CN108300210A - A kind of novel anti-anti-aging preparation method for coating of corruption - Google Patents
A kind of novel anti-anti-aging preparation method for coating of corruption Download PDFInfo
- Publication number
- CN108300210A CN108300210A CN201710918223.XA CN201710918223A CN108300210A CN 108300210 A CN108300210 A CN 108300210A CN 201710918223 A CN201710918223 A CN 201710918223A CN 108300210 A CN108300210 A CN 108300210A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- coating
- corruption
- preservative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The novel anti-anti-aging preparation method for coating of corruption of one kind provided by the invention includes following components, 50 70 parts of vinyltoluene alkyd resin by weight, 5 15 parts of titanium dioxide, 20 30 parts of epoxy resin, 8 12 parts of oyster shell whiting, 39 parts of bentonite, 35 parts of levelling agent, 13 parts of curing agent, 24 parts of preservative, 58 parts of organic solvent, composition is simple, configuration is convenient, and cost is relatively low, non-hazardous, strong adsorption is not easy the embrittlement that turns to be yellow, and effectively extends its service life, can more meet the needs of producer.
Description
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of novel anti-anti-aging preparation method for coating of corruption.
Background technology
Coating, in the entitled paint of Chinese tradition.So-called coating be coated in the body surface being protected or decorated, and
The continuous film of firm attachment can be formed with coated article, typically based on resin or oil or lotion, add or do not add face
Material, filler add corresponding additive, the thick liquid being formulated with organic solvent or water.However existing coating is used for a long time
After can turn to be yellow embrittlement, the phenomenon that generation falls off, it is readily volatilized go out toxic gas, there is security risk, can not meet user's
It needs.
Invention content
The object of the present invention is to provide a kind of novel anti-anti-aging preparation method for coating of corruption, and solve existing coating makes for a long time
Can turn to be yellow embrittlement after, generation the phenomenon that falling off, it is readily volatilized go out toxic gas, there is security risk, can not meet user
The problem of needs.
The purpose of the present invention can be achieved through the following technical solutions；
A kind of novel anti-anti-aging preparation method for coating of corruption, preparation method are as follows：
（1）Following components, 50-70 parts of vinyltoluene alkyd resin, 5-15 parts of titanium dioxide, asphalt mixtures modified by epoxy resin are weighed by weight
20-30 parts of fat, 8-12 parts of oyster shell whiting, 3-9 parts of bentonite, 3-5 parts of levelling agent, 1-3 parts of curing agent, 2-4 parts of preservative, You Jirong
5-8 parts of agent；
（2）Polyacrylic acid, carboxymethyl cellulose are put into reaction kettle, temperature is 25 DEG C -35 DEG C, and uniform stirring 7-15min is obtained
To levelling agent；
（3）Benzoic acid and sodium benzoate are put into reaction kettle, temperature is 35 DEG C -55 DEG C, and uniform stirring 10-20min is obtained into
Preservative；
（4）Toluene and dimethylbenzene are put into reaction kettle, temperature is 20 DEG C -40 DEG C, uniform stirring 15-30min, is obtained organic molten
Agent；
（5）Vinyltoluene alkyd resin and titanium dioxide are entered in reaction kettle, 10-20min is stirred, temperature is 35 DEG C -40 DEG C；When
After temperature is promoted to 45 DEG C -55 DEG C, it is separately added into epoxy resin and oyster shell whiting, continues to stir 5-15min, when temperature is promoted to 60
After DEG C -70 DEG C, bentonite, levelling agent and preservative is added, continues to stir 10-30min, when temperature is promoted to 80 DEG C -100 DEG C
Afterwards, organic solvent and curing agent is added, stirs 20-30min.
The above-mentioned novel anti-anti-aging preparation method for coating of corruption of one kind, wherein the levelling agent is polyacrylic acid, carboxylic first
Base cellulose mixes together, weight fraction ratio 3:2.
