CN108285768A - Tuner(LNB)It is bonded special room curing silicon rubber - Google Patents
Tuner(LNB)It is bonded special room curing silicon rubber Download PDFInfo
- Publication number
- CN108285768A CN108285768A CN201810125300.0A CN201810125300A CN108285768A CN 108285768 A CN108285768 A CN 108285768A CN 201810125300 A CN201810125300 A CN 201810125300A CN 108285768 A CN108285768 A CN 108285768A
- Authority
- CN
- China
- Prior art keywords
- parts
- tuner
- lnb
- hydroxyl
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses tuners (LNB) to be bonded special room curing silicon rubber, the invention belongs to functional product of the silicone adhesive sealant for the bonding of tuner (LNB) product, the silicone sealant gluing product that the present invention matches production connects bonding securely, soaked, high/low temperature recycle 72 hours, properties it is excellent, do not influence signal.
Description
Technical field
The invention belongs to functional product technology neck of the silicone adhesive sealant for the bonding of tuner (LNB) product
Domain, and in particular to be bonded special room curing silicon rubber to tuner (LNB).
Background technology
Tuner (LNB) is that television set is used for receiving high-frequency signal and demodulates a kind of device of video information, determines shadow
The stability of picture, but tuner itself is very easy to by electromagnetic interference.Therefore the sealing performance of tuner requires very stringent.At present
Using it is most be the sealants such as epoxy resin, silica gel, epoxy resin sealant stick is due to its water resistance and resistance to
High-temperature behavior is poor, and hardness is very high after solidification, is easily deformed under high/low temperature variation, damages product, is all made of in processing molten
Agent progress is dilute, does not meet present environmental requirement, therefore, epoxy resin is slowly replaced by organosilicon sealant, and early period has
Machine silicone sealant mostly uses ketoxime type crosslinking agent, and hardening time length, fugitive constituent are big, influence signal.
Invention content
The purpose of the present invention is that solve the above-mentioned problems and provides tuner (LNB) and be bonded special room temperature curing silicon
Rubber.
The present invention is achieved through the following technical solutions above-mentioned purpose:
Tuner (LNB) is bonded special room curing silicon rubber, which is characterized in that component includes by weight:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, precipitated silica
2 parts;
Color masterbatch:2-5 parts of iron oxide red;
Crosslinking agent:0-3 parts of ethyl orthosilicate, 0-3 parts of parts of tetramethoxy-silicane, 0-3 parts of TM stabilizers;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
Preferably, the preparation method is that:
Component by weight, by 100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, precipitation
2 parts of method white carbon, 2-5 parts of iron oxide red, 0-3 parts of ethyl orthosilicate, 0-3 parts of parts of tetramethoxy-silicane, 0-3 parts of TM stabilizers,
1 part of aminopropyl triethoxysilane, 5 parts of diethylin methyltriethoxysilane are added in power mixer in vacuum state
Lower mixing, is produced into organic silicon adhesive product, product is respectively coated on tuner, and solidification tests items after 48 hours
Energy.
