CN108380019A - A kind of polymerization macromolecule is dispelled taste agent concentrate and preparation method thereof except aldehyde - Google Patents
A kind of polymerization macromolecule is dispelled taste agent concentrate and preparation method thereof except aldehyde Download PDFInfo
- Publication number
- CN108380019A CN108380019A CN201810234533.4A CN201810234533A CN108380019A CN 108380019 A CN108380019 A CN 108380019A CN 201810234533 A CN201810234533 A CN 201810234533A CN 108380019 A CN108380019 A CN 108380019A
- Authority
- CN
- China
- Prior art keywords
- parts
- taste agent
- agent concentrate
- dispelled
- except aldehyde
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of polymerization macromolecule except aldehyde is dispelled taste agent concentrate and preparation method thereof, each ingredient used by this hair, it is safe and non-toxic, non-corrosive, the harmful substances such as decomposing formaldehyde, TVOC, ammonia, benzene can effectively be diluted, it goes to eliminate the unusual smell, and plant extraction liquid is also used, indoor air freshness is effectively promoted, salubrious emotional experience is given to people.The present invention is colourless transparent liquid, will not leave behind trace after construction, need not be cleared up again, does not have any corrosivity, construction is simple to household, fabrics, metal.The present invention, into adsorption-decomposition function, need not construct also unaffected by the gravitation of molecular structure by the instrumentality of light, the bad place of light.After the taste agent construction of dispelling of the present invention, not only cross-linking reaction can be generated with harmful chemicals such as formaldehyde, benzene, TVOC in air, the free formaldehyde that can also be adsorbed in package plank is decomposed again, is able to efficient and lasting have an effect.
Description
Technical field
The present invention relates to a kind of air purifying preparation, more particularly, to a kind of polymerization macromolecule except aldehyde dispel taste agent concentrate and its
Preparation method.
Background technology
For the primary pollution source of Chinese indoor environment from building, decoration and furniture, the pollution such as formaldehyde, benzene, ammonia is exceeded
Through the health for having seriously affected people.It can be mainly divided into finishing pollution and furniture pollute two aspects.It was fitting up
Coating, leather, the carpet etc. of the paint and various finishings that are used in journey, major pollutants caused by these materials are benzene, first
Benzene, TVOC etc., such as woodwork plate, itself is nontoxic from natural for timber, but using urine aldehyde glue sticking when its processing, and form first
The pollution sources of aldehyde, and it is formaldehyde that the main component of glue is used in fitting up.
Existing air purifying preparation on the market has the following disadvantages：The existing general air purifying preparation of air purifying preparation is logical
It is often milky white liquid, is wiped after on the one hand constructing, may be formed and be crystallized in body surface, influence furniture and wallpaper
Color, on the other hand may have certain corrosivity, can and metal chemically react, influence color and luster；Existing air is net
Agent is generally required using ultraviolet light or fluorescent lamp as medium, could be chemically reacted, bad at cloudy day or light
Place influences construction effect very much；On the market except formaldehyde removes peculiar smell product, there are certain taste removal effect, but product itself taste
Than heavier, so being to there is certain cover to act on；The chemicals of many formaldehyde scavengers on the market, after construction can and it is empty
Interior formaldehyde chemically reacts, but after reaction, then the formaldehyde released can not just react, and have no idea to reach and hold
Long effect.A kind of polymerization macromolecule is designed except aldehyde dispels taste agent concentrate solving the above problems.
Invention content
The present invention provides a kind of polymerization macromolecule except aldehyde is dispelled taste agent concentrate and preparation method thereof, can effectively solve above-mentioned
The problems in background technology.
