CN108192568A - 一种具有光催化活性的抑尘剂制备方法及喷洒施工方法 - Google Patents
一种具有光催化活性的抑尘剂制备方法及喷洒施工方法 Download PDFInfo
- Publication number
- CN108192568A CN108192568A CN201711467655.XA CN201711467655A CN108192568A CN 108192568 A CN108192568 A CN 108192568A CN 201711467655 A CN201711467655 A CN 201711467655A CN 108192568 A CN108192568 A CN 108192568A
- Authority
- CN
- China
- Prior art keywords
- dust suppressant
- dust
- weight
- parts
- photocatalytic activity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种具有光催化活性的抑尘剂制备方法及喷洒施工方法，所述抑尘剂制备方法包括采用如下步骤制备溶胶A和溶液B；将锐钛矿型的纳米二氧化钛粉末加水搅拌，超声处理后静置，取上层清液并添加浓度为0.2～5％的粘结剂，制得溶胶A，其中，所述纳米二氧化钛粉末粒径为1～100nm；将0.1～0.9：0.1～0.9重量份的醋酸钙和醋酸镁与30～100重量份的水充分混合，制成醋酸钙镁盐水溶液，并向所述醋酸钙镁盐水溶液加入0.04～0.2重量份的抑尘助剂，得到溶液B。本发明的制备方法能够制备出具有高效降解污染物能力的纳米TiO2/CMA复合材料，其在光照下具有很好的抑尘吸附性能、光催化活性，对环境无害。
Description
技术领域
本发明涉及一种抑尘剂制备方法，特别是涉及一种具有光催化活性的抑尘剂制备方法及喷洒施工方法。
背景技术
近年来，随着经济发展、煤炭运输业的增多、城市基础设施建设以及垃圾废料的堆放，使得城市扬尘和VOC污染日趋严重。
如何减少扬尘和VOC污染已引起人们的高度重视，目前常用的降尘方法有抑尘剂、湿法防尘、设置防风林防风网、建造封闭式结构、洒水法.其中，抑尘剂相较其它方法，由于其成本低廉、实用性强、有效期长、降尘效果明显，在实际工程实践中应用较多。
醋酸钙镁盐(CMA)是市面上常用抑尘剂的主要原料之一。而氧化钛常用于食品添加剂，无毒无害，当尺寸达到纳米粒径(1-100nm)可用于光催化剂。但是，目前尚无即用于光催化又能抑尘的材料的相关报道，因此研制一种既能用于光催化降解VOC污染物又能对颗粒物抑尘有效的新型抑尘剂将具有重要意义。
发明内容
本发明的目的是针对现有抑尘剂存在的不足，提出一种具有光催化活性的抑尘剂制备方法及喷洒施工方法，使得抑尘剂具有光催化性能，除了有抑尘作用还兼有降解VOC和杀菌功效，并且对环境无害，不产生二次污染。
为实现上述目的，本发明提供了一种具有光催化活性的抑尘剂制备方法，所述抑尘剂制备方法包括采用如下步骤制备溶胶A和溶液B：
步骤A、将锐钛矿型的纳米二氧化钛粉末加水搅拌，超声处理后静置，取上层清液并添加浓度为0.2～5％的粘结剂，制得溶胶A，其中，所述纳米二氧化钛粉末粒径为1～100nm；
