CN108359395A - 一种单组分防水抗开裂墙地砖填缝剂及其制备方法 - Google Patents
一种单组分防水抗开裂墙地砖填缝剂及其制备方法 Download PDFInfo
- Publication number
- CN108359395A CN108359395A CN201810163404.0A CN201810163404A CN108359395A CN 108359395 A CN108359395 A CN 108359395A CN 201810163404 A CN201810163404 A CN 201810163404A CN 108359395 A CN108359395 A CN 108359395A
- Authority
- CN
- China
- Prior art keywords
- parts
- floor tile
- modified starch
- solution
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种单组分防水抗开裂墙地砖填缝剂及其制备方法，涉及填缝剂技术领域，包括以下份计的原料：纳米丁苯乳胶45~55份、环氧丙烯酸酯35~45份、环氧树脂15~25份、聚乙烯醇15~25份、改性淀粉10~15份、抗裂剂10~15份、石英粉5~10份、绿原酸4~7份、葡萄糖酸钠3~5份、助剂5~15份和水适量。本发明固含量高，抗开裂性和防水性能优异，不易老化。
Description
技术领域
本发明涉及填缝剂技术领域，具体涉及一种单组分防水抗开裂墙地砖填缝剂及其制备方法。
背景技术
随着建筑装饰材料的发展，瓷砖、石材、马赛克、木线等材料的应用也日益普遍。在装饰过程中，材料拼接时必然会产生缝隙，传统的工艺一般会选择勾缝剂、填缝剂或白水泥进行填充，这些填缝材料在使用一段时间后会因灰尘、油烟、污渍等的沾染而发黄、变黑、发霉、滋生霉菌，影响家具环境。
目前市面上常见的填缝剂，固含量多在40%～50%，在施工后多会收缩下陷，对其使用有很大限制。为了提高固含量，常见的手段是添加填料，然而使用较多的填料后，胶液稠度较大，形成的胶膜在使用一段时间后易老化开裂，还会影响颜色鲜艳度以及光泽度。
发明内容
本发明的目的是提供一种单组分防水抗开裂墙地砖填缝剂及其制备方法，固含量高，抗开裂性和防水性能优异，不易老化。
本发明提供了如下的技术方案：一种单组分防水抗开裂墙地砖填缝剂，包括以下份计的原料：纳米丁苯乳胶45~55份、环氧丙烯酸酯35~45份、环氧树脂15~25份、聚乙烯醇15~25份、改性淀粉10~15份、抗裂剂10~15份、石英粉5~10份、绿原酸4~7份、葡萄糖酸钠3~5份、助剂5~15份和水适量；
所述助剂包括：紫外吸收剂、分散剂、颜料、憎水剂和增稠剂。
其中，所述纳米丁苯乳胶以丁二烯和苯乙烯单体经微乳化共聚技术而制成，固含量大于48％。
其中，
所述改性淀粉包括以下份计的原料：淀粉4~6份、环氧氯丙烷0.5~1.5份、硫酸铁0.3~0.8份、高锰酸钾0.2~0.4份、氯乙酸钠0.1~0.3份和70~80%乙醇溶液4~6份；
改性淀粉的制备方法为：
（1）、按照配比称取环氧氯丙烷和氯乙酸钠，加入至乙醇溶液中，分散搅拌，然后加入淀粉，继续分散均匀，得到悬浊液A；
（2）、将悬浊液A加热至60~65℃，然后按照配比加入硫酸铁和高锰酸钾，以200~300r/min的转速搅拌反应1~5h，得到混合物料B，干燥处理，即得。