Technical scheme of the present invention is summarized as follows：
A kind of polymerization macromolecule is dispelled taste agent concentrate except aldehyde, is made of the raw material of following weight parts：10-20 parts of ethyl alcohol, third
10-20 parts of vinyl resin, 1-3 parts of plant extraction liquid, 2-6 parts of antiseptic, 1-5 parts of sterilized solution, nonionic surfactant 5-10
Part, 2-6 parts of polyhydric alcohol polymer, 1-3 parts of stabilizer, 1-3 parts of chelating agent, 12-18 parts of deionized water；
Plant in the plant extraction liquid is one or more of lily, Jasmine orchid；
The antiseptic is mixed by chitin and polyolefin；
The sterilized solution is mixed by benzalkonium bromide and saponated cresol；
The nonionic surfactant is by octyl phenol polyoxyethylene ether, nonylphenol polyoxyethylene ether, carbon fatty alcohol polyoxy
Vinethene, polyoxyethylene carboxylate and fatty acid methyl ester ethoxylate mix.
Preferably, it is made of the raw material of following weight parts：15 parts of ethyl alcohol, 15 parts of propylene resin, plant extraction liquid 2
Part, 4 parts of antiseptic, 3 parts of sterilized solution, 8 parts of nonionic surfactant, 4 parts of polyhydric alcohol polymer, 2 parts of stabilizer, chelating agent 2
Part, 15 parts of deionized water.
Preferably, the mixing quality ratio of the chitin in the antiseptic and polyolefin is：1:3.
Preferably, the mixing quality of benzalkonium bromide and saponated cresol ratio is 2 in the sterilized solution:1.
Preferably, by octyl phenol polyoxyethylene ether, nonylphenol polyoxyethylene ether, carbon in the nonionic surfactant
The mixing quality ratio of fatty alcohol polyoxyethylene ether, polyoxyethylene carboxylate and fatty acid methyl ester ethoxylate is：1:1:2:
2:2。
A kind of polymerization macromolecule is dispelled the preparation method of taste agent concentrate except aldehyde, is included the following steps：
Ethyl alcohol and propylene resin are added in deionized water to be mixed evenly, adds antiseptic, sterilized solution, polynary
Alkoxide polymer, stabilizer and chelating agent are mixed evenly, and are eventually adding nonionic surfactant and plant extraction liquid, mixing
After obtain taste agent concentrate of dispelling, seal, in use, according to a certain percentage dilution sprinkling.
Preferably, dispel taste agent concentrate and the water dilution ratio are 1:50.
Compared with prior art, the beneficial effects of the invention are as follows：Each ingredient used by this hair, it is safe and non-toxic, without corruption
Corrosion can effectively dilute the harmful substances such as decomposing formaldehyde, TVOC, ammonia, benzene, go to eliminate the unusual smell, and also use plant extraction liquid, effectively
Indoor air freshness is promoted, salubrious emotional experience is given to people.
The present invention is colourless transparent liquid, will not leave behind trace after construction, need not be cleared up again, to household, fabrics,
Metal does not have any corrosivity, construction is simple.
The present invention by the gravitation of molecular structure into adsorption-decomposition function, need not be by the instrumentality of light, light is bad
Place construction is also unaffected.
The present invention has the effect of peculiar smell while removing formaldehyde, meanwhile, product itself insipidness.
After the taste agent construction of dispelling of the present invention, it can not only be generated with harmful chemicals such as formaldehyde, benzene, TVOC in air
Cross-linking reaction, the free formaldehyde that can also be adsorbed in package plank are decomposed again, are able to efficient and lasting have an effect.
Specific implementation mode
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments, based on the embodiments of the present invention, the common skill in this field
The every other embodiment that art personnel are obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment one
A kind of polymerization macromolecule is dispelled taste agent concentrate except aldehyde, is made of the raw material of following weight parts：10-20 parts of ethyl alcohol, third
10-20 parts of vinyl resin, 1-3 parts of plant extraction liquid, 2-6 parts of antiseptic, 1-5 parts of sterilized solution, nonionic surfactant 5-10
Part, 2-6 parts of polyhydric alcohol polymer, 1-3 parts of stabilizer, 1-3 parts of chelating agent, 12-18 parts of deionized water；
Plant in plant extraction liquid is one or more of lily, Jasmine orchid；
Antiseptic is mixed by chitin and polyolefin；
Sterilized solution is mixed by benzalkonium bromide and saponated cresol；
Nonionic surfactant is by octyl phenol polyoxyethylene ether, nonylphenol polyoxyethylene ether, carbon fatty alcohol polyoxyethylene
Ether, polyoxyethylene carboxylate and fatty acid methyl ester ethoxylate mix.
