CN108296426A - A kind of furan resin casting reinforcing agent and preparation method thereof - Google Patents
A kind of furan resin casting reinforcing agent and preparation method thereof Download PDFInfo
- Publication number
- CN108296426A CN108296426A CN201711477479.8A CN201711477479A CN108296426A CN 108296426 A CN108296426 A CN 108296426A CN 201711477479 A CN201711477479 A CN 201711477479A CN 108296426 A CN108296426 A CN 108296426A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- reinforcing agent
- furan resin
- ethyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to Casting Technology fields more particularly to a kind of furan resin casting reinforcing agent and preparation method thereof.Include the raw material of following volumes number, 22~28 parts of (3 aminopropyl) trimethoxy silane, 6~7 parts of phthalic acid, 8~9 parts of ethyl acetate+petroleum ether, 8~10 parts of acid.The present invention provides a kind of high temperature resistant, radiation hardness, wear-resistant furan resin casting reinforcing agent and preparation method thereof.
Description
Technical field
The present invention relates to Casting Technology field more particularly to a kind of furan resin casting reinforcing agent and its preparation sides
Method.
Background technology
Reinforcing agent is also known as coupling agent, and there are two different reactive groups in structure, and one is the bases of close inorganic matter
Group X (such as methoxyl group, ethyoxyl), can be hydrolyzed reaction and generate silicone hydroxyl (Si-OH), with the keys such as glass, silica
It closes;Another kind is organophilic group Y (such as vinyl, amino), can be with interpolymer interaction.Furane resins are as viscous
Agent is tied, an important indicator of performance is the intensity of resin sand.Mainly there are two aspects for the raising of mechanical strength of resin:First, passing through
Production technology is adjusted, the intensity of resin itself is improved;Second is that it is strong to reach reinforced resin that reinforcing agent such as silane coupling agent etc. is added
The purpose of degree.The structure feature of silane coupling agent make it have by inorganic matter (such as sand) and organic matter (such as synthetic resin) this two
The ability that the material that kind property differs greatly combines.
Invention content
The present invention is directed to synthesizing new reinforcing agents, and provide a kind of high temperature resistant, radiation hardness, wear-resistant furan resin casting
With reinforcing agent and preparation method thereof.
The present invention to achieve the above object, using following technical scheme:A kind of furan resin casting reinforcing agent, including with
The raw material of lower volume number, 22~28 parts of (3- aminopropyls) trimethoxy silane, 6~7 parts of phthalic acid, ethyl acetate+
8~9 parts of petroleum ether, 8~10 parts of acid.
Preferably:Include the raw material of following volumes number, 25 parts of (3- aminopropyls) trimethoxy silane, phthalic acid
6 parts, 9 parts of ethyl acetate+petroleum ether, acid 9 parts.
Preferably:The acid is concentrated acid.
Preferably:The volume ratio of ethyl acetate and petroleum ether is 1:1~2.
The present invention to achieve the above object, using following technical scheme:A kind of furan resin casting reinforcing agent preparation side
Method, (3- aminopropyls) trimethoxy silane, phthalic acid, ethyl acetate+petroleum ether are mixed 10 at 50~55 DEG C~
20min is added acid and mixes 1~2h at 85~90 DEG C after mixing.
The beneficial effects of the invention are as follows:The reinforcing agent that the present invention prepares introduces hetero-aromatic ring, enhances the resistance to of coupling agent
Warm nature, radiation resistance, abrasion resistance improve the performance of reinforcing agent, are conducive to the performance for improving furane resins.
Specific implementation mode
With reference to embodiment, the invention will be further described:
The present invention includes the raw material of following volumes number, 22~28 parts of (3- aminopropyls) trimethoxy silane, adjacent benzene two
6~7 parts of formic acid, 8~9 parts of ethyl acetate+petroleum ether, 8~10 parts of concentrated acid, the wherein volume ratio of ethyl acetate and petroleum ether are 1:
1~2.
The preparation method of the present invention is, by (3- aminopropyls) trimethoxy silane, phthalic acid, ethyl acetate+stone
Oily ether mixes 10~20min at 50~55 DEG C, and acid is added after mixing and mixes 1~2h at 85~90 DEG C.
