CN108359785A - 一种W6Mo5Cr4V2高速钢拉刀的强韧化处理方法 - Google Patents
一种W6Mo5Cr4V2高速钢拉刀的强韧化处理方法 Download PDFInfo
- Publication number
- CN108359785A CN108359785A CN201810224097.2A CN201810224097A CN108359785A CN 108359785 A CN108359785 A CN 108359785A CN 201810224097 A CN201810224097 A CN 201810224097A CN 108359785 A CN108359785 A CN 108359785A
- Authority
- CN
- China
- Prior art keywords
- speed steel
- salt bath
- broach
- salt
- w6mo5cr4v2
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (6)