively crack, reform so that tar removal rate is relatively low, and gasification result is poor, this problem is also that limitation biomass is effective
The critical issue of resource application.
The inventor of this patent by unremitting exploration for a long time, have finally chosen appropriate component as biomass with contain
Iron material reacts, coproduction imflammable gas and direct reduced iron, substantially increases gasification efficiency and the tar removal of biomass
There is rate substantive distinguishing features outstanding and significant progress, those skilled in the art more can not without performing creative labour
Additive so can be selected, and imflammable gas and the co-production of direct reduced iron are prepared applied to iron-bearing material.It is above-mentioned
Reaction mechanism it is not completely clear, and annoying the inventor of this patent always.In order to find out the reaction theory of the reaction, Shen
It asks someone to have carried out multiple seminar and discuss, and think wherein to may be following reason：
During 900 DEG C of heat preservations early period, forms to form micropore on iron content agglomerate, increases the specific surface area of agglomerate,
And larger reaction interface is provided with coke tar cracking is promoted for the oxides such as follow-up iron-nickel-magnesium or complex oxide, increase simultaneously
The big response area of biomass cracking gas reducing iron oxides, on the one hand promotes the reduction step by step of ferriferous oxide and life
Gasification substance, cracking process generate a large amount of H2, CO, hydrocarbon, there is higher reproducibility, which promotes
Ferriferous oxide low-temperature reduction, and additive promotes the generation of low melting point solid solution phase so that and biomass only need to be in lower temperature
Iron ore can be restored under degree, when biomass is as the reducing agent of ferriferous oxide and the sources C of imflammable gas and H
Source.Ferriferous oxide serves as the standby source of iron of steel and carbon reaction generates the oxygen source of CO.Direct reduced iron is produced with standard biologic matter
Method it is different, the inside cycle of the oxygen from iron content agglomerate of this method, rather than from by oxygen, to improve directly also
The degree of metalization of former iron；On the other hand the catalytic pyrolysis of other decomposition products of tar and biomass is promoted.
In addition, blast furnace ash and additive contain a large amount of alkaline metal ions, process of the metal ion in high-temperature heating
It is adsorbed on the surface of biomass and its decomposition product, under the high temperature conditions biomass and its decomposition product carbon atom and oxygen atom
Electronics is influenced to different extents, has promoted the offset of C-C and C-O bond angles, elongated, the carbocyclic ring irregular deformation of bond distance etc., and make
It is reduced at bond energy, tar and biomass other decomposition product thermal stability reduction.But when not adding additive, metal ion
It is difficult to be adsorbed on the surface of biomass cellulose so that biomass de- poly- reaction be leading, and generation is a series of containing carbocyclic
Hydrocarbon so that tar yield is higher.
Also, during the continuous raising biomass heating reducing iron oxides of temperature, produce a series of active iron-
The complex oxides such as nickel-magnesium, including：Calcium iron compound, calcium and magnesium compound, fayalite, iron-doped nickel oxide etc., high temperature item
These material surfaces have higher reactivity and polar activation position under part, on the one hand promote the movement of metal ion, add
Strong ion deviation effect of the metal ion to pyrolysis products such as tar at high temperature；In addition, the fused ring compound in tar contains
There are the pi-electron system of negatively charged, pi-electron cloud to be destroyed and loss of stability, C-C keys, c h bond is made to be easy to happen fracture, from
And cracking activation energy is reduced, the oxides such as iron-nickel-magnesium or complex oxide further promote the larger molecular organics such as tar to send out
Raw catalytic degradation so that open loop cleavage reaction occurs for the larger molecular organics in tar, easily degrades, and generate a series of
Low-molecular-weight hydrocarbon, improves the gasification transformation efficiency of biomass, and reduces the yield of tar.Wherein, especially nickel
Ferriferous oxide reduces hydrocarbon and CH4Content, H in fuel gas2It is dramatically increased with CO contents, certain ferriferous oxide
During organic matter is catalytically decomposed, itself is also constantly participating in reaction process, and constantly restores and obtain directly also
Former iron, to improve the degree of metalization of direct reduced iron.