Embodiment 1, the present invention include the raw material of following volumes number, 25 parts of (3- aminopropyls) trimethoxy silane, neighbour
The volume ratio of 6 parts of phthalic acid, 9 parts of ethyl acetate+petroleum ether, 9 parts of concentrated acid, ethyl acetate and petroleum ether is 1:1.
The preparation method of the present invention is, by 25 parts by volume (3- aminopropyls) trimethoxy silane, 6 parts of adjacent benzene
Dioctyl phthalate, 9 parts of ethyl acetate+petroleum ether mix 20min at 55 DEG C, and 9 parts of concentrated acid is added after mixing and is mixed at 90 DEG C
2h, wherein concentrated acid be the concentrated sulfuric acid, concentrated hydrochloric acid, concentrated nitric acid it is one or more.
The reinforcing agent that the present invention prepares introduces hetero-aromatic ring, enhances the temperature tolerance of coupling agent, radiation resistance, wear-resistant
Property, the performance of reinforcing agent is improved, the performance for improving furane resins is conducive to.
Embodiment 2, the present invention include the raw material of following volumes number, 22 parts of (3- aminopropyls) trimethoxy silane, neighbour
7 parts of phthalic acid, 8 parts of ethyl acetate+petroleum ether, 8 parts of concentrated acid, the wherein volume ratio of ethyl acetate and petroleum ether are 1:2.
The preparation method of the present invention is, by 22 parts by volume (3- aminopropyls) trimethoxy silane, 7 parts of adjacent benzene
Dioctyl phthalate, 8 parts of ethyl acetate+petroleum ether mix 10min at 50 DEG C, and 8 parts of concentrated acid is added after mixing and is mixed at 85 DEG C
1h, wherein concentrated acid be the concentrated sulfuric acid, concentrated hydrochloric acid, concentrated nitric acid it is one or more.
Embodiment 3, the present invention include the raw material of following volumes number, 28 parts of (3- aminopropyls) trimethoxy silane, neighbour
7 parts of phthalic acid, 9 parts of ethyl acetate+petroleum ether, 9 parts of concentrated acid, the wherein volume ratio of ethyl acetate and petroleum ether are 1:1.5.
The preparation method of the present invention is, by 28 parts by volume (3- aminopropyls) trimethoxy silane, 7 parts of adjacent benzene
Dioctyl phthalate, 9 parts of ethyl acetate+petroleum ether mix 15min at 53 DEG C, and 9 parts of concentrated acid is added after mixing and is mixed at 88 DEG C
1h, wherein concentrated acid be the concentrated sulfuric acid, concentrated hydrochloric acid, concentrated nitric acid it is one or more.
The present invention is exemplarily described above, it is clear that present invention specific implementation is not subject to the restrictions described above,
As long as using the various improvement of inventive concept and technical scheme of the present invention progress, or not improved directly apply to other fields
It closes, within protection scope of the present invention.
Claims (5)
1. a kind of furan resin casting reinforcing agent, it is characterised in that:Include the raw material of following volumes number, (3- aminopropyls)
22~28 parts of trimethoxy silane, 6~7 parts of phthalic acid, 8~9 parts of ethyl acetate+petroleum ether, 8~10 parts of acid.
2. furan resin casting reinforcing agent according to claim 1, it is characterised in that:Include the original of following volumes number
Material, 25 parts of (3- aminopropyls) trimethoxy silane, 6 parts of phthalic acid, 9 parts of ethyl acetate+petroleum ether, 9 parts of acid.
3. furan resin casting reinforcing agent according to claim 1, it is characterised in that:The acid is concentrated acid.
4. furan resin casting reinforcing agent according to claim 1, it is characterised in that:The body of ethyl acetate and petroleum ether
Product is than being 1:1~2.
5. a kind of preparation method of furan resin casting reinforcing agent according to claim 1:It is characterized in that:By (3-
Aminopropyl) trimethoxy silane, phthalic acid, ethyl acetate+petroleum ether mix 10~20min at 50~55 DEG C, it mixes
Acid is added after conjunction and mixes 1~2h at 85~90 DEG C.