CN108180255A - A kind of HI high impact environmental protection V bands and its manufacturing process - Google Patents
A kind of HI high impact environmental protection V bands and its manufacturing process Download PDFInfo
- Publication number
- CN108180255A CN108180255A CN201711372618.0A CN201711372618A CN108180255A CN 108180255 A CN108180255 A CN 108180255A CN 201711372618 A CN201711372618 A CN 201711372618A CN 108180255 A CN108180255 A CN 108180255A
- Authority
- CN
- China
- Prior art keywords
- parts
- butadiene
- agent
- bands
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of HI high impact environmental protection V bands and its manufacturing process, the manufacture raw material of the HI high impact environmental protection V bands to be made of canvas, raw rubber, infantees, industrial chemicals, cotton rope, primer, buffering adhesive and cloth glue.The present invention is using Japanese import aramid fiber skeleton cotton rope, in work is run, it can bear moment relatively high power, rotative power is 5 times of classical V-belt, whole strength is 3 times of classical V-belt, in operation process, it can play and not extend, it does not shrink, suitable for taking turns rotation more, during pinch roller clutch simultaneously, it is not likely to produce noise, in work is run, when encountering foreign matter and being stopped, belt is reduced with friction coefficient, the impact force being subject to can be slowed down, phenomena such as solution motor is burnt out and belt is broken, in work is run, working face is less prone to phenomena such as rubber powder, so as to protect ground environment.
Description
Technical field
The present invention relates to V band technical fields, specially a kind of HI high impact environmental protection V bands and its manufacturing process.
Background technology
V bands are the general designations that section is trapezoidal annular driving band, compared with flat transmission belt, have and install easy, occupation of land
The advantages that area is small, transmission efficiency and noise are small occupies an important position in entire transmission field, by its cross sectional shape and ruler
It is very little to be divided into classical V-belt, narrow V belt, width V bands, polywedge bet etc., it can be divided into type V-belt cloth wrapping and work(side Formula V band by girdle structure, press
Band cored structure can be divided into cord core V belt and rope core v belt, be mainly used in the power of motor and oil-engine driven mechanical equipment
Transmission, V bands are one kind of transmission belt, and general industry carries classical V-belt, narrow V belt and joined v-belt with V.
V bands on the market are when operating practical among compressing and rubbing against in long-time high intensity now, and this
A little frictions can greatly reduce the service life of V bands, for this purpose, it is proposed that a kind of novel high punching press V bands are to solve the problems, such as this.
Invention content
The purpose of the present invention is to provide a kind of HI high impact environmental protection V bands and its manufacturing process, to solve to carry in background technology
The problem of going out.
To achieve the above object, the present invention provides following technical solution：A kind of HI high impact environmental protection V bands and its manufacturing process,
The manufacture raw material of the HI high impact environmental protection V bands is by canvas, raw rubber, infantees, industrial chemicals, cotton rope, primer, buffering adhesive and cloth glue group
Into the manufacture material of the primer, buffering adhesive and cloth glue includes natural gum, butadiene-styrene rubber, carbon black, calcium carbonate, stearic acid, prevents always
Agent, zinc oxide, Cosan, accelerating agent and adhesive, the mass fraction needed for the primer manufacture material are natural gum 55-60
Part, 35-40 parts of butadiene-styrene rubber, 60-65 parts of carbon black, 35-40 parts of calcium carbonate, 2-3 parts of stearic acid, 2-3 parts of anti-aging agent, zinc oxide 7-9
Part, 2.5-2.8 parts of Cosan, 1-2 parts of accelerating agent, the mass fraction needed for the buffering adhesive manufacture material are natural gum 75-80
Part, 15-20 parts of butadiene-styrene rubber, 55-60 parts of carbon black, 55-60 parts of calcium carbonate, 1-1.5 parts of stearic acid, 3-5 parts of zinc oxide, accelerating agent 1-
2 parts, 2-2.5 parts of anti-aging agent, 2-2.5 parts of Cosan, mass fraction needed for the cloth glue manufacture material is natural gum 65-70
Part, 25-30 parts of butadiene-styrene rubber, 20-25 parts of carbon black, 25-30 parts of calcium carbonate, 3-5 parts of adhesive, 1-2 parts of stearic acid, zinc oxide 4-5
Part, 2.4-2.8 parts of accelerating agent, 4-5 parts of anti-aging agent, 2-2.5 parts of Cosan.