Preferably, the component by weight includes:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, precipitated silica
2 parts;
Color masterbatch:2 parts of iron oxide red;
Crosslinking agent:3 parts of ethyl orthosilicate, 3 parts of parts of tetramethoxy-silicane, 3 parts of TM stabilizers;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
Preferably, the component by weight includes:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, precipitated silica
2 parts;
Color masterbatch:5 parts of iron oxide red;
Crosslinking agent:3 parts of 3 parts of ethyl orthosilicate, tetramethoxy-silicane parts;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
Preferably, the component by weight includes:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, precipitated silica
2 parts;
Color masterbatch:3 parts of iron oxide red;
Crosslinking agent:3 parts of parts of tetramethoxy-silicane, 3 parts of TM stabilizers;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
Preferably, the component by weight includes:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, precipitated silica
2 parts;
Color masterbatch:4 parts of iron oxide red;
Crosslinking agent:3 parts of ethyl orthosilicate, 3 parts of TM stabilizers;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
Preferably, the component by weight includes:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, precipitated silica
2 parts;
Color masterbatch:5 parts of iron oxide red;
Crosslinking agent:1 part of ethyl orthosilicate, 2 parts of parts of tetramethoxy-silicane, 3 parts of TM stabilizers;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
Preferably, the component by weight includes:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, precipitated silica
2 parts;
Color masterbatch:5 parts of iron oxide red;
Crosslinking agent:3 parts of ethyl orthosilicate, 1 part of part of tetramethoxy-silicane, 1 part of TM stabilizers;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
Compared with prior art, the beneficial effects of the present invention are:
The present invention provides tuner (LNB) and is bonded special room curing silicon rubber, which belongs to silicone sealant gluing
Agent is for the functional product of the bonding of tuner (LNB) product, the silicone sealant glue sticking bonding of present invention proportioning production
Securely, soaked, high/low temperature recycle 72 hours, properties it is excellent, do not influence signal.
Specific implementation mode
Embodiment 1
Specific implementation process:
1, by iron oxide red 2 parts of additions, 15 parts of hydroxyl-terminated injecting two methyl siloxane mixings, three-roll grinder is ground three times, at
Color masterbatch is spare;
2,85 parts of hydroxyl-terminated injecting two methyl siloxanes are weighed to be added in reaction kettle;
3,30 parts of nano-calcium carbonate, 20 parts of silicon powder, 2 parts of precipitated silica are separately added into;
4, the ground acetylene carbon black color masterbatch of the first step is added;
5, motor is started, material is allowed to be stirred evenly in reaction kettle;
6, reaction kettle cover is risen, the residual powder on agitating shaft is cleaned, declines reaction kettle cover in place;
7, vacuum pump is started, reaction kettle holding is persistently vacuumized into state;
8, stirring motor is started, heater is opened simultaneously, allows material to be heated at 150 DEG C, to vacuumize lower high-speed stirred 5 small
When;
9, turn off heater after the completion of heating, continue to vacuumize stirring at low speed and be down to 60 DEG C or less to temperature of charge;
10, close stirring motor, be vented vacuum, from filling opening be added 3 parts of ethyl orthosilicate, 3 parts of parts of tetramethoxy-silicane,
3 parts of TM stabilizers;
11, it vacuumizes and closes stirring motor after stirring 30 minutes, emptying vacuum, 1 part of aminopropyl triethoxysilane of addition,
5 parts of diethylin methyltriethoxysilane;
12, stirring motor is closed after vacuumizing stirring 30 minutes, emptying Vacuum discharge packaging obtains (aluminium, zinc-plated to metal
Deng) be bonded securely, there is certain levelability and hardness is moderate, corrosion-free, fugitive constituent is small, does not influence to receive signal, has elasticity
Fluid sealant.
Embodiment 2
Specific implementation process:
1, by iron oxide red 5 parts of additions, 15 parts of hydroxyl-terminated injecting two methyl siloxane mixings, three-roll grinder is ground three times, at
Color masterbatch is spare;
2,85 parts of hydroxyl-terminated injecting two methyl siloxanes are weighed to be added in reaction kettle;
3,30 parts of nano-calcium carbonate, 20 parts of silicon powder, 2 parts of precipitated silica are separately added into;
4, the ground acetylene carbon black color masterbatch of the first step is added;
5, motor is started, material is allowed to be stirred evenly in reaction kettle;
6, reaction kettle cover is risen, the residual powder on agitating shaft is cleaned, declines reaction kettle cover in place;
7, vacuum pump is started, reaction kettle holding is persistently vacuumized into state;
8, stirring motor is started, heater is opened simultaneously, allows material to be heated at 150 DEG C, to vacuumize lower high-speed stirred 5 small
When;
9, turn off heater after the completion of heating, continue to vacuumize stirring at low speed and be down to 60 DEG C or less to temperature of charge;
10, stirring motor is closed, vacuum is vented, 3 parts of 3 parts of ethyl orthosilicate, tetramethoxy-silicane parts are added from filling opening;
11, it vacuumizes and closes stirring motor after stirring 30 minutes, emptying vacuum, 1 part of aminopropyl triethoxysilane of addition,
5 parts of diethylin methyltriethoxysilane;
12, stirring motor is closed after vacuumizing stirring 30 minutes, emptying Vacuum discharge packaging obtains (aluminium, zinc-plated to metal
Deng) be bonded securely, there is certain levelability and hardness is moderate, corrosion-free, fugitive constituent is small, does not influence to receive signal, has elasticity
Fluid sealant.
