CN108384330A - 一种具有耐擦洗功能的墙衣及其制备方法 - Google Patents
一种具有耐擦洗功能的墙衣及其制备方法 Download PDFInfo
- Publication number
- CN108384330A CN108384330A CN201810184214.7A CN201810184214A CN108384330A CN 108384330 A CN108384330 A CN 108384330A CN 201810184214 A CN201810184214 A CN 201810184214A CN 108384330 A CN108384330 A CN 108384330A
- Authority
- CN
- China
- Prior art keywords
- powder
- fiber
- parts
- wall clothing
- resistance function
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种具有耐擦洗功能的墙衣及其制备方法,包括如下质量比的成分:纤维60‑75%、金葱粉0.5‑3%、金银丝0.5‑3%、云母片1‑5%、粉体消泡剂0.2‑0.5%、粉体纤维柔顺剂0.2‑0.5%、粉体防霉剂0.2‑0.5%、可再分散乳胶粉5‑15%、羟丙基甲基纤维素2‑10%、粉体憎水剂5‑10%、聚乙烯醇2‑10%。通过本发明制备的墙衣涂料施工上墙后可以增强产品的硬度,用手抠不容易脱落掉纤维,生活上的污渍可擦洗,水笔涂画可以擦洗不需要添加水性乳液或罩面处理。
Description
技术领域
本发明涉及建筑涂料技术领域,具体涉及一种具有耐擦洗功能的墙衣及其制备方法。
背景技术
墙衣是一种以各种纤维为主要原材料,添加环保水性干粉粘结剂、金葱粉、PET彩色丝线、彩色云母片材料,加水混合均匀后制得的室内装饰壁材,其色彩丰富、富有质感并且具有优异的抗裂性、柔韧性、透气性及保温隔热性等,存在的问题纤维的材质硬度不够用手抠容易脱落掉纤维,喷水吸湿后软化容易脱落,墙体出现人为的污渍或水笔图画不能擦洗只能修补浪费材料。
发明内容
针对上述问题,本发明提供了一种具有耐擦洗功能的墙衣及其制备方法,其目的在于:通过本发明制备的墙衣涂料施工上墙后可以增强产品的硬度,用手抠不容易脱落掉纤维,生活上的污渍可擦洗,水笔涂画可以擦洗不需要添加水性乳液或罩面处理。
本发明的技术解决方案:一种具有耐擦洗功能的墙衣,其特征在于:包括如下质量比的成分:纤维 60-75%、金葱粉 0.5-3%、金银丝0.5-3%、云母片 1-5%、粉体消泡剂 0.2-0.5%、粉体纤维柔顺剂 0.2-0.5%、粉体防霉剂 0.2-0.5%、可再分散乳胶粉 5-15%、羟丙基甲基纤维素 2-10%、粉体憎水剂 5-10%、聚乙烯醇 2-10%。
所述纤维为棉纤维、竹纤维、木质纤维、粘胶纤维、聚酯纤维、聚酰胺纤维、聚丙烯晴纤维、聚氨酯纤维、聚氯乙烯纤维、粉体憎水剂 聚乙烯醇缩甲醛纤维的一种或几种的混合物,所述纤维的经纬范围为150D-300D,细度为20目。
