CN108218231A - A kind of health Magnetized porcelain - Google Patents
A kind of health Magnetized porcelain Download PDFInfo
- Publication number
- CN108218231A CN108218231A CN201810113187.4A CN201810113187A CN108218231A CN 108218231 A CN108218231 A CN 108218231A CN 201810113187 A CN201810113187 A CN 201810113187A CN 108218231 A CN108218231 A CN 108218231A
- Authority
- CN
- China
- Prior art keywords
- health
- glaze
- porcelain
- magnetization
- magnetized
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to ceramic glaze technical fields, are specifically related to a kind of health Magnetized porcelain.The breeding magnetisation glaze, is prepared by the raw material of following parts by weight：Feldspar 5 30%, quartz 3 10%, iron oxide 30 80%, CMC1 3%, bone ash 5 10%, colour former 1 3%.Above-mentioned health magnetization glaze belongs to high ferro glaze, needs to pay close attention to when firing, therefore the present invention also provides the method for cooking that health magnetization glaze is used to burn out health Magnetized porcelain.Above-mentioned health magnetization glaze is applicable to any ceramic body, is formed using the surface of ceramics that this kind of method is burnt out and contains high Fe3O4Glaze layer, make ceramic product with magnetizability, with good anti-corrosion effects and electric conductivity.
Description
Technical field
The present invention relates to ceramic glaze technical fields, are specifically related to a kind of health Magnetized porcelain.
Background technology
Magnetic material is a kind of critical function material, is had a wide range of applications in every field.In addition to other than industrial circle,
In the daily life of the mankind, it is seen everywhere the trace of magnetic material.Such as：Magnetic mattress, magnetic shoe pad, cup for magnetizing water, magnetic therapy article,
Magnetic hanging part etc. is brought convenience for people's daily life.At present can health Magnetized porcelain preparation method mainly
Magnetic product, such as magnetic stripe, magnetic patch and magnetic sheet are added, and then realize it using the methods of inlaying, pasting on the ceramics prepared
Magnetic function.This most important problem of preparation method is to need to be processed ceramics, such as burrow, paddle-tumble, due to ceramics
Brittleness, the yield rate of this processing method is very low.It is not carried out additionally, due to magnetisable material and ceramic body permanent firm
Connection, therefore phenomena such as is susceptible to loosening, shifts and come off, its use is made to be limited by system, also affects ceramic
It is beautiful.
To solve the above problems, the application for a patent for invention that application publication number is CN 102153333A discloses one kind and can support
The preparation method of raw Magnetized porcelain, it is that magnetisable substance is mixed in nonmagnetic ceramic powder, using ceramic preparation process, is prepared
Magnetizable ceramic.It is big using this kind of method firing required magnetisable amount of material of magnetizable ceramic, cause
Production cost is high, and the magnetized ceramic single effect in addition fired using kind of method, use scope is restricted.
Invention content
To overcome deficiency of the prior art, the present invention provides a kind of health Magnetized porcelain.
To achieve the above object, the technical solution adopted by the present invention is as follows：Health magnetize glaze, which is characterized in that by with
The raw material of lower parts by weight is prepared：Feldspar 5-30%, quartz 3-10%, iron oxide 30-80%, CMC1-3%, bone ash 5-
10%th, colour former 1-3%.
Optimization, health magnetization glaze is prepared by the raw material of following parts by weight：Feldspar 26%, quartz 7%, oxidation
Iron 55%, CMC2%, bone ash 8%, colour former 2%.
Optimization, health magnetization glaze is prepared by the raw material of following parts by weight：Feldspar 10%, quartz 3%, oxidation
Iron 80%, CMC1%, bone ash 5%, colour former 1%.
Optimization, health magnetization glaze is prepared by the raw material of following parts by weight：Feldspar 12%, quartz 10%, oxidation
Iron 67%, CMC3%, bone ash 6%, colour former 2%.
