CN108384399A - A kind of blue thermal resistance material and its preparation method and application - Google Patents
A kind of blue thermal resistance material and its preparation method and application Download PDFInfo
- Publication number
- CN108384399A CN108384399A CN201810301500.7A CN201810301500A CN108384399A CN 108384399 A CN108384399 A CN 108384399A CN 201810301500 A CN201810301500 A CN 201810301500A CN 108384399 A CN108384399 A CN 108384399A
- Authority
- CN
- China
- Prior art keywords
- thermal resistance
- blue
- resistance material
- parts
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of blue thermal resistance materials, are prepared by the component including following parts by weight：20~30 parts of epoxy resin；8~12 parts of polyamide curing agent；36~50 parts of color stuffing；The color stuffing is diatomite and rutile type titanium white；6~7.5 parts of blue-colored filler；18~28 parts of diluent；0.5~0.6 part of coalescents；The coalescents are antifoaming agent, levelling agent and dispersant.The present invention is based on epoxy resin, with the use of color stuffing diatomite and rutile type titanium white, and add blue-colored filler, under the effect of coalescents, diluent and polyamide curing agent, obtained blue thermal resistance material thermal resistance effect is good, easy for construction and have the function of beautifying the environment, and is suitble in popularization and application such as Lv Dao, park pavement, road in scenic area, urban road and highways.
Description
Technical field
The present invention relates to technical field of road engineering, and in particular to a kind of blue thermal resistance material and preparation method thereof and answers
With.
Background technology
Pitch is a kind of complex mixture of dark brown, and bituminous paving heat absorption capacity is very high, especially in summer high temperature
When, plain asphalt pavement temperature is significantly larger than temperature, up to 60~70 DEG C, up to 75 DEG C or more when highest.Pavement temperature is excessively high,
It is also easy to produce tropical island effect, and causes pavement track disease, is made troubles to driving and pedestrian.Be widely used with bituminous paving and
Global warming, people propose an urgent demand to reducing summer bituminous paving temperature, alleviation city " tropical island effect " etc..
Currently, mainly using the asphalt pavement structures such as big gap road surface, water conservation formula road surface or using phase transformation ground surface material,
Thermal resistance ground surface material reduces bituminous paving temperature, and still, preceding method generally existing cooling-down effect is undesirable, construction not side
Just the problem of.
Invention content
The purpose of the present invention is to provide a kind of blue thermal resistance material and its preparation method and application, indigo plants provided by the invention
Color thermal resistance material thermal resistance effect is good, easy for construction and have the function of beautifying the environment.
In order to achieve the above-mentioned object of the invention, the present invention provides following technical scheme：
The present invention provides a kind of blue thermal resistance materials, are prepared by the component including following parts by weight：
20~30 parts of epoxy resin；
8~12 parts of polyamide curing agent；
36~50 parts of color stuffing；The color stuffing is diatomite and rutile type titanium white；
6~7.5 parts of blue-colored filler；
18~28 parts of diluent；
0.5~0.6 part of coalescents；The coalescents are antifoaming agent, levelling agent and dispersant.
Preferably, the epoxy resin includes E-51 epoxy resin or E-44 epoxy resin.
Preferably, the polyamide curing agent includes 650 polyamide curing agents or T31 polyamide curing agents.
Preferably, the mass ratio of the diatomite and rutile type titanium white is (10~14)：(26~36).
Preferably, the blue-colored filler is iron oxide blue.
Preferably, the diluent includes one or more of acetone, cyclohexanone, methyl ethyl ketone and n-butanol.
Preferably, the antifoaming agent includes tributyl phosphate antifoaming agent, modified polyacrylate class antifoaming agent or non-
Silicone antifoaming agent；
The levelling agent includes acrylate levelling agent, polyurethanes levelling agent or modified polyorganosiloxane class levelling agent；
The dispersant includes nonionic modified fatty acid wetting dispersing agent, sodium polycarboxylate salt wetting dispersing agent or poly-
Acrylic amine salt wetting dispersing agent.
Preferably, the mass ratio of the antifoaming agent, levelling agent and dispersant is (1.7~2.3)：(2.7~3.3)：(2.7
~3.3).