其中，所述抗裂剂为石墨烯—碳纤维复合粉料和改性碳化硅按照2~5：1的比例混合而成。
其中，
所述石墨烯—碳纤维复合粉料的制备方法为：
（1）、将碳纤维加入浓度为2~10%的硝酸溶液中，在80~90℃下保温搅拌30~50min，过滤、洗涤至中性，得到预处理的碳纤维；
（2）、将石墨烯和纳米氮化铝加入至硅溶胶中，混合搅拌1~2h，得到混合浆体C；
（3）、向混合浆体C中加入预处理的碳纤维，然后加入偶联剂，在100~105℃条件下混合搅拌30~60min，过滤，得到固相物D，真空干燥3~4h，粉碎过筛，即得。
其中，
所述改性碳化硅的制备方法为：
（1）、取纳米级碳化硅加入至浓硫酸中，超声处理1~1.5h，抽滤，洗涤至中性，然后干燥处理，得到酸化碳化硅；
（2）、将酸化碳化硅和硅烷偶联剂按照1：1.1~1.2的比例混合，然后加入至丙酮溶液中，超声处理30~40min，真空干燥处理，即得。
其中，
所述石英粉中二氧化硅含量＞90％，目数为800~1000目；所述紫外吸收剂为2-羟基-4-正辛氧基二苯甲酮或者2-羟基-4-辛氧基二苯甲酮；分散剂为硬脂酸单甘油酯、硬脂酸锌或硬脂酸钙中的任一种；所述颜料为珠光颜料、荧光颜料和金属颜料中的至少一种；憎水剂为有机硅憎水剂或者矿物油类憎水剂中的一种；增稠剂为羟乙基纤维素醚、碱溶胀型增稠剂和聚氨酯类增稠剂中的至少一种。
其中，
所述绿原酸的制备方法为：称取金银花，洗净、烘干、粉碎，得到金银花粉末，将金银花粉末放入5~6倍体积的去离子水中，在65~75℃条件下搅拌提取，提取一次后过滤收集滤液，滤渣再次用6～10倍去离子水再次提取，每次提取时间为1～2h，合并滤液后再次过滤，使用大孔树脂吸附法纯化分离滤液，得到纯化液，经喷雾干燥处理，即得所述绿原酸。
本发明提供一种单组分防水抗开裂墙地砖填缝剂的制备方法，包括如下步骤：
（1）、制备增韧纤维
称取改性淀粉，加入水中，加热升温直至溶解，得到改性淀粉溶液，向其中加入聚乙烯醇，升温至80~90摄氏度，搅拌分散均匀，过滤并脱泡，得到纺丝原液；
将纺丝原液进行湿法纺丝，经过牵伸、热处理，干燥降温得到增韧纤维；
（2）、按照配比称取纳米丁苯乳、环氧丙烯酸酯、环氧树脂、助剂和水，分散均匀，得到混合溶液E；
（3）、向混合溶液E中加入剩余原料和步骤（1）得到的增韧纤维，加热，分散均匀，得到所述单组分防水抗开裂墙地砖填缝剂。
本发明的有益效果：固含量高，抗开裂性和防水性能优异，不易老化，具体如下：
（1）、本发明采用纳米丁苯乳胶、环氧丙烯酸酯、环氧树脂为基料，在其中以合理的配比添加聚乙烯醇、改性淀粉、抗裂剂、石英粉、绿原酸、葡萄糖酸钠和助剂，得到的填缝剂，固含量高，形成的胶膜收缩率小，具有较好的防水和抗开裂性能，具有很好的填充效果，可有效抵抗位移引起的断裂变形，安全环保且光泽度高；
（2）、本发明添加的抗裂剂，不仅可以起到抗裂作用，而且自身可以作为填料提高固含量，抗裂剂为石墨烯—碳纤维复合粉料和改性碳化硅按照2~5：1的比例混合而成，改性碳化硅为纳米粒子，具有应力集中的平衡效应，能够吸收冲击力，当受到外力冲击时，使基体微裂纹扩展受到阻碍或钝化，使收缩变形量减小；另外改性碳化硅与石墨烯—碳纤维相互吸附，并且可以稳定的分散在基体中，形成的粘结层致密均匀，且表面具有光泽度；
（3）、本发明用改性淀粉和聚乙烯醇制备增韧纤维，增韧补强，与其他原料粘结牢固，不易在粘结面处发生开裂，用于辅助抗开裂性和抗收缩性；
