CN108329763A - A kind of preparation method of wear-resisting welding equipment shell - Google Patents
A kind of preparation method of wear-resisting welding equipment shell Download PDFInfo
- Publication number
- CN108329763A CN108329763A CN201711474260.2A CN201711474260A CN108329763A CN 108329763 A CN108329763 A CN 108329763A CN 201711474260 A CN201711474260 A CN 201711474260A CN 108329763 A CN108329763 A CN 108329763A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- welding equipment
- preparation
- resisting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation method of wear-resisting welding equipment shell, including following operating procedure：（1）After mixing by styrene-acrylic emulsion, cyanurate melamine ester, manganese borate, behenyl amide, zinc oxide, bentonite, deionized water, wear-resistant paint is made；（2）By welding equipment surface clean it is clean after, the spraying modified liquid in surface is then placed in baking oven, baking processing after, wear-resistant paint on external coating.A kind of preparation method of wear-resisting welding equipment shell provided by the invention, it is easy to operate, it is of low cost, the shell of wear-resisting welding equipment obtained, surface evenness is high, the strong adhesive force of film layer, stability is high, and wear-resisting property is notable, can effectively promote the service life of welding equipment.
Description
Technical field
The invention belongs to welding equipment manufacturing technology fields, and in particular to a kind of preparation side of wear-resisting welding equipment shell
Method.
Background technology
Welding equipment refers to realizing the required equipment of welding procedure.Welding equipment include welding machine, welding procedure equipment and
Weld auxiliary implement.The working environment of welding equipment is more severe, should have sturdy and durable, working characteristics stabilization, reliability
Good, maintenance economic, practical, easy to repair, under conditions of normal use and correct maintenance, working life should be at 10 years or more
Advantage.But the shell of welding equipment obtained in the prior art, wear-resisting property is poor, and above-mentioned requirements are not achieved, and causes to weld
The service life of equipment is shorter.
Invention content
In order to solve the above technical problem, the present invention provides a kind of preparation methods of wear-resisting welding equipment shell.
The present invention is achieved by the following technical solutions.
A kind of preparation method of wear-resisting welding equipment shell, including following operating procedure：
（1）By weight, by 47-52 parts of styrene-acrylic emulsions, 11-15 parts of cyanurate melamine esters, 4-8 parts of manganese borates, 3-6 parts
After mixing, wear-resistant paint is made in behenyl amide, 5-9 part zinc oxide, 8-12 parts of bentonites, 13-15 parts of deionized waters；
（2）By welding equipment surface clean it is clean after, the spraying modified liquid in surface is then placed in baking oven, baking processing after, surface
It is brushed on wear-resistant paint, wherein modification liquid is made of the component of following parts by weight：17-22 parts of ethylenediamine base propanesulfonate, 1- heptan
11-15 parts of alkyl sulfonic acid sodium, 8-10 parts of four water kodalk, 240-300 parts of water.
Specifically, above-mentioned steps（1）In, the solid content 42-45% of styrene-acrylic emulsion.
Specifically, above-mentioned steps（1）In, the Average Particle Diameters of cyanurate melamine ester are 50 μm.
Specifically, above-mentioned steps（2）In, the temperature of baking oven is 75-80 DEG C, and the time of drying is 2-3 hours.
From the above technical scheme, it can be seen that the excellent effect of the present invention is：
A kind of preparation method of wear-resisting welding equipment shell provided by the invention, easy to operate, of low cost, wear-resisting weldering obtained
The shell of equipment is connect, surface evenness is high, the strong adhesive force of film layer, and stability is high, and wear-resisting property is notable, can effectively promote weldering
Connect the service life of equipment.Wherein, step（2）In modification liquid, it is notable in the dispersion performance of welding equipment shell, can be effective
The surface energy of welding equipment is promoted, enhancing wear-resistant paint can effectively prevent wear-resistant paint in the adhesion strength on welding equipment surface
There is a phenomenon where crack, fall off during welding equipment use for the film layer of formation.
Specific implementation mode
Following embodiment cannot be used for limiting the scope of the invention for illustrating the present invention.The reality used in embodiment
The condition of applying can be for further adjustments according to the condition of producer, and unaccounted implementation condition is usually conventional laboratory conditions.
Embodiment 1
A kind of preparation method of wear-resisting welding equipment shell, including following operating procedure：
（1）By weight, by 47 parts of styrene-acrylic emulsions, 11 parts of cyanurate melamine esters, 4 parts of manganese borates, 3 parts of behenyl amides, 5
After mixing, wear-resistant paint is made in part zinc oxide, 8 parts of bentonites, 13 parts of deionized waters；
（2）By welding equipment surface clean it is clean after, the spraying modified liquid in surface is then placed in baking oven, baking processing after, surface
It is brushed on wear-resistant paint, wherein modification liquid is made of the component of following parts by weight：17 parts of ethylenediamine base propanesulfonate, 1- heptane sulphurs
11 parts of sour sodium, 8 parts of four water kodalk, 240 parts of water.
