CN108342618A - 一种电阻合金丝 - Google Patents
一种电阻合金丝 Download PDFInfo
- Publication number
- CN108342618A CN108342618A CN201810518620.2A CN201810518620A CN108342618A CN 108342618 A CN108342618 A CN 108342618A CN 201810518620 A CN201810518620 A CN 201810518620A CN 108342618 A CN108342618 A CN 108342618A
- Authority
- CN
- China
- Prior art keywords
- electric resistance
- alloy silk
- resistance alloy
- manganese
- silver
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种电阻合金丝,所述电阻合金丝由镍、硅、锰、银、铅、锌、镁和铁组成。通过上述方式,本发明提供的电阻合金丝,在保证电阻率的情况下,高温寿命得到明显提高。
Description
技术领域
本发明涉及电阻材料领域,特别是涉及一种电阻合金丝。
背景技术
电阻合金丝应用于生产过热保护和精准控制电流过载的过热保护元件,有效地
防止( 电机、变压器... 等) 因电流过大而产生过热。现有的电阻合金丝在高温使用时,寿命较低。
发明内容
本发明主要解决的技术问题是提供一种电阻合金丝,在保证电阻率的情况下,高温寿命得到明显提高。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种电阻合金丝,所述电阻合金丝由镍、硅、锰、银、铅、锌、镁和铁组成,所述电阻合金丝中各组分的质量百分比含量为:
镍:80-90%;
硅:0.5-1.2%;
锰:0.9-1.8%;
银:0.2-1.1%;
铅:0.01-0.08%;
锌:0.02-0.09%;
镁:0.03-0.11%;
铁:余量。
在本发明一个较佳实施例中,所述电阻合金丝中各组分的质量百分比含量为:镍80%、硅0.5%、锰0.9%、银0.2%、铅0.01%、锌0.02%、镁0.03%和余量为铁。
在本发明一个较佳实施例中,所述电阻合金丝中各组分的质量百分比含量为:镍81%、硅0.6%、锰1.1%、银0.3%、铅0.02%、锌0.03%、镁0.04%和余量为铁。
在本发明一个较佳实施例中,所述电阻合金丝中各组分的质量百分比含量为:镍83%、硅0.7%、锰1.2%、银0.5%、铅0.03%、锌0.04%、镁0.05%和余量为铁。
在本发明一个较佳实施例中,所述电阻合金丝中各组分的质量百分比含量为:镍85%、硅0.8%、锰1.3%、银0.6%、铅0.04%、锌0.05%、镁0.07%和余量为铁。
在本发明一个较佳实施例中,所述电阻合金丝中各组分的质量百分比含量为:镍86%、硅0.9%、锰1.4%、银0.7%、铅0.05%、锌0.06%、镁0.08%和余量为铁。
本发明的有益效果是:本发明指出的一种电阻合金丝,在保证电阻率的情况下,高温寿命得到明显提高。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅是本发明的一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
实施例1:所述电阻合金丝中各组分的质量百分比含量为:镍80%、硅0.5%、锰0.9%、银0.2%、铅0.01%、锌0.02%、镁0.03%和余量为铁。
实施例2:所述电阻合金丝中各组分的质量百分比含量为:镍81%、硅0.6%、锰1.1%、银0.3%、铅0.02%、锌0.03%、镁0.04%和余量为铁。
实施例3:所述电阻合金丝中各组分的质量百分比含量为:镍83%、硅0.7%、锰1.2%、银0.5%、铅0.03%、锌0.04%、镁0.05%和余量为铁。
实施例4:所述电阻合金丝中各组分的质量百分比含量为:镍85%、硅0.8%、锰1.3%、银0.6%、铅0.04%、锌0.05%、镁0.07%和余量为铁。
实施例5:所述电阻合金丝中各组分的质量百分比含量为:镍86%、硅0.9%、锰1.4%、银0.7%、铅0.05%、锌0.06%、镁0.08%和余量为铁。
测试例:对实施例1-5中的电阻合金丝进行性能测试,测试方法参照相应的国家标准,测试结果见表1。
表1:
抗拉强度(MPa) | 延伸率(%) | 1200℃寿命(h) | |
实施例1 | 552 | 36 | 4.3 |
实施例2 | 553 | 38 | 4.1 |
实施例3 | 554 | 37 | 3.9 |
实施例4 | 555 | 35 | 4.0 |
实施例5 | 557 | 36 | 4.4 |
现有产品 | 532 | 31 | 2.3 |
综上所述,本发明指出的一种电阻合金丝,在保证电阻率的情况下,高温寿命得到明显提高。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其它相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (6)
1.一种电阻合金丝,其特征在于,所述电阻合金丝由镍、硅、锰、银、铅、锌、镁和铁组成,所述电阻合金丝中各组分的质量百分比含量为:
镍:80-90%;
硅:0.5-1.2%;
锰:0.9-1.8%;
银:0.2-1.1%;
铅:0.01-0.08%;
锌:0.02-0.09%;
镁:0.03-0.11%;
铁:余量。
2.根据权利要求1所述的电阻合金丝,其特征在于,所述电阻合金丝中各组分的质量百分比含量为:镍80%、硅0.5%、锰0.9%、银0.2%、铅0.01%、锌0.02%、镁0.03%和余量为铁。
3.根据权利要求1所述的电阻合金丝,其特征在于,所述电阻合金丝中各组分的质量百分比含量为:镍81%、硅0.6%、锰1.1%、银0.3%、铅0.02%、锌0.03%、镁0.04%和余量为铁。
4.根据权利要求1所述的电阻合金丝,其特征在于,所述电阻合金丝中各组分的质量百分比含量为:镍83%、硅0.7%、锰1.2%、银0.5%、铅0.03%、锌0.04%、镁0.05%和余量为铁。
5.根据权利要求1所述的电阻合金丝,其特征在于,所述电阻合金丝中各组分的质量百分比含量为:镍85%、硅0.8%、锰1.3%、银0.6%、铅0.04%、锌0.05%、镁0.07%和余量为铁。
6.根据权利要求1所述的电阻合金丝,其特征在于,所述电阻合金丝中各组分的质量百分比含量为:镍86%、硅0.9%、锰1.4%、银0.7%、铅0.05%、锌0.06%、镁0.08%和余量为铁。