CN108192705A - A kind of environment-friendly type mechanical lubrication fluid composition and its preparation process - Google Patents

A kind of environment-friendly type mechanical lubrication fluid composition and its preparation process Download PDF

Info

Publication number
CN108192705A
CN108192705A CN201711467630.XA CN201711467630A CN108192705A CN 108192705 A CN108192705 A CN 108192705A CN 201711467630 A CN201711467630 A CN 201711467630A CN 108192705 A CN108192705 A CN 108192705A
Authority
CN
China
Prior art keywords
parts
tackifier
environment
fluid composition
friendly type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711467630.XA
Other languages
Chinese (zh)
Inventor
张艳雪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711467630.XA priority Critical patent/CN108192705A/en
Publication of CN108192705A publication Critical patent/CN108192705A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of environment-friendly type mechanical lubrication fluid composition and its preparation processes, lubricant oil composite component includes 15 30 parts of methyl-silicone oil in parts by weight, 68 14 parts of di-tert-butyl p-cresol, 8 16 parts of sorbierite, 5 15 parts of tackifier, 3 12 parts of graphene, 4 12 parts of polyurethane, 28 parts of methylcellulose, 4 12 parts of sodium citrate, 2 10 parts of cocounut oil acyl diethanol ammonium, preparation process of the present invention is simple, lubricant oil composite obtained has excellent wear-resisting, greasy property, layer protecting film can be formed on mechanical gear surface, effectively extend its service life.

