CN108192552A - A kind of flame-proof antibiotic polyurethane glass glue - Google Patents
A kind of flame-proof antibiotic polyurethane glass glue Download PDFInfo
- Publication number
- CN108192552A CN108192552A CN201711444646.9A CN201711444646A CN108192552A CN 108192552 A CN108192552 A CN 108192552A CN 201711444646 A CN201711444646 A CN 201711444646A CN 108192552 A CN108192552 A CN 108192552A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame
- glass glue
- proof antibiotic
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of flame-proof antibiotic polyurethane glass glue, raw material includes by weight:50 60 parts of base polyurethane prepolymer for use as, 8 15 parts of plasticizer, 2 10 parts of diatomite, 3 20 parts of talcum powder, 3 15 parts of lanthana, 3 16 parts of montmorillonite, 15 parts of carbon nanotube, 18 parts of galapectite, 1 2.5 parts of antioxidant, 0.3 1.2 parts of ultra-violet absorber, 0.1 0.35 parts of thixotropic agent, 0.1 0.5 parts of catalyst, 25 parts of antiseptic, 3 14 parts of fire retardant;The fire retardant is hydroxymethyl phenyl phosphinic acids, the mixture of polyimide modified magnesium hydroxide, three (neopentyl glycol phosphate phosphorus methylene) amine, polyphosphoric acid amine;The antiseptic is curcumin, the mixture of Citrated chitosan, 8 oxyquinolines, dandelion polyphenol, ε poly-D-lysines, glycine zine, zinc lactate.
Description
Technical field
The present invention relates to glass cement technical field more particularly to a kind of flame-proof antibiotic polyurethane glass glue.
Background technology
Glass cement is that various glass are carried out material that is be bonded and sealing with other base materials, is broadly divided into silicone adhesive and poly- ammonia
Two major class of ester gum.Polyurethane is a kind of high molecular material, wide, adaptable, resistance to its manufactured glass cement performance adjustable extent
Biological aging, moderate cost are widely used in numerous industries such as upholstery, construction industry, transportation industry.But polyurethane conduct has
Machine object, anti-flammability are not fine, while do not have antibiotic property yet, and with its manufactured glass cement, there are anti-flammability and antibiotic property are poor
The defects of, limit the application of glass cement.
Invention content
Technical problems based on background technology, the present invention propose a kind of flame-proof antibiotic polyurethane glass glue, glue
Knotting strength is high, quick solidifying, excellent fireproof performance, and antibiotic property is strong.
A kind of flame-proof antibiotic polyurethane glass glue proposed by the present invention, raw material include by weight:Base polyurethane prepolymer for use as
50-60 parts, 8-15 parts of plasticizer, 2-10 parts of diatomite, 3-20 parts of talcum powder, 3-15 parts of lanthana, 3-16 parts of montmorillonite, carbon receives
1-5 parts of mitron, 1-2.5 parts of antioxidant, 0.3-1.2 parts of ultra-violet absorber, 0.1-0.35 parts of thixotropic agent, is urged at 1-8 parts of galapectite
0.1-0.5 parts of agent, 2-5 parts of antiseptic, 3-14 parts of fire retardant;
Wherein, the fire retardant is hydroxymethyl phenyl phosphinic acids, polyimide modified magnesium hydroxide, three (neopentyl glycol phosphorus
Acid esters-phosphorus-methylene) amine, polyphosphoric acid amine mixture;
The antiseptic for curcumin, Citrated chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly-D-lysine,
The mixture of glycine zine, zinc lactate.
Preferably, the plasticizer for chlorinated paraffin, ethylene-butyl acrylate copolymer, 5- hydroxyl dodecanoic acids glyceride,
Tetraoctyl 1,2,4,5-benzenetetra-carboxylate is 3-10 by weight:5-12:1-4:The mixture of 3-15.
Preferably, the antioxidant is antioxidant 1010.
Preferably, the ultra-violet absorber is benzophenone tetracarboxylic dianhydride, 2- (bis- tertiary amyls of 2'- hydroxyls -3', 5'-
Phenyl) benzotriazole, ultra-violet absorber UV234 by weight be 2-10:4-8:The mixture of 3-14.
