CN108348053A - Ornaments - Google Patents
Ornaments Download PDFInfo
- Publication number
- CN108348053A CN108348053A CN201680063683.2A CN201680063683A CN108348053A CN 108348053 A CN108348053 A CN 108348053A CN 201680063683 A CN201680063683 A CN 201680063683A CN 108348053 A CN108348053 A CN 108348053A
- Authority
- CN
- China
- Prior art keywords
- pearl
- dyed layer
- ornaments
- fired body
- carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides the ornaments with the pearl for being less prone to defect in the dyed layer being formed in around carbon fired body.The ornaments (1) are formed by multiple pearls are worn string and annularly, are formed with around the carbon fired body (3) of crystalline texture of at least one pearl (2) in the shape for being processed into the pearl (2):Permeable formation (4) has the part permeated to the small gap of the circumferential surface of carbon fired body (3);Dyed layer (5) is set to the outside of permeable formation (4), and by being coated with the coating containing pigment and being fired;And transparent overlay (6), it is set to the outside of the dyed layer.
Description
Technical field
The present invention relates to bracelet, necklace, ankletbangle, bead string, the isothrausmatic ornaments of watchband.
Background technology
In the past, as bracelet, necklace, ankletbangle, bead string, the isothrausmatic ornaments of watchband, using and propose various to decorate
And the article for the purpose of health, beauty.In the pearl of this ornaments containing magnetic generate substance, anion generate substance or
Far-infrared radioactive substance etc..For example, Patent Document 1 discloses by works such as silicon carbide, silicon nitride, titanium nitride, obsidians
For far-infrared radioactive substance.
In addition, being disclosed the following contents in the patent document 2 of present inventor:By multiple pearls wear string and formed
In cricoid ornaments, at least one pearl is the carbon fired body of the crystalline texture for the shape for being processed into the pearl and has been carried out coating.
Citation
Patent document
Patent document 1:Japanese Patent Publication 7-11919 bulletins
Patent document 2:Japanese Unexamined Patent Publication 2008-200491 bulletins
Invention content
Problems to be solved by the invention
However, carbon fired body is in black, it is sometimes desirable to which coloring has different color around it.
For coloring, according to color difference, there are coating of the coating containing pigment, the feelings fired at high temperature later
Condition.Present inventor has found in this case, the coating containing pigment and to fire at high temperature when being only coated with to carbon fired body
When, small defect is susceptible in the dyed layer formed in this way, defect makes the color of the part change, durability reduces,
The present invention has been obtained to be furtherd investigate.
The present invention has been made in view of the above-described circumstances, and an object thereof is to provide with forming around carbon fired body
The ornaments of the pearl of defect are less prone in dyed layer.
Solution for solving the problem
To achieve the goals above, the ornaments involved by embodiments of the present invention by by multiple pearls wear string by formed and
Annularly, wherein at least one pearl is formed with around the carbon fired body of the crystalline texture for the shape for being processed into the pearl:Infiltration
Layer has the part permeated to the small gap of the circumferential surface of the carbon fired body;Dyed layer is set to the outside of the permeable formation,
And by being coated with the coating containing pigment and being fired;And transparent overlay, it is set to the outer of the dyed layer
Side.
In ornaments involved by embodiments of the present invention, can also be that the pigment of the dyed layer is red,
The red overlay of the black and the dyed layer of the carbon fired body, to which the pearl is in peony or ox blood color.
In ornaments involved by embodiments of the present invention, or, the permeable formation and the dyed layer it
Between be provided with adhesive linkage.
Invention effect
In accordance with the invention it is possible to provide with the pearl for being less prone to defect in the dyed layer formed around carbon fired body
Ornaments.
Description of the drawings
Fig. 1 is the schematic top view of the ornaments involved by embodiments of the present invention.
Fig. 2 is the figure for showing to constitute the pearl of the ornaments, and (a) is enlarged side view, is (b) by the section shown in A-A
Locate the enlarged cross-sectional view of cut-out.
Fig. 3 is the enlarged cross-sectional view for a part for the pearl for constituting the ornaments being amplified and being shown each layer.