The present invention provides the preparation methods of blue thermal resistance material described in above-mentioned technical proposal, include the following steps：
Epoxy resin, color stuffing are mixed with portion of diluent, obtain the first slurry；
First slurry is mixed with blue-colored filler, coalescents, obtains the second slurry；
Second slurry is mixed with polyamide curing agent, remaining diluent, obtains blue thermal resistance material.
The present invention provides preparation method systems described in blue thermal resistance material described in above-mentioned technical proposal or above-mentioned technical proposal
Application of the standby obtained blue thermal resistance material in pavement engineering.
The present invention provides a kind of blue thermal resistance materials, are prepared by the component including following parts by weight：Epoxy resin
20~30 parts；8~12 parts of polyamide curing agent；36~50 parts of color stuffing；The color stuffing is diatomite and rutile titanium dioxide
Powder；6~7.5 parts of blue-colored filler；18~28 parts of diluent；0.5~0.6 part of coalescents；The coalescents are defoaming
Agent, levelling agent and dispersant.The present invention is used cooperatively color stuffing diatomite and rutile titanium dioxide based on epoxy resin
Powder, and add blue-colored filler, under the effect of coalescents, diluent and polyamide curing agent, obtained blue thermal resistance material
Material directly sprays and is covered in bituminous paving surface with good thermal resistance effect and easy for construction, can " initiatively " drop
Low excessively high pavement temperature controls road surface vehicle not increasing or reduce plus on the basis of pavement engineering cost, reduce pavement temperature
Rut disease；Meanwhile the reduction of pavement temperature, so that the amount of stored heat of road body is reduced, reduces the thermal exposure of road surface outwardly, can improve
The thermal environment of surrounding area alleviates the urban heat land effect of getting worse, and more suitable living environment is provided for city dweller,
The air-conditioning system energy load brought due to tropical island effect is reduced, it, can be with to play environmental protection and energy saving effect
Promote social sustainable development, realizes harmony between man and nature development.In addition, blue thermal resistance material color provided by the invention compares
It is bright-coloured, colored road surface can be played the role of, beautify the environment, alleviate driver tired driving, be suitble to Lv Dao, park pavement,
The popularization and application such as road in scenic area, urban road and highway.Embodiment the experimental results showed that, under the same conditions, sprinkling this
The experiment test specimen of the blue thermal resistance material provided is invented than low 9 DEG C of blank control surface of test piece temperature or more, internal temperature low 10
DEG C or more, illustrate that blue thermal resistance material provided by the invention has excellent thermal resistance effect.
It is easy to operate the present invention provides the preparation method of the blue thermal resistance material, it is suitable for scale production.
Specific implementation mode
The present invention provides a kind of blue thermal resistance materials, are prepared by the component including following parts by weight：
20~30 parts of epoxy resin；
8~12 parts of polyamide curing agent；
36~50 parts of color stuffing；The color stuffing is diatomite and rutile type titanium white；
6~7.5 parts of blue-colored filler；
18~28 parts of diluent；
0.5~0.6 part of coalescents；The coalescents are antifoaming agent, levelling agent and dispersant.
In the present invention, if without specified otherwise, all raw material components are commercially available quotient well known to those skilled in the art
Product.
In the present invention, it counts in parts by weight, the raw material for preparing the blue thermal resistance material includes epoxy resin 20~30
Part, preferably 22~28 parts, more preferably 24~26 parts, most preferably 25 parts.In the present invention, the epoxy resin preferably wraps
Include E-51 epoxy resin or E-44 epoxy resin, more preferably E-51 epoxy resin.In the present invention, epoxy resin has mechanics
Performance height, strong adhesive force, cure shrinkage be small, good manufacturability, the advantage that stability is good and chemical proof is excellent, together
When, the heat resistance of epoxy curing compound is high (heat resistant variety of epoxy resin is up to 200 DEG C or higher).
