CN108316094A - A kind of bituminous paving reclaimed materials and its warm mix regeneration technology - Google Patents
A kind of bituminous paving reclaimed materials and its warm mix regeneration technology Download PDFInfo
- Publication number
- CN108316094A CN108316094A CN201810226085.3A CN201810226085A CN108316094A CN 108316094 A CN108316094 A CN 108316094A CN 201810226085 A CN201810226085 A CN 201810226085A CN 108316094 A CN108316094 A CN 108316094A
- Authority
- CN
- China
- Prior art keywords
- parts
- rap
- matrix pitch
- primary material
- bituminous paving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of bituminous paving reclaimed materials and its warm mix regeneration technology, and material is by RAP:35 45 parts, primary material:55 65 parts, 1.5 2 parts of cement, 2.3 3.5 parts of compositions of regeneration matrix pitch;RAP by the percent of pass for design of gathering materials, is sent by measuring belt in RAP heating rollers by present invention process in proportion respectively, carries out heating mixing, and heating temperature is 130 135 DEG C;Primary material is sent into primary material by measuring belt by design mixture proportion to heat in roller, is heated to 140 145 DEG C;RAP and primary material are added to by design proportioning respectively and mixed in cylinder, spray into regeneration matrix pitch, after 3 seconds, cement is added to be mixed and stirred, mixing time controlled at 35 45 seconds, and regeneration ratio is greatly improved in the present invention, and ratios of the RAP in regenerating mixture is up to 40 45%, temperature also reduces 30 DEG C or more, and the secondary problem of aging of pitch is greatly reduced.
Description
Technical field
The present invention relates to highway recycling road material deep process technology field, specific more particularly to a kind of bituminous paving reclaimed materials and
Its warm mix regeneration technology.
Background technology
Currently, highway pavement largely uses pitch as road surface cementitious material.And bituminous paving is rolled by long-term vehicle
After traveling, there are the diseases such as fatigue cracking, breakage, pit slot in road surface, for this purpose, road surface can using after several years, can in repair or overhaul,
Top course or middle cutting optimal milling are got off, after handling sub-layer, overlay road surface again;Conventional method is by road
The material that facing cut is dug i.e. road surface reclaimed materials RAP falls as waste disposal, then does new road surface again;As resource is nervous,
Environmental protection ideas gos deep into, and RAP for this purpose, there is shutting mechanism to develop cold renewal, i.e., works as RAP as rubbish not permitted in government
At building stones, the base on road surface is done, the place of a storage actually or by RAP has been changed as rubbish, this is one
Value not reciprocity " regeneration " utilizes.
In order to realize that equivalent regeneration, people mix and stir RAP together with primary material, reclaimed asphalt mixture is formed, but this
High temperature regeneration so that RAP ginsengs are not high with ratio, and China is substantially 20% or so, and temperature is up to 170 DEG C or more, leads to pitch
The secondary aging of material;
The present invention solves the chronic illness of above-mentioned conventional regeneration, and regeneration ratio is greatly improved, and RAP is in regenerating mixture
In ratio be up to 40-45%, temperature also reduces 30 DEG C or more, the secondary problem of aging of pitch is greatly reduced, under
Secondary regeneration, creates condition.
Invention content
For this purpose, a kind of bituminous paving reclaimed materials of present invention proposition and its warm mix regeneration technology, are greatly improved reproduction ratio
Example, ratios of the RAP in regenerating mixture are up to 40-45%, and temperature also reduces 30 DEG C or more, pitch is greatly reduced
Secondary problem of aging creates condition for the regeneration of next time.
The present invention is realized by following means:
A kind of bituminous paving reclaimed materials, is made of following material by weight:RAP:35-45 parts, primary material:55-65 parts,
1.5-2 parts of cement regenerates 2.3-3.5 parts of matrix pitch.
Preferably, the regeneration matrix pitch is made of warm mix regenerative agent with matrix pitch, and the matrix pitch is public affairs
Road with A grades of pitches at 120-130 DEG C, with regeneration warm-mixing agent be stirred after, the homogeneous mixture of formation.
