CN108297504A - A kind of corrosion-resistant metal materials - Google Patents
A kind of corrosion-resistant metal materials Download PDFInfo
- Publication number
- CN108297504A CN108297504A CN201810434554.0A CN201810434554A CN108297504A CN 108297504 A CN108297504 A CN 108297504A CN 201810434554 A CN201810434554 A CN 201810434554A CN 108297504 A CN108297504 A CN 108297504A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer material
- ingredient
- corrosion
- resistant metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of corrosion-resistant metal materials, including:First layer material and the second layer material, first layer material are made of magnesium, silicon nitride, borax and nickel, and second layer material is made of iron, yttrium, copper and cobalt, parts by weight shared by each ingredient in first layer material:2 10 parts of 10 18 parts of magnesium, 15 25 parts of silicon nitride, 19 parts of borax and nickel, parts by weight shared by each ingredient in second layer material:4 12 parts of 50 59 parts of iron, 3 11 parts of yttrium, 12 18 parts of copper and cobalt, the first layer material is in the top of the second layer material in the corrosion-resistant metal materials, and is connected by way of seamless welding.By the above-mentioned means, corrosion-resistant metal materials provided by the invention, have preferable corrosion resistance and low manufacture cost.
Description
Technical field
The present invention relates to metal material fields, more particularly to a kind of corrosion-resistant metal materials.
Background technology
With the continuous progress of science, the place for using alloy is more and more extensive, and the either vehicles, life is used
Product, household items etc., such as:Automobile industry, building material industry, kitchen article, alloy articles for use have risen quite big in daily life
Effect, but metal materials many on the market now are poor corrosion resistance, of high cost, especially in the various friendships being prone to wear out
Logical tool's engine field is particularly acute.
Invention content
The invention mainly solves the technical problem of providing a kind of corrosion-resistant metal materials, have preferable corrosion resistance
And low manufacture cost.
In order to solve the above technical problems, one aspect of the present invention is:A kind of corrosion-resistant metal materials are provided,
Including:First layer material and the second layer material, first layer material are made of magnesium, silicon nitride, borax and nickel, the second layer
Material is made of iron, yttrium, copper and cobalt, parts by weight shared by each ingredient in first layer material:10-18 parts of magnesium, silicon nitride 15-
2-10 parts of 25 parts, 1-9 parts of borax and nickel, parts by weight shared by each ingredient in second layer material:50-59 parts of iron, yttrium 3-11
Part, 4-12 parts of 12-18 parts of copper and cobalt, in the corrosion-resistant metal materials the first layer material in the top of the second layer material, and
It is connected by way of seamless welding.
In a preferred embodiment of the present invention, parts by weight shared by each ingredient in first layer material:10 parts of magnesium, nitrogen
2 parts of 15 parts of SiClx, 1 part of borax and nickel, parts by weight shared by each ingredient in second layer material:50 parts of iron, 3 parts of yttrium, copper 12
4 parts of part and cobalt.
In a preferred embodiment of the present invention, parts by weight shared by each ingredient in first layer material:11 parts of magnesium, nitrogen
3 parts of 17 parts of SiClx, 2 parts of borax and nickel, parts by weight shared by each ingredient in second layer material:51 parts of iron, 4 parts of yttrium, copper 13
6 parts of part and cobalt.
In a preferred embodiment of the present invention, parts by weight shared by each ingredient in first layer material:13 parts of magnesium, nitrogen
4 parts of 19 parts of SiClx, 3 parts of borax and nickel, parts by weight shared by each ingredient in second layer material:53 parts of iron, 5 parts of yttrium, copper 14
7 parts of part and cobalt.
In a preferred embodiment of the present invention, parts by weight shared by each ingredient in first layer material:15 parts of magnesium, nitrogen
7 parts of 22 parts of SiClx, 6 parts of borax and nickel, parts by weight shared by each ingredient in second layer material:56 parts of iron, 7 parts of yttrium, copper 16
8 parts of part and cobalt.
In a preferred embodiment of the present invention, parts by weight shared by each ingredient in first layer material:18 parts of magnesium, nitrogen
9 parts of 24 parts of SiClx, 8 parts of borax and nickel, parts by weight shared by each ingredient in second layer material:59 parts of iron, 10 parts of yttrium, copper 17
9 parts of part and cobalt.
The beneficial effects of the invention are as follows:A kind of corrosion-resistant metal materials that the present invention points out have preferable corrosion resistance
Energy and low manufacture cost.
Specific implementation mode
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
All other embodiment that technical staff is obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1:Parts by weight shared by each ingredient in first layer material:10 parts of magnesium, 15 parts of silicon nitride, 1 part of borax
With 2 parts of nickel, parts by weight shared by each ingredient in second layer material:4 parts of 50 parts of iron, 3 parts of yttrium, 12 parts of copper and cobalt.