（4）、本发明制备过程中，环氧树脂中含有的极性基团能够与其他原料中的形成立体交联网状结构，提高本发明的耐水性，配合石英粉，可以降低填缝剂的吸水率；
（5）、本发明经过大量实验验证，在合适的各原料配比范围内，可使填缝剂的应用性能得到极大的提升，具有优良的防水性能、抗开裂性能，同时还绿原酸的加入还使得本发明具有较好的抗菌效果。
具体实施方式
下面结合具体实施例，进一步阐述本发明。这些实施例仅用于说明本发明而不用于限制本发明的范围。
实施例1
一种单组分防水抗开裂墙地砖填缝剂，包括以下份计的原料：纳米丁苯乳胶45份、环氧丙烯酸酯35份、环氧树脂15份、聚乙烯醇15份、改性淀粉10份、抗裂剂10份、石英粉5份、绿原酸4份、葡萄糖酸钠3份、助剂5份和水适量；
所述助剂包括：紫外吸收剂、分散剂、颜料、憎水剂和增稠剂。
其中，所述纳米丁苯乳胶以丁二烯和苯乙烯单体经微乳化共聚技术而制成，固含量大于48％。
其中，
所述改性淀粉包括以下份计的原料：淀粉4份、环氧氯丙烷0.5份、硫酸铁0.3份、高锰酸钾0.2份、氯乙酸钠0.1份和70%乙醇溶液4份；
改性淀粉的制备方法为：
（1）、按照配比称取环氧氯丙烷和氯乙酸钠，加入至乙醇溶液中，分散搅拌，然后加入淀粉，继续分散均匀，得到悬浊液A；
（2）、将悬浊液A加热至60℃，然后按照配比加入硫酸铁和高锰酸钾，以200r/min的转速搅拌反应1h，得到混合物料B，干燥处理，即得。
其中，所述抗裂剂为石墨烯—碳纤维复合粉料和改性碳化硅按照2：1的比例混合而成。
其中，
所述石墨烯—碳纤维复合粉料的制备方法为：
（1）、将碳纤维加入浓度为2%的硝酸溶液中，在80℃下保温搅拌30min，过滤、洗涤至中性，得到预处理的碳纤维；
（2）、将石墨烯和纳米氮化铝加入至硅溶胶中，混合搅拌1h，得到混合浆体C；
（3）、向混合浆体C中加入预处理的碳纤维，然后加入偶联剂，在100℃条件下混合搅拌30min，过滤，得到固相物D，真空干燥3h，粉碎过筛，即得。
其中，
所述改性碳化硅的制备方法为：
（1）、取纳米级碳化硅加入至浓硫酸中，超声处理1h，抽滤，洗涤至中性，然后干燥处理，得到酸化碳化硅；
（2）、将酸化碳化硅和硅烷偶联剂按照1：1.1的比例混合，然后加入至丙酮溶液中，超声处理30min，真空干燥处理，即得。
其中，
所述石英粉中二氧化硅含量＞90％，目数为800目；所述紫外吸收剂为2-羟基-4-正辛氧基二苯甲酮；分散剂为硬脂酸单甘油酯；所述颜料为珠光颜料；憎水剂为有机硅憎水剂；增稠剂为羟乙基纤维素醚。
所述绿原酸的制备方法为：称取金银花，洗净、烘干、粉碎，得到金银花粉末，将金银花粉末放入5~6倍体积的去离子水中，在65~75℃条件下搅拌提取，提取一次后过滤收集滤液，滤渣再次用6～10倍去离子水再次提取，每次提取时间为1～2h，合并滤液后再次过滤，使用大孔树脂吸附法纯化分离滤液，得到纯化液，经喷雾干燥处理，即得所述绿原酸。
本实施例中提供一种单组分防水抗开裂墙地砖填缝剂的制备方法，包括如下步骤：
（1）、制备增韧纤维
称取改性淀粉，加入水中，加热升温直至溶解，得到改性淀粉溶液，向其中加入聚乙烯醇，升温至80摄氏度，搅拌分散均匀，过滤并脱泡，得到纺丝原液；
将纺丝原液进行湿法纺丝，经过牵伸、热处理，干燥降温得到增韧纤维；
（2）、按照配比称取纳米丁苯乳、环氧丙烯酸酯、环氧树脂、助剂和水，分散均匀，得到混合溶液E；
（3）、向混合溶液E中加入剩余原料和步骤（1）得到的增韧纤维，加热，分散均匀，得到所述单组分防水抗开裂墙地砖填缝剂。
实施例2