Preferably, a kind of bituminous paving reclaimed materials, is made of following material by weight:AP:35 parts, primary material:65 parts,
1.5 parts of cement, 2.9 parts of of regeneration matrix pitch
Preferably, a kind of bituminous paving reclaimed materials, is made of following material by weight:RAP:40 parts, primary material:60
Part, 1.5 parts of cement regenerates 2.6 parts of matrix pitch.
Preferably, a kind of bituminous paving reclaimed materials, is made of following material by weight:RAP:45 parts, primary material:55
Part, 1.5 parts of cement regenerates 3.4 parts of matrix pitch.
A kind of bituminous paving reclaimed materials warm mix regeneration method, comprises the following steps that:By RAP passing through by design of gathering materials
Rate is sent by measuring belt in RAP heating rollers, carries out heating mixing, heating temperature 130-135 in proportion respectively
℃;Primary material is sent into primary material by measuring belt by design mixture proportion to heat in roller, is heated to 140-145 DEG C;Respectively
RAP and primary material are added to by design proportioning and mixed in cylinder, regeneration matrix pitch is sprayed into, after 3 seconds, cement is added and is mixed and stirred,
Mixing time controlled at 35-45 seconds.
A kind of bituminous paving reclaimed materials warm mix regeneration method, includes following processing step:Each material is mixed, and
The proportional region of warm mix regenerative agent and water is added thereto 1:10-1:20 dilution, and the spy of 0.3-1% is added thereto
Kind of activating agent is added cement and is mixed and stirred, and mixing time control was at 35-45 seconds, 140-145 DEG C of heating temperature.
Advantageous effect of the present invention:Regeneration ratio is greatly improved in the present invention, and ratios of the RAP in regenerating mixture can be high
Up to 40-45%, temperature also reduces 30 DEG C or more, and the secondary problem of aging of pitch is greatly reduced, for the regeneration of next time, wound
Condition is made, bituminous paving reclaimed materials of the present invention has following material characteristic:Marshall stability:AC classes mixture 11~
20KN, flow valuve 15~40, Marshall residual stability 80-85%, 3000-6000 times/mm of dynamic stability.
Specific implementation mode:
In order to make those skilled in the art more fully understand technical scheme of the present invention, with reference to embodiment to this hair
It is bright to be described further:
A kind of bituminous paving reclaimed materials, is made of following material by weight:RAP:35-45 parts, primary material:55-65 parts,
1.5-2 parts of cement regenerates 2.3-3.5 parts of matrix pitch.
Preferably, the regeneration matrix pitch is made of warm mix regenerative agent with matrix pitch, and the matrix pitch is public affairs
Road with A grades of pitches at 120-130 DEG C, with regeneration warm-mixing agent be stirred after, the homogeneous mixture of formation.
Preferably, a kind of bituminous paving reclaimed materials, is made of following material by weight:AP:35 parts, primary material:65 parts,
1.5 parts of cement, 2.9 parts of of regeneration matrix pitch
Preferably, a kind of bituminous paving reclaimed materials, is made of following material by weight:RAP:40 parts, primary material:60
Part, 1.5 parts of cement regenerates 2.6 parts of matrix pitch.
Preferably, a kind of bituminous paving reclaimed materials, is made of following material by weight:RAP:45 parts, primary material:55
Part, 1.5 parts of cement regenerates 3.4 parts of matrix pitch.
A kind of bituminous paving reclaimed materials warm mix regeneration method, comprises the following steps that:By RAP passing through by design of gathering materials
Rate is sent by measuring belt in RAP heating rollers, carries out heating mixing, heating temperature 130-135 in proportion respectively
℃;Primary material is sent into primary material by measuring belt by design mixture proportion to heat in roller, is heated to 140-145 DEG C;Respectively
RAP and primary material are added to by design proportioning and mixed in cylinder, regeneration matrix pitch is sprayed into, after 3 seconds, cement is added and is mixed and stirred,
Mixing time controlled at 35-45 seconds.
