A kind of fibre reinforced alloy composite material and preparation method thereof
Technical field
The invention belongs to metal material field more particularly to a kind of fibre reinforced alloy composite material and its preparation sides
Method.
Background technology
Renewable, free of contamination biomass fuel is one of developing direction of following green regenerative energy sources, is had wide
Development prospect.Compared with coal fired power generation, generating power with biomass combustion will to the corrosion resistance of the equipment such as station boiler superheater tube
It asks higher, that is, requires resistance to potassium, chlorine, salt and the ability of alkaline matter high temperature corrosion.Country's boiler superheater tubing at present
Common alloy material is TP91,304 stainless steels etc., and there are high outlet header, superheater outlet safety valve again in the application scenario of T91
Pipeline section exceeds pipe, shielded pipe, Gao Zaiguan and exceeds delivery channel;The application scenario of 15CrMo has rear water wall hanging manage, is low
Cross diode group, low triode group, steam pipe, the low group of diode again and low triode group again excessively;The application of SUS316
Occasion, which has, to be exceeded pipe, shielded pipe, Gao Zaiguan, exceeds delivery channel.
TP91 ingredients are 0.1C-9Cr-1Mo, and institutional framework is tempered martensite, have good comprehensive mechanical property
Energy and mechanical behavior under high temperature.C, the compound of Cr and Mo elements composition has good high-temperature stability, ensure that long-time service
Under the conditions of stable mechanical property.The Cr elements of 18% content of 304 stainless steels improve its anti-corrosion current potential, and comparison TP91 has
Good corrosion resisting property.Two kinds of alloys of TP91 and 304 stainless steels all have good processability and welding performance.
The alloys such as TP91 are suitable for common thermoelectricity use condition, have good operational characteristic and service life.For straw
The biomass fermentations electric conditions such as stalk burning, due to containing K in combustion atmosphere+、Na+、Cl-Plasma and its esters, thermoelectricity boiler mistake
Hot device tubing fouling and is corroded and aoxidizes quickly, and service life is shorter.In high temperature and contain K+、Na+、Cl-Plasma and water
Under the conditions of gas etc., the protective effect of the oxide, carbide of above-mentioned alloy surface is limited.
The material that external boiler superheater tubing uses is other than above-mentioned alloy, and also HR3C of high alloy content etc. is heat-resisting
Steel.The ingredient of HR3C is 25Cr-20Ni-Nb-N, since with high Cr, high Ni contents, anti-corrosion and oxidation resistent susceptibility is excellent, uses
Also there is good performance in terms of biomass power plant tubing.This alloy is the alloy of austenitic structure, due to containing
A large amount of Ni elements, price is higher, and tubular object extruding acquires a certain degree of difficulty, and additionally, due to N element is contained in material, tubing welds
Weld seam is susceptible to the defects of stomata.
For HR3C alloys, austenite is organized as, because of the presence of high-content Cr and high-content Ni, conventional high temperature is resistance to
Corrosion energy, high-temperature oxidation resistance and the resistance to K of high temperature+、Na+、Cl-Plasma etching performance is all very high.Alkali in China's fire coal ashes
Metal sulfide content is higher.For the ashes of stalk biomass burning, since stalk absorbs largely in growth course
Minerals, salt etc., containing a large amount of alkali metal chloride in ashes, containing chlorine, hydrogen chloride gas etc. in combustion atmosphere,
It is contacted with superheater tubes and corrosiveness occurs, captured the oxygen in oxide film, corrosion product is iron-containing low melting point
Chloride, iron-containing low melting point sulfide, make corrosion continue to occur.
Invention content
The present invention provides a kind of fibre reinforced alloy composite material and preparation method thereof, for solving current boiler mistake
The problem of high temperature corrosion-resisting performance and oxidative resistance of hot device pipe material can meet China's biomass power plant tubing.