Embodiment 3
Specific implementation process:
1, by iron oxide red 3 parts of additions, 15 parts of hydroxyl-terminated injecting two methyl siloxane mixings, three-roll grinder is ground three times, at
Color masterbatch is spare;
2,85 parts of hydroxyl-terminated injecting two methyl siloxanes are weighed to be added in reaction kettle;
3,30 parts of nano-calcium carbonate, 20 parts of silicon powder, 2 parts of precipitated silica are separately added into;
4, the ground acetylene carbon black color masterbatch of the first step is added;
5, motor is started, material is allowed to be stirred evenly in reaction kettle;
6, reaction kettle cover is risen, the residual powder on agitating shaft is cleaned, declines reaction kettle cover in place;
7, vacuum pump is started, reaction kettle holding is persistently vacuumized into state;
8, stirring motor is started, heater is opened simultaneously, allows material to be heated at 150 DEG C, to vacuumize lower high-speed stirred 5 small
When;
9, turn off heater after the completion of heating, continue to vacuumize stirring at low speed and be down to 60 DEG C or less to temperature of charge;
10, stirring motor is closed, vacuum is vented, 3 parts of parts of tetramethoxy-silicane, 3 parts of TM stabilizers is added from filling opening;
11, it vacuumizes and closes stirring motor after stirring 30 minutes, emptying vacuum, 1 part of aminopropyl triethoxysilane of addition,
5 parts of diethylin methyltriethoxysilane;
12, stirring motor is closed after vacuumizing stirring 30 minutes, emptying Vacuum discharge packaging obtains (aluminium, zinc-plated to metal
Deng) be bonded securely, there is certain levelability and hardness is moderate, corrosion-free, fugitive constituent is small, does not influence to receive signal, has elasticity
Fluid sealant.
Embodiment 4
Specific implementation process:
1, by iron oxide red 4 parts of additions, 15 parts of hydroxyl-terminated injecting two methyl siloxane mixings, three-roll grinder is ground three times, at
Color masterbatch is spare;
2,85 parts of hydroxyl-terminated injecting two methyl siloxanes are weighed to be added in reaction kettle;
3,30 parts of nano-calcium carbonate, 20 parts of silicon powder, 2 parts of precipitated silica are separately added into;
4, the ground acetylene carbon black color masterbatch of the first step is added;
5, motor is started, material is allowed to be stirred evenly in reaction kettle;
6, reaction kettle cover is risen, the residual powder on agitating shaft is cleaned, declines reaction kettle cover in place;
7, vacuum pump is started, reaction kettle holding is persistently vacuumized into state;
8, stirring motor is started, heater is opened simultaneously, allows material to be heated at 150 DEG C, to vacuumize lower high-speed stirred 5 small
When;
9, turn off heater after the completion of heating, continue to vacuumize stirring at low speed and be down to 60 DEG C or less to temperature of charge;
10, stirring motor is closed, vacuum is vented, 3 parts of ethyl orthosilicate, 3 parts of TM stabilizers is added from filling opening;
11, it vacuumizes and closes stirring motor after stirring 30 minutes, emptying vacuum, 1 part of aminopropyl triethoxysilane of addition,
5 parts of diethylin methyltriethoxysilane;
12, stirring motor is closed after vacuumizing stirring 30 minutes, emptying Vacuum discharge packaging obtains (aluminium, zinc-plated to metal
Deng) be bonded securely, there is certain levelability and hardness is moderate, corrosion-free, fugitive constituent is small, does not influence to receive signal, has elasticity
Fluid sealant.
