CN108192460A - A kind of aqueous inorganic zinc-rich anti-corrosion primer - Google Patents
A kind of aqueous inorganic zinc-rich anti-corrosion primer Download PDFInfo
- Publication number
- CN108192460A CN108192460A CN201711334478.8A CN201711334478A CN108192460A CN 108192460 A CN108192460 A CN 108192460A CN 201711334478 A CN201711334478 A CN 201711334478A CN 108192460 A CN108192460 A CN 108192460A
- Authority
- CN
- China
- Prior art keywords
- zinc
- rich
- water
- component
- aqueous inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of aqueous inorganic zinc-rich anti-corrosion primers, are related to technical field of coatings, and 3 are pressed by water-thinned epoxy zinc-rich paint component A and water-thinned epoxy zinc-rich paint B component:1 mass ratio mixes;Aqueous inorganic zinc-rich anti-corrosion primer prepared by the present invention, not only with excellent antiseptic property, meanwhile, there is good adhesive force.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of aqueous inorganic zinc-rich anti-corrosion primer.
Background technology
The phenomenon that metal erosion refers to metal by chemistry or the electrochemical action of surrounding medium and is destroyed.Corrosion causes huge
Big economic loss, according to incompletely statistics, the whole world are lost per the 1/3 of annual steel yield due to corrosion;China it is annual because
Direct economic loss caused by metal erosion accounts for about the 4% of gross national product, and economic loss reaches caused by steel corrosion every year
Trillion yuan, it can be seen that, the protection of corrosion is particularly significant.It was verified that it is most effective, most to carry out anti-corrosion to metal using coating
It is economical, using most common method.Coating to the obstacle that diffuses to form of corrosive medium, the adhesion strength of the matrixes such as coating and steel and
The barrier property of medium plays a crucial role the service life of coating.The corrosion rate of coating depends on:Water passes through diffusion
Oozed coating and in the accumulation of coating/substrate interface and medium ionic by spreading and conduction is oozed overprotection layer and final occurred
Corrosion reaction.Coating mainly shields to base material by barrier and chemical mechanism.
Invention content
The purpose of the present invention is being directed to the problem of existing, a kind of aqueous inorganic zinc-rich anti-corrosion primer is provided.
The present invention is achieved by the following technical solutions:
A kind of aqueous inorganic zinc-rich anti-corrosion primer presses 3 by water-thinned epoxy zinc-rich paint component A and water-thinned epoxy zinc-rich paint B component:1
Mass ratio mixes;The water-thinned epoxy zinc-rich paint component A is made by weight of following component:Water-base epoxy is anhydrous
Curing agent 70-80, dispersant 14-16, propylene glycol monomethyl ether 33-35, propylene glycol 20-30, antifoaming agent 2-4, modified gas phase titanium dioxide
Silicon 5-8, zinc powder 810-830, diethylenetriamine 4-6;The water-thinned epoxy zinc-rich paint B component is by weight by following component system
Into:Aqueous epoxy emulsion 320-330, coupling agent 6-8, polyvinyl acetate 1.2-1.5, graphene oxide 3-5.
Further, the dispersant is fatty acid polyethylene glycol ester.
Further, the antifoaming agent is polyoxyethylene polyoxypropylene pentaerythrite ether.
Further, the modified aerosil preparation method is:
(1) aerosil is distributed in the suberic acid solution that mass fraction is 0.5% and impregnates 15min, then taken out
Filter, then isothermal holding 40min is carried out at 180 DEG C;
(2) by step(1)Treated, and aerosil presses 1 with polyoxyethylene polyoxy propyl alcohol amidogen ether:2 mass ratioes are at 200 DEG C
Lower stirring 2 hours, then cooled to room temperature, is added in deionized water, stirs 40min, then filtered to get modification
Aerosil.
Further, the coupling agent is organo silane coupling agent.
