CN108237116A - Cleaning before PC material film platings - Google Patents
Cleaning before PC material film platings Download PDFInfo
- Publication number
- CN108237116A CN108237116A CN201810064139.0A CN201810064139A CN108237116A CN 108237116 A CN108237116 A CN 108237116A CN 201810064139 A CN201810064139 A CN 201810064139A CN 108237116 A CN108237116 A CN 108237116A
- Authority
- CN
- China
- Prior art keywords
- materials
- prerinse
- prerinse liquid
- time
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the cleanings before a kind of PC material film platings, specifically include following operating procedure：S1：Prerinse liquid is modulated, and PC materials are immersed in prerinse liquid, until prerinse liquid temperature keeps stablizing；S2：Prerinse；S3：It rinses for the first time；S4：Second of flushing；S5：Third time is rinsed；S6：It is dry.The present invention impregnates PC materials by prerinse liquid, be conducive to the decomposition of the impurity on PC materials to loosen, under the action of supersonic wave cleaning machine, adequately PC material surfaces can be cleaned, it is good to be with one's heart at effect, by rinsing three times, remaining cleaning agent, tap water on PC materials can be taken out, finally by methanol absorption moisture, and remaining methanol on PC materials is eliminated in the volatilization for passing through methanol, prevents moisture from forming water mark in the remained on surface of PC materials.
Description
Technical field
The invention belongs to cleaning technical fields, and in particular to the cleaning before a kind of PC material film platings.
Background technology
Makrolon (abbreviation PC) is the high molecular polymer containing carbonate group in strand, can according to the structure of ester group
It is divided into the multiple types such as aliphatic, aromatic series, aliphatic-aromatic.Three big application fields of PC engineering plastics are glass assemblings
Industry, auto industry and electronics, electrical equipment industry, secondly also have the office equipments such as industrial machinery part, CD, packaging, computer,
Medical treatment and health care, film, leisure and protective equipment etc..PC can be used as door glass, PC laminates be widely used in bank, embassy,
The house of detention and the protective window of public place, for aircraft hatch cover, lighting apparatus, industry security plate washer and bulletproof glass.
Before plated film is carried out to PC materials, it usually needs PC materials are cleaned.Existing cleaning is simple, difficult
Thoroughly to remove oil stain, fat and the dust on PC materials, so as to influence coating effects, in addition, easily in PC materials after cleaning
Residual moisture on the surface of material and cause water mark, influence product quality.
Invention content
The purpose of the present invention is to provide the cleaning before a kind of PC material film platings, to solve to carry in above-mentioned background technology
The problem of going out.
To achieve the above object, the present invention provides following technical solution：A kind of cleaning before PC material film platings, specifically
Including following operating procedure：
S1：Prerinse liquid is modulated, and component weighs following substance by weight：
5-8 parts of sodium chloride,
1-2 parts of barium stearate,
4-7 parts of emulsifier,
20-30 parts of water, is sufficiently stirred in a reservoir, is uniformly mixed in backward system and adds in 3-5 parts of sodium hydroxide, is again stirring for mixing
Uniform prerinse liquid is closed, container is placed in water bath with thermostatic control and is heated, and PC materials are immersed in prerinse liquid, until
Prerinse liquid temperature keeps stablizing；
S2：Prerinse liquid and PC materials are transferred in supersonic wave cleaning machine by prerinse, and opening supersonic wave cleaning machine starts pre- clear
It washes, the prerinse time is set as 20-30 minutes, removes oil stain, fat and dust on PC materials；
S3：It rinses, takes out PC materials from supersonic wave cleaning machine after ultrasonic cleaning, by tap water repeatedly for the first time
It rinses, the prerinse liquid of removal PC material surfaces remnants；
S4：Second of flushing, then PC materials are rinsed by ultra-pure water, washing time is 6-8 seconds, removes PC material surfaces
Remaining tap water；
S5：Third time is rinsed, then PC materials are rinsed by methanol, and washing time is 4-6 seconds, to PC material surfaces remnants
Ultra-pure water adsorbed, take out the moisture of PC material surfaces remnants；
S6：It is dry, by the PC storerooms for completing to rinse three times every expansion, it is placed in vacuum drying oven and is dried, by PC materials
Methanol volatilization on surface, natural cooling is taken out after completing drying.
Preferably, the temperature of water bath with thermostatic control is 55-65 DEG C in step S1.
Preferably, it needs immediately to clean supersonic wave cleaning machine by clean water after step S2.
Preferably, pressure is 10-30Pa in vacuum drying oven in step S6, and temperature is 35-45 DEG C, drying time 3-6 hour.