Description

A kind of environment-friendly type mechanical lubrication fluid composition and its preparation process
Technical field
The present invention relates to machine oil preparing technical field, specially a kind of environment-friendly type mechanical lubrication fluid composition and its Preparation process.
Background technology
Lubricating oil is based on mineral base oil or synthetic base oil, adds in extreme pressure anti-wear additives and oiliness improver modulates what is formed A kind of important lubricating oil for various gear assemblies, to prevent tooth surface abrasion, scratch, sintering etc., extends it and uses the longevity Life improves and transmits power efficiency, reduces power loss.Lubricating oil has good wear-resistant, load resistance energy and suitable viscosity. Even if in addition, should also have good thermal oxidation stability, anti-foaming property, water separable performance energy and rustless property synthetic gear oil very Under high operation temperature and load, still ensure that all parts of transmission system are not frayed.
Lubricating oil for machinery can play certain lubricant effect at present, but its long-term greasy property is poor, and not Have repair function, be further improved.
Invention content
It is above-mentioned to solve the purpose of the present invention is to provide a kind of environment-friendly type mechanical lubrication fluid composition and its preparation process The problem of being proposed in background technology.
To achieve the above object, the present invention provides following technical solution：A kind of environment-friendly type mechanical lubrication fluid composition, lubrication Fluid composition component includes 15-30 parts of methyl-silicone oil, 8-14 parts of 6- di-tert-butyl p-cresol, sorbierite 8-16 in parts by weight Part, 5-15 parts of tackifier, 3-12 parts of graphene, 4-12 parts of polyurethane, 2-8 parts of methylcellulose, 4-12 parts of sodium citrate, cocounut oil 2-10 parts of acyl diethanol ammonium.
Preferably, the preferred composition proportion of lubricant oil composite includes 22 parts of methyl-silicone oil, 6- di-tert-butyl p-cresol 11 Part, 12 parts of sorbierite, 10 parts of tackifier, 8 parts of graphene, 8 parts of polyurethane, 5 parts of methylcellulose, 8 parts of sodium citrate, cocounut oil acyl 6 parts of diethanol ammonium.
The tackifier are sweet by 20% sodium pyrophosphate, 30% sulfide isobutene, 20% ethyl alcohol, 15% flavones, 15% rosin Oleyl alcohol forms.
Preferably, preparation process includes the following steps：
A, it adds in and stirs after mixing methyl-silicone oil, 6- di-tert-butyl p-cresol, sorbierite, tackifier, graphene, polyurethane Stirring at low speed in kettle is mixed, stir speed (S.S.) is 200-400 revs/min, and mixing time 12min-22min obtains mixture A；
B, it is added in kneading machine after methylcellulose, sodium citrate, the mixing of cocounut oil acyl diethanol ammonium are added in mixture A It is kneaded, melting temperature is 120 DEG C -160 DEG C, and mixing time 8min-12min is slowly cooled to room temperature, obtains mixture later B；
C, mixture B is stood into 2h-6h to get to lubricant oil composite at normal temperatures.
Compared with prior art, the beneficial effects of the invention are as follows：Preparation process of the present invention is simple, lubricating oil composition obtained Object has excellent wear-resisting, greasy property, can form layer protecting film on mechanical gear surface, effectively extend its use Service life；Wherein, the tackifier added in the present invention can improve the stability of lubricating oil, extend the holding time of lubricating oil； The graphene of addition is wear-resisting, good pressure-resistant performance, can repair metal surface fine defects, being capable of further prolonged mechanical product Service life.
Specific embodiment
The technical solution in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment Only part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field Art personnel all other embodiments obtained without making creative work belong to the model that the present invention protects It encloses.
The present invention provides following technical solution：A kind of environment-friendly type mechanical lubrication fluid composition, lubricant oil composite component are pressed Parts by weight include 15-30 parts of methyl-silicone oil, 8-14 parts of 6- di-tert-butyl p-cresol, 8-16 parts of sorbierite, 5-15 parts of tackifier, 3-12 parts of graphene, 4-12 parts of polyurethane, 2-8 parts of methylcellulose, 4-12 parts of sodium citrate, cocounut oil acyl diethanol ammonium 2-10 Part；Tackifier are made of 20% sodium pyrophosphate, 30% sulfide isobutene, 20% ethyl alcohol, 15% flavones, 15% rosin glyceryl alcohol.
Embodiment one：
Lubricant oil composite component includes 15 parts of methyl-silicone oil, 8 parts of 6- di-tert-butyl p-cresol, sorbierite in parts by weight 8 parts, 5 parts of tackifier, 3 parts of graphene, 4 parts of polyurethane, 2 parts of methylcellulose, 4 parts of sodium citrate, cocounut oil acyl diethanol ammonium 2 Part.
The preparation process of the present embodiment includes the following steps：
A, it adds in and stirs after mixing methyl-silicone oil, 6- di-tert-butyl p-cresol, sorbierite, tackifier, graphene, polyurethane Stirring at low speed in kettle is mixed, stir speed (S.S.) is 200 revs/min, and mixing time 12min obtains mixture A；
B, it is added in kneading machine after methylcellulose, sodium citrate, the mixing of cocounut oil acyl diethanol ammonium are added in mixture A It is kneaded, melting temperature is 120 DEG C, and mixing time 8min is slowly cooled to room temperature later, obtains mixture B；
C, mixture B is stood into 2h to get to lubricant oil composite at normal temperatures.
Embodiment two：
Lubricant oil composite component includes 30 parts of methyl-silicone oil, 14 parts of 6- di-tert-butyl p-cresol, sorb in parts by weight 16 parts of alcohol, 15 parts of tackifier, 12 parts of graphene, 12 parts of polyurethane, 8 parts of methylcellulose, 12 parts of sodium citrate, cocounut oil acyl diethyl 10 parts of alcohol ammonium.
The preparation process of the present embodiment includes the following steps：
A, it adds in and stirs after mixing methyl-silicone oil, 6- di-tert-butyl p-cresol, sorbierite, tackifier, graphene, polyurethane Stirring at low speed in kettle is mixed, stir speed (S.S.) is 400 revs/min, and mixing time 22min obtains mixture A；
B, it is added in kneading machine after methylcellulose, sodium citrate, the mixing of cocounut oil acyl diethanol ammonium are added in mixture A It is kneaded, melting temperature is 160 DEG C, and mixing time 12min is slowly cooled to room temperature later, obtains mixture B；
C, mixture B is stood into 6h to get to lubricant oil composite at normal temperatures.
Embodiment three：
Lubricant oil composite component includes 20 parts of methyl-silicone oil, 10 parts of 6- di-tert-butyl p-cresol, sorb in parts by weight 10 parts of alcohol, 7 parts of tackifier, 4 parts of graphene, 6 parts of polyurethane, 3 parts of methylcellulose, 6 parts of sodium citrate, cocounut oil acyl diethanol ammonium 4 parts.
The preparation process of the present embodiment includes the following steps：
A, it adds in and stirs after mixing methyl-silicone oil, 6- di-tert-butyl p-cresol, sorbierite, tackifier, graphene, polyurethane Stirring at low speed in kettle is mixed, stir speed (S.S.) is 250 revs/min, and mixing time 14min obtains mixture A；
B, it is added in kneading machine after methylcellulose, sodium citrate, the mixing of cocounut oil acyl diethanol ammonium are added in mixture A It is kneaded, melting temperature is 130 DEG C, and mixing time 9min is slowly cooled to room temperature later, obtains mixture B；
C, mixture B is stood into 3h to get to lubricant oil composite at normal temperatures.
Example IV：
Lubricant oil composite component includes 22 parts of methyl-silicone oil, 11 parts of 6- di-tert-butyl p-cresol, sorb in parts by weight 12 parts of alcohol, 10 parts of tackifier, 8 parts of graphene, 8 parts of polyurethane, 5 parts of methylcellulose, 8 parts of sodium citrate, cocounut oil acyl diethanol 6 parts of ammonium.
The preparation process of the present embodiment includes the following steps：
A, it adds in and stirs after mixing methyl-silicone oil, 6- di-tert-butyl p-cresol, sorbierite, tackifier, graphene, polyurethane Stirring at low speed in kettle is mixed, stir speed (S.S.) is 300 revs/min, and mixing time 17min obtains mixture A；
B, it is added in kneading machine after methylcellulose, sodium citrate, the mixing of cocounut oil acyl diethanol ammonium are added in mixture A It is kneaded, melting temperature is 140 DEG C, and mixing time 10min is slowly cooled to room temperature later, obtains mixture B；
C, mixture B is stood into 4h to get to lubricant oil composite at normal temperatures.
Preparation process of the present invention is simple, and lubricant oil composite obtained has excellent wear-resisting, greasy property, can be in machine Tool gear surface forms layer protecting film, effectively extends its service life；Wherein, the tackifier added in the present invention can The stability of lubricating oil is improved, extends the holding time of lubricating oil；The graphene of addition is wear-resisting, good pressure-resistant performance, Neng Gouxiu Multiple metal surface fine defects are capable of the service life of further prolonged mechanical product.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace And modification, the scope of the present invention is defined by the appended.