In the present invention, on the basis of the parts by weight of the epoxy resin, the raw material of the blue thermal resistance material is prepared
Including 8~12 parts of polyamide curing agent, preferably 9~11 parts, more preferably 10 parts.In the present invention, the polyamide cure
Agent preferably includes 650 polyamide curing agents or T31 polyamide curing agents, more preferably 650 polyamide curing agents.In the present invention
In, the selection needs of the polyamide curing agent type are corresponding with the type of the epoxy resin, specifically, such as E51 epoxies
Resin corresponds to 650 polyamide curing agents, and E44 epoxy resin corresponds to T310 polyamide curing agents.In the present invention, the polyamide
After curing agent is combined with epoxy resin, epoxy resin can be allowed to generate chemical reaction, to reach cured purpose, be conducive to shorten
The time of the blue thermal resistance material drying, while also allowing blue thermal resistance material firmer.
In the present invention, on the basis of the parts by weight of the epoxy resin, the raw material of the blue thermal resistance material is prepared
Including 36~50 parts of color stuffing, preferably 38~48 parts, more preferably 35~45 parts, most preferably 40 parts.In the present invention, institute
It is diatomite and rutile type titanium white, the mass ratio preferably (10 of the diatomite and rutile type titanium white to state color stuffing
~14)：(26~36), more preferably (11~13)：(28~34), most preferably 12：(30~32).In the present invention, described
Diatomite has the characteristics that porosity is big, absorbability is strong, chemical property is stable, wear-resisting, heat-resisting, can be provided for blue thermal resistance material
Excellent surface property, increase-volume, thickening and raising adhesive force；The rutile type titanium white refraction coefficient is high, can more have
Effect makes the blue thermal resistance material reach cooling-down effect.
In the present invention, on the basis of the parts by weight of the epoxy resin, the raw material of the blue thermal resistance material is prepared
Including 6~7.5 parts of blue-colored filler, preferably 6.3~7.2 parts, more preferably 6.5~7 parts.The present invention is for the blue
The specific type of colored filler does not have special restriction, using blue-colored filler well known to those skilled in the art；This
Invention preferably uses iron oxide blue as blue-colored filler.The present invention obtains blue thermal resistance material by using blue-colored filler
Material, can beautify the environment, and alleviate driver tired driving.
In the present invention, on the basis of the parts by weight of the epoxy resin, the raw material of the blue thermal resistance material is prepared
Including 18~28 parts of diluent, preferably 20~26 parts, more preferably 22~24 parts.In the present invention, the diluent is preferred
Including one or more of acetone, cyclohexanone, methyl ethyl ketone and n-butanol, more preferably acetone.In the present invention, the dilution
Agent can adjust the viscosity of blue thermal resistance material, be conducive to the construction workability for improving blue thermal resistance material.
In the present invention, on the basis of the parts by weight of the epoxy resin, the raw material of the blue thermal resistance material is prepared
Including 0.5~0.6 part of coalescents, preferably 0.52~0.58 part, more preferably 0.54~0.56 part.In the present invention, institute
It is antifoaming agent, levelling agent and dispersant to state coalescents, and the mass ratio of the antifoaming agent, levelling agent and dispersant is preferably (1.7
~2.3)：(2.7~3.3)：(2.7~3.3), more preferably 2：3：3.
In the present invention, the antifoaming agent preferably includes tributyl phosphate antifoaming agent, modified polyacrylate class disappears
Infusion or non-silicone antifoaming agent；More preferably tributyl phosphate antifoaming agent.The present invention is for the modified acroleic acid polyisocyanate polyaddition
The specific type and model of species antifoaming agent and non-silicone antifoaming agent do not have special restriction, ripe using those skilled in the art
The commercial goods known, specifically, such as 827 antifoaming agent of Defoamex or Surfynol MD-20 antifoaming agent.In the present invention
In, the antifoaming agent can eliminate the foam generated in blue thermal resistance material production and work progress, be conducive to improve film
Planarization.