Embodiment 2
The substance of the present embodiment is with embodiment 1, the difference is that the additive is by sodium carbonate, laterite nickel
Mine, dolomite, plant ash and chromium slag composition；The mass percent of each component is：Sodium carbonate：15%, lateritic nickel ore：30%, white
Marble：30%, plant ash：15%, chromium slag：10%.The chromium slag chemical composition mass percent is as follows：SiO2：28%,
Al2O3：8%, CaO：30%, MgO：15%, Fe2O3：10%, Cr2O6：0.8% and Na2Cr2O7：1%, remaining is impurity.Detection
The degree of metalization of direct reduced iron after reaction, gasification of biomass yield, tar yield.Experimental result record is as shown in table 1.One side
Face chromium slag is effectively restored under the high reductive condition of gasification of biomass, to chromium slag, generates the chromated oxide of reserve price, chromium oxygen
Compound with roll into a ball ferriferous oxide in the block, calcium and magnesium compound is combined, the high efficiency for promoting the larger molecular organics in tar cracks,
To generate small molecule imflammable gas, ferriferous oxide is constantly restored and is obtained certainly during organic matter is catalytically decomposed
Direct reduced iron.
Embodiment 3
Yang Di, Tu Balang powder, Canadian fine powder, Kazakhstan mixes powder and Jin Buba powder forms, the ingredient such as table 2 of mine by breathing out for iron ore concentrate
Shown, the mass percent of various miberal powders is：Breathe out Yang Di：10%, Tu Balang powder：20%, Canadian fine powder：40%, it breathes out and mixes powder：
15%, Jin Buba powder：15%.The degree of metalization of direct reduced iron after detection reaction, gasification of biomass yield, tar yield are real
It is as shown in table 1 to test result record.
2 miberal powder ingredient (wt/%) of table
The degree of metalization of direct reduced iron further increases, and by discussing repeatedly, inventor thinks：This process may be
During 900 DEG C of heat preservations, the crystallization water in Iron Ore Powder is thermally decomposed, and more gap is generated in iron content agglomerate, to
The gas-solid reaction interface of ferriferous oxide reduction is increased, these gaps increase ferriferous oxide and its complex compound in tar
Larger molecular organics catalytic action, and the crystallization water by thermal decomposition generate H2O diffuses in the reactor, and the vapor is in iron
Under oxide catalyst, cracking/reformation of macromolecular is promoted, to improve the transformation efficiency of tar, iron oxidation during this
Object constantly restores during organic matter is catalytically decomposed and obtains direct reduced iron.
Embodiment 4
Additive is made of sodium carbonate, potassium chloride, lateritic nickel ore, dolomite, plant ash, the mass percent of each component
For：Sodium carbonate：15%, potassium chloride：20%, lateritic nickel ore：25%, dolomite：30%, plant ash：10%.It is straight after detection reaction
Connect the degree of metalization of reduced iron, gasification of biomass yield, tar yield.Experimental result record is as shown in table 1.Alkali metal ion master
If alkali metal promotes the further cracking of the larger molecular organics such as tar, it is suppressed that small molecule is reunited under hot environment, is carried
The high transformation efficiency of tar, additive promote ferriferous oxide and are combined with larger molecular organics, and ferriferous oxide is being catalytically decomposed
During organic matter, constantly restores and obtain direct reduced iron.
Embodiment 5
Additive is made of sodium carbonate, lateritic nickel ore, dolomite, plant ash, chromium slag and v-ti magnetite slag, each component
Mass percent is：Sodium carbonate：15%, lateritic nickel ore：30%, dolomite：20%, plant ash：10%, chromium slag：10%, vanadium titanium
Magnet slag：15%.The degree of metalization of direct reduced iron, gasification of biomass yield, tar yield after detection reaction.Experimental result
Record is as shown in table 1.
The oxide of ferrovanadium, iron nickel, the larger molecular organics in metal ion promotes tar are generated during heating
Electronic migration occurs, on the basis of reducing degrading activity, ferrovanadium, iron nickel oxide promote the tar in biomass and split
Solution, ferrovanadium, iron nickel oxide during organic matter be catalytically decomposed, constantly restore and obtain direct reduced iron, raising
Degree of metalization.