In the above-described embodiments, it is made of the raw material of following weight parts：15 parts of ethyl alcohol, 15 parts of propylene resin, plant carry
Take 2 parts of liquid, 4 parts of antiseptic, 3 parts of sterilized solution, 8 parts of nonionic surfactant, 4 parts of polyhydric alcohol polymer, 2 parts of stabilizer, chela
2 parts of mixture, 15 parts of deionized water.
In the above-described embodiments, the mixing quality of the chitin in antiseptic and polyolefin ratio is：1:3.
In the above-described embodiments, the mixing quality of benzalkonium bromide and saponated cresol ratio is 2 in sterilized solution:1.
In the above-described embodiments, in nonionic surfactant by octyl phenol polyoxyethylene ether, nonylphenol polyoxyethylene ether,
The mixing quality ratio of carbon fatty alcohol polyoxyethylene ether, polyoxyethylene carboxylate and fatty acid methyl ester ethoxylate is：1:1:
2:2:2。
A kind of polymerization macromolecule is dispelled the preparation method of taste agent concentrate except aldehyde, is included the following steps：
Ethyl alcohol and propylene resin are added in deionized water to be mixed evenly, adds antiseptic, sterilized solution, polynary
Alkoxide polymer, stabilizer and chelating agent are mixed evenly, and are eventually adding nonionic surfactant and plant extraction liquid, mixing
After obtain taste agent concentrate of dispelling, seal, in use, according to a certain percentage dilution sprinkling.
In the above-described embodiments, taste agent concentrate and the water dilution ratio of dispelling are 1:50.
Embodiment two
A kind of polymerization macromolecule is dispelled taste agent concentrate except aldehyde, is made of the raw material of following weight parts：10-20 parts of ethyl alcohol, third
10-20 parts of vinyl resin, 1-3 parts of plant extraction liquid, 2-6 parts of antiseptic, 1-5 parts of sterilized solution, nonionic surfactant 5-10
Part, 2-6 parts of polyhydric alcohol polymer, 1-3 parts of stabilizer, 1-3 parts of chelating agent, 12-18 parts of deionized water；
Plant in plant extraction liquid is one or more of lily, Jasmine, orchid；
Antiseptic is mixed by chitin and polyolefin；
Sterilized solution is mixed by benzalkonium bromide and saponated cresol；
Nonionic surfactant is by octyl phenol polyoxyethylene ether, nonylphenol polyoxyethylene ether, carbon fatty alcohol polyoxyethylene
Ether, polyoxyethylene carboxylate and fatty acid methyl ester ethoxylate mix.
In the above-described embodiments, it is made of the raw material of following weight parts：10 parts of ethyl alcohol, 10 parts of propylene resin, plant carry
Take 1 part of liquid, 2 parts of antiseptic, 1 part of sterilized solution, 5 parts of nonionic surfactant, 2 parts of polyhydric alcohol polymer, 1 part of stabilizer, chela
1 part of mixture, 12 parts of deionized water.
In the above-described embodiments, the mixing quality of the chitin in antiseptic and polyolefin ratio is：1:3.
In the above-described embodiments, the mixing quality of benzalkonium bromide and saponated cresol ratio is 2 in sterilized solution:1.
In the above-described embodiments, in nonionic surfactant by octyl phenol polyoxyethylene ether, nonylphenol polyoxyethylene ether,
The mixing quality ratio of carbon fatty alcohol polyoxyethylene ether, polyoxyethylene carboxylate and fatty acid methyl ester ethoxylate is：1:1:
2:2:2。
A kind of polymerization macromolecule is dispelled the preparation method of taste agent concentrate except aldehyde, is included the following steps：
Ethyl alcohol and propylene resin are added in deionized water to be mixed evenly, adds antiseptic, sterilized solution, polynary
Alkoxide polymer, stabilizer and chelating agent are mixed evenly, and are eventually adding nonionic surfactant and plant extraction liquid, mixing
After obtain taste agent concentrate of dispelling, seal, in use, according to a certain percentage dilution sprinkling.
