CN108264327A - A kind of concrete of water proof anti-seepage - Google Patents
A kind of concrete of water proof anti-seepage Download PDFInfo
- Publication number
- CN108264327A CN108264327A CN201810390089.5A CN201810390089A CN108264327A CN 108264327 A CN108264327 A CN 108264327A CN 201810390089 A CN201810390089 A CN 201810390089A CN 108264327 A CN108264327 A CN 108264327A
- Authority
- CN
- China
- Prior art keywords
- parts
- concrete
- water proof
- seepage
- proof anti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of concrete of water proof anti-seepage, includes following component by weight percentage：20 30 parts of bentonite, 7 15 parts of redispersable latex powder, 20 25 parts of boron carbide, 20 30 parts of land plaster, 36 parts of magnesium hydroxide, 17 26 parts of petroleum sodium sulfonate, 28 parts of alum, 2.5~5.5 parts of sodium alkyl sulfonate, 15 25 parts of silicon powder, 17 23 parts of trbasic zinc phosphate, 12 15 parts of superfined flyash, 1.7 6.2 parts of polyimide resin, 11 18 parts of butyl acrylate.The concrete of the water proof anti-seepage of the present invention has preferable water resistance, which obviate in concrete construction, needing separately to set waterproof layer, significantly improve the efficiency of construction, and avoid the generation of leakage problems.
Description
Technical field
The present invention relates to a kind of concrete more particularly to a kind of concrete of water proof anti-seepage.
Background technology
Concrete is the construction material that the realm of building construction often needs to use.During practice of construction, need to solve
The waterproof problem of concrete.In this regard, needing while concrete construction, waterproof layer is set on concrete, to avoid leakage.
However, above-mentioned waterproof type not only increases the step of construction, while after long-time use, also asking there are waterproof layer cracking
Topic.Therefore, in view of the above-mentioned problems, it is necessary to propose further solution.
Invention content
The purpose of the present invention is to provide a kind of concrete of water proof anti-seepage, to overcome the deficiencies in the prior art.
For achieving the above object, the present invention provides a kind of concrete of water proof anti-seepage, includes by weight percentage
Following component：20-30 parts of bentonite, 7-15 parts of redispersable latex powder, 20-25 parts of boron carbide, 20-30 parts of land plaster, hydrogen-oxygen
Change 3-6 parts of magnesium, 17-26 parts of petroleum sodium sulfonate, 2-8 parts of alum, 2.5~5.5 parts of sodium alkyl sulfonate, 15-25 parts of silicon powder,
17-23 parts of trbasic zinc phosphate, 12-15 parts of superfined flyash, 1.7-6.2 parts of polyimide resin, 11-18 parts of butyl acrylate.
The improvement of the concrete of water proof anti-seepage as the present invention, the concrete of the water proof anti-seepage wrap by weight percentage
Include following component：25 parts of bentonite, 12 parts of redispersable latex powder, 21 parts of boron carbide, 22 parts of land plaster, 3 parts of magnesium hydroxide, stone
Oily 23 parts of sodium sulfonate, 5 parts of alum, 3.5 parts of sodium alkyl sulfonate, 18 parts of silicon powder, 18 parts of trbasic zinc phosphate, superfined flyash 14
Part, 5.3 parts of polyimide resin, 16 parts of butyl acrylate.
The improvement of the concrete of water proof anti-seepage as the present invention, the concrete of the water proof anti-seepage wrap by weight percentage
Include following component：28 parts of bentonite, 9 parts of redispersable latex powder, 23 parts of boron carbide, 28 parts of land plaster, 5 parts of magnesium hydroxide, stone
Oily 23 parts of sodium sulfonate, 6 parts of alum, 4.5 parts of sodium alkyl sulfonate, 19 parts of silicon powder, 22 parts of trbasic zinc phosphate, superfined flyash 13
Part, 5.2 parts of polyimide resin, 17 parts of butyl acrylate.
