CN103272877A - Low-carbon inconel seamless tube - Google Patents
Low-carbon inconel seamless tube Download PDFInfo
- Publication number
- CN103272877A CN103272877A CN2013101943291A CN201310194329A CN103272877A CN 103272877 A CN103272877 A CN 103272877A CN 2013101943291 A CN2013101943291 A CN 2013101943291A CN 201310194329 A CN201310194329 A CN 201310194329A CN 103272877 A CN103272877 A CN 103272877A
- Authority
- CN
- China
- Prior art keywords
- blank
- ferroalloy
- nichrome
- seamless pipe
- low carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a low-carbon inconel seamless tube which comprises the ingredients of nickel, cuprum, ferrum, manganese, carbon, silicon, sulfur and chromium. A method for manufacturing the low-carbon inconel seamless tube comprises the steps of: (1) preparing a blank material; (2) carrying out first pickling on the blank material, and carrying out lubricating treatment on the blank material which is subjected to first pickling; (3) carrying out cold drawing and rolling treatment on the lubricated blank material; (4) carrying out heat treatment on the blank material; (5) carrying out straightening treatment on the blank material; (6) carrying out finishing treatment on the blank material; and (7) finally inspecting a finished product, and marking and warehousing. The low-carbon inconel seamless tube disclosed by the invention has the functions of corrosion resistance, high temperature resistance, strong acid resistance, strong alkali resistance and cost saving.
Description
Technical field
The present invention relates to a kind of manufacturing of seamless pipe, be specifically related to the low carbon nichrome ferroalloy seamless pipe that a kind of UNS NO6690 alloy is made.
Background technology
Seamless pipe is a kind of circle that hollow section, periphery do not have seam that has, and is square, the rectangle steel.Seamless pipe is to make hollow billet with steel ingot or the solid pipe hole that wears long, and makes through hot rolling, cold rolling or cold group then.Seamless pipe has hollow section, a large amount of as the pipeline of carrying fluid, steel pipe is compared with solid steel such as round steel, when the bending resistance torsional strength is identical, weight is lighter, be a kind of economic cross-section steel, be widely used in manufacturing structure spare and machine components, as steel scaffold of using in oil drill rocker, truck drive shaft, bicycle rack and the construction etc.
At aspects such as some high temperature, the inorganic acid that is mixed with impurity and organic acid (as formic acid and acetic acid), corrosive environment of sea water, general pipe can't extensive use in this environment, and maintenance cost is bigger, can't promote on a large scale.
Therefore, the seamless pipe of research and develop a kind of corrosion-resistant, high temperature resistant, anti-strong acid, anti-highly basic, saving cost is problem demanding prompt solution.
Summary of the invention
The object of the present invention is to provide the low carbon nichrome ferroalloy seamless pipe of a kind of corrosion-resistant, high temperature resistant, anti-strong acid, anti-highly basic, saving cost.
Technical scheme of the present invention is, a kind of low carbon nichrome ferroalloy seamless pipe, described low carbon nichrome ferroalloy seamless pipe comprises by weight percentage: nickel is 58%-67%, and copper is 0.15%-0.5%, and iron is 7%-11%, manganese is 0.22%-0.5%, carbon is 0.011%-0.05%, and silicon is 0.35%-0.75%, and sulphur is 0.009%-0.015%, and chromium is 27%-31%, and the manufacturing step of described low carbon nichrome ferroalloy seamless pipe is:
(1) the at first preparation of blank,
(2) then blank is carried out the pickling first time, the blank good to the pickling first time is lubricated processing,
(3) blank after lubricated is carried out cold drawing and rolling and handles,
(4) blank is heat-treated operation,
(5) blank is carried out straightening processing,
(6) blank is carried out finishing and handles,
(7) at last finished product is tested, and the sign warehouse-in.
In a preferred embodiment of the present invention, described Acidwash solution is mixed by nitric acid and hydrofluoric acid, and the composition of the pickle in the described Acidwash solution comprises that mass percent is that nitric acid and the mass percent of 8.5%-12.5% is the hydrofluoric acid of 1.9%-2.6%.
In a preferred embodiment of the present invention, butter and lime that described lubricated employing weight ratio is 1.8:8.5 mix.
In a preferred embodiment of the present invention, the deformation coefficient scope of described cold drawing and rolling is 1.7%-2.4%.
In a preferred embodiment of the present invention, described heat treatment process temperature is 890 ℃-1155 ℃, and the described type of cooling is cold quenching.