In the present invention, the levelling agent preferably includes acrylate levelling agent, polyurethanes levelling agent or modified poly- silicon
Oxygen alkanes levelling agent, more preferably acrylate levelling agent.The present invention is for the polyurethanes levelling agent and modified poly- silica
The specific type and model of alkanes levelling agent do not have special restriction, are using commercial goods well known to those skilled in the art
Can, specifically, such as RM-2020 levelling agents, XY-500 series levelling agent or SM-601A levelling agents.In the present invention, the levelling
Agent can promote the blue thermal resistance material to form a smooth, smooth, uniform film during drying and forming-film, be conducive to
It reduces the surface tension of the blue thermal resistance material, improve the wetting ability to bituminous paving surface.
In the present invention, the dispersant preferably includes nonionic modified fatty acid wetting dispersing agent, polycarboxylate sodium
Class wetting dispersing agent or polyacrylic acid amine salt wetting dispersing agent, more preferably nonionic modified fatty acid wetting dispersing agent.
The present invention is for the nonionic modified fatty acid wetting dispersing agent, sodium polycarboxylate salt wetting dispersing agent and poly amic acid
The specific type and model of salt wetting dispersing agent do not have special restriction, using commercial goods well known to those skilled in the art
, specifically, such as TEGO Dispers 740W wetting dispersing agents, SN-5040 wetting dispersing agents or W-519 wetting dispersing agents；
In an embodiment of the present invention, TEGO Dispers 740W wetting dispersing agents are specifically used.In the present invention, the dispersant
Main function is evenly dispersed filler solid particle, while preventing the sedimentation and cohesion of solid particle, with ensure color stuffing and
Blue-colored filler forms stable complex, improves the thermal resistance effect of the blue thermal resistance material.
The present invention provides the preparation methods of blue thermal resistance material described in above-mentioned technical proposal, include the following steps：
Epoxy resin, color stuffing are mixed with portion of diluent, obtain the first slurry；
First slurry is mixed with blue-colored filler, coalescents, obtains the second slurry；
Second slurry is mixed with polyamide curing agent, remaining diluent, obtains blue thermal resistance material.
The present invention mixes epoxy resin, color stuffing with portion of diluent, obtains the first slurry.In the present invention, described
The mixing of epoxy resin, color stuffing and portion of diluent preferably mixes epoxy resin with color stuffing, is stirred at 50~70rpm
2~4min is mixed, portion of diluent then is added into gained mixed material, 3~5min is stirred at 50~70rpm, obtains the
One slurry.In the present invention, epoxy resin, color stuffing are mixed with portion of diluent, is for the ease of making epoxy by stirring
Resin is sufficiently mixed with color stuffing；The present invention does not have the additive amount of diluent described in the first slurry special restriction, energy
It is enough to ensure epoxy resin and color stuffing being sufficiently mixed.
After obtaining the first slurry, the present invention mixes first slurry with blue-colored filler, coalescents, obtains
Two slurries.In the present invention, first slurry and blue-colored filler, coalescents mixing preferably by the first slurry with
Blue-colored filler mixing, stirs to the uniform mixed material of color is obtained at 50~70rpm, coalescents is then added,
2~4min is stirred at 50~70rpm, obtains the second slurry.
After obtaining the second slurry, the present invention mixes second slurry with polyamide curing agent, remaining diluent, obtains
Blue thermal resistance material.In the present invention, the mixing of second slurry and polyamide curing agent, remaining diluent is preferably by the
Two slurries are mixed with polyamide curing agent, and 4~6min is stirred at 50~70rpm, are then added into gained mixed material surplus
Remaining diluent stirs 3~5min at 50~70rpm, obtains blue thermal resistance material.In the present invention, the blue thermal resistance material
Material is used by spraying, and diluent is added to make blue thermal resistance material to achieve the effect that spray.
The present invention provides preparation method systems described in blue thermal resistance material described in above-mentioned technical proposal or above-mentioned technical proposal
The blue thermal resistance material is preferably applied to Lv Dao, public affairs by application of the standby obtained blue thermal resistance material in pavement engineering
In garden pavement, road in scenic area, urban road or highway paving.In the present invention, the blue thermal resistance material is to pass through sprinkling
It uses, the blue thermal resistance material is specifically sprayed directly on to the surface on road surface；The fountain height of the blue thermal resistance material is excellent
It is selected as 0.5~0.8kg/m2, more preferably 0.6~0.7kg/m2。
Below in conjunction with the embodiment in the present invention, the technical solution in the present invention is clearly and completely described.It is aobvious
So, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the reality in the present invention
Example is applied, every other embodiment obtained by those of ordinary skill in the art without making creative efforts all belongs to
In the scope of protection of the invention.