The improvement of the concrete of water proof anti-seepage as the present invention, the concrete of the water proof anti-seepage wrap by weight percentage
Include following component：21 parts of bentonite, 8 parts of redispersable latex powder, 24 parts of boron carbide, 22 parts of land plaster, 4.5 parts of magnesium hydroxide,
23 parts of petroleum sodium sulfonate, 7 parts of alum, 3.5 parts of sodium alkyl sulfonate, 23 parts of silicon powder, 21 parts of trbasic zinc phosphate, superfined flyash 14
Part, 5.4 parts of polyimide resin, 16 parts of butyl acrylate.
The improvement of the concrete of water proof anti-seepage as the present invention, the concrete of the water proof anti-seepage are given birth to as follows
Production：
S1, by 20-30 parts of bentonite, 7-15 parts of redispersable latex powder, 20-25 parts of boron carbide, 20-30 parts of land plaster,
3-6 parts of magnesium hydroxide, 17-26 parts of petroleum sodium sulfonate are mixed with water, obtain mixed serum；
S2, by 2-8 parts of alum, 2.5~5.5 parts of sodium alkyl sulfonate, 15-25 parts of silicon powder, 17-23 parts of trbasic zinc phosphate,
12-15 parts of superfined flyash, 1.7-6.2 parts of polyimide resin, 11-18 parts of butyl acrylate are uniformly mixed, and by it gradually
Ground is added in above-mentioned mixed serum.
The improvement of the concrete of water proof anti-seepage as the present invention, the concrete of the water proof anti-seepage further include surface-active
Agent, the surfactant are one or more of citric acid, oleic acid, stearic acid.
The improvement of the concrete of water proof anti-seepage as the present invention, the concrete of the water proof anti-seepage further include swelling agent,
The mixture that the swelling agent is gypsum, alunite and gangue are formed.
The improvement of the concrete of water proof anti-seepage as the present invention, the concrete for stating water proof anti-seepage further include modification
Agent, the modifying agent is 2.5-6.2 parts of triethanolamine, 3.5-6.5 parts of slag powders, 2.6-4.7 parts of acetic acid lignin, acetate fiber
The mixture of 5.5-7.5 parts of formation.
Compared with prior art, the beneficial effects of the invention are as follows：The concrete of the water proof anti-seepage of the present invention has preferable
Water resistance which obviate in concrete construction, needing separately to set waterproof layer, significantly improves the efficiency of construction,
And avoid the generation of leakage problems.
Specific embodiment
With reference to specific embodiment, the present invention is described in detail, but it should explanation, these embodiment party
Formula is not limitation of the present invention, and those of ordinary skill in the art are according to these embodiment institute work energy, method or knots
Equivalent transformation or replacement on structure, all belong to the scope of protection of the present invention within.
The present invention provides a kind of concrete of water proof anti-seepage, includes following component by weight percentage：Bentonite 20-30
Part, 7-15 parts of redispersable latex powder, 20-25 parts of boron carbide, 20-30 parts of land plaster, 3-6 parts of magnesium hydroxide, petroleum sodium sulfonate
17-26 parts, 2-8 parts of alum, 2.5~5.5 parts of sodium alkyl sulfonate, 15-25 parts of silicon powder, 17-23 parts of trbasic zinc phosphate, superfine powder
12-15 parts of coal ash, 1.7-6.2 parts of polyimide resin, 11-18 parts of butyl acrylate.
In addition, the concrete of the water proof anti-seepage of the present invention further includes surfactant.Preferably, the surfactant is
One or more of citric acid, oleic acid, stearic acid.The concrete of the water proof anti-seepage further includes swelling agent.Preferably, it is described
The mixture that swelling agent is gypsum, alunite and gangue are formed.The concrete for stating water proof anti-seepage further includes modifying agent.
Preferably, the modifying agent is 2.5-6.2 parts of triethanolamine, 3.5-6.5 parts of slag powders, 2.6-4.7 parts of acetic acid lignin, acetic acid
The mixture of 5.5-7.5 parts of formation of fiber.
The concrete of above-mentioned water proof anti-seepage is illustrated With reference to embodiment.