Claims (4)

1. a kind of environment-friendly type mechanical lubrication fluid composition, it is characterised in that：Lubricant oil composite component includes first in parts by weight 15-30 parts of base silicone oil, 8-14 parts of 6- di-tert-butyl p-cresol, 8-16 parts of sorbierite, 5-15 parts of tackifier, 3-12 parts of graphene, 4-12 parts of polyurethane, 2-8 parts of methylcellulose, 4-12 parts of sodium citrate, 2-10 parts of cocounut oil acyl diethanol ammonium.
2. a kind of environment-friendly type mechanical lubrication fluid composition according to claim 1, it is characterised in that：Lubricant oil composite is excellent The composition proportion of choosing includes 22 parts of methyl-silicone oil, 11 parts of 6- di-tert-butyl p-cresol, 12 parts of sorbierite, 10 parts of tackifier, graphite 8 parts of alkene, 8 parts of polyurethane, 5 parts of methylcellulose, 8 parts of sodium citrate, 6 parts of cocounut oil acyl diethanol ammonium.
3. a kind of environment-friendly type mechanical lubrication fluid composition according to claim 1 or 2, it is characterised in that：The tackifier It is made of 20% sodium pyrophosphate, 30% sulfide isobutene, 20% ethyl alcohol, 15% flavones, 15% rosin glyceryl alcohol.
4. realize a kind of preparation process of environment-friendly type mechanical lubrication fluid composition described in claims 1 or 2, it is characterised in that： Its preparation process includes the following steps：
A, stirred tank is added in after mixing methyl-silicone oil, 6- di-tert-butyl p-cresol, sorbierite, tackifier, graphene, polyurethane Middle stirring at low speed, stir speed (S.S.) are 200-400 revs/min, and mixing time 12min-22min obtains mixture A；
B, it adds in after methylcellulose, sodium citrate, cocounut oil acyl diethanol ammonium mix to add in kneading machine in mixture A and mix Refining, melting temperature are 120 DEG C -160 DEG C, and mixing time 8min-12min is slowly cooled to room temperature later, obtains mixture B；
C, mixture B is stood into 2h-6h to get to lubricant oil composite at normal temperatures.
CN201711467630.XA 2017-12-27 2017-12-27 A kind of environment-friendly type mechanical lubrication fluid composition and its preparation process Withdrawn CN108192705A (en)