Specific technical solution is as follows:
A kind of fibre reinforced alloy composite material, the fibre reinforced alloy composite material using alloy as matrix, with
Carbon fiber is prepared for reinforcement;
The alloy includes:By percentage to the quality, Cr:20%~22%, Al:0.5%~2%, Ni:2%~8%,
C:0.02%~0.08%, Ti:0.2%~0.8% and Nb:0.2%~0.8%;Remaining is iron.
Preferably, the alloy further includes:By percentage to the quality, Mo:0.1%~0.3%, Si3N4:0.1%~
0.5%th, Co:0.01%~0.05%, Cu:0.01%~0.05% and Si:0.005%~0.02%.
Preferably, the alloy further includes:Rare earth element.
Preferably, the rare earth element is the one or more of Nd, La, Pr, Y and V.
Preferably, the rare earth element is Nd, La, Pr, Y and V.
Preferably, the rare earth element includes:By percentage to the quality, Nd:0.02%~0.08%, La:0.0005%
~0.002%, Pr:0.002%~0.008%, Y:0.02%~0.08% and V:0.02%~0.08%.
The present invention also provides a kind of preparation method of fibre reinforced alloy composite material described in above-mentioned technical proposal, packets
It includes:
A) by the alloy vacuum melting, melt is obtained;
B) carbon fiber is added in into the melt, obtains the fibre reinforced alloy composite material.
Preferably, the temperature of the step a) vacuum meltings is 1100~1600 DEG C;
The vacuum degree of the step a) vacuum meltings is 40~60Pa.
Preferably, by percentage to the quality, the quality of the carbon fiber is the fibre reinforced alloy composite material
0.02%~0.08%.
The present invention also provides described in fibre reinforced alloy composite material described in above-mentioned technical proposal or above-mentioned technical proposal
Fibre reinforced alloy composite material prepared by preparation method is in the application for preparing high temperature corrosion-resisting and resistance to oxidation tubing.
In conclusion the present invention provides a kind of fibre reinforced alloy composite material, the fibre reinforced alloy is answered
Condensation material is prepared using alloy as matrix by reinforcement of carbon fiber;The alloy includes:By percentage to the quality, Cr:
20%~22%, Al:0.5%~2%, Ni:2%~8%, C:0.02%~0.08%, Ti:0.2%~0.8% and Nb:
0.2%~0.8%;Remaining is iron.High temperature corrosion dynamic test and high-temperature oxydation dynamic test show carbon fiber of the present invention
The enhancing alloy composite materials variable quantity that increases weight in corrosion test is concentrated mainly on 1.3~2.9mg/cm2In the range of, the present invention
Fibre reinforced alloy composite material has the high temperature resistant potassium chloride corrosive nature for being substantially better than the commercial metals material such as TP316.
Compared with the austenitic alloys such as 304, HR3C, fibre reinforced alloy composite material of the present invention has better heat conductivility, more
Low coefficient of thermal expansion and excellent intensity, toughness properties.In organizational aspects, fibre reinforced alloy composite wood of the present invention
Expect that crystal grain is relatively fine, be single ferritic structure, there is good processing performance, Nb, Ti close fibre reinforced of the present invention
The structure refinement and corrosion resisting property of metal/composite material, which improve, has good influence.
Description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, to embodiment or will show below
There is attached drawing needed in technology description to be briefly described.
Fig. 1 is the metallurgical microscopic of fibre reinforced alloy composite material prepared by the embodiment of the present invention 1;
Fig. 2 is the high-temperature oxydation dynamic curve diagram of fibre reinforced alloy composite material prepared by the embodiment of the present invention 1;
Fig. 3 is the high temperature corrosion dynamic curve diagram of fibre reinforced alloy composite material prepared by the embodiment of the present invention 1;
Fig. 4 is after fibre reinforced alloy composite material prepared by the embodiment of the present invention 1 carries out 700 DEG C of high temperature corrosion experiments
SEM characterization pictures (scale be 200 μm);
Fig. 5 is after fibre reinforced alloy composite material prepared by the embodiment of the present invention 1 carries out 700 DEG C of high temperature corrosion experiments
SEM characterization pictures (scale be 20 μm);
Fig. 6 is after fibre reinforced alloy composite material prepared by the embodiment of the present invention 1 carries out 700 DEG C of high temperature corrosion experiments
SEM characterization pictures (scale be 10 μm);
Fig. 7 is the high temperature corrosion dynamics block diagram of fibre reinforced alloy composite material prepared by the embodiment of the present invention 1;
Fig. 8 is the energy spectrum diagram of fibre reinforced alloy composite material prepared by embodiment 1.