Embodiment 1
The concrete of the water proof anti-seepage includes following component by weight percentage：25 parts of bentonite, Redispersable latex
12 parts of powder, 21 parts of boron carbide, 22 parts of land plaster, 3 parts of magnesium hydroxide, 23 parts of petroleum sodium sulfonate, 5 parts of alum, alkyl sulfonic acid
3.5 parts of sodium, 18 parts of silicon powder, 18 parts of trbasic zinc phosphate, 14 parts of superfined flyash, 5.3 parts of polyimide resin, butyl acrylate 16
Part.
The concrete of the water proof anti-seepage produces as follows：By 25 parts of bentonite, 12 parts of redispersable latex powder,
21 parts of boron carbide, 22 parts of land plaster, 3 parts of magnesium hydroxide, 23 parts of petroleum sodium sulfonate are mixed with water, obtain mixed serum.By sulfuric acid
5 parts of aluminium potassium, 3.5 parts of sodium alkyl sulfonate, 18 parts of silicon powder, 18 parts of trbasic zinc phosphate, 14 parts of superfined flyash, polyimide resin 5.3
Part, 16 parts of butyl acrylate are uniformly mixed, and be gradually added in above-mentioned mixed serum.
Embodiment 2
The concrete of the water proof anti-seepage includes following component by weight percentage：28 parts of bentonite, Redispersable latex
9 parts of powder, 23 parts of boron carbide, 28 parts of land plaster, 5 parts of magnesium hydroxide, 23 parts of petroleum sodium sulfonate, 6 parts of alum, sodium alkyl sulfonate
4.5 parts, 19 parts of silicon powder, 22 parts of trbasic zinc phosphate, 13 parts of superfined flyash, 5.2 parts of polyimide resin, 17 parts of butyl acrylate.
The concrete of the water proof anti-seepage produces as follows：28 parts of bentonite, 9 parts of redispersable latex powder, carbon
Change 23 parts of boron, 28 parts of land plaster, 5 parts of magnesium hydroxide, 23 parts of petroleum sodium sulfonate to mix with water, obtain mixed serum.By aluminum sulfate
6 parts of potassium, 4.5 parts of sodium alkyl sulfonate, 19 parts of silicon powder, 22 parts of trbasic zinc phosphate, 13 parts of superfined flyash, 5.2 parts of polyimide resin,
17 parts of butyl acrylate is uniformly mixed, and be gradually added in above-mentioned mixed serum.
Embodiment 3
The concrete of the water proof anti-seepage includes following component by weight percentage：21 parts of bentonite, Redispersable latex
8 parts of powder, 24 parts of boron carbide, 22 parts of land plaster, 4.5 parts of magnesium hydroxide, 23 parts of petroleum sodium sulfonate, 7 parts of alum, alkyl sulfonic acid
3.5 parts of sodium, 23 parts of silicon powder, 21 parts of trbasic zinc phosphate, 14 parts of superfined flyash, 5.4 parts of polyimide resin, butyl acrylate 16
Part.
The concrete of the water proof anti-seepage produces as follows：21 parts of bentonite, 8 parts of redispersable latex powder, carbon
Change 24 parts of boron, 22 parts of land plaster, 4.5 parts of magnesium hydroxide, 23 parts of petroleum sodium sulfonate to mix with water, obtain mixed serum.By sulfuric acid
7 parts of aluminium potassium, 3.5 parts of sodium alkyl sulfonate, 23 parts of silicon powder, 21 parts of trbasic zinc phosphate, 14 parts of superfined flyash, polyimide resin 5.4
Part, 16 parts of butyl acrylate are uniformly mixed, and be gradually added in above-mentioned mixed serum.
In conclusion the concrete of the water proof anti-seepage of the present invention has preferable water resistance, which obviate in concrete
It in work progress, needs separately to set waterproof layer, significantly improves the efficiency of construction, and avoid the generation of leakage problems.