In the above-described embodiments, taste agent concentrate and the water dilution ratio of dispelling are 1:50.
Embodiment three
A kind of polymerization macromolecule is dispelled taste agent concentrate except aldehyde, is made of the raw material of following weight parts：10-20 parts of ethyl alcohol, third
10-20 parts of vinyl resin, 1-3 parts of plant extraction liquid, 2-6 parts of antiseptic, 1-5 parts of sterilized solution, nonionic surfactant 5-10
Part, 2-6 parts of polyhydric alcohol polymer, 1-3 parts of stabilizer, 1-3 parts of chelating agent, 12-18 parts of deionized water；
Plant in plant extraction liquid is one or more of lily, Jasmine orchid；
Antiseptic is mixed by chitin and polyolefin；
Sterilized solution is mixed by benzalkonium bromide and saponated cresol；
Nonionic surfactant is by octyl phenol polyoxyethylene ether, nonylphenol polyoxyethylene ether, carbon fatty alcohol polyoxyethylene
Ether, polyoxyethylene carboxylate and fatty acid methyl ester ethoxylate mix.
In the above-described embodiments, it is made of the raw material of following weight parts：20 parts of ethyl alcohol, 20 parts of propylene resin, plant carry
Take 3 parts of liquid, 6 parts of antiseptic, 5 parts of sterilized solution, 10 parts of nonionic surfactant, 6 parts of polyhydric alcohol polymer, 3 parts of stabilizer, chela
3 parts of mixture, 18 parts of deionized water.
In the above-described embodiments, the mixing quality of the chitin in antiseptic and polyolefin ratio is：1:3.
In the above-described embodiments, the mixing quality of benzalkonium bromide and saponated cresol ratio is 2 in sterilized solution:1.
In the above-described embodiments, in nonionic surfactant by octyl phenol polyoxyethylene ether, nonylphenol polyoxyethylene ether,
The mixing quality ratio of carbon fatty alcohol polyoxyethylene ether, polyoxyethylene carboxylate and fatty acid methyl ester ethoxylate is：1:1:
2:2:2。
A kind of polymerization macromolecule is dispelled the preparation method of taste agent concentrate except aldehyde, is included the following steps：
Ethyl alcohol and propylene resin are added in deionized water to be mixed evenly, adds antiseptic, sterilized solution, polynary
Alkoxide polymer, stabilizer and chelating agent are mixed evenly, and are eventually adding nonionic surfactant and plant extraction liquid, mixing
After obtain taste agent concentrate of dispelling, seal, in use, according to a certain percentage dilution sprinkling.
In the above-described embodiments, taste agent concentrate and the water dilution ratio of dispelling are 1:50.
Concrete principle：High molecular polymer is with molecular weight being to be up to the supra polymer of 2000-3000 ten thousand if stating
Compound is as main component, has and locks chain-like molecular structure, the spiral polymer being actually intricately intertwined,
In water-soluble.Construction sparges pollution sources (plank, carpet, wallpaper) surface or section, passes through drawing between molecule and molecule
Power not only can crosslink reaction with harmful chemicals such as formaldehyde, benzene, TVOC in air, can also adsorb encapsulation plate
Free formaldehyde in material is decomposed again, is able to effective and lasting have an effect.
According to above-described embodiment 1-3, by the detection of formaldehyde, TVOC, benzene and ammonia in the present invention entrust CMA safety certifications into
Row detection, and the approval of China National Accreditation Service for Conformity Assessment and International Laboratory safety certification is obtained, averagely removed
Aldehyde rate is 99.1%, and it is 88.3% averagely to remove TVOC rates, and it is 80.1% averagely to remove benzene rate, and it is 83.8% averagely to remove ammonia rate, thus
As it can be seen that the embodiment in the present invention can effectively remove the harmful substances such as formaldehyde, TVOC, benzene and ammonia in air.