The present invention is described in detail above in conjunction with specific exemplary embodiment.It is understood, however, that can not take off
It is carry out various modifications in the case of from the scope of the present invention being defined by the following claims and modification.Detailed description should only by
It is considered illustrative and not restrictive, if there is any such modifications and variations, then they fall within
In the scope of the present invention of this description.In addition, background technology is intended to Development Status and meaning in order to illustrate this technology, not purport
In the limitation present invention or the application field of the application and the present invention.
More specifically, although exemplary embodiment of the present invention has been described herein, the invention is not limited in
These embodiments, but include those skilled in the art according to the detailed description of front it can be appreciated that it is modified, omit,
Any and whole embodiments of (such as between each embodiment) combination, adaptive change and/or replacement.In claim
Restriction can widely be explained according to the language used in claim, and be not limited in foregoing detailed description or in reality
The example described during this application is applied, these examples should be considered as nonexcludability.For example, in the present invention, term is " preferably
Ground " not exclusively, preferably, here it means that " but be not restricted to that ".It is in office where method or process claims
In any step for enumerating can execute in any order and be not limited to the sequence proposed in claim.Therefore, of the invention
Range should only be determined by appended claims and its legal equivalents, rather than by descriptions and examples given above Lai
It determines.
Claims (10)
1. a kind of gasification of biomass and direct reduced iron coproduction additive, it is characterised in that：Including sodium carbonate, lateritic nickel ore,
Dolomite and plant ash.
2. a kind of gasification of biomass according to claim 1 and direct reduced iron coproduction additive, it is characterised in that：Institute
The additive stated further includes chromium slag.
3. a kind of gasification of biomass according to claim 1 and direct reduced iron coproduction additive, it is characterised in that：Institute
The additive stated further includes potassium chloride.
4. a kind of gasification of biomass according to claim 1 and direct reduced iron coproduction additive, it is characterised in that：Respectively
The mass percent of component is：Sodium carbonate：20%, lateritic nickel ore：45%, dolomite：30%, plant ash：5%.
5. a kind of gasification of biomass according to claim 2 and direct reduced iron coproduction additive, it is characterised in that：Respectively
The mass percent of component is：Sodium carbonate：15%, lateritic nickel ore：30%, dolomite：30%, plant ash：15%, chromium slag：
10%.
6. a kind of gasification of biomass according to claim 3 and direct reduced iron coproduction additive, it is characterised in that：Respectively
The mass percent of component is：Sodium carbonate：15%, potassium chloride：20%, lateritic nickel ore：25%, dolomite：30%, plant ash：
10%.
7. special according to a kind of gasification of biomass of claim 1-6 any one of them and direct reduced iron coproduction additive
Sign is：Lateritic nickel ore chemical composition mass percent is：Ni：1.8%, TFe：24%, SiO2：35%, CaO：1.3%,
MgO：16%, Al2O3：3.5%, Cr：0.5%, remaining is impurity.
8. using application of the additive of claim 1-7 in gasification of biomass coproduction direct reduced iron, it is characterised in that：It will
Iron content agglomerate is obtained after iron-bearing material, biomass and additive mixing, iron content agglomerate is put into elevated temperature vessel and is heated, it is raw
Substance generates imflammable gas by gasification, and ferriferous oxide is reduced generation direct reduced iron；The iron-bearing material includes iron essence
Mine, blast furnace ash and sinter return fine.
9. application of the additive according to claim 8 in gasification of biomass coproduction direct reduced iron, it is characterised in that：
Yang Di, Tu Balang powder, Canadian fine powder, Kazakhstan mixes powder and Jin Buba powder forms by breathing out for the iron ore concentrate.
10. application of the additive according to claim 8 in gasification of biomass coproduction direct reduced iron, feature exist
In：Iron content agglomerate is put into 800-900 DEG C of elevated temperature vessel, keeps 5-10min, then be warming up to 1150-1250 DEG C, and keep the temperature
30-60min。