所述可再分散乳胶粉为醋酸乙烯酯与乙烯共聚胶粉(Vac/E)、乙烯与氯乙烯及月硅酸乙烯酯三元共聚胶粉(E/Vc/VL)、醋酸乙烯酯与乙烯及高级脂肪酸乙烯酯三元共聚胶粉(Vac/E/VeoVa)、醋酸乙烯酯与高级脂肪酸乙烯酯共聚胶粉(Vac/VeoVa)、丙烯酸酯与苯乙烯共聚胶粉(A/S)、醋酸乙烯酯与丙烯酸酯及高级脂肪酸乙烯酯三元共聚胶粉(Vac/A/VeoVa)、醋酸乙烯酯均聚胶粉(PVac)的一种或几种的混合物。
一种具有耐擦洗功能的墙衣的制备方法,其特征在于,包括:
第一步:按质量分数计,将60-75份纤维、0.5-3份金葱粉、丝0.5-3份金银、1-5份云母片、0.2-0.5份粉体消泡剂、0.2-0.5份粉体纤维柔顺剂、0.2-0.5份粉体防霉剂、5-15份可再分散乳胶粉、2-10份羟丙基甲基纤维素、5-10份粉体憎水剂、2-10份聚乙烯醇加入干净自来水充分润湿后在搅拌机中搅拌5分钟,达到均匀状态。
第二步 将第一步中的混合物静置半小时,然后补足需水量,调整到合适稠度充分搅拌5分钟。
第三步 使用墙衣专用滚筒和批刀进行施工,施工温度1~50℃,涂层要求厚度1-2mm,平整均匀。
本发明的有益效果:
本发明通过耐水性胶粉、可分散乳胶粉、粉体消泡剂、羟丙基甲基纤维素加纤维加水溶解后混合搅拌施工上墙后可以增强产品的硬度,用手抠不容易脱落掉纤维,喷水后不容易软化,生活上的污渍可擦洗,水笔图画可以擦洗不需要添加水性乳液或罩面处理施工简单环保不浪费材料。
具体实施方式
下面结合实施例进一步阐明本发明的方案及效果,但本发明不仅仅局限于以下实施例:
实施例1:
原料 用量(wt)
纤维 66%;
金葱粉 0.7%;
金银丝 0.8%;
云母片 2%;
粉体消泡剂 0.5%;
粉体纤维柔顺剂 0.2%;
粉体防霉剂 0.3%;
可再分散乳胶粉 5%;
羟丙基甲基纤维素 6%;
耐水性胶粉 10%。
将上述实施例1配方中的原料,经过不锈钢混料机进行混合10分钟,然后出料,包装即制得具有耐擦洗功能的墙衣。
施工工艺为:将制得的具有耐擦洗功能的墙衣加水搅拌均匀浸泡30分钟左右用滚筒或劈刀均匀的涂抹在要施工的墙面干后即可达到耐擦洗,不需要任何液体乳液或罩面处理。
实施例2:
原料 用量(wt)
纤维 67%;
金葱粉 1%;
金银丝 0.5%;
云母片 2%;
粉体消泡剂 0.4%;
粉体纤维柔顺剂 0.3%;
粉体防霉剂 0.3%;
可再分散乳胶粉 6%;
羟丙基甲基纤维素 7%;
耐水性胶粉 10%。
将上述实施例2配方中的原料,经过不锈钢混料机进行混合10分钟,然后出料,包装即制得具有耐擦洗功能的墙衣。
施工工艺为:将制得的具有耐擦洗功能的墙衣加水搅拌均匀浸泡30分钟左右用滚筒或劈刀均匀的涂厚度达到1-2mm在要施工的墙面干后即可达到耐擦洗,不需要任何液体乳液或罩面处理。
实施例3:
原料 用量(wt)
纤维 64%;
金葱粉 1%;
金银丝 1%;
云母片 2%;
粉体消泡剂 0.3%;
粉体纤维柔顺剂 0.5%;
粉体防霉剂 0.2%;
可再分散乳胶粉 8%;
羟丙基甲基纤维素 6%;
耐水性胶粉 10%。
将上述实施例3配方中的原料,经过不锈钢混料机进行混合10分钟,然后出料,包装即制得具有耐擦洗功能的墙衣。
施工工艺为:将制得的具有耐擦洗功能的墙衣加水搅拌均匀浸泡30分钟左右用滚筒或劈刀均匀的涂厚度达到1-2mm在要施工的墙面干后即可达到耐擦洗,不需要任何液体乳液或罩面处理。
表一 实施例性能对比表:
检测项目 | 实例一 | 实例二 | 实例三 | 对照例 |