Embodiment 1
It counts in parts by weight, 11 parts of diatomite, 27.1 parts of rutile type titanium whites and 22.6 parts of E-51 epoxy resin is mixed
It closes, stirs 3min at 60 rpm, 10 parts of acetone are then added, stirs 4min at 60 rpm, obtains the first slurry；
6.5 parts of iron oxide blues are added into first slurry, stir at 60 rpm uniform to color；Then it is added 0.6
Part coalescents (coalescents include tributyl phosphate, acrylate and TEGO Dispers 740W wetting dispersing agents,
The mass ratio of the tributyl phosphate, acrylate and TEGO Dispers 740W wetting dispersing agents is 2：3：3), in 60rpm
Lower stirring 3min, obtains the second slurry；
9 part of 650 polyamide curing agent is added into second slurry, stirs 5min at 60 rpm, is then added 13 parts
Acetone stirs 4min at 60 rpm, obtains blue thermal resistance material.
Embodiment 2
It counts in parts by weight, 9 parts of diatomite, 26 parts of rutile type titanium whites is mixed with 26 parts of E-51 epoxy resin,
3min is stirred under 60rpm, and 11 parts of acetone are then added, stirs 4min at 60 rpm, obtains the first slurry；
7 parts of iron oxide blues are added into first slurry, stir at 60 rpm uniform to color；Then it is added 0.6 part
(coalescents include tributyl phosphate, acrylate and TEGO Dispers 740W wetting dispersing agents, institute to coalescents
The mass ratio for stating tributyl phosphate, acrylate and TEGO Dispers 740W wetting dispersing agents is 2：3：3), at 60 rpm
3min is stirred, the second slurry is obtained；
10 part of 650 polyamide curing agent is added into second slurry, stirs 5min at 60 rpm, is then added 11
Part acetone, stirs 4min, obtains blue thermal resistance material at 60 rpm.
Embodiment 3
It counts in parts by weight, 10 parts of diatomite, 26.6 parts of rutile type titanium whites is mixed with 24 parts of E-51 epoxy resin,
3min is stirred at 60 rpm, and 9 parts of acetone are then added, stirs 4min at 60 rpm, obtains the first slurry；
6.9 parts of iron oxide blues are added into first slurry, stir at 60 rpm uniform to color；Then it is added 0.6
Part coalescents (coalescents include tributyl phosphate, acrylate and TEGO Dispers 740W wetting dispersing agents,
The mass ratio of the tributyl phosphate, acrylate and TEGO Dispers 740W wetting dispersing agents is 2：3：3), in 60rpm
Lower stirring 3min, obtains the second slurry；
9 part of 650 polyamide curing agent is added into second slurry, stirs 5min at 60 rpm, is then added 14 parts
Acetone stirs 4min at 60 rpm, obtains blue thermal resistance material.
Embodiment 4
Blue thermal resistance material prepared by Examples 1 to 3 is tested for the property, and blank control is set, it is specific as follows：
2 groups of 5cmAC-13 track plate test specimens are prepared, by fountain height 0.65kg/m2, the surface sprinkling of one group of test specimen wherein
Blue thermal resistance material, as experiment test specimen；Another set is not processed, as blank control test specimen；By the experiment test specimen and
Illumination 3h, the surface temperature of blank control test specimen reach 75 DEG C to blank control test specimen under the same conditions；Test the experiment examination
(internal temperature refers to test specimen inner distance test specimen upper surface to the surface temperature and internal temperature of part and blank control test specimen
Temperature at 4cm), it calculates the two surface temperature difference and internal difference in temperature, concrete outcome is shown in Table 1.