Content in order to verify heavy metal in the substance in the present invention will not be exceeded, and special commission holds in the palm Guangdong Province's microbiological analysis inspection
Measured center is detected the heavy metal of substance in the present invention, and it is equal to obtain arsenic, cadmium, lead, the content of mercury<0.05, it is in corresponding
Critical field in.
In order to which the substance verified in the present invention not will produce toxicity, special commission's support Shanghai disease detection center is detected, on
Extra large disease detection center carries out test sample to rabbit, does not occur erythema and oedema, it was demonstrated that the substance in the present invention is non-stimulated
Property.
Although the embodiments of the present invention have been disclosed as above, but its is not only in the description and the implementation listed
With it can be fully applied to various fields suitable for the present invention, for those skilled in the art, can be easily
Realize other modification, therefore without departing from the general concept defined in the claims and the equivalent scope, the present invention is simultaneously unlimited
In specific details and embodiment shown here.
Claims (7)
1. a kind of polymerization macromolecule is dispelled taste agent concentrate except aldehyde, which is characterized in that be made of the raw material of following weight parts：Ethyl alcohol
10-20 parts, 10-20 parts of propylene resin, 1-3 parts of plant extraction liquid, 2-6 parts of antiseptic, 1-5 parts of sterilized solution, non-ionic surface
5-10 parts of activating agent, 2-6 parts of polyhydric alcohol polymer, 1-3 parts of stabilizer, 1-3 parts of chelating agent, 12-18 parts of deionized water；
Plant in the plant extraction liquid is one or more of lily, Jasmine, orchid；
The antiseptic is mixed by chitin and polyolefin；
The sterilized solution is mixed by benzalkonium bromide and saponated cresol；
The nonionic surfactant is by octyl phenol polyoxyethylene ether, nonylphenol polyoxyethylene ether, carbon fatty alcohol polyoxyethylene
Ether, polyoxyethylene carboxylate and fatty acid methyl ester ethoxylate mix.
2. a kind of polymerization macromolecule according to claim 1, is dispelled taste agent concentrate except aldehyde, which is characterized in that by following heavy
Measure the raw material composition of part：15 parts of ethyl alcohol, 15 parts of propylene resin, 2 parts of plant extraction liquid, 4 parts of antiseptic, 3 parts of sterilized solution, it is non-from
8 parts of sub- surfactant, 4 parts of polyhydric alcohol polymer, 2 parts of stabilizer, 2 parts of chelating agent, 15 parts of deionized water.
3. a kind of polymerization macromolecule according to claim 1, is dispelled taste agent concentrate except aldehyde, which is characterized in that the antibacterial
The mixing quality ratio of chitin and polyolefin in agent is：1:3.
4. a kind of polymerization macromolecule according to claim 1, is dispelled taste agent concentrate except aldehyde, which is characterized in that the sterilizing
The mixing quality of benzalkonium bromide and saponated cresol ratio is 2 in liquid:1.
5. a kind of polymerization macromolecule according to claim 1, is dispelled taste agent concentrate except aldehyde, which is characterized in that it is described it is non-from
By octyl phenol polyoxyethylene ether, nonylphenol polyoxyethylene ether, carbon fatty alcohol polyoxyethylene ether, fatty acid polyglycol in sub- surfactant
The mixing quality of ethylene oxide ester and fatty acid methyl ester ethoxylate ratio is：1:1:2:2:2.
6. a kind of polymerization macromolecule is dispelled the preparation method of taste agent concentrate except aldehyde, which is characterized in that include the following steps：
Ethyl alcohol is added in deionized water and propylene resin is mixed evenly, it is poly- to add antiseptic, sterilized solution, polyalcohol
It closes object, stabilizer and chelating agent to be mixed evenly, is eventually adding nonionic surfactant and plant extraction liquid, after mixing
To taste agent concentrate of dispelling, sealing, in use, dilution sprinkling according to a certain percentage.
7. a kind of polymerization macromolecule according to claim 6, is dispelled the preparation method of taste agent concentrate except aldehyde, feature exists
In dispel taste agent concentrate and the water dilution ratio are 1:50.