Fig. 4 is the enlarged cross-sectional view for a part for the variation for the pearl for constituting the ornaments being amplified and being shown each layer.
Fig. 5 is to amplify a part for the pearl when the pearl for constituting the ornaments is provided with dyed layer and schematically show small
The enlarged cross-sectional view in gap.
Fig. 6 be shown schematically in compare be not provided with permeable formation in the case of occur defect in dyed layer
Situation enlarged cross-sectional view.
Specific implementation mode
Hereinafter, modes for carrying out the present invention will be described with reference to the drawings.Fig. 1 is involved by embodiments of the present invention
And ornaments 1 schematic top view.The ornaments 1 be by multiple pearls 2,2 ... wear string and formed cricoid component.Such as Fig. 2 institutes
Show, the through hole 2a passed through for rope (not shown) be provided in pearl 2, will pass through whole pearls 2,2 ... through hole 2a, 2a ...
The end of rope afterwards knots and forms ring.
As shown in figure 3, pearl 2 be formed with around the carbon fired body 3 of the crystalline texture for the shape for being processed into pearl 2 it is aftermentioned
Each layer (permeable formation 4, dyed layer 5, overlay 6).Carbon fired body 3 has with the crystalline texture that high density is integrated and whole one
Change.The carbon fired body 3 can lead to manufacture as described below.That is, adding pitch (coal to the carbon dust of the carbide such as graphite or bamboo carbon
Tar asphalt etc.) etc. make its solidification as adhesive, by from omnidirectional pressurization etc., being compressed and molded into based on hydraulic pressure
Defined block (such as square block).Next, the block is fired in the state of anoxic with about 1200 DEG C or so.At this point,
Multiple small gaps are generated in the inside of the block, therefore pitch (coal tar asphalt etc.) is made to immerse, and carry out the system of reburning.The pitch
It immerses and fires again and usually carry out repeatedly.Later, by the block, (for example, 2000~3000 DEG C or so) carry out at higher temperatures
It fires.Then, due to crystallization (graphitization), which becomes with whole integrated with the crystalline texture that high density is integrated
Component.It should be noted that in press molding in the case that hydraulic pressure is pressurizeed from omnidirection, crystallization can be formed
The component that the direction of change does not shift.Later, stop heating and cool down, be separated into shape that is multiple and processing beading 2.At this
In carbon fired body 3, adhesive volatilization, therefore substantially 100% (99% or more) is carbon material.In addition, bulk density (volume ratio
Weight) 1.77Mg/m can be set as3More than.
Carbon fired body 3 is carbon material, therefore very light-duty, the composition substance phase of carbon material and the organic matter for forming human body
Together, therefore for the safe of human body.Pearl 2 sometimes due tos contacting, falling etc. with other objects (other pearls 2 etc.) unexpectedly with
Object collides, even if when in this situation, carbon fired body 3 is hard and has enough physical strengths, not cracky.
In addition, carbon fired body 3 substantially 100% is carbon material, therefore absorbs human body and the heat of outside etc. and radiate a large amount of remote red
Outside line acts on subcutaneous tissue, blood vessel for wearing ornaments etc. and improves blood flow, thereby assists in and improve health.
The outside of carbon fired body 3 is provided with permeable formation 4.There is permeable formation 4 the small gap to the circumferential surface of carbon fired body 3 to ooze
Saturating part.Carbon fired body 3 generates small gap when firing.The gap is become smaller or is subtracted by the immersion of pitch and fire again by
It is few, but be difficult to completely eliminate.It should be noted that the degree of the number for gap, it can be using bulk density as index.This
The carbon fired body 3 of sample is dipped into waits solution made of resins dissolving by solvent by cellulose-based.It is attached in the circumferential surface of carbon fired body 3
Closely have it is areolate in the case of, possessed moisture or air etc. are replaced into the solution in the gap.Later, solution is molten
Agent is volatilized and is solidified.Permeable formation 4 is the concretionary layer of the solution, the very thin (example compared with the layers such as dyed layer 5, overlay 6
Such as, about 0.5 μm or less).