The present invention has the following advantages compared with prior art:Aqueous inorganic zinc-rich anti-corrosion primer prepared by the present invention, not only
With excellent antiseptic property, meanwhile, there is good adhesive force;Aqueous inorganic zinc-rich anti-corrosion primer contains a large amount of metallic zinc
Powder, zinc powder by the collaboration facilitation of modified aerosil can close-packed arrays and contact in the coating, so as to play length
Imitate antisepsis.Aqueous inorganic zinc-rich anti-corrosion primer has following characteristic:Quick-drying, the 20 min surface dryings under standard environment;2h
It does solid work;Thick coated type, disposable spray finishing thickness are excellent up to 70 μm of antiseptic properties;Using water as diluent, cleaning agent is non-ignitable, nothing
VOC emission, construction is simple, storage safety, heat-resisting quantity, continuous heat-resisting reachable 300 DEG C of aqueous inorganic zinc-rich anti-corrosion primers have
Electro-chemical protection, current potential than iron more more negative mechanism, using a large amount of high-purity superfine zinc powder as anti-corrosion more active than iron according to zinc
Pigment makes steel in electrolyte solution, even if coating is locally damaged, since zinc is as sacrificial anode, and obtains steel
To protection, durability is good, by the physics and chemical bonding of coating and steel, makes the strong adhesive force of coating and steel substrate, zinc
The zinc salt and the complex compound of zinc that powder is formed in coating surface can block gap, crackle and the hole of coating, prevent oxygen, water and
The corrosion of other media, and do not influenced by atmospheric conditions and ultraviolet light irradiation, the service life of coating is long, and maintenance cost is low,
It can be suitable for the anticorrosion of steel structure priming paint such as steel tower, pipeline, port facilities, means of transportation, water conservancy projects, need high-temperature corrosion resistance
Under the conditions of iron structure, the iron structure coating under other mal-conditions.
Specific embodiment
Embodiment 1
A kind of aqueous inorganic zinc-rich anti-corrosion primer presses 3 by water-thinned epoxy zinc-rich paint component A and water-thinned epoxy zinc-rich paint B component:1
Mass ratio mixes;The water-thinned epoxy zinc-rich paint component A is made by weight of following component:Water-base epoxy is anhydrous
Curing agent 70, dispersant 14, propylene glycol monomethyl ether 33, propylene glycol 20, antifoaming agent 2, modified aerosil 5, zinc powder 810, two
Ethylene triamine 4;The water-thinned epoxy zinc-rich paint B component is made by weight of following component:Aqueous epoxy emulsion 320, idol
Join agent 6, polyvinyl acetate 1.2, graphene oxide 3.
Further, the dispersant is fatty acid polyethylene glycol ester.
Further, the antifoaming agent is polyoxyethylene polyoxypropylene pentaerythrite ether.
Further, the modified aerosil preparation method is:
(1) aerosil is distributed in the suberic acid solution that mass fraction is 0.5% and impregnates 15min, then taken out
Filter, then isothermal holding 40min is carried out at 180 DEG C;
(2) by step(1)Treated, and aerosil presses 1 with polyoxyethylene polyoxy propyl alcohol amidogen ether:2 mass ratioes are at 200 DEG C
Lower stirring 2 hours, then cooled to room temperature, is added in deionized water, stirs 40min, then filtered to get modification
Aerosil.
Further, the coupling agent is organo silane coupling agent.
Embodiment 2
A kind of aqueous inorganic zinc-rich anti-corrosion primer presses 3 by water-thinned epoxy zinc-rich paint component A and water-thinned epoxy zinc-rich paint B component:1
Mass ratio mixes;The water-thinned epoxy zinc-rich paint component A is made by weight of following component:Water-base epoxy is anhydrous
Curing agent 80, dispersant 16, propylene glycol monomethyl ether 35, propylene glycol 30, antifoaming agent 4, modified aerosil 8, zinc powder 830, two
Ethylene triamine 6;The water-thinned epoxy zinc-rich paint B component is made by weight of following component:Aqueous epoxy emulsion 330, idol
Join agent 8, polyvinyl acetate 1.5, graphene oxide 5.
Further, the dispersant is fatty acid polyethylene glycol ester.
Further, the antifoaming agent is polyoxyethylene polyoxypropylene pentaerythrite ether.
Further, the modified aerosil preparation method is:
(1) aerosil is distributed in the suberic acid solution that mass fraction is 0.5% and impregnates 15min, then taken out
Filter, then isothermal holding 40min is carried out at 180 DEG C;
(2) by step(1)Treated, and aerosil presses 1 with polyoxyethylene polyoxy propyl alcohol amidogen ether:2 mass ratioes are at 200 DEG C
Lower stirring 2 hours, then cooled to room temperature, is added in deionized water, stirs 40min, then filtered to get modification
Aerosil.
Further, the coupling agent is organo silane coupling agent.
Embodiment 3
A kind of aqueous inorganic zinc-rich anti-corrosion primer presses 3 by water-thinned epoxy zinc-rich paint component A and water-thinned epoxy zinc-rich paint B component:1
Mass ratio mixes;The water-thinned epoxy zinc-rich paint component A is made by weight of following component:Water-base epoxy is anhydrous
Curing agent 75, dispersant 15, propylene glycol monomethyl ether 34, propylene glycol 25, antifoaming agent 3, modified aerosil 6, zinc powder 820, two
Ethylene triamine 5;The water-thinned epoxy zinc-rich paint B component is made by weight of following component:Aqueous epoxy emulsion 325, idol
Join agent 7, polyvinyl acetate 1.3, graphene oxide 4.
