CN108239431A - Heat preservation putty - Google Patents
Heat preservation putty Download PDFInfo
- Publication number
- CN108239431A CN108239431A CN201711466721.1A CN201711466721A CN108239431A CN 108239431 A CN108239431 A CN 108239431A CN 201711466721 A CN201711466721 A CN 201711466721A CN 108239431 A CN108239431 A CN 108239431A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat preservation
- powder
- polyethylene glycol
- bentonite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of heat preservation putties, are made by weight ratio of following components：30 50 parts of activating and regenerating concrete micro mist, 15 20 parts of aluminum sulfate, 79 parts of bentonite, 46 parts of talcum powder, 13 15 parts of powdered whiting, 20 40 parts of glass bead, 1.4 1.8 parts of latex powder, 15 parts of polyvinyl alcohol 0.1 0.3 part, watt gram rubber powder, 0.1 0.3 parts of starch ether, 8 ~ 12 parts of polyethylene glycol for energy storage, auspicious safe 0.2 1.2 parts of cellulose, 0.05 0.2 parts of superbhort fiber, 0.2 0.6 parts of wood fibre.The heat preservation putty adhesion strength is high, and with base and float coat strong adhesive force, anti-autoclasis effect is good, and Easy dosing is easy for construction.
Description
Technical field
The present invention relates to building material technical field, more particularly to a kind of heat preservation putty.
Background technology
Powder of lacquer putty for use on is one kind of building and ornament materials, for a kind of levelling base material of wall-surface patching, for decoration (brush in next step
Paint wallpaper) it lays a good foundation.Putty is divided into two kinds of interior wall and exterior wall, and exterior wall putty, which will be resisted, exposes to the weather so glue
Property is big, intensity is high, and environmentally friendly index is slightly lower, and inner wall putty composite index is preferable, health environment-friendly.
Traditional inner wall putty powder often using inorganic gel materials as base-material, be equipped with binding material and other auxiliary combinations and
Into can not only play the function of auxiliary heat-insulation and heat-preservation, also cracking can be generated due to the cold and hot of insulating layer, hollowing etc. shows
As, at the same the whiteness of existing inner wall putty powder and texture have it is to be strengthened.
Invention content
In view of the deficiencies of the prior art, the present invention intends to provide a kind of water-fast heat preservation putty.This is water-fast guarantor
Warm putty has excellent water resistance, can effectively reduce dusting and the generation of mildew phenomena.
A kind of heat preservation putty is made by weight ratio of following components：30-50 parts of activating and regenerating concrete micro mist, sulphur
Sour aluminium 15-20 parts, 7-9 parts of bentonite, 4-6 parts of talcum powder, 13-15 parts of powdered whiting, 20-40 parts of glass bead, latex powder
1.4-1.8 parts, 0.1-0.3 parts of polyvinyl alcohol, watt 1-5 parts of gram rubber powder, 0.1-0.3 parts of starch ether, polyethylene glycol phase-change accumulation energy material
8 ~ 12 parts of material, auspicious safe 0.2-1.2 parts of cellulose, 0.05-0.2 parts of superbhort fiber, 0.2-0.6 parts of wood fibre.
It is made by weight ratio of following components in one of the embodiments,：40 parts of activating and regenerating concrete micro mist,
18 parts of aluminum sulfate, 8 parts of bentonite, 5 parts of talcum powder, 14 parts of powdered whiting, 30 parts of glass bead, 1.6 parts of latex powder, polyethylene
It is 3 parts of alcohol 0.2 part, watt gram rubber powder, 0.2 part of starch ether, 10 parts of polyethylene glycol for energy storage, auspicious safe 0.7 part of cellulose, ultrashort
0.1 part of fiber, 0.4 part of wood fibre.
Above-mentioned heat preservation putty, using activating and regenerating concrete micro mist, thermal insulation material uses polyethylene glycol for energy storage,
Urban construction, alkaline environmental protection of enterprise pressure and building materials enterprise shortage of resources pressure can be alleviated, building energy-saving emission reduction is realized, mitigate
Enterprise's waste discharge burden, increases income and improves the ecological environment.The heat preservation putty adhesion strength is high, with base and float coat adhesive force
By force, anti-autoclasis effect is good, and Easy dosing is easy for construction.
Specific embodiment
In order to make the foregoing objectives, features and advantages of the present invention clearer and more comprehensible, below to the specific reality of the present invention
The mode of applying is described in detail.Many details are elaborated in the following description in order to fully understand the present invention.But
The invention can be embodied in many other ways as described herein, and those skilled in the art can be without prejudice to this hair
Similar improvement is done in the case of bright intension, therefore the present invention is not limited by following public specific embodiment.