Preferably, the thixotropic agent is aerosil.
Preferably, the catalyst is dibutyl tin laurate.
Preferably, hydroxymethyl phenyl phosphinic acids, polyimide modified magnesium hydroxide, three (neopentyl glycol phosphates-phosphorus-Asia
Methyl) amine, polyphosphoric acid amine weight ratio be 4-10:4-16:3-9:5-10.
Preferably, curcumin, Citrated chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly-D-lysine, sweet ammonia
Sour zinc, zinc lactate weight ratio be 3-10:3-9:4-10:4-18:5-10:5-9:3-10.
Flame-proof antibiotic polyurethane glass glue of the present invention, with hydroxymethyl phenyl phosphinic acids, polyimide modified hydrogen-oxygen
Change magnesium, three (neopentyl glycol phosphate-phosphorus-methylene) amine, polyphosphoric acid amine cooperation as in fire retardant, with system diatomite,
Lanthana, montmorillonite, carbon nanotube, galapectite cooperation, excellent fire-retardant of imparting glass cement while glass cement intensity is improved
Property;With curcumin, Citrated chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly-D-lysine, glycine zine, zinc lactate
Cooperation plays best synergistic effect, assigns glass cement excellent antibiotic property as antiseptic.
Specific embodiment
In the following, technical scheme of the present invention is described in detail by specific embodiment.
Embodiment 1
A kind of flame-proof antibiotic polyurethane glass glue proposed by the present invention, raw material include by weight:Base polyurethane prepolymer for use as
60 parts, 8 parts of plasticizer, 10 parts of diatomite, 3 parts of talcum powder, 15 parts of lanthana, 3 parts of montmorillonite, 5 parts of carbon nanotube, galapectite 1
Part, 2.5 parts of antioxidant, 0.3 part of ultra-violet absorber, 0.35 part of thixotropic agent, 0.1 part of catalyst, 5 parts of antiseptic, fire retardant 3
Part;
Wherein, the fire retardant is hydroxymethyl phenyl phosphinic acids, polyimide modified magnesium hydroxide, three (neopentyl glycol phosphorus
Acid esters-phosphorus-methylene) amine, polyphosphoric acid amine mixture;
The antiseptic for curcumin, Citrated chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly-D-lysine,
The mixture of glycine zine, zinc lactate.
Embodiment 2
A kind of flame-proof antibiotic polyurethane glass glue proposed by the present invention, raw material include by weight:Base polyurethane prepolymer for use as
50 parts, 15 parts of plasticizer, 2 parts of diatomite, 20 parts of talcum powder, 3 parts of lanthana, 16 parts of montmorillonite, 1 part of carbon nanotube, galapectite 8
Part, 1 part of antioxidant, 1.2 parts of ultra-violet absorber, 0.1 part of thixotropic agent, 0.5 part of catalyst, 2 parts of antiseptic, 14 parts of fire retardant;
Wherein, the fire retardant is hydroxymethyl phenyl phosphinic acids, polyimide modified magnesium hydroxide, three (neopentyl glycol phosphorus
Acid esters-phosphorus-methylene) amine, polyphosphoric acid amine mixture;
The antiseptic for curcumin, Citrated chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly-D-lysine,
The mixture of glycine zine, zinc lactate.