Specific embodiment
The present invention provides a kind of fibre reinforced alloy composite material and preparation method thereof, for solving current boiler mistake
The problem of high temperature corrosion-resisting performance and oxidative resistance of hot device pipe material can meet China's biomass power plant tubing.
The technical solution in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's all other embodiments obtained without making creative work belong to the model that the present invention protects
It encloses.
A kind of fibre reinforced alloy composite material, fibre reinforced alloy composite material is using alloy as matrix, with carbon fibre
It ties up and is prepared for reinforcement;
Alloy includes:By percentage to the quality, Cr:20%~22%, Al:0.5%~2%, Ni:2%~8%, C:
0.02%~0.08%, Ti:0.2%~0.8% and Nb:0.2%~0.8%;Remaining is iron.
High temperature corrosion dynamic test and high-temperature oxydation dynamic test show fibre reinforced alloy composite wood of the present invention
Material weightening variable quantity in corrosion test is concentrated mainly on 1.3~2.9mg/cm2In the range of, fibre reinforced alloy of the present invention
Composite material has the high temperature resistant potassium chloride corrosive nature for being substantially better than the commercial metals material such as TP316.It is difficult to understand with 304, HR3C etc.
Family name's body alloy is compared, and fibre reinforced alloy composite material of the present invention has better heat conductivility, lower coefficient of thermal expansion,
And good processability, welding performance.In organizational aspects, fibre reinforced alloy composite material crystal grain of the present invention is thinner
It is small, it is single ferritic structure, there is good processing performance, Nb, Ti are to fibre reinforced alloy composite material of the present invention
Structure refinement and corrosion resisting property, which improve, has good influence.Also, the cost of fibre reinforced alloy composite material of the present invention compared with
It is low.
In the present invention, Ni and Cr pairing gold utensils have good protective value.Ni can change the crystal structure of alloy, be formed
Austenitic crystal structure;And austenite material has extraordinary corrosion resistance and comprehensive mechanical property, Ni makes material have more
Good oxidation resistent susceptibility.Cr2O3Oxidation film is fine and close, and Cr makes material have better corrosion resistance, improves the anti-molten salt hot corrosion of alloy
Ability.
Further, by percentage to the quality, Cr:21.2%th, Al:1.0%th, Ni:5.0%th, C:0.05%th, Ti:
0.5% and Nb:0.5%.
Further, it further includes:By percentage to the quality, Mo:0.1%~0.3%, Si3N4:0.1%~0.5%, Co:
0.01%~0.05%, Cu:0.01%~0.05% and Si:0.005%~0.02%.
Further, by percentage to the quality, Mo:0.2%th, Si3N4:0.3%th, Co:0.02%th, Cu:0.02% He
Si:0.01%.
Further, it further includes:Rare earth element.
In the present invention, rare earth element Nd, La, Pr, Y and V's is one or more.
In the present invention, rare earth element Nd, La, Pr, Y and V.
In the present invention, by percentage to the quality, Nd:0.02%~0.08%, La:0.0005%~0.002%, Pr:
0.002%~0.008%, Y:0.02%~0.08% and V:0.02%~0.08%.
Further, by percentage to the quality, Nd:0.05%th, La:0.001%th, Pr:0.005%th, Y:0.05% and V:
0.05%.
In the present invention, mass percent of the carbon fiber in fibre reinforced alloy composite material is 0.05%.
In the present invention, fibre reinforced alloy composite material further includes:P, S and Mn, by percentage to the quality, P<
0.045%th, S<0.03%th, Mn<2.0%.