Preferably, a kind of manufacturing process of HI high impact environmental protection V bands includes the following steps：
（1）Mixing：Different industrial chemicals according to certain mass fraction is mixed, obtains primer, buffering adhesive and cloth glue；
（2）Raw rubber processing：Then raw rubber plasticate and industrial chemicals carries out mixing process；
（3）Canvas processing：Canvas is subjected to calendering process, then the canvas of calendering is carried out using the raw rubber being kneaded after completing
Gluing processing, processing are cut spare after completing；
（4）Cotton rope processing：Cotton rope is soaked line all-in-one machine by coiling to handle；
（5）Bonding：The raw rubber completed, canvas, cotton rope will be handled to carry out bonding infantees using primer, buffering adhesive and cloth glue；
（6）Vulcanization：The infantees progress vulcanizing treatment completed will be bonded；
（7）It examines：The infantees vulcanized after completing is tested, as massless problem can be used.
Preferably, the mass fraction needed for the primer manufacture material is 60 parts of natural gum, 40 parts of butadiene-styrene rubber, carbon black 65
Part, 40 parts of calcium carbonate, 3 parts of stearic acid, 3 parts of anti-aging agent, 9 parts of zinc oxide, 2.8 parts of Cosan, 2 parts of accelerating agent, the buffering adhesive
Mass fraction needed for manufacture material is 80 parts of natural gum, 20 parts of butadiene-styrene rubber, 60 parts of carbon black, 60 parts of calcium carbonate, stearic acid 1.5
Part, 5 parts of zinc oxide, 2 parts of accelerating agent, 2.5 parts of anti-aging agent, 2.5 parts of Cosan, the mass fraction needed for the cloth glue manufacture material
For 70 parts of natural gum, 30 parts of butadiene-styrene rubber, 25 parts of White Carbon black, 30 parts of calcium carbonate, 5 parts of adhesive, 2 parts of stearic acid, 5 parts of zinc oxide,
2.8 parts of accelerating agent, 5 parts of anti-aging agent, 2.5 parts of Cosan.
The present invention uses Japanese import aramid fiber skeleton cotton rope, in work is run, can bear moment relatively high power,
Rotative power is 5 times of classical V-belt, whole strength is 3 times of classical V-belt, in operation process, can play and not extend, do not receive
Contracting, suitable for taking turns rotation, while during pinch roller clutch, is not likely to produce noise more, in work is run, encounters foreign matter and be stopped
When, belt is reduced with friction coefficient, can slow down the impact force being subject to, and is solved motor and is burnt out and phenomena such as belt is broken, is transporting
In row work, phenomena such as working face is less prone to rubber powder, so as to protect ground environment.
Specific embodiment
Technical solution in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is only
It is part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, ordinary skill people
Member's all other embodiments obtained without making creative work, shall fall within the protection scope of the present invention.
Embodiment one：
A kind of HI high impact environmental protection V bands and its manufacturing process, the manufacture raw material of the HI high impact environmental protection V bands is by canvas, raw rubber, packet
Cloth, industrial chemicals, cotton rope, primer, buffering adhesive and cloth glue composition, the manufacture material of the primer, buffering adhesive and cloth glue include day
Right glue, butadiene-styrene rubber, carbon black, calcium carbonate, stearic acid, anti-aging agent, zinc oxide, Cosan, accelerating agent and adhesive, the primer system
Mass fraction needed for producing material material is 55 parts of natural gum, 35 parts of butadiene-styrene rubber, 60 parts of carbon black, 35 parts of calcium carbonate, 2 parts of stearic acid, is prevented
Old 2 parts of agent, 7 parts of zinc oxide, 2.5 parts of Cosan, 1 part of accelerating agent, the mass fraction needed for the buffering adhesive manufacture material are day
Right 75 parts of glue, 15 parts of butadiene-styrene rubber, 55 parts of carbon black, 55 parts of calcium carbonate, 1 part of stearic acid, 3 parts of zinc oxide, 1 part of accelerating agent, anti-aging agent 2
Part, 2 parts of Cosan, mass fraction needed for the cloth glue manufacture material is 65 parts of natural gum, 25 parts of butadiene-styrene rubber, 20 parts of carbon black,
25 parts of calcium carbonate, 3 parts of adhesive, 1 part of stearic acid, 4 parts of zinc oxide, 2.4 parts of accelerating agent, 4 parts of anti-aging agent, 2 parts of Cosan.