Embodiment 3
A kind of flame-proof antibiotic polyurethane glass glue proposed by the present invention, raw material include by weight:Base polyurethane prepolymer for use as
58 parts, 10 parts of plasticizer, 8.7 parts of diatomite, 5 parts of talcum powder, 13 parts of lanthana, 5 parts of montmorillonite, 2 parts of carbon nanotube, galapectite
2 parts, 2.3 parts of antioxidant, 0.5 part of ultra-violet absorber, 0.3 part of thixotropic agent, 0.15 part of catalyst, 4.3 parts of antiseptic, fire retardant
5 parts;
Wherein, the fire retardant is hydroxymethyl phenyl phosphinic acids, polyimide modified magnesium hydroxide, three (neopentyl glycol phosphorus
Acid esters-phosphorus-methylene) amine, polyphosphoric acid amine mixture, and hydroxymethyl phenyl phosphinic acids, polyimide modified magnesium hydroxide, three
(neopentyl glycol phosphate-phosphorus-methylene) amine, polyphosphoric acid amine weight ratio be 4:16:3:10;
The antiseptic for curcumin, Citrated chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly-D-lysine,
The mixture of glycine zine, zinc lactate, and curcumin, Citrated chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly
Lysine, glycine zine, zinc lactate weight ratio be 3:9:4:4:10:5:10;
The plasticizer is chlorinated paraffin, ethylene-butyl acrylate copolymer, 5- hydroxyl dodecanoic acids glyceride, equal benzene four
Sour four monooctyl esters are 3 by weight:12:1:15 mixture;
The antioxidant is antioxidant 1010;
The ultra-violet absorber is benzophenone tetracarboxylic dianhydride, 2- (bis- tertiary amyl phenyl of 2'- hydroxyls -3', 5'-) benzene
And triazole, ultra-violet absorber UV234 are 2 by weight:8:3 mixture;
The thixotropic agent is aerosil;
The catalyst is dibutyl tin laurate.
Embodiment 4
A kind of flame-proof antibiotic polyurethane glass glue proposed by the present invention, raw material include by weight:Base polyurethane prepolymer for use as
52 parts, 13 parts of plasticizer, 4 parts of diatomite, 17 parts of talcum powder, 6 parts of lanthana, 12 parts of montmorillonite, 3 parts of carbon nanotube, galapectite 7
Part, 1.6 parts of antioxidant, 1 part of ultra-violet absorber, 0.15 part of thixotropic agent, 0.4 part of catalyst, 2.6 parts of antiseptic, fire retardant 12
Part;
Wherein, the fire retardant is hydroxymethyl phenyl phosphinic acids, polyimide modified magnesium hydroxide, three (neopentyl glycol phosphorus
Acid esters-phosphorus-methylene) amine, polyphosphoric acid amine mixture, and hydroxymethyl phenyl phosphinic acids, polyimide modified magnesium hydroxide, three
(neopentyl glycol phosphate-phosphorus-methylene) amine, polyphosphoric acid amine weight ratio be 10:4:9:5;
The antiseptic for curcumin, Citrated chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly-D-lysine,
The mixture of glycine zine, zinc lactate, and curcumin, Citrated chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly
Lysine, glycine zine, zinc lactate weight ratio be 10:3:10:18:5:9:3;
The plasticizer is chlorinated paraffin, ethylene-butyl acrylate copolymer, 5- hydroxyl dodecanoic acids glyceride, equal benzene four
Sour four monooctyl esters are 10 by weight:5:4:3 mixture;
The antioxidant is antioxidant 1010;
The ultra-violet absorber is benzophenone tetracarboxylic dianhydride, 2- (bis- tertiary amyl phenyl of 2'- hydroxyls -3', 5'-) benzene
And triazole, ultra-violet absorber UV234 are 10 by weight:4:14 mixture;
The thixotropic agent is aerosil;
The catalyst is dibutyl tin laurate.