一种单组分防水抗开裂墙地砖填缝剂，包括以下份计的原料：纳米丁苯乳胶55份、环氧丙烯酸酯45份、环氧树脂25份、聚乙烯醇25份、改性淀粉15份、抗裂剂15份、石英粉10份、绿原酸7份、葡萄糖酸钠5份、助剂15份和水适量；
所述助剂包括：紫外吸收剂、分散剂、颜料、憎水剂和增稠剂。
其中，所述纳米丁苯乳胶以丁二烯和苯乙烯单体经微乳化共聚技术而制成，固含量大于48％。
其中，
所述改性淀粉包括以下份计的原料：淀粉6份、环氧氯丙烷1.5份、硫酸铁0.8份、高锰酸钾0.4份、氯乙酸钠0.3份和80%乙醇溶液6份；
改性淀粉的制备方法为：
（1）、按照配比称取环氧氯丙烷和氯乙酸钠，加入至乙醇溶液中，分散搅拌，然后加入淀粉，继续分散均匀，得到悬浊液A；
（2）、将悬浊液A加热至65℃，然后按照配比加入硫酸铁和高锰酸钾，以300r/min的转速搅拌反应5h，得到混合物料B，干燥处理，即得。
其中，所述抗裂剂为石墨烯—碳纤维复合粉料和改性碳化硅按照5：1的比例混合而成。
其中，
所述石墨烯—碳纤维复合粉料的制备方法为：
（1）、将碳纤维加入浓度为10%的硝酸溶液中，在90℃下保温搅拌50min，过滤、洗涤至中性，得到预处理的碳纤维；
（2）、将石墨烯和纳米氮化铝加入至硅溶胶中，混合搅拌2h，得到混合浆体C；
（3）、向混合浆体C中加入预处理的碳纤维，然后加入偶联剂，在105℃条件下混合搅拌60min，过滤，得到固相物D，真空干燥4h，粉碎过筛，即得。
其中，
所述改性碳化硅的制备方法为：
（1）、取纳米级碳化硅加入至浓硫酸中，超声处理1.5h，抽滤，洗涤至中性，然后干燥处理，得到酸化碳化硅；
（2）、将酸化碳化硅和硅烷偶联剂按照1：1.2的比例混合，然后加入至丙酮溶液中，超声处理40min，真空干燥处理，即得。
其中，
所述石英粉中二氧化硅含量＞90％，目数为1000目；所述紫外吸收剂为2-羟基-4-辛氧基二苯甲酮；分散剂为硬脂酸锌；所述颜料为荧光颜料；憎水剂为矿物油类憎水剂中的一种；增稠剂为碱溶胀型增稠剂。
其中，
所述绿原酸的制备方法为：称取金银花，洗净、烘干、粉碎，得到金银花粉末，将金银花粉末放入6倍体积的去离子水中，在75℃条件下搅拌提取，提取一次后过滤收集滤液，滤渣再次用10倍去离子水再次提取，每次提取时间为2h，合并滤液后再次过滤，使用大孔树脂吸附法纯化分离滤液，得到纯化液，经喷雾干燥处理，即得所述绿原酸。
本实施例中提供一种单组分防水抗开裂墙地砖填缝剂的制备方法，包括如下步骤：
（1）、制备增韧纤维
称取改性淀粉，加入水中，加热升温直至溶解，得到改性淀粉溶液，向其中加入聚乙烯醇，升温至90摄氏度，搅拌分散均匀，过滤并脱泡，得到纺丝原液；
将纺丝原液进行湿法纺丝，经过牵伸、热处理，干燥降温得到增韧纤维；
（2）、按照配比称取纳米丁苯乳、环氧丙烯酸酯、环氧树脂、助剂和水，分散均匀，得到混合溶液E；
（3）、向混合溶液E中加入剩余原料和步骤（1）得到的增韧纤维，加热，分散均匀，得到所述单组分防水抗开裂墙地砖填缝剂。
实施例3
一种单组分防水抗开裂墙地砖填缝剂，包括以下份计的原料：纳米丁苯乳胶50份、环氧丙烯酸酯40份、环氧树脂20份、聚乙烯醇20份、改性淀粉12.5份、抗裂剂12.5份、石英粉7.5份、绿原酸5.5份、葡萄糖酸钠4份、助剂10份和水适量；
所述助剂包括：紫外吸收剂、分散剂、颜料、憎水剂和增稠剂。
其中，所述纳米丁苯乳胶以丁二烯和苯乙烯单体经微乳化共聚技术而制成，固含量大于48％。
其中，