It is obvious to a person skilled in the art that the present invention is not limited to the details of above-mentioned exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Profit requirement rather than above description limit, it is intended that all by what is fallen within the meaning and scope of the equivalent requirements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in each embodiment can also be properly combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (8)
1. a kind of concrete of water proof anti-seepage, which is characterized in that the concrete of the water proof anti-seepage is included such as by weight percentage
Lower component：20-30 parts of bentonite, 7-15 parts of redispersable latex powder, 20-25 parts of boron carbide, 20-30 parts of land plaster, hydroxide
3-6 parts of magnesium, 17-26 parts of petroleum sodium sulfonate, 2-8 parts of alum, 2.5~5.5 parts of sodium alkyl sulfonate, 15-25 parts of silicon powder, phosphorus
Sour zinc 17-23 parts, 12-15 parts of superfined flyash, 1.7-6.2 parts of polyimide resin, 11-18 parts of butyl acrylate.
2. the concrete of water proof anti-seepage according to claim 1, which is characterized in that the concrete of the water proof anti-seepage is by weight
It measures percentage and includes following component：25 parts of bentonite, 12 parts of redispersable latex powder, 21 parts of boron carbide, 22 parts of land plaster, hydrogen-oxygen
Change 3 parts of magnesium, 23 parts of petroleum sodium sulfonate, 5 parts of alum, 3.5 parts of sodium alkyl sulfonate, 18 parts of silicon powder, 18 parts of trbasic zinc phosphate, ultra-fine
14 parts of flyash, 5.3 parts of polyimide resin, 16 parts of butyl acrylate.
3. the concrete of water proof anti-seepage according to claim 1, which is characterized in that the concrete of the water proof anti-seepage is by weight
It measures percentage and includes following component：28 parts of bentonite, 9 parts of redispersable latex powder, 23 parts of boron carbide, 28 parts of land plaster, hydrogen-oxygen
Change 5 parts of magnesium, 23 parts of petroleum sodium sulfonate, 6 parts of alum, 4.5 parts of sodium alkyl sulfonate, 19 parts of silicon powder, 22 parts of trbasic zinc phosphate, ultra-fine
13 parts of flyash, 5.2 parts of polyimide resin, 17 parts of butyl acrylate.
4. the concrete of water proof anti-seepage according to claim 1, which is characterized in that the concrete of the water proof anti-seepage is by weight
It measures percentage and includes following component：21 parts of bentonite, 8 parts of redispersable latex powder, 24 parts of boron carbide, 22 parts of land plaster, hydrogen-oxygen
Change 4.5 parts of magnesium, 23 parts of petroleum sodium sulfonate, 7 parts of alum, 3.5 parts of sodium alkyl sulfonate, 23 parts of silicon powder, 21 parts of trbasic zinc phosphate, surpass
14 parts of fine powdered coal, 5.4 parts of polyimide resin, 16 parts of butyl acrylate.
5. the concrete of water proof anti-seepage according to claim 1, which is characterized in that the concrete of the water proof anti-seepage according to
Following method production：
S1, by 20-30 parts of bentonite, 7-15 parts of redispersable latex powder, 20-25 parts of boron carbide, 20-30 parts of land plaster, hydrogen-oxygen
Change 3-6 parts of magnesium, 17-26 parts of petroleum sodium sulfonate is mixed with water, acquisition mixed serum；
S2, by 2-8 parts of alum, 2.5~5.5 parts of sodium alkyl sulfonate, 15-25 parts of silicon powder, 17-23 parts of trbasic zinc phosphate, ultra-fine
12-15 parts of flyash, 1.7-6.2 parts of polyimide resin, 11-18 parts of butyl acrylate are uniformly mixed, and it is added step by step
Enter into above-mentioned mixed serum.
6. the concrete of water proof anti-seepage according to claim 1, which is characterized in that the concrete of the water proof anti-seepage also wraps
Surfactant is included, the surfactant is one or more of citric acid, oleic acid, stearic acid.
7. the concrete of water proof anti-seepage according to claim 1, which is characterized in that the concrete of the water proof anti-seepage also wraps
Swelling agent is included, the mixture that the swelling agent is gypsum, alunite and gangue are formed.
8. the concrete of water proof anti-seepage according to claim 1, which is characterized in that the concrete for stating water proof anti-seepage is also
Including modifying agent, the modifying agent for 2.5-6.2 parts of triethanolamine, 3.5-6.5 parts of slag powders, 2.6-4.7 parts of acetic acid lignin,
The mixture of 5.5-7.5 parts of formation of acetate fiber.