A kind of heat preservation putty is made by weight ratio of following components：30-50 parts of activating and regenerating concrete micro mist, sulphur
Sour aluminium 15-20 parts, 7-9 parts of bentonite, 4-6 parts of talcum powder, 13-15 parts of powdered whiting, 20-40 parts of glass bead, latex powder
1.4-1.8 parts, 0.1-0.3 parts of polyvinyl alcohol, watt 1-5 parts of gram rubber powder, 0.1-0.3 parts of starch ether, polyethylene glycol phase-change accumulation energy material
8 ~ 12 parts of material, auspicious safe 0.2-1.2 parts of cellulose, 0.05-0.2 parts of superbhort fiber, 0.2-0.6 parts of wood fibre.
Above-mentioned heat preservation putty, using activating and regenerating concrete micro mist, thermal insulation material uses polyethylene glycol for energy storage,
Urban construction, alkaline environmental protection of enterprise pressure and building materials enterprise shortage of resources pressure can be alleviated, building energy-saving emission reduction is realized, mitigate
Enterprise's waste discharge burden, increases income and improves the ecological environment.The heat preservation putty adhesion strength is high, with base and float coat adhesive force
By force, anti-autoclasis effect is good, and Easy dosing is easy for construction.
Heat preservation putty is made by weight ratio of following components in one of the embodiments,：Activating and regenerating concrete
50 parts of micro mist, 20 parts of aluminum sulfate, 9 parts of bentonite, 6 parts of talcum powder, 15 parts of powdered whiting, 40 parts of glass bead, latex powder 1.8
Part, 5 parts of polyvinyl alcohol 0.3 part, watt gram rubber powder, 0.3 part of starch ether, 12 parts of polyethylene glycol for energy storage, auspicious safe cellulose
1.2 parts, 0.2 part of superbhort fiber, 0.6 part of wood fibre.
Heat preservation putty is made by weight ratio of following components in one of the embodiments,：Activating and regenerating concrete
30 parts of micro mist, 15 parts of aluminum sulfate, 7 parts of bentonite, 4 parts of talcum powder, 13 parts of powdered whiting, 20 parts of glass bead, latex powder 1.4
Part, 1 part of polyvinyl alcohol 0.1 part, watt gram rubber powder, 0.1 part of starch ether, 8 parts of polyethylene glycol for energy storage, auspicious safe cellulose
0.2 part, 0.05 part of superbhort fiber, 0.2 part of wood fibre.
It is made by weight ratio of following components in one of the embodiments,：40 parts of activating and regenerating concrete micro mist,
18 parts of aluminum sulfate, 8 parts of bentonite, 5 parts of talcum powder, 14 parts of powdered whiting, 30 parts of glass bead, 1.6 parts of latex powder, polyethylene
It is 3 parts of alcohol 0.2 part, watt gram rubber powder, 0.2 part of starch ether, 10 parts of polyethylene glycol for energy storage, auspicious safe 0.7 part of cellulose, ultrashort
0.1 part of fiber, 0.4 part of wood fibre.
Each technical characteristic of embodiment described above can be combined arbitrarily, to make description succinct, not to above-mentioned reality
It applies all possible combination of each technical characteristic in example to be all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, it is all considered to be the range of this specification record.
Embodiment described above only expresses the several embodiments of the present invention, and description is more specific and detailed, but simultaneously
It cannot therefore be construed as limiting the scope of the patent.It should be pointed out that those of ordinary skill in the art are come
It says, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the protection of the present invention
Range.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (2)
1. a kind of heat preservation putty, which is characterized in that be made by weight ratio of following components：Activating and regenerating concrete micro mist
30-50 parts, 15-20 parts of aluminum sulfate, 7-9 parts of bentonite, 4-6 parts of talcum powder, 13-15 parts of powdered whiting, glass bead 20-40
Part, 1.4-1.8 parts of latex powder, 0.1-0.3 parts of polyvinyl alcohol, watt 1-5 parts of gram rubber powder, 0.1-0.3 parts of starch ether, polyethylene glycol phase
8 ~ 12 parts of change energy-storage material, auspicious safe 0.2-1.2 parts of cellulose, 0.05-0.2 parts of superbhort fiber, 0.2-0.6 parts of wood fibre.
2. heat preservation putty according to claim 1, which is characterized in that be made by weight ratio of following components：Activation
40 parts of regeneration concrete micro mist, 18 parts of aluminum sulfate, 8 parts of bentonite, 5 parts of talcum powder, 14 parts of powdered whiting, glass bead 30
Part, 1.6 parts of latex powder, 3 parts of polyvinyl alcohol 0.2 part, watt gram rubber powder, 0.2 part of starch ether, polyethylene glycol for energy storage 10
Part, auspicious safe 0.7 part of cellulose, 0.1 part of superbhort fiber, 0.4 part of wood fibre.