The above-mentioned novel anti-anti-aging preparation method for coating of corruption of one kind, wherein the curing agent is amine curing agent.
The above-mentioned novel anti-anti-aging preparation method for coating of corruption of one kind, wherein the preservative is benzoic acid and benzene first
Sour sodium mixes together, weight fraction ratio 2:1.
The above-mentioned novel anti-anti-aging preparation method for coating of corruption of one kind, wherein the organic solvent is toluene and diformazan
Benzene mixes together, weight fraction ratio 1:5.
The advantageous effect of this programme：
The novel anti-anti-aging preparation method for coating of corruption of one kind provided by the invention, composition is simple, and configuration is convenient, and cost is relatively low, nothing
Harm, strong adsorption are not easy the embrittlement that turns to be yellow, effectively extend its service life, can more meet the needs of producer.
Specific implementation mode
Embodiment 1：A kind of novel anti-anti-aging preparation method for coating of corruption, preparation method are as follows：
（1）Following components, 70 parts of vinyltoluene alkyd resin, 15 parts of titanium dioxide, epoxy resin 30 are weighed by weight
Part, 12 parts of oyster shell whiting, 9 parts of bentonite, 5 parts of levelling agent, 3 parts of curing agent, 4 parts of preservative, 8 parts of organic solvent；
（2）Polyacrylic acid, carboxymethyl cellulose are put into reaction kettle, temperature is 25 DEG C, and uniform stirring 7min obtains levelling
Agent；
（3）Benzoic acid and sodium benzoate are put into reaction kettle, temperature is 35 DEG C, and uniform stirring 10min obtains into preservative；
（4）Toluene and dimethylbenzene are put into reaction kettle, temperature is 40 DEG C, and uniform stirring 15min obtains organic solvent；
（5）Vinyltoluene alkyd resin and titanium dioxide are entered in reaction kettle, 10min is stirred, temperature is 35 DEG C；When temperature is promoted
To after 45 DEG C, it is separately added into epoxy resin and oyster shell whiting, continues to stir 5min, after temperature is promoted to 60 DEG C, addition bentonite,
Levelling agent and preservative continue to stir 10min, and after temperature is promoted to 80 DEG C, organic solvent and curing agent, stirring is added
20min.
Embodiment 2：A kind of novel anti-anti-aging preparation method for coating of corruption, preparation method are as follows：
（1）Following components, 60 parts of vinyltoluene alkyd resin, 10 parts of titanium dioxide, epoxy resin 25 are weighed by weight
Part, 10 parts of oyster shell whiting, 6 parts of bentonite, 4 parts of levelling agent, 2 parts of curing agent, 3 parts of preservative, 6 parts of organic solvent；
（2）Polyacrylic acid, carboxymethyl cellulose are put into reaction kettle, temperature is 30 DEG C, and uniform stirring 10min obtains levelling
Agent；
（3）Benzoic acid and sodium benzoate are put into reaction kettle, temperature is 40 DEG C, and uniform stirring 15min obtains into preservative；
（4）Toluene and dimethylbenzene are put into reaction kettle, temperature is 30 DEG C, and uniform stirring 25min obtains organic solvent；
（5）Vinyltoluene alkyd resin and titanium dioxide are entered in reaction kettle, 15min is stirred, temperature is 37 DEG C；When temperature is promoted
To after 40 DEG C, it is separately added into epoxy resin and oyster shell whiting, continues to stir 10min, after temperature is promoted to 65 DEG C, swelling is added
Soil, levelling agent and preservative continue to stir 20min, and after temperature is promoted to 90 DEG C, organic solvent and curing agent, stirring is added
25min.