步骤B、将0.1～0.9：0.1～0.9重量份的醋酸钙和醋酸镁与30～100重量份的水充分混合，制成醋酸钙镁盐水溶液，并向所述醋酸钙镁盐水溶液加入0.04～0.2重量份的抑尘助剂，得到溶液B，其中，所述的抑尘助剂为十二烷基硫酸钠、烷基酚聚氧乙烯醚TX-10、润湿剂X-405、十二烷基苯磺酸钠、吐温、司盘中的一种或几种表面活性剂的混合物。
优选地，在步骤A中，所述上层清液为在暗室用可见光照射产生光亮通路的溶胶。
优选地，所述粘结剂选自水性氟树脂、纯丙乳液、苯丙乳液、醋丙乳液、水性聚氨酯中的一种或任意几种的混合物。
本发明的另一目的在于提供一种采用具有光催化活性抑尘剂的喷洒施工方法，其特征在于：所述喷洒施工方法包括如下步骤：
(1)、将含有纳米级二氧化钛和粘结剂的溶胶A混合质量分数为0.1～0.5％双氧水喷洒到路面上；
(2)、在20～120分钟完成粘结后，再将含有醋酸钙镁盐的溶液B喷洒到经过步骤(1)粘结预处理后的路面上。
基于上述技术方案，本发明的优点是：
本发明的具有光催化活性的抑尘剂制备方法能够制备出具有高效降解污染物能力的纳米TiO2/CMA复合材料，其在光照下具有很好的抑尘吸附性能、光催化活性，对环境无害。通过将粒径为1～100nm的纳米二氧化钛(锐钛矿型)分散在粘结剂中不易发生团聚，分散性好。通过本发明的方法制备的抑尘剂能够有效地降低道路上可吸入颗粒物及氮氧化物、硫化物、细菌、VOC等有害物质，并且其具有环境友好、对车辆和路面腐蚀性弱、效用持续时间长等特点。
本发明方法制备的道路抑尘剂能够对近地表已有的可吸入颗粒物、细菌、行驶车辆所携带的可吸入颗粒物以及车轮与地面的摩擦产生的炭黑均能够进行有效地抑尘、无害化处理，且能够在铺装、非铺装道路等领域广泛地应用，可以显著地降低总悬浮颗粒物(TSP)、PM10，PM2.5以及氮氧化物、硫化物、VOC等有害物的浓度。
具体实施方式
下面实施例，对本发明的技术方案做进一步的详细描述。
本发明提供了一种具有光催化活性的抑尘剂制备方法，所述抑尘剂制备方法包括采用如下步骤制备溶胶A和溶液B：
步骤A、将锐钛矿型的纳米二氧化钛粉末加水搅拌，超声处理后静置，取上层清液并添加浓度为0.2～5％的粘结剂，制得溶胶A，其中，所述纳米二氧化钛粉末粒径为1～100nm。
在步骤A中，所述上层清液为在暗室用可见光照射产生光亮通路的溶胶。通过在暗室用可见光照射上层清液，发现有一光亮通路(即丁达尔效应)，则证明所述上层清液为胶体，以此对上层清液的质量进行质量确定，并选择优质的上层清液。优选地，所述粘结剂选自水性氟树脂、纯丙乳液、苯丙乳液、醋丙乳液、水性聚氨酯中的一种或任意几种的混合物，具有粘结性好且对环境无害的优点。
步骤B、将0.1～0.9：0.1～0.9重量份的醋酸钙和醋酸镁与30～100重量份的水充分混合，制成醋酸钙镁盐水溶液(即CMA溶液)，并向所述醋酸钙镁盐水溶液加入0.04～0.2重量份的抑尘助剂，得到溶液B，其中，所述的抑尘助剂为十二烷基硫酸钠、烷基酚聚氧乙烯醚TX-10、润湿剂X-405、十二烷基苯磺酸钠、吐温、司盘中的一种或几种表面活性剂的混合物。
本发明的还提供一种采用具有光催化活性抑尘剂的喷洒施工方法，其特征在于：所述喷洒施工方法包括如下步骤：
(1)、将含有纳米级二氧化钛和粘结剂的溶胶A混合质量分数为0.1～0.5％双氧水喷洒到路面上；
(2)、在20～120分钟完成粘结后，再将含有醋酸钙镁盐的溶液B喷洒到经过步骤(1)粘结预处理后的路面上。
本发明方法制备的道路抑尘剂能够对近地表已有的可吸入颗粒物、细菌、行驶车辆所携带的可吸入颗粒物以及车轮与地面的摩擦产生的炭黑均能够进行有效地抑尘、无害化处理，且能够在铺装、非铺装道路等领域广泛地应用，可以显著地降低总悬浮颗粒物(TSP)、PM10，PM2.5以及氮氧化物、硫化物、VOC等有害物的浓度。