Wherein, in order to ensure the accuracy of experiment, during the experiment, specifically by the experiment test specimen and blank control
Test specimen is put into heat preservation zone, is filled in thermal insulation foam in test specimen surrounding gap, is prevented illumination from entering from its surrounding, and the standard of experiment is influenced
True property；Test specimen center is identified, temperature sensor is placed at test specimen center；In order to make uniform illumination, pass through plumb line tune
Whole iodine-tungsten lamp position is at the surface at test specimen center；Connect temperature sensor and moisture recorder, opening temperature record
Instrument and light irradiation apparatus, press every 30min gathered datas 1 time, and the surface temperature of blank control test specimen is 75 DEG C after 3h, experiment with computing examination
The temperature difference of part and blank control test specimen.
The performance test results of blue thermal resistance material prepared by 1 Examples 1 to 3 of table
| Test the temperature difference of test specimen and blank control test specimen | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Surface temperature difference (DEG C) | 9.6℃ | 9.4℃ | 9.2℃ |
| Internal difference in temperature (DEG C) | 10.6℃ | 10.5℃ | 10.1℃ |
As shown in Table 1, under the same conditions, the experiment examination for the blue thermal resistance material that prepared by the sprinkling embodiment of the present invention 1~3
Part illustrates blue thermal resistance provided by the invention than low 9 DEG C of blank control surface of test piece temperature or more, low 10 DEG C of internal temperature or more
Material has excellent thermal resistance effect.
As seen from the above embodiment, the present invention is used cooperatively color stuffing diatomite and rutile based on epoxy resin
Type titanium dioxide, and add blue-colored filler, under the effect of coalescents, diluent and polyamide curing agent, obtained blue
Thermal resistance material thermal resistance effect is good, easy for construction and have the function of beautifying the environment, and is suitble in Lv Dao, park pavement, scenic spot road
The popularization and application such as road, urban road and highway.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications are also answered
It is considered as protection scope of the present invention.
Claims (10)
1. a kind of blue thermal resistance material, is prepared by the component including following parts by weight：
20~30 parts of epoxy resin；
8~12 parts of polyamide curing agent；
36~50 parts of color stuffing；The color stuffing is diatomite and rutile type titanium white；
6~7.5 parts of blue-colored filler；
18~28 parts of diluent；
0.5~0.6 part of coalescents；The coalescents are antifoaming agent, levelling agent and dispersant.
2. blue thermal resistance material according to claim 1, which is characterized in that the epoxy resin includes E-51 epoxy resin
Or E-44 epoxy resin.
3. blue thermal resistance material according to claim 1, which is characterized in that the polyamide curing agent includes 650 polyamides
Amine hardener or T31 polyamide curing agents.
4. blue thermal resistance material according to claim 1, which is characterized in that the diatomite and rutile type titanium white
Mass ratio is (10~14)：(26~36).
5. blue thermal resistance material according to claim 1, which is characterized in that the blue-colored filler is iron oxide blue.
6. blue thermal resistance material according to claim 1, which is characterized in that the diluent includes acetone, cyclohexanone, first
One or more of ethyl ketone and n-butanol.
7. blue thermal resistance material according to claim 1, which is characterized in that the antifoaming agent includes tributyl phosphate defoaming
Agent, modified polyacrylate class antifoaming agent or non-silicone antifoaming agent；
The levelling agent includes acrylate levelling agent, polyurethanes levelling agent or modified polyorganosiloxane class levelling agent；
The dispersant includes nonionic modified fatty acid wetting dispersing agent, sodium polycarboxylate salt wetting dispersing agent or polypropylene
Acid amide salt wetting dispersing agent.
8. blue thermal resistance material according to claim 1 or claim 7, which is characterized in that the antifoaming agent, levelling agent and dispersant
Mass ratio be (1.7~2.3)：(2.7~3.3)：(2.7~3.3).
9. the preparation method of any one of the claim 1~8 blue thermal resistance material, includes the following steps：
Epoxy resin, color stuffing are mixed with portion of diluent, obtain the first slurry；
First slurry is mixed with blue-colored filler, coalescents, obtains the second slurry；
Second slurry is mixed with polyamide curing agent, remaining diluent, obtains blue thermal resistance material.
10. the indigo plant that preparation method is prepared described in any one of the claim 1~8 blue thermal resistance material or claim 9
Application of the color thermal resistance material in pavement engineering.