A kind of manufacturing process of HI high impact environmental protection V bands includes the following steps：
（1）Mixing：Different industrial chemicals according to certain mass fraction is mixed, obtains primer, buffering adhesive and cloth glue；
（2）Raw rubber processing：Then raw rubber plasticate and industrial chemicals carries out mixing process；
（3）Canvas processing：Canvas is subjected to calendering process, then the canvas of calendering is carried out using the raw rubber being kneaded after completing
Gluing processing, processing are cut spare after completing；
（4）Cotton rope processing：Cotton rope is soaked line all-in-one machine by coiling to handle；
（5）Bonding：The raw rubber completed, canvas, cotton rope will be handled to carry out bonding infantees using primer, buffering adhesive and cloth glue；
（6）Vulcanization：The infantees progress vulcanizing treatment completed will be bonded；
（7）It examines：The infantees vulcanized after completing is tested, as massless problem can be used.
Mass fraction needed for the primer manufacture material is 60 parts of natural gum, 40 parts of butadiene-styrene rubber, 65 parts of carbon black, calcium carbonate
40 parts, 3 parts of stearic acid, 3 parts of anti-aging agent, 9 parts of zinc oxide, 2.8 parts of Cosan, 2 parts of accelerating agent, the buffering adhesive manufacture material institute
The mass fraction needed is 80 parts of natural gum, 20 parts of butadiene-styrene rubber, 60 parts of carbon black, 60 parts of calcium carbonate, 1.5 parts of stearic acid, zinc oxide 5
Part, 2 parts of accelerating agent, 2.5 parts of anti-aging agent, 2.5 parts of Cosan, the mass fraction needed for the cloth glue manufacture material are natural gum 70
Part, 30 parts of butadiene-styrene rubber, 25 parts of White Carbon black, 30 parts of calcium carbonate, 5 parts of adhesive, 2 parts of stearic acid, 5 parts of zinc oxide, accelerating agent 2.8
Part, 5 parts of anti-aging agent, 2.5 parts of Cosan.
Embodiment two：
A kind of HI high impact environmental protection V bands and its manufacturing process, the manufacture raw material of the HI high impact environmental protection V bands is by canvas, raw rubber, packet
Cloth, industrial chemicals, cotton rope, primer, buffering adhesive and cloth glue composition, the manufacture material of the primer, buffering adhesive and cloth glue include day
Right glue, butadiene-styrene rubber, carbon black, calcium carbonate, stearic acid, anti-aging agent, zinc oxide, Cosan, accelerating agent and adhesive, the primer system
Mass fraction needed for producing material material is 60 parts of natural gum, 40 parts of butadiene-styrene rubber, 65 parts of carbon black, 40 parts of calcium carbonate, 3 parts of stearic acid, is prevented
Old 3 parts of agent, 9 parts of zinc oxide, 2.8 parts of Cosan, 2 parts of accelerating agent, the mass fraction needed for the buffering adhesive manufacture material are day
Right 80 parts of glue, 60 parts of carbon black, 60 parts of calcium carbonate, 1.5 parts of stearic acid, 5 parts of zinc oxide, 2 parts of accelerating agent, is prevented always 20 parts of butadiene-styrene rubber
2.5 parts of agent, 2.5 parts of Cosan, the mass fraction needed for the cloth glue manufacture material is 70 parts of natural gum, 30 parts of butadiene-styrene rubber, carbon
Black 25 parts, 30 parts of calcium carbonate, 5 parts of adhesive, 2 parts of stearic acid, 5 parts of zinc oxide, 2.8 parts of accelerating agent, 5 parts of anti-aging agent, Cosan
2.5 part.
A kind of manufacturing process of HI high impact environmental protection V bands includes the following steps：
（1）Mixing：Different industrial chemicals according to certain mass fraction is mixed, obtains primer, buffering adhesive and cloth glue；
（2）Raw rubber processing：Then raw rubber plasticate and industrial chemicals carries out mixing process；
（3）Canvas processing：Canvas is subjected to calendering process, then the canvas of calendering is carried out using the raw rubber being kneaded after completing
Gluing processing, processing are cut spare after completing；
（4）Cotton rope processing：Cotton rope is soaked line all-in-one machine by coiling to handle；
（5）Bonding：The raw rubber completed, canvas, cotton rope will be handled to carry out bonding infantees using primer, buffering adhesive and cloth glue；
（6）Vulcanization：The infantees progress vulcanizing treatment completed will be bonded；
（7）It examines：The infantees vulcanized after completing is tested, as massless problem can be used.