实施例1
本实施例的具有光催化活性的抑尘剂制备方法的步骤如下：
①、将足量锐钛矿型的纳米二氧化钛粉末加水搅拌，超声处理后，静置，取上清液，在暗室用可见光照射，发现有一光亮通路，则证明该上清液为胶体，二氧化钛选用粒径为1～100nm，并添加浓度为1％的苯丙乳液，制得溶胶A；
②、将0.3：0.2重量份的醋酸钙和醋酸镁与30重量份的水充分混合，制成醋酸钙镁盐水溶液；
③、向步骤②中的醋酸钙镁盐水溶液加入0.04重量份的十二烷基苯磺酸钠，制备得到溶液B。
实施例2
本实施例的具有光催化活性的抑尘剂制备方法的步骤如下：
①、将足量锐钛矿型的纳米二氧化钛粉末加水搅拌，超声处理后，静置，取上清液，在暗室用可见光照射，发现有一光亮通路，则证明该上清液为胶体，二氧化钛选用粒径为1～100nm，并添加浓度为3％的苯丙乳液，制得溶胶A；
②、将0.6：0.1重量份的醋酸钙和醋酸镁与30重量份的水充分混合，制成醋酸钙镁盐水溶液；
③、向步骤②中的醋酸钙镁盐水溶液加入0.04重量份的十二烷基苯磺酸钠，制备得到溶液B。
本发明的具有光催化活性的抑尘剂制备方法能够制备出具有高效降解污染物能力的纳米TiO2/CMA复合材料，其在光照下具有很好的抑尘吸附性能、光催化活性，对环境无害。通过将粒径为1～100nm的纳米二氧化钛(锐钛矿型)分散在粘结剂中不易发生团聚，分散性好。通过本发明的方法制备的抑尘剂能够有效地降低道路上可吸入颗粒物及氮氧化物、硫化物、细菌、VOC等有害物质，并且其具有环境友好、对车辆和路面腐蚀性弱、效用持续时间长等特点。
最后应当说明的是:以上实施例仅用以说明本发明的技术方案而非对其限制；尽管参照较佳实施例对本发明进行了详细的说明，所属领域的普通技术人员应当理解：依然可以对本发明的具体实施方式进行修改或者对部分技术特征进行等同替换；而不脱离本发明技术方案的精神，其均应涵盖在本发明请求保护的技术方案范围当中。
Claims (4)
1.一种具有光催化活性的抑尘剂制备方法，其特征在于：所述抑尘剂制备方法包括采用如下步骤制备溶胶A和溶液B：
步骤A、将锐钛矿型的纳米二氧化钛粉末加水搅拌，超声处理后静置，取上层清液并添加浓度为0.2～5％的粘结剂，制得溶胶A，其中，所述纳米二氧化钛粉末粒径为1～100nm；
步骤B、将0.1～0.9：0.1～0.9重量份的醋酸钙和醋酸镁与30～100重量份的水充分混合，制成醋酸钙镁盐水溶液，并向所述醋酸钙镁盐水溶液加入0.04～0.2重量份的抑尘助剂，得到溶液B，其中，所述的抑尘助剂为十二烷基硫酸钠、烷基酚聚氧乙烯醚TX-10、润湿剂X-405、十二烷基苯磺酸钠、吐温、司盘中的一种或几种表面活性剂的混合物。
2.根据权利要求1所述的抑尘剂制备方法，其特征在于：在步骤A中，所述上层清液为在暗室用可见光照射产生光亮通路的溶胶。
3.根据权利要求1所述的抑尘剂制备方法，其特征在于：所述粘结剂选自水性氟树脂、纯丙乳液、苯丙乳液、醋丙乳液、水性聚氨酯中的一种或任意几种的混合物。
4.一种采用具有光催化活性抑尘剂的喷洒施工方法，其特征在于：所述喷洒施工方法包括如下步骤：
(1)、将上述权利要求1～3中任意一项权利要求中所述的含有纳米级二氧化钛和粘结剂的溶胶A混合质量分数为0.1～0.5％双氧水喷洒到路面上；
(2)、在20～120分钟完成粘结后，再将上述权利要求1～3中任意一项权利要求中所述的含有醋酸钙镁盐的溶液B喷洒到经过步骤(1)粘结预处理后的路面上。