A kind of bituminous paving reclaimed materials warm mix regeneration method, includes following processing step:Each material is mixed, and
The proportional region of warm mix regenerative agent and water is added thereto 1:10-1:20 dilution, and the spy of 0.3-1% is added thereto
Kind of activating agent is added cement and is mixed and stirred, and mixing time control was at 35-45 seconds, 140-145 DEG C of heating temperature.
Testing inspection:By People's Republic of China's professional standard:Highway engineering pitch and Asphalt Mixture Experiment regulation
T709-2011, T719-2011, as a result such as following table:
Above certain exemplary embodiments that the present invention is only described by way of explanation, undoubtedly, for ability
The those of ordinary skill in domain without departing from the scope of the invention can be with a variety of different modes to described reality
Example is applied to be modified.Therefore, foregoing description is regarded as illustrative in nature, and should not be construed as protecting model to the claims in the present invention
The limitation enclosed.
Unless otherwise defined, all academic and scientific terminologies used herein have the technical field of the invention common
The identical meanings that technical staff is understood.
In the case of inconsistent, the definition in this specification shall prevail.
Unless otherwise indicated, all percentage, number, ratio etc. are by weight.
When providing numerical value or numberical range, a series of preferred scope or lower preferable values and upper limit preferred value, should manage
It is solved to specifically disclose by any of any smaller range limit or preferred value and any larger range limit or preferred value
One logarithm is formed by any range, regardless of whether range is disclosed respectively.Unless otherwise indicated, it is described in this specification
In place of numberical range, the range is intended to include all integers and the score in range endpoints and range.
When term " about " or " left and right " are used to describe the end value of number value or range, disclosure of that should be include this
Concrete numerical value or involved end value.
Using the element and component of the usage of " one " and "/kind " the description present invention, this only for it is convenient and in order to
Provide ordinary circumstance of the present invention.Unless otherwise apparent statement, which should be interpreted as include/kind or at least one/kind.
Claims (6)
1. a kind of bituminous paving reclaimed materials, it is characterised in that:It is made of by weight following material:RAP:It is 35-45 parts, primary
Material:55-65 parts, 1.5-2 parts of cement regenerates 2.3-3.5 parts of matrix pitch.
2. a kind of bituminous paving reclaimed materials according to claim 1, it is characterised in that:The regeneration matrix pitch is by temperature
Regenerative agent and matrix pitch is mixed to constitute, the matrix pitch be highway with A grade pitches at 120-130 DEG C, and regenerate warm-mixing agent
After being stirred, the homogeneous mixture of formation.
3. a kind of bituminous paving reclaimed materials according to claim 1, it is characterised in that:By weight by following material structure
At:AP:35 parts, primary material:65 parts, 1.5 parts of cement regenerates 2.9 parts of matrix pitch.
4. a kind of bituminous paving reclaimed materials according to claim 1, it is characterised in that:By weight by following material structure
At:RAP:40 parts, primary material:60 parts, 1.5 parts of cement regenerates 2.6 parts of matrix pitch.
5. a kind of bituminous paving reclaimed materials according to claim 1, it is characterised in that:By weight by following material structure
At:RAP:45 parts, primary material:55 parts, 1.5 parts of cement regenerates 3.4 parts of matrix pitch.
6. a kind of bituminous paving reclaimed materials warm mix regeneration method, it is characterised in that:It comprises the following steps that:By RAP by gathering materials
The percent of pass of design is sent by measuring belt in RAP heating rollers, carries out heating mixing, heating temperature in proportion respectively
It is 130-135 DEG C;Primary material is sent into primary material by measuring belt by design mixture proportion to heat in roller, is heated to 140-
145℃;RAP and primary material are added to by design proportioning respectively and mixed in cylinder, regeneration matrix pitch is sprayed into, after 3 seconds, cement is added
It is mixed and stirred, the mixing time controlled at 35-45 seconds.