Embodiment 5
A kind of flame-proof antibiotic polyurethane glass glue proposed by the present invention, raw material include by weight:Base polyurethane prepolymer for use as
55 parts, 12 parts of plasticizer, 7 parts of diatomite, 13 parts of talcum powder, 8 parts of lanthana, 12 parts of montmorillonite, 2 parts of carbon nanotube, galapectite 5
Part, 2 parts of antioxidant, 1 part of ultra-violet absorber, 0.3 part of thixotropic agent, 0.25 part of catalyst, 3 parts of antiseptic, 11 parts of fire retardant;
Wherein, the fire retardant is hydroxymethyl phenyl phosphinic acids, polyimide modified magnesium hydroxide, three (neopentyl glycol phosphorus
Acid esters-phosphorus-methylene) amine, polyphosphoric acid amine mixture, and hydroxymethyl phenyl phosphinic acids, polyimide modified magnesium hydroxide, three
(neopentyl glycol phosphate-phosphorus-methylene) amine, polyphosphoric acid amine weight ratio be 7:11:5:8;
The antiseptic for curcumin, Citrated chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly-D-lysine,
The mixture of glycine zine, zinc lactate, and curcumin, Citrated chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly
Lysine, glycine zine, zinc lactate weight ratio be 7:5:8:12:7:6:8;
The plasticizer is chlorinated paraffin, ethylene-butyl acrylate copolymer, 5- hydroxyl dodecanoic acids glyceride, equal benzene four
Sour four monooctyl esters are 7 by weight:11:3:12 mixture;
The antioxidant is antioxidant 1010;
The ultra-violet absorber is benzophenone tetracarboxylic dianhydride, 2- (bis- tertiary amyl phenyl of 2'- hydroxyls -3', 5'-) benzene
And triazole, ultra-violet absorber UV234 are 8 by weight:5:12 mixture;
The thixotropic agent is aerosil;
The catalyst is dibutyl tin laurate.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of flame-proof antibiotic polyurethane glass glue, which is characterized in that its raw material includes by weight:Base polyurethane prepolymer for use as 50-
60 parts, 8-15 parts of plasticizer, 2-10 parts of diatomite, 3-20 parts of talcum powder, 3-15 parts of lanthana, 3-16 parts of montmorillonite, carbon nanometer
1-5 parts of pipe, 1-8 parts of galapectite, 1-2.5 parts of antioxidant, 0.3-1.2 parts of ultra-violet absorber, 0.1-0.35 parts of thixotropic agent, catalysis
0.1-0.5 parts of agent, 2-5 parts of antiseptic, 3-14 parts of fire retardant;
Wherein, the fire retardant for hydroxymethyl phenyl phosphinic acids, polyimide modified magnesium hydroxide, three (neopentyl glycol phosphate-
Phosphorus-methylene) amine, polyphosphoric acid amine mixture;
The antiseptic is curcumin, Citrated chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly-D-lysine, sweet ammonia
The mixture of sour zinc, zinc lactate.
2. flame-proof antibiotic polyurethane glass glue according to claim 1, which is characterized in that the plasticizer for chlorinated paraffin,
Ethylene-butyl acrylate copolymer, 5- hydroxyl dodecanoic acids glyceride, tetraoctyl 1,2,4,5-benzenetetra-carboxylate are 3-10 by weight:5-12:1-
4:The mixture of 3-15.
3. flame-proof antibiotic polyurethane glass glue according to claim 1 or claim 2, which is characterized in that the antioxidant is antioxidant
1010。
4. according to any one of the claim 1-3 flame-proof antibiotic polyurethane glass glue, which is characterized in that the ultraviolet light is inhaled
Receipts agent is benzophenone tetracarboxylic dianhydride, 2- (bis- tertiary amyl phenyl of 2'- hydroxyls -3', 5'-) benzotriazole, ultra-violet absorber
UV234 is 2-10 by weight:4-8:The mixture of 3-14.
5. according to any one of the claim 1-4 flame-proof antibiotic polyurethane glass glue, which is characterized in that the thixotropic agent is
Aerosil.
6. according to any one of the claim 1-5 flame-proof antibiotic polyurethane glass glue, which is characterized in that the catalyst is
Dibutyl tin laurate.
7. according to any one of the claim 1-6 flame-proof antibiotic polyurethane glass glue, which is characterized in that hydroxymethyl phenyl
Phosphonic acids, polyimide modified magnesium hydroxide, three (neopentyl glycol phosphate-phosphorus-methylene) amine, polyphosphoric acid amine weight ratio be 4-
10:4-16:3-9:5-10.
8. according to any one of the claim 1-7 flame-proof antibiotic polyurethane glass glue, which is characterized in that curcumin, lemon
Acidified chitosan, 8-hydroxyquinoline, dandelion polyphenol, ε-poly-D-lysine, glycine zine, zinc lactate weight ratio be 3-10:
3-9:4-10:4-18:5-10:5-9:3-10.