Claims (8)
1. tuner (LNB) is bonded special room curing silicon rubber, which is characterized in that component includes by weight:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, 2 parts of precipitated silica;
Color masterbatch:2-5 parts of iron oxide red;
Crosslinking agent:0-3 parts of ethyl orthosilicate, 0-3 parts of parts of tetramethoxy-silicane, 0-3 parts of TM stabilizers;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
2. tuner (LNB) according to claim 1 is bonded special room curing silicon rubber, which is characterized in that the system
Preparation Method is:
Component by weight, by 100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, the precipitation method are white
2 parts of carbon black, 2-5 parts of iron oxide red, 0-3 parts of ethyl orthosilicate, 0-3 parts of parts of tetramethoxy-silicane, 0-3 parts of TM stabilizers, ammonia third
1 part of ethyl triethoxy silicane alkane, 5 parts of diethylin methyltriethoxysilane are added in power mixer and mix under vacuum conditions
It closes, is produced into organic silicon adhesive product, product is respectively coated on tuner, solidification tests properties after 48 hours.
3. tuner (LNB) according to claim 1 is bonded special room curing silicon rubber, which is characterized in that described to press
Composition by weight includes:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, 2 parts of precipitated silica;
Color masterbatch:2 parts of iron oxide red;
Crosslinking agent:3 parts of ethyl orthosilicate, 3 parts of parts of tetramethoxy-silicane, 3 parts of TM stabilizers;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
4. tuner (LNB) according to claim 1 is bonded special room curing silicon rubber, which is characterized in that described to press
Composition by weight includes:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, 2 parts of precipitated silica;
Color masterbatch:5 parts of iron oxide red;
Crosslinking agent:3 parts of 3 parts of ethyl orthosilicate, tetramethoxy-silicane parts;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
5. tuner (LNB) according to claim 1 is bonded special room curing silicon rubber, which is characterized in that described to press
Composition by weight includes:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, 2 parts of precipitated silica;
Color masterbatch:3 parts of iron oxide red;
Crosslinking agent:3 parts of parts of tetramethoxy-silicane, 3 parts of TM stabilizers;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
6. tuner (LNB) according to claim 1 is bonded special room curing silicon rubber, which is characterized in that described to press
Composition by weight includes:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, 2 parts of precipitated silica;
Color masterbatch:4 parts of iron oxide red;
Crosslinking agent:3 parts of ethyl orthosilicate, 3 parts of TM stabilizers;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
7. tuner (LNB) according to claim 1 is bonded special room curing silicon rubber, which is characterized in that described to press
Composition by weight includes:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, 2 parts of precipitated silica;
Color masterbatch:5 parts of iron oxide red;
Crosslinking agent:1 part of ethyl orthosilicate, 2 parts of parts of tetramethoxy-silicane, 3 parts of TM stabilizers;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.
8. tuner (LNB) according to claim 1 is bonded special room curing silicon rubber, which is characterized in that described to press
Composition by weight includes:
Base-material:100 parts of hydroxyl-terminated injecting two methyl siloxane;30 parts of nano-calcium carbonate, 20 parts of silicon powder, 2 parts of precipitated silica;
Color masterbatch:5 parts of iron oxide red;
Crosslinking agent:3 parts of ethyl orthosilicate, 1 part of part of tetramethoxy-silicane, 1 part of TM stabilizers;
Coupling agent:1 part of aminopropyl triethoxysilane;
Catalyst:5 parts of diethylin methyltriethoxysilane.