Specifically, above-mentioned steps（1）In, the solid content 42% of styrene-acrylic emulsion.
Specifically, above-mentioned steps（1）In, the Average Particle Diameters of cyanurate melamine ester are 50 μm.
Specifically, above-mentioned steps（2）In, the temperature of baking oven is 75 DEG C, and the time of drying is 2 hours.
Embodiment 2
A kind of preparation method of wear-resisting welding equipment shell, including following operating procedure：
（1）By weight, by 49 parts of styrene-acrylic emulsions, 13 parts of cyanurate melamine esters, 6 parts of manganese borates, 5 parts of behenyl amides, 7
After mixing, wear-resistant paint is made in part zinc oxide, 10 parts of bentonites, 14 parts of deionized waters；
（2）By welding equipment surface clean it is clean after, the spraying modified liquid in surface is then placed in baking oven, baking processing after, surface
It is brushed on wear-resistant paint, wherein modification liquid is made of the component of following parts by weight：20 parts of ethylenediamine base propanesulfonate, 1- heptane sulphurs
13 parts of sour sodium, 9 parts of four water kodalk, 260 parts of water.
Specifically, above-mentioned steps（1）In, the solid content 43% of styrene-acrylic emulsion.
Specifically, above-mentioned steps（1）In, the Average Particle Diameters of cyanurate melamine ester are 50 μm.
Specifically, above-mentioned steps（2）In, the temperature of baking oven is 78 DEG C, and the time of drying is 2.5 hours.
Embodiment 3
A kind of preparation method of wear-resisting welding equipment shell, including following operating procedure：
（1）By weight, by 52 parts of styrene-acrylic emulsions, 15 parts of cyanurate melamine esters, 8 parts of manganese borates, 6 parts of behenyl amides, 9
After mixing, wear-resistant paint is made in part zinc oxide, 12 parts of bentonites, 15 parts of deionized waters；
（2）By welding equipment surface clean it is clean after, the spraying modified liquid in surface is then placed in baking oven, baking processing after, surface
It is brushed on wear-resistant paint, wherein modification liquid is made of the component of following parts by weight：22 parts of ethylenediamine base propanesulfonate, 1- heptane sulphurs
15 parts of sour sodium, 10 parts of four water kodalk, 300 parts of water.
Specifically, above-mentioned steps（1）In, the solid content 45% of styrene-acrylic emulsion.
Specifically, above-mentioned steps（1）In, the Average Particle Diameters of cyanurate melamine ester are 50 μm.
Specifically, above-mentioned steps（2）In, the temperature of baking oven is 80 DEG C, and the time of drying is 3 hours.
It should be understood that the application of the present invention is not limited to the above for those of ordinary skills can
With improvement or transformation based on the above description, all these modifications and variations should all belong to the guarantor of appended claims of the present invention
Protect range.
Claims (4)
1. a kind of preparation method of wear-resisting welding equipment shell, which is characterized in that including following operating procedure：
（1）By weight, by 47-52 parts of styrene-acrylic emulsions, 11-15 parts of cyanurate melamine esters, 4-8 parts of manganese borates, 3-6 parts
After mixing, wear-resistant paint is made in behenyl amide, 5-9 part zinc oxide, 8-12 parts of bentonites, 13-15 parts of deionized waters；
（2）By welding equipment surface clean it is clean after, the spraying modified liquid in surface is then placed in baking oven, baking processing after, surface
It is brushed on wear-resistant paint, wherein modification liquid is made of the component of following parts by weight：17-22 parts of ethylenediamine base propanesulfonate, 1- heptan
11-15 parts of alkyl sulfonic acid sodium, 8-10 parts of four water kodalk, 240-300 parts of water.
2. a kind of preparation method of wear-resisting welding equipment shell according to claim 1, which is characterized in that above-mentioned steps
（1）In, the solid content 42-45% of styrene-acrylic emulsion.
3. a kind of preparation method of wear-resisting welding equipment shell according to claim 1, which is characterized in that above-mentioned steps
（1）In, the Average Particle Diameters of cyanurate melamine ester are 50 μm.
4. a kind of preparation method of wear-resisting welding equipment shell according to claim 1, which is characterized in that above-mentioned steps
（2）In, the temperature of baking oven is 75-80 DEG C, and the time of drying is 2-3 hours.