CN108373753A - A kind of metallic plate powdery paints - Google Patents
A kind of metallic plate powdery paints Download PDFInfo
- Publication number
- CN108373753A CN108373753A CN201611030253.9A CN201611030253A CN108373753A CN 108373753 A CN108373753 A CN 108373753A CN 201611030253 A CN201611030253 A CN 201611030253A CN 108373753 A CN108373753 A CN 108373753A
- Authority
- CN
- China
- Prior art keywords
- parts
- metallic plate
- powdery paints
- pigment
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of metallic plate powdery paints, which is characterized in that be made of each component of following mass percent：60 70 parts of E42 epoxy resin, 12 parts of zinc powder, 12 parts of copper powder, 68 parts of polyethylene wax, 35 parts of pigment, 12 parts of filler, 0.2 0.5 parts of accelerating agent, 10 15 parts of titanium dioxide, 56 parts of precipitated calcium carbonate.This method manufacture craft is simple, and raw material mix is simple, and adds titanium dioxide and precipitated calcium carbonate makes coating be easy absorption, is convenient for industrialized production.
Description
Technical field
The present invention relates to a kind of powdery paints, and in particular to a kind of metallic plate powdery paints.
Technical background
As coating products kind is more and more, the continuous expansion of application range, coatings industry has become in chemical industry
One important Independent Industrial production section.And in coatings industry, powdery paints belongs to one kind with fastest developing speed.Due to the world
On there is serious atmosphere pollution, environmental regulation is increasingly strict to contamination control, it is desirable that nuisanceless, resource-saving the coating of exploitation
Kind.Therefore, solvent-free, with protecting and the powdery paints of decoration comprehensive performance, the economic benefit just having by it and society
Benefit and developed rapidly.
But the defect that the powdery paints generally existing hardness that occurs on domestic market now is low, not wear-resisting, friction is several times
Film coated surface will be destroyed, and the aesthetics of product is caused to decline, and service life declines, the defect rate in client's assembling process
It is high.
In view of the above shortcomings, the designer, is actively subject to research and innovation, to found a kind of novel metal plate powder
Last coating makes it with more the utility value in industry.
Invention content
In order to solve the above technical problems, the object of the present invention is to provide a kind of metallic plate powdery paints.
Technical scheme is as follows：
A kind of metallic plate powdery paints, which is characterized in that be made of each component of following mass percent：
60-70 parts of E42 epoxy resin, 1-2 parts of zinc powder, 1-2 parts of copper powder, 6-8 parts of polyethylene wax, 3-5 parts of pigment, filler 1-
2 parts, 0.2-0.5 parts of accelerating agent, 10-15 parts of titanium dioxide, 5-6 parts of precipitated calcium carbonate.
Further, the pigment is cinnabar or laterite.
Further, the filler is barium carbonate.
Further, the accelerating agent is aluminium oxide C.
Further, the antiwear assistant is any one of aluminium oxide, silicon nitride or mixture.
A kind of preparation method of metallic plate powdery paints, which is characterized in that including following steps:
A, E42 epoxy resin, polyethylene wax, zinc powder, copper powder, titanium dioxide, precipitated calcium carbonate are subjected to mixed at high speed；
B, mixture in step A is obtained into screening object after melting extrusion, broken, screening；
C, object being sieved in step B and carrying out mixed at high speed with pigment, filler, accelerating agent, metal powder painting is obtained after screening
Material.
According to the above aspect of the present invention, the present invention has at least the following advantages：
This method manufacture craft is simple, and raw material mix is simple, and adds titanium dioxide and precipitated calcium carbonate makes coating hold
Industrialized production is convenient in easily absorption.
Specific implementation mode
With reference to embodiment, the embodiment of the present invention is furthur described in detail.Following embodiment is used for
Illustrate the present invention, but is not limited to the scope of the present invention.
The preparation method of metal powder of the present invention is as follows：
A, E42 epoxy resin, polyethylene wax, zinc powder, copper powder, titanium dioxide, precipitated calcium carbonate are subjected to mixed at high speed；
B, mixture in step A is obtained into screening object after melting extrusion, broken, screening；
C, object being sieved in step B and carrying out mixed at high speed with pigment, filler, accelerating agent, metal powder painting is obtained after screening
Material.
It is as follows for the specific each component composition of each component in the above method：
Embodiment 1
60 parts of E42 epoxy resin, 1 part of zinc powder, 1 part of copper powder, 6 parts of polyethylene wax, 3 parts of pigment, 1 part of filler, accelerating agent 0.2
Part, 10 parts of titanium dioxide, 5 parts of precipitated calcium carbonate.
Embodiment 2
65 parts of E42 epoxy resin, 1.5 parts of copper powder, 7 parts of polyethylene wax, 4 parts of pigment, 1.5 parts of filler, promotees 1.5 parts of zinc powder
Into 0.3 part of agent, 13 parts of titanium dioxide, 5.5 parts of precipitated calcium carbonate.
Embodiment 3
70 parts of E42 epoxy resin, 2 parts of zinc powder, 2 parts of copper powder, 8 parts of polyethylene wax, 5 parts of pigment, 2 parts of filler, accelerating agent 0.5
Part, 15 parts of titanium dioxide, 6 parts of precipitated calcium carbonate.
Pigment described in various embodiments of the present invention is that Zhu is few or laterite；The filler is barium carbonate；The accelerating agent is
Aluminium oxide C.
The above is only a preferred embodiment of the present invention, it is not intended to restrict the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is several improvement and
Modification, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of metallic plate powdery paints, which is characterized in that be made of each component of following mass percent：
60-70 parts of E42 epoxy resin, 1-2 parts of zinc powder, 1-2 parts of copper powder, 6-8 parts of polyethylene wax, 3-5 parts of pigment, 1-2 parts of filler,
0.2-0.5 parts of accelerating agent, 10-15 parts of titanium dioxide, 5-6 parts of precipitated calcium carbonate.
2. a kind of metallic plate powdery paints according to claim 1, it is characterised in that：The pigment is cinnabar or red
Soil.
3. a kind of metallic plate powdery paints according to claim 1, it is characterised in that：The filler is barium carbonate.
4. a kind of metallic plate powdery paints according to claim 1, it is characterised in that：The accelerating agent is aluminium oxide C.
5. a kind of metallic plate powdery paints according to claim 1, it is characterised in that：The antiwear assistant is oxidation
Any one of aluminium, silicon nitride or mixture.
6. a kind of preparation method of metallic plate powdery paints according to claim 1, which is characterized in that including following several
A step:
A, E42 epoxy resin, polyethylene wax, zinc powder, copper powder, titanium dioxide, precipitated calcium carbonate are subjected to mixed at high speed；
B, mixture in step A is obtained into screening object after melting extrusion, broken, screening；
C, object being sieved in step B and carrying out mixed at high speed with pigment, filler, accelerating agent, metal powder coating is obtained after screening.