CN108373747A - A kind of bright metal powdery paints - Google Patents
A kind of bright metal powdery paints Download PDFInfo
- Publication number
- CN108373747A CN108373747A CN201611016771.5A CN201611016771A CN108373747A CN 108373747 A CN108373747 A CN 108373747A CN 201611016771 A CN201611016771 A CN 201611016771A CN 108373747 A CN108373747 A CN 108373747A
- Authority
- CN
- China
- Prior art keywords
- parts
- powdery paints
- bright metal
- brightener
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of bright metal powdery paints, which is characterized in that be made of each component of following mass percent：60 70 parts of E42 epoxy resin, 12 parts of zinc powder, 12 parts of copper powder, 68 parts of polyethylene wax, 35 parts of pigment, 12 parts of filler, 0.2 0.5 parts of accelerating agent, 25 parts of brightener.This method manufacture craft is simple, and raw material mix is simple, and adds brightener, can reinforce metal powder brightness, is convenient for industrialized production.
Description
Technical field
The present invention relates to metal powder coatings, and in particular to a kind of bright metal powdery paints.
Technical background
As coating products kind is more and more, the continuous expansion of application range, coatings industry has become in chemical industry
One important Independent Industrial production section.And in coatings industry, powdery paints belongs to one kind with fastest developing speed.Due to the world
On there is serious atmosphere pollution, environmental regulation is increasingly strict to contamination control, it is desirable that nuisanceless, resource-saving the coating of exploitation
Kind.Therefore, solvent-free, with protecting and the powdery paints of decoration comprehensive performance, the economic benefit just having by it and society
Benefit and developed rapidly.
But the metal powder coating generally existing brightness occurred on domestic market now is insufficient, the aesthetics of product
Not enough, using effect is bad, and defect rate is high in client's assembling process.
In view of the above shortcomings, the designer, is actively subject to research and innovation, to found a kind of new structural light
Metal powder coating makes it with more the utility value in industry.
Invention content
In order to solve the above technical problems, the object of the present invention is to provide a kind of bright metal powdery paints.
Technical scheme is as follows：
A kind of bright metal powdery paints, which is characterized in that be made of each component of following mass percent：
60-70 parts of E42 epoxy resin, 1-2 parts of zinc powder, 1-2 parts of copper powder, 6-8 parts of polyethylene wax, 3-5 parts of pigment, filler 1-
2 parts, 0.2-0.5 parts of accelerating agent, 2-5 parts of brightener.
Further, the pigment is cinnabar or laterite.
Further, the filler is barium carbonate.
Further, the accelerating agent is aluminium oxide C.
Further, the brightener is microwax.
A kind of preparation method of bright metal powdery paints, which is characterized in that including following steps:
A, E42 epoxy resin, polyethylene wax, zinc powder, copper powder are subjected to mixed at high speed；
B, mixture in step A is obtained into screening object after melting extrusion, broken, screening；
C, object being sieved in step B and carrying out mixed at high speed with pigment, filler, accelerating agent, brightener, metal is obtained after screening
Powdery paints.
According to the above aspect of the present invention, the present invention has at least the following advantages：
This method manufacture craft is simple, and raw material mix is simple, and adds brightener, can reinforce metal powder light
Degree is convenient for industrialized production.
Specific implementation mode
With reference to embodiment, the embodiment of the present invention is furthur described in detail.Following embodiment is used for
Illustrate the present invention, but is not limited to the scope of the present invention.
The preparation method of metal powder of the present invention is as follows：
A, E42 epoxy resin, polyethylene wax, zinc powder, copper powder are subjected to mixed at high speed；
B, mixture in step A is obtained into screening object after melting extrusion, broken, screening；
C, object being sieved in step B and carrying out mixed at high speed with pigment, filler, accelerating agent, brightener, metal is obtained after screening
Powdery paints.
It is as follows for the specific each component composition of each component in the above method：
Embodiment 1
60 parts of E42 epoxy resin, 1 part of zinc powder, 1 part of copper powder, 6 parts of polyethylene wax, 3 parts of pigment, 1 part of filler, accelerating agent 0.2
Part, 2 parts of brightener.
Embodiment 2
65 parts of E42 epoxy resin, 1.5 parts of copper powder, 7 parts of polyethylene wax, 4 parts of pigment, 1.5 parts of filler, promotees 1.5 parts of zinc powder
Into 0.3 part of agent, 3 parts of brightener.
Embodiment 3
70 parts of E42 epoxy resin, 2 parts of zinc powder, 2 parts of copper powder, 8 parts of polyethylene wax, 5 parts of pigment, 2 parts of filler, accelerating agent 0.5
Part, 5 parts of brightener.
Pigment described in various embodiments of the present invention is that Zhu is few or laterite；The filler is barium carbonate；The accelerating agent is
Aluminium oxide C；The brightener is microwax.
The above is only a preferred embodiment of the present invention, it is not intended to restrict the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is several improvement and
Modification, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of bright metal powdery paints, which is characterized in that be made of each component of following mass percent：
60-70 parts of E42 epoxy resin, 1-2 parts of zinc powder, 1-2 parts of copper powder, 6-8 parts of polyethylene wax, 3-5 parts of pigment, 1-2 parts of filler,
0.2-0.5 parts of accelerating agent, 2-5 parts of brightener.
2. a kind of bright metal powdery paints according to claim 1, it is characterised in that：The pigment is cinnabar or red
Soil.
3. a kind of bright metal powdery paints according to claim 1, it is characterised in that：The filler is barium carbonate.
4. a kind of bright metal powdery paints according to claim 1, it is characterised in that：The accelerating agent is aluminium oxide C.
5. a kind of bright metal powdery paints according to claim 1, it is characterised in that：The brightener is microwax.
6. a kind of preparation method of bright metal powdery paints according to claim 1, which is characterized in that including following several
A step:
A, E42 epoxy resin, polyethylene wax, zinc powder, copper powder are subjected to mixed at high speed；
B, mixture in step A is obtained into screening object after melting extrusion, broken, screening；
C, object being sieved in step B and carrying out mixed at high speed with pigment, filler, accelerating agent, brightener, metal powder is obtained after screening
Coating.