Embodiment 3：A kind of novel anti-anti-aging preparation method for coating of corruption, preparation method are as follows：
（1）Following components, 70 parts of vinyltoluene alkyd resin, 15 parts of titanium dioxide, epoxy resin 30 are weighed by weight
Part, 12 parts of oyster shell whiting, 9 parts of bentonite, 5 parts of levelling agent, 3 parts of curing agent, 4 parts of preservative, 8 parts of organic solvent；
（2）Polyacrylic acid, carboxymethyl cellulose are put into reaction kettle, temperature is 35 DEG C, and uniform stirring 15min obtains levelling
Agent；
（3）Benzoic acid and sodium benzoate are put into reaction kettle, temperature is 55 DEG C, and uniform stirring 20min obtains into preservative；
（4）Toluene and dimethylbenzene are put into reaction kettle, temperature is 40 DEG C, and uniform stirring 30min obtains organic solvent；
（5）Vinyltoluene alkyd resin and titanium dioxide are entered in reaction kettle, 20min is stirred, temperature is 40 DEG C；When temperature is promoted
To after 55 DEG C, it is separately added into epoxy resin and oyster shell whiting, continues to stir 15min, after temperature is promoted to 70 DEG C, swelling is added
Soil, levelling agent and preservative continue to stir 30min, and after temperature is promoted to 100 DEG C, organic solvent and curing agent, stirring is added
30min.
The novel anti-anti-aging preparation method for coating of corruption of one kind provided by the invention, composition is simple, and configuration is convenient, cost compared with
Low, non-hazardous, strong adsorption is not easy the embrittlement that turns to be yellow, and effectively extends its service life, can more meet the needs of producer.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, the change or replacement that can be readily occurred in,
Should all it cover within the scope of the present invention.Therefore, protection scope of the present invention should be with the protection domain of claims
Subject to.
Claims (5)
1. a kind of novel anti-anti-aging preparation method for coating of corruption, it is characterized in that, preparation method is as follows：
（1）Following components, 50-70 parts of vinyltoluene alkyd resin, 5-15 parts of titanium dioxide, asphalt mixtures modified by epoxy resin are weighed by weight
20-30 parts of fat, 8-12 parts of oyster shell whiting, 3-9 parts of bentonite, 3-5 parts of levelling agent, 1-3 parts of curing agent, 2-4 parts of preservative, You Jirong
5-8 parts of agent；
（2）Polyacrylic acid, carboxymethyl cellulose are put into reaction kettle, temperature is 25 DEG C -35 DEG C, and uniform stirring 7-15min is obtained
To levelling agent；
（3）Benzoic acid and sodium benzoate are put into reaction kettle, temperature is 35 DEG C -55 DEG C, and uniform stirring 10-20min is obtained into
Preservative；
（4）Toluene and dimethylbenzene are put into reaction kettle, temperature is 20 DEG C -40 DEG C, uniform stirring 15-30min, is obtained organic molten
Agent；
（5）Vinyltoluene alkyd resin and titanium dioxide are entered in reaction kettle, 10-20min is stirred, temperature is 35 DEG C -40 DEG C；When
After temperature is promoted to 45 DEG C -55 DEG C, it is separately added into epoxy resin and oyster shell whiting, continues to stir 5-15min, when temperature is promoted to 60
After DEG C -70 DEG C, bentonite, levelling agent and preservative is added, continues to stir 10-30min, when temperature is promoted to 80 DEG C -100 DEG C
Afterwards, organic solvent and curing agent is added, stirs 20-30min.
2. a kind of novel anti-anti-aging preparation method for coating of corruption as described in claim 1, it is characterized in that, the levelling agent is
Polyacrylic acid, carboxymethyl cellulose mix together, weight fraction ratio 3:2.
3. a kind of novel anti-anti-aging preparation method for coating of corruption as described in claim 1, it is characterized in that, the curing agent is
Amine curing agent.
4. a kind of novel anti-anti-aging preparation method for coating of corruption as described in claim 1, it is characterized in that, the preservative is
Benzoic acid is mixed together with sodium benzoate, weight fraction ratio 2:1.
5. a kind of novel anti-anti-aging preparation method for coating of corruption as described in claim 1, it is characterized in that, the organic solvent
It is mixed together for toluene and dimethylbenzene, weight fraction ratio 1:5.