Further, the dispersant is fatty acid polyethylene glycol ester.
Further, the antifoaming agent is polyoxyethylene polyoxypropylene pentaerythrite ether.
Further, the modified aerosil preparation method is:
(1) aerosil is distributed in the suberic acid solution that mass fraction is 0.5% and impregnates 15min, then taken out
Filter, then isothermal holding 40min is carried out at 180 DEG C;
(2) by step(1)Treated, and aerosil presses 1 with polyoxyethylene polyoxy propyl alcohol amidogen ether:2 mass ratioes are at 200 DEG C
Lower stirring 2 hours, then cooled to room temperature, is added in deionized water, stirs 40min, then filtered to get modification
Aerosil.
Further, the coupling agent is organo silane coupling agent.
Comparative example 1:It is differed only in embodiment 1 and modified aerosil is replaced with into conventional gas phase silica.
Comparative example 2:It is differed only in embodiment 1 and graphene oxide is replaced with into common graphite alkene.
Experiment:
Performance test
Test method is:By the component A of embodiment and comparative example and B component paint, using deionized-distilled water be diluted to
Spray viscosity (40-50S, T-4 glasss), standard tinplate sheet carry out phosphatization or grinding process, and thickness control is in 20- in tinplate sheet
30 μm, all-round property testing is done after 48 hours do solid work completely, type inspection dry plate thickness control at 80-100 μm, treat 7 days it is complete
Pattern detection is done after doing solid work entirely;Drying time, adhesive force was according to GB/T1720, and resistance to neutral salt spray is according to GB/ according to GB/T1728
T1771;The results are shown in table below;
Table 1
Solid content % | Do solid work h | Adhesive force/grade | Water resistance/h | Salt fog resistance/h | Resistant to acetone immersion/h | |
Embodiment 1 | 72.8 | 2 | 1 | 860 | 4500 | 780 |
Embodiment 2 | 73.1 | 2 | 1 | 850 | 4600 | 780 |
Embodiment 3 | 72.9 | 2 | 1 | 860 | 4500 | 770 |
Comparative example 1 | 72.6 | 5 | 2 | 780 | 4000 | 720 |
Comparative example 2 | 71.5 | 8 | 1 | 820 | 4200 | 750 |
As can be seen from Table 1, the anticorrosion with coat performance that prepared by the present invention is good.
Claims (5)
1. a kind of aqueous inorganic zinc-rich anti-corrosion primer, which is characterized in that by water-thinned epoxy zinc-rich paint component A and water-thinned epoxy zinc-rich
It paints B component and presses 3:1 mass ratio mixes;The water-thinned epoxy zinc-rich paint component A is made by weight of following component:
The anhydrous curing agent 70-80 of water-base epoxy, dispersant 14-16, propylene glycol monomethyl ether 33-35, propylene glycol 20-30, antifoaming agent 2-4, change
Property aerosil 5-8, zinc powder 810-830, diethylenetriamine 4-6;The water-thinned epoxy zinc-rich paint B component is by weight
It is made of following component:Aqueous epoxy emulsion 320-330, coupling agent 6-8, polyvinyl acetate 1.2-1.5, graphene oxide 3-
5。
2. a kind of aqueous inorganic zinc-rich anti-corrosion primer as described in claim 1, which is characterized in that the dispersant is aliphatic acid
Macrogol ester.
3. a kind of aqueous inorganic zinc-rich anti-corrosion primer as described in claim 1, which is characterized in that the antifoaming agent is polyoxy second
Alkene polyoxypropylene pentaerythrite ether.
A kind of 4. aqueous inorganic zinc-rich anti-corrosion primer as described in claim 1, which is characterized in that the modified gas phase titanium dioxide
Silicon preparation method is:
(1) aerosil is distributed in the suberic acid solution that mass fraction is 0.5% and impregnates 15min, then taken out
Filter, then isothermal holding 40min is carried out at 180 DEG C;
(2) by step(1)Treated, and aerosil presses 1 with polyoxyethylene polyoxy propyl alcohol amidogen ether:2 mass ratioes are at 200 DEG C
Lower stirring 2 hours, then cooled to room temperature, is added in deionized water, stirs 40min, then filtered to get modification
Aerosil.
5. a kind of aqueous inorganic zinc-rich anti-corrosion primer as described in claim 1, which is characterized in that the coupling agent is organosilicon
Alkane coupling agent.