In the present invention, fibre reinforced alloy composite material adds in Mo, Co, Nb, Ti, Cu, Si element simultaneously, forms Mo-
The multielement enhanced phases of Co-Nb-Ti-Cu-Si, cooperative reinforcing improve the anti-alkali metal and chlorine corrosion of fibre reinforced alloy composite material
Performance.Ni elements can prevent austenite material from generating spot corrosion and crevice corrosion;Ni-Mo-Co interacts, and forms fine and close rusty scale
Chlorion is prevented to invade, resistance to spot corrosion effect is stronger;Nb, Ti are carbide stabilizing elements, can reduce fibre reinforced alloy
Composite material intercrystalline corrosion;Cu can improve corrosion resistance of the fibre reinforced alloy composite material in acidic environment, in material
Surface forms fine and close sulfide film or indissoluble salt prevents spot corrosion to basic Internal Amplification;Si can make fibre reinforced
The ability of the stress corrosion resistant fracture of alloy composite materials improves.
Fibre reinforced alloy composite material of the present invention adds rare earth element, and collaboration adds in rare earth element and improves carbon fiber
Enhance alloy composite materials corrosion resistance, and by the way that inclusion morphology is controlled to improve fibre reinforced alloy composite material
Ductility and toughness.Neodymium and lanthanum can improve the high-temperature behavior and corrosion resistance of fibre reinforced alloy composite material;Pr is bright
The aobvious antioxygenic property and mechanical performance for improving fibre reinforced alloy composite material;It is compound that Y can enhance fibre reinforced alloy
The inoxidizability and ductility of material;V is the excellent deoxidier of fibre reinforced alloy composite material, and fibre reinforced alloy is multiple
Added in condensation material vanadium can thinning microstructure crystal grain, improve intensity and toughness, the sulfide that V is formed with sulphur at high temperature under high pressure may be used
Improve hydrogen attack resistance.With other compositions in the present invention recombination reaction can occur for V, improve material capability, for example Ti-V is answered
When closing addition, to play the precipitation strength effect of V, it should be noted that Ti contents are unsuitable excessively high.Ti too high levels will reduce carbon
Fiber reinforcement alloy composite materials toughness, Ti contents of the present invention are 0.5%;The compound additions of Nb-V, intensity ratio are individually added into Nb
Height, while austenite grain can be made further to refine, make ferrite crystal grain after cooling more tiny, finally improve fibre reinforced
The intensity and toughness of alloy composite materials.
For the present invention using alloy as matrix, reinforcement forms fibre reinforced alloy composite material using carbon (graphite) fiber,
The specific strength and specific modulus of fibre reinforced alloy composite material are significantly improved, there is very high intensity, toughness and impact resistance,
Greatly improve the resistance to alkali metal of fibre reinforced alloy composite material and chlorine corrosion ability.Composite material be by two kinds or two kinds with
A kind of more body materials that the upper physics substance different with chemical property is composed.In the composite, usually there is a phase to connect
Continuous phase is matrix;Another phase is dispersed phase, referred to as reinforcement.Although each component of composite material keeps its relative independentability,
The performance of composite material is not but the simple adduction of composition material performance, but has this important improvement.Composite material each group divides it
Between can be with " learning from other's strong points to offset one's weaknesses ", " synergistic effect ", the shortcomings that compensating for homogenous material.
The present invention also provides the preparation method of above-mentioned technical proposal fibre reinforced alloy composite material, including:
A) by alloy vacuum melting, melt is obtained;
B) into melt, hot extrusion adds in carbon fiber, obtains fibre reinforced alloy composite material.
In the present invention, the temperature of step a) vacuum meltings is 1100~1600 DEG C;
The vacuum degree of step a) vacuum meltings is 40~60Pa.
The mass ratio of step b) melts and carbon fiber is 0.02%~0.08%.