容器中状态 | 呈乳白色,纤维无结块顺滑 | 呈乳白色,纤维无结块顺滑 | 呈乳白色,纤维无结块顺滑 | 呈乳白色,纤维无结块顺滑 |
施工性 | 混合均匀,施工无障碍 | 混合均匀,施工无障碍 | 混合均匀,施工无障碍 | 混合均匀,施工无障碍 |
涂层 | 表面光滑,硬度高 | 表面光滑,硬度高 | 表面光滑,硬度高 | 表面光滑,硬度高 |
本发明耐擦洗功能升级,不需要添加任何的化学液体,无任何气味,直接加水搅拌干后增加牢固度,用手抠或用坚硬的物体刮蹭不破损,具有较好的透气效果,施工简单操作不需要干后做封闭处理,可二次利用不霉变健康环保。市面上耐擦洗缺陷:要在墙衣材料里添加化学液体,有甲醛跟有害物质,施工过程中有刺激性气味容易对皮肤造成伤害,化学液体干后滴到地板或家具难清理,施工人员手上残留的化学液体干后结块很难清理对皮肤有害。失去了墙衣最重要的环保性能跟传统的乳胶漆没什么区别了,一旦加了化学液体干后就不能二次利用,墙面失去了呼吸功能相当于一面死墙,时间久了容易霉变,墙衣干后上面做封闭也是一样的。
以上所述,仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,可轻易想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求所界定的保护范围为准。
Claims (5)
1.一种具有耐擦洗功能的墙衣,其特征在于,所述墙衣包括如下质量比的成分:
纤维 60-75%;
金葱粉 0.5-3%;
金银丝 0.5-3%;
云母片 1-5%;
粉体消泡剂 0.2-0.5%;
粉体纤维柔顺剂 0.2-0.5%;
粉体防霉剂 0.2-0.5%;
可再分散乳胶粉 5-15%;
羟丙基甲基纤维素 2-10%;
聚乙烯醇 2-10%;
粉体憎水剂 5-10%
如权利要求1所述的具有耐擦洗功能的墙衣,其特征在于:所述纤维为棉纤维、竹纤维、木质纤维、粘胶纤维、聚酯纤维、聚酰胺纤维、聚丙烯晴纤维、聚氨酯纤维、聚氯乙烯纤维、聚乙烯醇缩甲醛纤维的一种或几种的混合物,所述纤维的经纬范围为150D-300D,细度为20目。
2.如权利要求1所述的具有耐擦洗功能的墙衣,其特征在于:所述可再分散乳胶粉为醋酸乙烯酯与乙烯共聚胶粉(Vac/E)、乙烯与氯乙烯及月硅酸乙烯酯三元共聚胶粉(E/Vc/VL)、醋酸乙烯酯与乙烯及高级脂肪酸乙烯酯三元共聚胶粉(Vac/E/VeoVa)、醋酸乙烯酯与高级脂肪酸乙烯酯共聚胶粉(Vac/VeoVa)、丙烯酸酯与苯乙烯共聚胶粉(A/S)、醋酸乙烯酯与丙烯酸酯及高级脂肪酸乙烯酯三元共聚胶粉(Vac/A/VeoVa)、醋酸乙烯酯均聚胶粉(PVac)、粉体憎水剂(HA)的一种或几种的混合物。
3.一种具有耐擦洗功能的墙衣的制备方法,其特征在于,包括:
第一步:按质量分数计,将60-75份纤维、0.5-3份金葱粉、丝0.5-3份金银、1-5份云母片、0.2-0.5份粉体消泡剂、0.2-0.5份粉体纤维柔顺剂、0.2-0.5份粉体防霉剂、5-15份可再分散乳胶粉、2-10份羟丙基甲基纤维素、5-10份粉体憎水剂、2-10份聚乙烯醇加入干净自来水充分润湿后在搅拌机中搅拌5分钟,达到均匀状态。
4.第二步 将第一步中的混合物静置半小时,然后补足需水量,调整到合适稠度充分搅拌5分钟。
5.第三步 使用墙衣专用滚筒和批刀进行施工,施工温度为1~50℃,涂层要求厚度1-2mm,平整均匀。