The technique effect and advantage of the present invention：
The present invention impregnates PC materials by prerinse liquid, is conducive to the decomposition of the impurity on PC materials and loosens, in ultrasonic wave
Under the action of cleaning machine, adequately PC material surfaces can be cleaned, it is good to be with one's heart at effect, by rinsing three times, Ke Yiqu
Go out remaining cleaning agent, tap water on PC materials, finally by methanol absorption moisture, and PC materials are eliminated in the volatilization for passing through methanol
Upper remaining methanol prevents moisture from forming water mark in the remained on surface of PC materials.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical solution in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, those of ordinary skill in the art's all other embodiments obtained without making creative work, all
Belong to the scope of protection of the invention.
Embodiment 1
A kind of cleaning before PC material film platings, specifically includes following operating procedure：
S1：Prerinse liquid is modulated, and component weighs following substance by weight：
5 parts of sodium chloride,
1 part of barium stearate,
4 parts of emulsifier,
20 parts of water, is sufficiently stirred in a reservoir, is uniformly mixed in backward system and adds in 3 parts of sodium hydroxide, and it is equal to be again stirring for mixing
It is even to obtain prerinse liquid, container is placed in water bath with thermostatic control and is heated, the temperature of water bath with thermostatic control is 55 DEG C, and PC materials are submerged
In prerinse liquid, until prerinse liquid temperature keeps stablizing, in the heating process of prerinse liquid, PC materials can be carried out
It impregnates, is conducive to the oil stain on PC materials, fat and dust and is loosened from PC material surfaces；
S2：Prerinse liquid and PC materials are transferred in supersonic wave cleaning machine by prerinse, and opening supersonic wave cleaning machine starts pre- clear
It washes, the prerinse time is set as 20 minutes, removes oil stain, fat and dust on PC materials, needs to pass through after ultrasonic wave
Clean water immediately cleans supersonic wave cleaning machine, prevents prerinse liquid from causing to corrode to supersonic wave cleaning machine；
S3：It rinses, takes out PC materials from supersonic wave cleaning machine after ultrasonic cleaning, by tap water repeatedly for the first time
It rinses, the prerinse liquid of removal PC material surfaces remnants；
S4：Second of flushing, then PC materials are rinsed by ultra-pure water, washing time is 6 seconds, and removal PC material surfaces are residual
Remaining tap water；
S5：Third time is rinsed, then PC materials are rinsed by methanol, and washing time is 4 seconds, remaining to PC material surfaces
Ultra-pure water is adsorbed, and takes out the moisture of PC material surfaces remnants；
S6：It is dry, the PC storerooms rinsed three times will be completed every expansion, be placed in vacuum drying oven and be dried, vacuum is set
Pressure is 10Pa in baking oven, and temperature is 35 DEG C, and 3 hours drying times volatilized the methanol on PC material surfaces, after completing drying
Take out natural cooling.
Embodiment 2
A kind of cleaning before PC material film platings, specifically includes following operating procedure：
S1：Prerinse liquid is modulated, and component weighs following substance by weight：
7 parts of sodium chloride,
1.5 parts of barium stearate,
6 parts of emulsifier,
25 parts of water, is sufficiently stirred in a reservoir, is uniformly mixed in backward system and adds in 4 parts of sodium hydroxide, and it is equal to be again stirring for mixing
It is even to obtain prerinse liquid, container is placed in water bath with thermostatic control and is heated, the temperature of water bath with thermostatic control is 60 DEG C, and PC materials are submerged
In prerinse liquid, until prerinse liquid temperature keeps stablizing, in the heating process of prerinse liquid, PC materials can be carried out
It impregnates, is conducive to the oil stain on PC materials, fat and dust and is loosened from PC material surfaces；
S2：Prerinse liquid and PC materials are transferred in supersonic wave cleaning machine by prerinse, and opening supersonic wave cleaning machine starts pre- clear
It washes, the prerinse time is set as 25 minutes, removes oil stain, fat and dust on PC materials, needs to pass through after ultrasonic wave
Clean water immediately cleans supersonic wave cleaning machine, prevents prerinse liquid from causing to corrode to supersonic wave cleaning machine；
S3：It rinses, takes out PC materials from supersonic wave cleaning machine after ultrasonic cleaning, by tap water repeatedly for the first time
It rinses, the prerinse liquid of removal PC material surfaces remnants；
S4：Second of flushing, then PC materials are rinsed by ultra-pure water, washing time is 7 seconds, and removal PC material surfaces are residual
Remaining tap water；
S5：Third time is rinsed, then PC materials are rinsed by methanol, and washing time is 5 seconds, remaining to PC material surfaces
Ultra-pure water is adsorbed, and takes out the moisture of PC material surfaces remnants；
S6：It is dry, the PC storerooms rinsed three times will be completed every expansion, be placed in vacuum drying oven and be dried, vacuum is set
Pressure is 20Pa in baking oven, and temperature is 40 DEG C, and 4.5 hours drying times volatilized the methanol on PC material surfaces, completed drying
After take out natural cooling.