In the present invention, in alloy the addition of the elements such as Cr, Mo master alloy may be used.Vacuum melting is specially vacuum induction
Melting, step b) are added in after carbon fiber using hot extrusion technique into melt, are obtained fibre reinforced alloy composite material, will close
Gold carries out hot-working, cold working and annealing successively, obtains the uniform fibre reinforced alloy composite material of ferritic structure crystal grain.
In the present invention, for the preparation method of fibre reinforced alloy composite material using alloy as matrix, reinforcement is carbon fiber,
With high specific strength, high-modulus, high-temperature behavior, high low thermal expansion etc., coordinate with parent metal, obtain the excellent combination of material
Energy.Reinforcement also has good chemical stability, has good wellability and compatibility with parent metal.Metal-base composites
Interface is formed by diffusion-osmotic mode, you can spread with being reinforcement to matrix, matrix again to reinforcement diffusion into the surface-
Infiltration, mutual phased soln.When containing carbon fiber, in extrusion process carbon fiber gradually fracture and along squeeze axis it is arranged in parallel.It squeezes
Press temperature higher, strain rate reduces, then the breaking degree of carbon fiber will reduce, and is conducive to keep the major diameter ratio of carbon fiber.
The present invention also provides above-mentioned technical proposal fibre reinforced alloy composite material or above-mentioned technical proposal preparation methods
The fibre reinforced alloy composite material of preparation is in the application for preparing high temperature corrosion-resisting and resistance to oxidation tubing.
In conclusion the present invention provides a kind of fibre reinforced alloy composite material, the fibre reinforced alloy is answered
Condensation material is prepared using alloy as matrix by reinforcement of carbon fiber;The alloy includes:By percentage to the quality, Cr:
20%~22%, Al:0.5%~2%, Ni:2%~8%, C:0.02%~0.08%, Ti:0.2%~0.8% and Nb:
0.2%~0.8%;Remaining is iron.High temperature corrosion dynamic test and high-temperature oxydation dynamic test show carbon fiber of the present invention
The enhancing alloy composite materials variable quantity that increases weight in corrosion test is concentrated mainly on 1.3~2.9mg/cm2In the range of, the present invention
Fibre reinforced alloy composite material has the high temperature resistant potassium chloride corrosive nature for being substantially better than the commercial metals material such as TP316.
Compared with the austenitic alloys such as 304, HR3C, fibre reinforced alloy composite material of the present invention has better heat conductivility, more
Low coefficient of thermal expansion and excellent intensity, toughness properties.In organizational aspects, fibre reinforced alloy composite wood of the present invention
Expect that crystal grain is relatively fine, be single ferritic structure, there is good processing performance, Nb, Ti close fibre reinforced of the present invention
The structure refinement and corrosion resisting property of metal/composite material, which improve, has good influence.
Embodiment 1
Weigh 707.94g pure iron ingot, 212.2g chromium ingot and 1.8g molybdenum alloys, 10g fine aluminiums ingot, 50g pure nickels ingot, the pure titaniums of 5g
The pure niobium ingot of ingot, 5g, 3g silicon nitrides (Si3N4), the pure cobalts of 0.2g, 0.2g fine copper block, 0.1g pure silicons powder and 4.06g rare earths be (including 0.5g
Neodymium, 0.01g lanthanums, 0.05g praseodymiums, 0.5g yttriums, 3g vanadium), stock.
Raw metal in stock is subjected to melting, method of smelting is vacuum induction melting.It is right after raw metal enters stove
Entire burner hearth vacuumizes, and ensures that fusion process carries out under vacuum;Heating furnace temperature is suitably stirred to 1100~1600 DEG C of ranges
It mixes, ensures that raw metal all melts and each ingredient is uniformly distributed;Divide it should be noted that can be used according to the performance of each metal
Feed postition is criticized, reduces the probability that raw metal is aoxidized.
After the raw metal in stove is fused into equally distributed solution status, 0.5g graphite fibres are added in, are put into fiber
It in casting, pressurizes and molten metal is entered into fiber casting, then the compound melt of carbon fiber is cast to the gold being fully warmed-up again
Casting is frozen into genotype casting mould or sand mold casting mold.Carbon fiber compound casting is by hot-working and cold working and moves back
Fire processing, obtains the uniform fibre reinforced alloy composite material of ferritic structure crystal grain.