所述改性淀粉包括以下份计的原料：淀粉5份、环氧氯丙烷1份、硫酸铁0.5份、高锰酸钾0.3份、氯乙酸钠0.2份和75%乙醇溶液5份；
改性淀粉的制备方法为：
（1）、按照配比称取环氧氯丙烷和氯乙酸钠，加入至乙醇溶液中，分散搅拌，然后加入淀粉，继续分散均匀，得到悬浊液A；
（2）、将悬浊液A加热至63℃，然后按照配比加入硫酸铁和高锰酸钾，以250r/min的转速搅拌反应3h，得到混合物料B，干燥处理，即得。
其中，所述抗裂剂为石墨烯—碳纤维复合粉料和改性碳化硅按照3：1的比例混合而成。
其中，
所述石墨烯—碳纤维复合粉料的制备方法为：
（1）、将碳纤维加入浓度为8%的硝酸溶液中，在85℃下保温搅拌40min，过滤、洗涤至中性，得到预处理的碳纤维；
（2）、将石墨烯和纳米氮化铝加入至硅溶胶中，混合搅拌1.5h，得到混合浆体C；
（3）、向混合浆体C中加入预处理的碳纤维，然后加入偶联剂，在103℃条件下混合搅拌40min，过滤，得到固相物D，真空干燥3.5h，粉碎过筛，即得。
其中，
所述改性碳化硅的制备方法为：
（1）、取纳米级碳化硅加入至浓硫酸中，超声处理1h，抽滤，洗涤至中性，然后干燥处理，得到酸化碳化硅；
（2）、将酸化碳化硅和硅烷偶联剂按照1： 1.2的比例混合，然后加入至丙酮溶液中，超声处理35min，真空干燥处理，即得。
其中，
所述石英粉中二氧化硅含量＞90％，目数为900目；所述紫外吸收剂为2-羟基-4-正辛氧基二苯甲酮；分散剂为硬脂酸钙；所述颜料为荧光颜料；憎水剂为矿物油类憎水剂；增稠剂为碱溶胀型增稠剂。
所述绿原酸的制备方法为：称取金银花，洗净、烘干、粉碎，得到金银花粉末，将金银花粉末放入5倍体积的去离子水中，在70℃条件下搅拌提取，提取一次后过滤收集滤液，滤渣再次用8倍去离子水再次提取，每次提取时间为1.5h，合并滤液后再次过滤，使用大孔树脂吸附法纯化分离滤液，得到纯化液，经喷雾干燥处理，即得所述绿原酸。
本实施例中提供一种单组分防水抗开裂墙地砖填缝剂的制备方法，包括如下步骤：
（1）、制备增韧纤维
称取改性淀粉，加入水中，加热升温直至溶解，得到改性淀粉溶液，向其中加入聚乙烯醇，升温至85摄氏度，搅拌分散均匀，过滤并脱泡，得到纺丝原液；
将纺丝原液进行湿法纺丝，经过牵伸、热处理，干燥降温得到增韧纤维；
（2）、按照配比称取纳米丁苯乳、环氧丙烯酸酯、环氧树脂、助剂和水，分散均匀，得到混合溶液E；
（3）、向混合溶液E中加入剩余原料和步骤（1）得到的增韧纤维，加热，分散均匀，得到所述单组分防水抗开裂墙地砖填缝剂。
参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种单组分防水抗开裂墙地砖填缝剂，其特征在于，包括以下份计的原料：纳米丁苯乳胶45~55份、环氧丙烯酸酯35~45份、环氧树脂15~25份、聚乙烯醇15~25份、改性淀粉10~15份、抗裂剂10~15份、石英粉5~10份、绿原酸4~7份、葡萄糖酸钠3~5份、助剂5~15份和水适量；
所述助剂包括：紫外吸收剂、分散剂、颜料、憎水剂和增稠剂。
2.根据权利要求1所述的单组分防水抗开裂墙地砖填缝剂，其特征在于，包括以下份计的原料：纳米丁苯乳胶50份、环氧丙烯酸酯40份、环氧树脂20份、聚乙烯醇20份、改性淀粉12.5份、抗裂剂12.5份、石英粉7.5份、绿原酸5.5份、葡萄糖酸钠4份、助剂10份和水适量；
所述助剂包括：紫外吸收剂、分散剂、颜料、憎水剂和增稠剂。