The outside of permeable formation 4 is provided with dyed layer 5.Dyed layer 5 is by being coated with the coating containing pigment and at high temperature
It fires.Pigment is the pigment of red etc..Coating is, for example, the coating of the resin of acrylic acid series, passes through the coatings such as spraying method
For defined thickness (for example, about 15 μm or so).Firing for example carries out at about 180 DEG C about 1 hour or so.According to dyed layer 5,
To improve cementability, as shown in figure 4, adhesive linkage 7 can be arranged between dyed layer 5 and permeable formation 4.Adhesive linkage 7 can lead to
It crosses compared with coating (for example, resin of acrylic acid series) of unfertile land (for example, the about 1 μm or so) coating without containing pigment and burns at high temperature
It makes.
The outside of dyed layer 5 is provided with overlay 6.Overlay 6 is transparent.Overlay 6 can not contain face by coating
The coating of material is simultaneously fired at high temperature.Coating is, for example, the coating of the resin of acrylic acid series, passes through the coatings such as spraying method
For defined thickness (for example, about 10 μm or so).Firing for example carries out at about 180 DEG C about 1 hour or so.
The color of the pigment of dyed layer 5 is presented in the pearl 2 of this structure, but is superimposed with the black of carbon fired body 3.For example,
In the case that the pigment of dyed layer 5 is set as red, the red overlay of the black and dyed layer 5 of carbon fired body 3, to which pearl 2 is in
Peony or ox blood color.Overlay 6 protects dyed layer 5 in a manner of defect is not present near the circumferential surface in dyed layer 5.Infiltration
Layer 4 permeates to the small gap of the circumferential surface of carbon fired body 3 and is full of the gap, so that at least containing pigment in dyed layer 5
When coating is burned at high temperature, even if there is the small gap (being shown in Figure 5 with reference numeral G) of the circumferential surface of carbon fired body 3
Be not in moisture or air etc. expand and ooze out and the case where the inner surface of dyed layer 5 is formed about small defect.It is tied
Fruit is can to prevent the case where pearl 2 makes the color of the part change because of defect, durability reduces.It should be noted that
Fig. 6 shows the case where there is no permeable formation 4, and reference numeral D shows defect.
It should be noted that the shape of pearl 2 is, for example, spherical shape, circular plate type, chess piece shape or spindle, it is not limited.Pearl 2
Size, the quantity that uses in ornaments 1 appoints according to hobby or occupation mode (bracelet, necklace, ankletbangle, bead string, watchband etc.)
Meaning determines.For example, the size of pearl 2 is 6mm, 10mm etc..Alternatively, it is also possible to by pearl 2 of different sizes, 2 ... form ornaments 1.Separately
Outside, at least one of the multiple pearls for forming ornaments 1 can also be set as above-mentioned pearl 2, remaining pearl is set as other structures.
More than, the ornaments involved by embodiments of the present invention are illustrated, but the present invention is not limited to embodiments
Recorded content can carry out the various design alterations in the range of the content recorded in technical solution.
Reference sign
1 ornaments;
2 pearls;
3 carbon fired bodies;
4 permeable formations;
5 dyed layers;
6 overlays;
7 adhesive linkages;
D defects;
The gaps G.
Claims (3)
1. a kind of ornaments are formed and annular in shape by multiple pearls are worn string, which is characterized in that
At least one pearl is formed with around the carbon fired body of the crystalline texture for the shape for being processed into the pearl:Permeable formation, tool
The part of the small gap infiltration of the circumferential surface of the oriented carbon fired body;Dyed layer, is set to the outside of the permeable formation, and passes through painting
Coating that cloth contains pigment is simultaneously fired;And transparent overlay, it is set to the outside of the dyed layer.
2. ornaments according to claim 1, which is characterized in that
The pigment of the dyed layer is red, the red overlay of the black and the dyed layer of the carbon fired body, to
The pearl is in peony or ox blood color.
3. ornaments according to claim 1 or 2, which is characterized in that
It is provided with adhesive linkage between the permeable formation and the dyed layer.