Embodiment 2
Fibre reinforced alloy composite material prepared by embodiment 1 carries out micro- detection, as shown in Figure 1, for the present invention
The metallurgical microscopic of fibre reinforced alloy composite material prepared by embodiment 1.
As shown in Figure 1, although fibre reinforced alloy composite material of the present invention adds more element species, element contains
Amount is higher, and tissue is caused to have more substructure, but still is Alfer.Fibre reinforced alloy composite material of the present invention by
In adding Nb and Ti, structure refinement illustrates that fibre reinforced alloy composite material of the present invention has good mechanical property.Chromium
It is the most basic element of heat resisting steel, fine and close oxidation film can be formed, makes fibre reinforced alloy composite material of the present invention that there is height
Corrosion resisting property and high antioxygenic property.Nickel, which is added in fibre reinforced alloy composite material of the present invention, dissolves in solid solution, makes
The mechanical property of fibre reinforced alloy composite material of the present invention significantly improves, moreover it is possible to improve fibre reinforced alloy of the present invention and answer
The antioxygenic property of condensation material.Aluminium, silicon addition fibre reinforced alloy composite material of the present invention can form protective oxide film, carry
The antioxygenic property of high fibre reinforced alloy composite material of the present invention.Vanadium, niobium and titanium add in fibre reinforced alloy of the present invention
In composite material, stable carbide can be formed, improves the intensity and thermohardening of fibre reinforced alloy composite material of the present invention.
Performance detection is carried out to fibre reinforced alloy composite material of the present invention, T316, T91,15CrMo and HR3C, as a result
As shown in table 1, show compared with T316, T91,15CrMo and HR3C, fibre reinforced alloy composite material of the present invention has more
Heat conductivility well, lower coefficient of thermal expansion and excellent intensity, toughness properties.
The performance parameter of 1 fibre reinforced alloy composite material of the present invention of table
Embodiment 3
Fibre reinforced alloy composite material prepared by embodiment 1 carries out high-temperature oxidation test, and it is fine to detect carbon of the present invention
The antiseptic property of dimension enhancing alloy composite materials, puts after fibre reinforced alloy composite material test piece of the present invention is pre-processed
It puts and is heated in chamber type electric resistance furnace, the temperature of high-temperature oxidation test is 700 DEG C, and the period of high-temperature oxidation test is 30h.It is high
Warm oxidation test is according to HB5258-2000《Steel and high temperature alloy antioxygenic property measure test method》It carries out.Referring to Fig. 2,
The high-temperature oxydation dynamic curve diagram of fibre reinforced alloy composite material for the preparation of the embodiment of the present invention 1, in 700 DEG C of conditions
Under, and compared with the high-temperature oxydation kinetic curve of commercial metal material, which is the examination of high-temperature oxidation test
It tests the time, the weight change amount on unit area that ordinate measures after being taken out for strip materials, every curve generation of the figure
A kind of metal material of table.As shown in Figure 2:High-temperature oxydation of the fibre reinforced alloy composite material of the present invention under the conditions of 700 DEG C
In the process the weight change amount (Δ W) on unit area less, substantially all in 0.2mg/cm2Within, illustrate carbon fiber of the present invention
It is preferable to enhance alloy composite materials high temperature oxidation resistance, and other commercial metal materials high-temperature oxidation process under the conditions of 700 DEG C
Middle Δ W higher, is distributed in 0.2~1.2mg/cm substantially2Between, and negative value situation occur and (show weightening at this time
Substance has apparent obscission), Δ W variation ranges are in -1..2~+1.2mg/cm2Between, high-temperature oxydation effect is undesirable, goes out
The weighting material of adhesion difference is showed, has led to weightening negative value occur.