3.根据权利要求1所述的单组分防水抗开裂墙地砖填缝剂，其特征在于，所述纳米丁苯乳胶以丁二烯和苯乙烯单体经微乳化共聚技术而制成，固含量大于48％。
4.根据权利要求1所述的单组分防水抗开裂墙地砖填缝剂，其特征在于，所述改性淀粉包括以下份计的原料：淀粉4~6份、环氧氯丙烷0.5~1.5份、硫酸铁0.3~0.8份、高锰酸钾0.2~0.4份、氯乙酸钠0.1~0.3份和70~80%乙醇溶液4~6份；
改性淀粉的制备方法为：
（1）、按照配比称取环氧氯丙烷和氯乙酸钠，加入至乙醇溶液中，分散搅拌，然后加入淀粉，继续分散均匀，得到悬浊液A；
（2）、将悬浊液A加热至60~65℃，然后按照配比加入硫酸铁和高锰酸钾，以200~300r/min的转速搅拌反应1~5h，得到混合物料B，干燥处理，即得。
5.根据权利要求1所述的单组分防水抗开裂墙地砖填缝剂，其特征在于，所述抗裂剂为石墨烯—碳纤维复合粉料和改性碳化硅按照2~5：1的比例混合而成。
6.根据权利要求5所述的单组分防水抗开裂墙地砖填缝剂，其特征在于，所述石墨烯—碳纤维复合粉料的制备方法为：
（1）、将碳纤维加入浓度为2~10%的硝酸溶液中，在80~90℃下保温搅拌30~50min，过滤、洗涤至中性，得到预处理的碳纤维；
（2）、将石墨烯和纳米氮化铝加入至硅溶胶中，混合搅拌1~2h，得到混合浆体C；
（3）、向混合浆体C中加入预处理的碳纤维，然后加入偶联剂，在100~105℃条件下混合搅拌30~60min，过滤，得到固相物D，真空干燥3~4h，粉碎过筛，即得。
7.根据权利要求5所述的单组分防水抗开裂墙地砖填缝剂，其特征在于，所述改性碳化硅的制备方法为：
（1）、取纳米级碳化硅加入至浓硫酸中，超声处理1~1.5h，抽滤，洗涤至中性，然后干燥处理，得到酸化碳化硅；
（2）、将酸化碳化硅和硅烷偶联剂按照1：1.1~1.2的比例混合，然后加入至丙酮溶液中，超声处理30~40min，真空干燥处理，即得。
8.根据权利要求1所述的单组分防水抗开裂墙地砖填缝剂，其特征在于，所述石英粉中二氧化硅含量＞90％，目数为800~1000目；所述紫外吸收剂为2-羟基-4-正辛氧基二苯甲酮或者2-羟基-4-辛氧基二苯甲酮；分散剂为硬脂酸单甘油酯、硬脂酸锌或硬脂酸钙中的任一种；所述颜料为珠光颜料、荧光颜料和金属颜料中的至少一种；憎水剂为有机硅憎水剂或者矿物油类憎水剂中的一种；增稠剂为羟乙基纤维素醚、碱溶胀型增稠剂和聚氨酯类增稠剂中的至少一种。
9.根据权利要求1所述的单组分防水抗开裂墙地砖填缝剂，其特征在于，所述绿原酸的制备方法为：称取金银花，洗净、烘干、粉碎，得到金银花粉末，将金银花粉末放入5~6倍体积的去离子水中，在65~75℃条件下搅拌提取，提取一次后过滤收集滤液，滤渣再次用6～10倍去离子水再次提取，每次提取时间为1～2h，合并滤液后再次过滤，使用大孔树脂吸附法纯化分离滤液，得到纯化液，经喷雾干燥处理，即得所述绿原酸。
10.一种根据权利要求1~9任一项所述的单组分防水抗开裂墙地砖填缝剂的制备方法，其特征在于，包括如下步骤：
（1）、制备增韧纤维
称取改性淀粉，加入水中，加热升温直至溶解，得到改性淀粉溶液，向其中加入聚乙烯醇，升温至80~90摄氏度，搅拌分散均匀，过滤并脱泡，得到纺丝原液；
将纺丝原液进行湿法纺丝，经过牵伸、热处理，干燥降温得到增韧纤维；
（2）、按照配比称取纳米丁苯乳、环氧丙烯酸酯、环氧树脂、助剂和水，分散均匀，得到混合溶液E；
（3）、向混合溶液E中加入剩余原料和步骤（1）得到的增韧纤维，加热，分散均匀，得到所述单组分防水抗开裂墙地砖填缝剂。