Mass fraction needed for the primer manufacture material is 60 parts of natural gum, 40 parts of butadiene-styrene rubber, 65 parts of carbon black, calcium carbonate
40 parts, 3 parts of stearic acid, 3 parts of anti-aging agent, 9 parts of zinc oxide, 2.8 parts of Cosan, 2 parts of accelerating agent, the buffering adhesive manufacture material institute
The mass fraction needed is 80 parts of natural gum, 20 parts of butadiene-styrene rubber, 60 parts of carbon black, 60 parts of calcium carbonate, 1.5 parts of stearic acid, zinc oxide 5
Part, 2 parts of accelerating agent, 2.5 parts of anti-aging agent, 2.5 parts of Cosan, the mass fraction needed for the cloth glue manufacture material are natural gum 70
Part, 30 parts of butadiene-styrene rubber, 25 parts of White Carbon black, 30 parts of calcium carbonate, 5 parts of adhesive, 2 parts of stearic acid, 5 parts of zinc oxide, accelerating agent 2.8
Part, 5 parts of anti-aging agent, 2.5 parts of Cosan.
Embodiment three：
A kind of HI high impact environmental protection V bands and its manufacturing process, the manufacture raw material of the HI high impact environmental protection V bands is by canvas, raw rubber, packet
Cloth, industrial chemicals, cotton rope, primer, buffering adhesive and cloth glue composition, the manufacture material of the primer, buffering adhesive and cloth glue include day
Right glue, butadiene-styrene rubber, carbon black, calcium carbonate, stearic acid, anti-aging agent, zinc oxide, Cosan, accelerating agent and adhesive, the primer system
Mass fraction needed for producing material material is 58 parts of natural gum, 37 parts of butadiene-styrene rubber, 63 parts of carbon black, 37 parts of calcium carbonate, 2-3 parts of stearic acid,
2-3 parts of anti-aging agent, 7-9 parts of zinc oxide, 2.5-2.8 parts of Cosan, 1.5 parts of accelerating agent, needed for the buffering adhesive manufacture material
Mass fraction is 78 parts of natural gum, 17 parts of butadiene-styrene rubber, 58 parts of carbon black, 58 parts of calcium carbonate, 1.3 parts of stearic acid, 4 parts of zinc oxide, is promoted
Into 1.5 parts of agent, 2.3 parts of anti-aging agent, 2.2 parts of Cosan, the mass fraction needed for the cloth glue manufacture material is 68 parts of natural gum,
28 parts of butadiene-styrene rubber, 23 parts of carbon black, 28 parts of calcium carbonate, 4 parts of adhesive, 1.5 parts of stearic acid, 4.5 parts of zinc oxide, 2.6 parts of accelerating agent,
4.5 parts of anti-aging agent, 2.3 parts of Cosan.
A kind of manufacturing process of HI high impact environmental protection V bands includes the following steps：
（1）Mixing：Different industrial chemicals according to certain mass fraction is mixed, obtains primer, buffering adhesive and cloth glue；
（2）Raw rubber processing：Then raw rubber plasticate and industrial chemicals carries out mixing process；
（3）Canvas processing：Canvas is subjected to calendering process, then the canvas of calendering is carried out using the raw rubber being kneaded after completing
Gluing processing, processing are cut spare after completing；
（4）Cotton rope processing：Cotton rope is soaked line all-in-one machine by coiling to handle；
（5）Bonding：The raw rubber completed, canvas, cotton rope will be handled to carry out bonding infantees using primer, buffering adhesive and cloth glue；
（6）Vulcanization：The infantees progress vulcanizing treatment completed will be bonded；
（7）It examines：The infantees vulcanized after completing is tested, as massless problem can be used.