Embodiment 4
Fibre reinforced alloy composite material prepared by embodiment 1 carries out high temperature corrosion experiment, and it is fine to detect carbon of the present invention
The antiseptic property of dimension enhancing alloy composite materials, is respectively adopted weightening finish method and weight-loss method measures test piece etching extent, and it is dynamic to draw corrosion
Force diagram.High temperature corrosion experiment increases KCl media on the basis of high-temperature oxidation test, medium meeting in higher temperature
It evaporates and forms aggressive steam, so as to form the experimental condition of high temperature corrosion.The temperature of high temperature corrosion experiment is 700 DEG C, high
The time cycle of warm corrosion test is 30h.Referring to Fig. 3, the fibre reinforced alloy composite wood prepared for the embodiment of the present invention 1
The high temperature corrosion dynamic curve diagram of material, under the conditions of 700 DEG C, and with the high temperature corrosion kinetic curve of commercial metal material into
Row comparison, the figure abscissa are the test period of high temperature corrosion experiment, and ordinate is the unit measured after strip materials take out
Weight change amount on area;Every curve of the figure represents a kind of test material.As shown in Figure 3:Fibre reinforced of the present invention
Weight change amount (Δ W) on the unit area of each moment point of the alloy composite materials under 700 DEG C, potassium chloride ambient condition
Increase than high-temperature oxidation test much, Δ W values are in 4.0mg/cm2Within.And other commercial metal materials are in 700 DEG C, chlorination
The Δ W values fluctuation of each moment point under potassium ambient condition is larger, illustrates fibre reinforced alloy composite material of the present invention 700
DEG C, the corrosion resistance under potassium chloride ambient condition be better than commercial metal material.
Embodiment 5
Fig. 4 to fig. 6 is please referred to, the fibre reinforced alloy composite material prepared for the embodiment of the present invention 1 carries out 700 DEG C of height
SEM characterization pictures after warm corrosion test, wherein comprising 3 pictures, the scale of fig. 4 to fig. 6 is followed successively by 200 μm, 20 μm and 10 μ
m.From fig. 4 to fig. 6:In different enlargement ratio pictures, strip is overall than more uniform.Although exist in Fig. 4
Apparent interface, but its further microstructure shows uniform compactness, especially in figure 6, carbon fiber of the present invention
Enhancing alloy composite materials surface shows the homogeneity of height.
Embodiment 6
Referring to Fig. 7, the high temperature corrosion dynamics of the fibre reinforced alloy composite material prepared for the embodiment of the present invention 1
Block diagram is compared under the conditions of 700 DEG C, and with the high temperature corrosion dynamics block diagram of conventional superheater tubing, and the figure is horizontal
Coordinate is the test period of high temperature corrosion experiment, and the weight on unit area that ordinate measures after being taken out for strip materials becomes
Change amount (Δ W).As shown in Figure 7:Fibre reinforced alloy composite material of the present invention has excellent corrosion resistance, TP316 materials
Material is under the conditions of 700 DEG C, KCl, when test period is 0~7h, shows relatively low surrosion, and test period is more than 10h
Afterwards, the corrosion resistance of TP316 materials declines rapidly, quickly forms the corrosion product that can not adhere to, TP316 materials can not test into
Row to 30h at the time of points, HR3C materials at the trial between quickly increase for 20h post-etching products.
Embodiment 7
Referring to Fig. 8, the energy spectrum diagram of the fibre reinforced alloy composite material prepared for embodiment 1, the abscissa of Fig. 8 are
The energy value of launching electronics, unit keV;Ordinate is the anti-of fibre reinforced alloy composite material of the present invention under emitted energy
Penetrate intensity.As shown in Figure 8:Fibre reinforced alloy composite material of the present invention embodies stronger high-temperature corrosion resistance ability and is height
Chromium content makes material form the very big chromium oxide adhesive layer of intensity, which can be resistant to the erosion of high-temp chlorination potassium.Separately
Outside, the adhesive layer rigid is effectively protected the integrality of fibre reinforced alloy composite material entirety of the present invention.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications also should
It is considered as protection scope of the present invention.