Embodiment 2:Parts by weight shared by each ingredient in first layer material:11 parts of magnesium, 17 parts of silicon nitride, 2 parts of borax
With 3 parts of nickel, parts by weight shared by each ingredient in second layer material:6 parts of 51 parts of iron, 4 parts of yttrium, 13 parts of copper and cobalt.
Embodiment 3:Parts by weight shared by each ingredient in first layer material:13 parts of magnesium, 19 parts of silicon nitride, 3 parts of borax
With 4 parts of nickel, parts by weight shared by each ingredient in second layer material:7 parts of 53 parts of iron, 5 parts of yttrium, 14 parts of copper and cobalt.
Embodiment 4:Parts by weight shared by each ingredient in first layer material:15 parts of magnesium, 22 parts of silicon nitride, 6 parts of borax
With 7 parts of nickel, parts by weight shared by each ingredient in second layer material:8 parts of 56 parts of iron, 7 parts of yttrium, 16 parts of copper and cobalt.
Embodiment 5:Parts by weight shared by each ingredient in first layer material:18 parts of magnesium, 24 parts of silicon nitride, 8 parts of borax
With 9 parts of nickel, parts by weight shared by each ingredient in second layer material:9 parts of 59 parts of iron, 10 parts of yttrium, 17 parts of copper and cobalt.
Test case:
The corrosion resistance assessment of metal material is carried out using etch test.The corrosive medium used is 2%H2SO4+3%Na2SO4
(It is mass percentage concentration, the PH of solution is 1.3), test temperature is 100 DEG C, and the etch time is 16 hours, and test result is such as
Shown in table 1.
Table 1:
In conclusion a kind of corrosion-resistant metal materials that the present invention points out, have preferable corrosion resistance and low manufacture cost.
Example the above is only the implementation of the present invention is not intended to limit the scope of the invention, every to utilize this hair
Equivalent structure or equivalent flow shift made by bright description is applied directly or indirectly in other relevant technology necks
Domain is included within the scope of the present invention.
Claims (6)
1. a kind of corrosion-resistant metal materials, which is characterized in that including:First layer material and the second layer material, the first layer material
Material is made of magnesium, silicon nitride, borax and nickel, and second layer material is made of iron, yttrium, copper and cobalt, in first layer material
Parts by weight shared by each ingredient:2-10 parts of 10-18 parts of magnesium, 15-25 parts of silicon nitride, 1-9 parts of borax and nickel, second layer material
In parts by weight shared by each ingredient:4-12 parts of 50-59 parts of iron, 3-11 parts of yttrium, 12-18 parts of copper and cobalt, the corrosion resistant metal material
The first layer material is in the top of the second layer material in material, and is connected by way of seamless welding.
2. corrosion-resistant metal materials according to claim 1, which is characterized in that in first layer material shared by each ingredient
Parts by weight:2 parts of 10 parts of magnesium, 15 parts of silicon nitride, 1 part of borax and nickel, parts by weight shared by each ingredient in second layer material:
4 parts of 50 parts of iron, 3 parts of yttrium, 12 parts of copper and cobalt.
3. corrosion-resistant metal materials according to claim 1, which is characterized in that in first layer material shared by each ingredient
Parts by weight:3 parts of 11 parts of magnesium, 17 parts of silicon nitride, 2 parts of borax and nickel, parts by weight shared by each ingredient in second layer material:
6 parts of 51 parts of iron, 4 parts of yttrium, 13 parts of copper and cobalt.
4. corrosion-resistant metal materials according to claim 1, which is characterized in that in first layer material shared by each ingredient
Parts by weight:4 parts of 13 parts of magnesium, 19 parts of silicon nitride, 3 parts of borax and nickel, parts by weight shared by each ingredient in second layer material:
7 parts of 53 parts of iron, 5 parts of yttrium, 14 parts of copper and cobalt.
5. corrosion-resistant metal materials according to claim 1, which is characterized in that in first layer material shared by each ingredient
Parts by weight:7 parts of 15 parts of magnesium, 22 parts of silicon nitride, 6 parts of borax and nickel, parts by weight shared by each ingredient in second layer material:
8 parts of 56 parts of iron, 7 parts of yttrium, 16 parts of copper and cobalt.
6. corrosion-resistant metal materials according to claim 1, which is characterized in that in first layer material shared by each ingredient
Parts by weight:9 parts of 18 parts of magnesium, 24 parts of silicon nitride, 8 parts of borax and nickel, parts by weight shared by each ingredient in second layer material:
9 parts of 59 parts of iron, 10 parts of yttrium, 17 parts of copper and cobalt.