Mass fraction needed for the primer manufacture material is 60 parts of natural gum, 40 parts of butadiene-styrene rubber, 65 parts of carbon black, calcium carbonate
40 parts, 3 parts of stearic acid, 3 parts of anti-aging agent, 9 parts of zinc oxide, 2.8 parts of Cosan, 2 parts of accelerating agent, the buffering adhesive manufacture material institute
The mass fraction needed is 80 parts of natural gum, 20 parts of butadiene-styrene rubber, 60 parts of carbon black, 60 parts of calcium carbonate, 1.5 parts of stearic acid, zinc oxide 5
Part, 2 parts of accelerating agent, 2.5 parts of anti-aging agent, 2.5 parts of Cosan, the mass fraction needed for the cloth glue manufacture material are natural gum 70
Part, 30 parts of butadiene-styrene rubber, 25 parts of White Carbon black, 30 parts of calcium carbonate, 5 parts of adhesive, 2 parts of stearic acid, 5 parts of zinc oxide, accelerating agent 2.8
Part, 5 parts of anti-aging agent, 2.5 parts of Cosan.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (3)
1. a kind of HI high impact environmental protection V bands and its manufacturing process, it is characterised in that：The manufacture raw material of the HI high impact environmental protection V bands by
Canvas, raw rubber, infantees, industrial chemicals, cotton rope, primer, buffering adhesive and cloth glue composition, the system of the primer, buffering adhesive and cloth glue
Producing material material includes natural gum, butadiene-styrene rubber, carbon black, calcium carbonate, stearic acid, anti-aging agent, zinc oxide, Cosan, accelerating agent and bonding
Agent, the mass fraction needed for the primer manufacture material is 55-60 parts of natural gum, 35-40 parts of butadiene-styrene rubber, 60-65 parts of carbon black, carbon
Sour calcium 35-40 parts, 2-3 parts of stearic acid, 2-3 parts of anti-aging agent, 7-9 parts of zinc oxide, 2.5-2.8 parts of Cosan, 1-2 parts of accelerating agent,
Mass fraction needed for the buffering adhesive manufacture material is 75-80 parts of natural gum, 15-20 parts of butadiene-styrene rubber, 55-60 parts of carbon black, carbon
Sour calcium 55-60 parts, 1-1.5 parts of stearic acid, 3-5 parts of zinc oxide, 1-2 parts of accelerating agent, 2-2.5 parts of anti-aging agent, Cosan 2-2.5
Part, the mass fraction needed for the cloth glue manufacture material is 65-70 parts of natural gum, 25-30 parts of butadiene-styrene rubber, 20-25 parts of carbon black, carbon
Sour calcium 25-30 parts, 3-5 parts of adhesive, 1-2 parts of stearic acid, 4-5 parts of zinc oxide, 2.4-2.8 parts of accelerating agent, 4-5 parts of anti-aging agent,
2-2.5 parts of Cosan.
2. a kind of HI high impact environmental protection V bands according to claim 1 and its manufacturing process, it is characterised in that：It is described a kind of high
The manufacturing process of impact environmental protection V bands includes the following steps：
（1）Mixing：Different industrial chemicals according to certain mass fraction is mixed, obtains primer, buffering adhesive and cloth glue；
（2）Raw rubber processing：Then raw rubber plasticate and industrial chemicals carries out mixing process；
（3）Canvas processing：Canvas is subjected to calendering process, then the canvas of calendering is carried out using the raw rubber being kneaded after completing
Gluing processing, processing are cut spare after completing；
（4）Cotton rope processing：Cotton rope is soaked line all-in-one machine by coiling to handle；
（5）Bonding：The raw rubber completed, canvas, cotton rope will be handled to carry out bonding infantees using primer, buffering adhesive and cloth glue；
（6）Vulcanization：The infantees progress vulcanizing treatment completed will be bonded；
（7）It examines：The infantees vulcanized after completing is tested, as massless problem can be used.
3. a kind of HI high impact environmental protection V bands according to claim 1 and its manufacturing process, it is characterised in that：The primer system
Mass fraction needed for producing material material is 60 parts of natural gum, 40 parts of butadiene-styrene rubber, 65 parts of carbon black, 40 parts of calcium carbonate, 3 parts of stearic acid, is prevented
Old 3 parts of agent, 9 parts of zinc oxide, 2.8 parts of Cosan, 2 parts of accelerating agent, the mass fraction needed for the buffering adhesive manufacture material are day
Right 80 parts of glue, 60 parts of carbon black, 60 parts of calcium carbonate, 1.5 parts of stearic acid, 5 parts of zinc oxide, 2 parts of accelerating agent, is prevented always 20 parts of butadiene-styrene rubber
2.5 parts of agent, 2.5 parts of Cosan, mass fraction needed for the cloth glue manufacture material is 70 parts of natural gum, 30 parts of butadiene-styrene rubber, white
25 parts of carbon black, 30 parts of calcium carbonate, 5 parts of adhesive, 2 parts of stearic acid, 5 parts of zinc oxide, 2.8 parts of accelerating agent, 5 parts of anti-aging agent, sulphur
2.5 parts of powder.