Embodiment 3
A kind of cleaning before PC material film platings, specifically includes following operating procedure：
S1：Prerinse liquid is modulated, and component weighs following substance by weight：
8 parts of sodium chloride,
2 parts of barium stearate,
7 parts of emulsifier,
30 parts of water, is sufficiently stirred in a reservoir, is uniformly mixed in backward system and adds in 5 parts of sodium hydroxide, and it is equal to be again stirring for mixing
It is even to obtain prerinse liquid, container is placed in water bath with thermostatic control and is heated, the temperature of water bath with thermostatic control is 65 DEG C, and PC materials are submerged
In prerinse liquid, until prerinse liquid temperature keeps stablizing, in the heating process of prerinse liquid, PC materials can be carried out
It impregnates, is conducive to the oil stain on PC materials, fat and dust and is loosened from PC material surfaces；
S2：Prerinse liquid and PC materials are transferred in supersonic wave cleaning machine by prerinse, and opening supersonic wave cleaning machine starts pre- clear
It washes, the prerinse time is set as 30 minutes, removes oil stain, fat and dust on PC materials, needs to pass through after ultrasonic wave
Clean water immediately cleans supersonic wave cleaning machine, prevents prerinse liquid from causing to corrode to supersonic wave cleaning machine；
S3：It rinses, takes out PC materials from supersonic wave cleaning machine after ultrasonic cleaning, by tap water repeatedly for the first time
It rinses, the prerinse liquid of removal PC material surfaces remnants；
S4：Second of flushing, then PC materials are rinsed by ultra-pure water, washing time is 8 seconds, and removal PC material surfaces are residual
Remaining tap water；
S5：Third time is rinsed, then PC materials are rinsed by methanol, and washing time is 6 seconds, remaining to PC material surfaces
Ultra-pure water is adsorbed, and takes out the moisture of PC material surfaces remnants；
S6：It is dry, the PC storerooms rinsed three times will be completed every expansion, be placed in vacuum drying oven and be dried, vacuum is set
Pressure is 30Pa in baking oven, and temperature is 45 DEG C, and 6 hours drying times volatilized the methanol on PC material surfaces, after completing drying
Take out natural cooling.
The present invention impregnates PC materials by prerinse liquid, is conducive to the decomposition of the impurity on PC materials and loosens, super
Under the action of sound wave cleaning machine, adequately PC material surfaces can be cleaned, it is good to be with one's heart at effect, can by rinsing three times
To take out remaining cleaning agent, tap water on PC materials, finally by methanol absorption moisture, and PC is eliminated in the volatilization for passing through methanol
Remaining methanol on material prevents moisture from forming water mark in the remained on surface of PC materials.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify to the technical solution recorded in foregoing embodiments or carry out equivalent replacement to which part technical characteristic,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in the present invention's
Within protection domain.
Claims (4)
1. the cleaning before a kind of PC material film platings, which is characterized in that specifically include following operating procedure：
S1：Prerinse liquid is modulated, and component weighs following substance by weight：
5-8 parts of sodium chloride,
1-2 parts of barium stearate,
4-7 parts of emulsifier,
20-30 parts of water, is sufficiently stirred in a reservoir, is uniformly mixed in backward system and adds in 3-5 parts of sodium hydroxide, is again stirring for mixing
Uniform prerinse liquid is closed, container is placed in water bath with thermostatic control and is heated, and PC materials are immersed in prerinse liquid, until
Prerinse liquid temperature keeps stablizing；
S2：Prerinse liquid and PC materials are transferred in supersonic wave cleaning machine by prerinse, and opening supersonic wave cleaning machine starts pre- clear
It washes, the prerinse time is set as 20-30 minutes, removes oil stain, fat and dust on PC materials；
S3：It rinses, takes out PC materials from supersonic wave cleaning machine after ultrasonic cleaning, by tap water repeatedly for the first time
It rinses, the prerinse liquid of removal PC material surfaces remnants；
S4：Second of flushing, then PC materials are rinsed by ultra-pure water, washing time is 6-8 seconds, removes PC material surfaces
Remaining tap water；
S5：Third time is rinsed, then PC materials are rinsed by methanol, and washing time is 4-6 seconds, to PC material surfaces remnants
Ultra-pure water adsorbed, take out the moisture of PC material surfaces remnants；
S6：It is dry, by the PC storerooms for completing to rinse three times every expansion, it is placed in vacuum drying oven and is dried, by PC materials
Methanol volatilization on surface, natural cooling is taken out after completing drying.
2. the cleaning before a kind of PC material film platings according to claim 1, it is characterised in that：Thermostatted water in step S1
The temperature of bath is 55-65 DEG C.
3. the cleaning before a kind of PC material film platings according to claim 1, it is characterised in that：It is needed after step S2
Supersonic wave cleaning machine is cleaned immediately by clean water.
4. the cleaning before a kind of PC material film platings according to claim 1, it is characterised in that：Vacuum is dried in step S6
Pressure is 10-30Pa in case, and temperature is 35-45 DEG C, drying time 3-6 hour.