Of the present invention is a kind of low carbon nichrome ferroalloy seamless pipe, the function that makes the Hastelloy seamless pipe have corrosion-resistant, high temperature resistant, anti-strong acid, anti-highly basic and save cost.
Description of drawings
Fig. 1 be a preferred embodiment of the present invention process flow diagram.
The specific embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
Of the present invention is a kind of low carbon nichrome ferroalloy seamless pipe, referring to shown in Figure 1, described low carbon nichrome ferroalloy seamless pipe comprises by weight percentage: nickel is 58%-67%, copper is 0.15%-0.5%, and iron is 7%-11%, and manganese is 0.22%-0.5%, carbon is 0.011%-0.05%, silicon is 0.35%-0.75%, and sulphur is 0.009%-0.015%, and chromium is 27%-31%.
The manufacturing step of described low carbon nichrome ferroalloy seamless pipe is:
(1) the at first preparation of blank,
(2) then blank is carried out the pickling first time, the blank good to the pickling first time is lubricated processing,
(3) blank after lubricated is carried out cold drawing and rolling and handles,
(4) blank is heat-treated operation,
(5) blank is carried out straightening processing,
(6) blank is carried out finishing and handles,
(7) at last finished product is tested, and the sign warehouse-in.
Further specify, described Acidwash solution is mixed by nitric acid and hydrofluoric acid, the composition of the pickle in the described Acidwash solution comprises that mass percent is that nitric acid and the mass percent of 8.5%-12.5% is the hydrofluoric acid of 1.9%-2.6%, butter and lime that described lubricated employing weight ratio is 1.8:8.5 mix, the deformation coefficient scope of described cold drawing and rolling is 1.7%-2.4%, described heat treatment process temperature is 890 ℃-1155 ℃, and the described type of cooling is cold quenching.
Further specify, in heat treatment process, can not contact sulphur, phosphorus, lead and other low-melting-point metal, otherwise can damage the performance of material, should note removing such as dirts such as lubricating oil, fuel.Control time is at 30min, hydrofluoric acid plays the effect of deoiling enough fast and effectively and tube surface is not had the influence of turning white of any peracid; the material of light-wall pipe also can adopt quick air cooling, and the above purpose reaches desirable surperficial decay resistance and improves, improve the superior performance standard 1.1-1.2 times.
A kind of low carbon nichrome ferroalloy seamless pipe of the present invention, the function that makes the Hastelloy seamless pipe have corrosion-resistant, high temperature resistant, anti-strong acid, anti-highly basic and save cost.
The above only is the specific embodiment of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the disclosed technical scope of the present invention; variation or the replacement that can expect without creative work all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (5)
1. low carbon nichrome ferroalloy seamless pipe, it is characterized in that: described low carbon nichrome ferroalloy seamless pipe comprises by weight percentage: nickel is 58%-67%, copper is 0.15%-0.5%, iron is 7%-11%, and manganese is 0.22%-0.5%, and carbon is 0.011%-0.05%, silicon is 0.35%-0.75%, sulphur is 0.009%-0.015%, and chromium is 27%-31%, and the manufacturing step of described low carbon nichrome ferroalloy seamless pipe is:
(1) the at first preparation of blank,
(2) then blank is carried out the pickling first time, the blank good to the pickling first time is lubricated processing,
(3) blank after lubricated is carried out cold drawing and rolling and handles,
(4) blank is heat-treated operation,
(5) blank is carried out straightening processing,
(6) blank is carried out finishing and handles,
(7) at last finished product is tested, and the sign warehouse-in.
2. low carbon nichrome ferroalloy seamless pipe according to claim 1, it is characterized in that: described Acidwash solution is mixed by nitric acid and hydrofluoric acid, and the composition of the pickle in the described Acidwash solution comprises that mass percent is that nitric acid and the mass percent of 8.5%-12.5% is the hydrofluoric acid of 1.9%-2.6%.
3. low carbon nichrome ferroalloy seamless pipe according to claim 1, it is characterized in that: butter and lime that described lubricated employing weight ratio is 1.8:8.5 mix.
4. low carbon nichrome ferroalloy seamless pipe according to claim 1, it is characterized in that: the deformation coefficient scope of described cold drawing and rolling is 1.7%-2.4%.
5. low carbon nichrome ferroalloy seamless pipe according to claim 1, it is characterized in that: described heat treatment process temperature is 890 ℃-1155 ℃, and the described type of cooling is cold quenching.