The method for cooking of health Magnetized porcelain, which is characterized in that use above-mentioned arbitrary health magnetization glaze, specific steps
It is as follows：
Step 1, health magnetization glaze is applied on ceramic body；
Step 2, ceramic blank is put in kiln；
Step 3, kiln is warming up to 450-500 DEG C by room temperature；
Step 4, kiln continues to heat up, and 850 DEG C are at the uniform velocity warming up to by 500 DEG C；
Step 5, when kiln temperature rises to 900 DEG C -1000 DEG C, kiln is switched into reducing flame from oxidizing flame；
Step 6, when kiln is continuously heating to 1200 DEG C, the water of 1-10ml is injected into kiln；
Step 7, when kiln is continuously heating to 1250-1300 DEG C, fire is closed immediately, is quickly cooled down.
Further, kiln is warming up to 450-500 DEG C by room temperature and passes through 2.5-3 hours.
Further, step 4 kiln is warming up to 850 DEG C by 500 DEG C and passes through 3-4 hours.
By the above-mentioned description of this invention it is found that health provided by the invention magnetization glaze is applicable to any ceramic body
And the method for health Magnetized porcelain is burnt out using health magnetization glaze, the surface of ceramics burnt out, which is formed, contains high Fe3O4
Glaze layer, make ceramic product with magnetizability, with good anti-corrosion effects and electric conductivity.
Specific embodiment
Below by way of specific embodiment, the invention will be further described.
Health magnetizes glaze, which is characterized in that is prepared by the raw material of following parts by weight：Feldspar 5-30%, quartz 3-
10%th, iron oxide 30-80%, CMC1-3%, bone ash 5-10%, colour former 1-3%.
Specific embodiment one：
Health magnetizes glaze, is prepared by the raw material of following parts by weight：Feldspar 26%, quartz 7%, iron oxide 55%,
CMC2%, bone ash 8%, colour former 2%.
Specific embodiment two：
Health magnetizes glaze, is prepared by the raw material of following parts by weight：Feldspar 10%, quartz 3%, iron oxide 80%,
CMC1%, bone ash 5%, colour former 1%.
Specific embodiment three：
Health magnetizes glaze, is prepared by the raw material of following parts by weight：Feldspar 12%, quartz 10%, iron oxide 67%,
CMC3%, bone ash 6%, colour former 2%.
Above-mentioned health magnetization glaze is applicable to the health magnetization glaze of any ceramic body and can burn out health magnetization
The method for cooking of porcelain, the surface of ceramics burnt out, which is formed, contains high Fe3O4Glaze layer, make ceramic product have magnetizability,
With good anti-corrosion effects and electric conductivity.
Several specific embodiments of the present invention are above are only, but the design concept of the present invention is not limited thereto, all profits
The change of unsubstantiality is carried out to the present invention with this design, the behavior for invading the scope of the present invention should all be belonged to.
Claims (4)
1. a kind of health Magnetized porcelain, which is characterized in that the health Magnetized porcelain is fired using health magnetization glaze, the health magnetic
The surface formation for changing porcelain contains Fe3O4Glaze layer, health magnetization glaze is prepared by the raw material of following parts by weight：
2. health Magnetized porcelain according to claim 1, which is characterized in that the health magnetizes glaze by following parts by weight
Raw material is prepared：Feldspar 26%, quartz 7%, iron oxide 55%, CMC2%, bone ash 8%, colour former 2%.
3. health Magnetized porcelain according to claim 1, which is characterized in that the health magnetizes glaze by following parts by weight
Raw material is prepared：Feldspar 10%, quartz 3%, iron oxide 80%, CMC1%, bone ash 5%, colour former 1%.
4. health Magnetized porcelain according to claim 1, which is characterized in that the health magnetizes glaze by following parts by weight
Raw material is prepared：Feldspar 12%, quartz 10%, iron oxide 67%, CMC3%, bone ash 6%, colour former 2%.