CN108178564A - A kind of st types fire protection flame retarding composite material - Google Patents
A kind of st types fire protection flame retarding composite material Download PDFInfo
- Publication number
- CN108178564A CN108178564A CN201810069807.9A CN201810069807A CN108178564A CN 108178564 A CN108178564 A CN 108178564A CN 201810069807 A CN201810069807 A CN 201810069807A CN 108178564 A CN108178564 A CN 108178564A
- Authority
- CN
- China
- Prior art keywords
- parts
- cinder
- ceramic powders
- perlite
- graphene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to building field, especially a kind of st types fire protection flame retarding composite material.Its raw material is calculated as by weight:45~55 parts of cement, 8~12 parts of cinder, 16~22 parts of rock wool silk, 18~22 parts of perlite, 8~12 parts of glass bead, 8~12 parts of ceramic powders, 6~10 parts of graphene, surplus are water and carbon cloth.It can be used for adding the composite material inside mobile national treasury wall, have fire protection flame retarding function while enhancing national treasury intensity.
Description
Technical field
The present invention relates to building field, especially a kind of st types fire protection flame retarding composite material.
Background technology
It is mostly mixed mud to be used to move the material filled inside national treasury on the market at present, material weight is not considered, to entirety
Quality influence is very big, can not meet existing fire protection flame retarding function simultaneously, there is low-quality requirement.And existing just to have be scene
It is filling, it has greater environmental impacts.
Invention content
To solve the above problems, the present invention provides a kind of st types applied fireproofing, it can be used for addition in mobile gold
Composite material inside the wall of library has fire protection flame retarding function while enhancing national treasury intensity.
To achieve these goals, the present invention uses following technical scheme, a kind of st types applied fireproofing, raw material
It is calculated as by weight:45~55 parts of cement, 8~12 parts of cinder, 16~22 parts of rock wool silk, 18~22 parts of perlite, glass bead 8
~12 parts, 8~12 parts of ceramic powders, 6~10 parts of graphene, surplus be water and carbon cloth.
Preferably, a kind of st types applied fireproofing, raw material are calculated as by weight:50 parts of cement, 10 parts of cinder, rock
20 parts of staple, 20 parts of perlite, 10 parts of glass bead, 10 parts of ceramic powders, 9 parts of graphene, surplus are water and carbon cloth.
Preferably, by weight, cinder:Glass bead:Ceramic powders=1:1:1.
St applied fireproofings as described above, preparation method include the following steps:
It takes cement, cinder, rock wool silk, perlite, glass bead, ceramic powders, graphene after mixing, water is added to stir evenly
Add in die freeze molding afterwards, module after molding using flame-retardant glue in module table face paste multilayer carbon fiber sheet, after produced
Product.
It is had the following advantages using fire protection flame retarding of the present invention:It is fire prevention, fire-retardant, high intensity, sound insulation, anti-oxidant, again
Amount is lighter, easily molded, non-friable, modularization molding, when in use, it is thus only necessary to which product is passed through flame-retardant glue and steel sticking
Molding, pours without scene.
Specific embodiment
The present invention is described in further detail below by specific embodiment.
Embodiment 1:A kind of st types applied fireproofing, raw material are calculated as by weight:50 parts of cement, 10 parts of cinder, rock
20 parts of staple, 20 parts of perlite, 10 parts of glass bead, 10 parts of ceramic powders, 9 parts of graphene, surplus are water and carbon cloth.
St applied fireproofings as described above, preparation method include the following steps:
It takes cement, cinder, rock wool silk, perlite, glass bead, ceramic powders, graphene after mixing, water is added to stir evenly
Add in die freeze molding afterwards, module after molding using flame-retardant glue in module table face paste multilayer carbon fiber sheet, after produced
Product.
Embodiment 2:A kind of st types applied fireproofing, raw material are calculated as by weight:45 parts of cement, 8 parts of cinder, rock wool
16 parts of silk, 18 parts of perlite, 8 parts of glass bead, 8 parts of ceramic powders, 6 parts of graphene, surplus are water and carbon cloth.
St applied fireproofings as described above, preparation method include the following steps:
It takes cement, cinder, rock wool silk, perlite, glass bead, ceramic powders, graphene after mixing, water is added to stir evenly
Add in die freeze molding afterwards, module after molding using flame-retardant glue in module table face paste multilayer carbon fiber sheet, after produced
Product.
Embodiment 3:A kind of st types applied fireproofing, raw material are calculated as by weight:55 parts of cement, 12 parts of cinder, rock
22 parts of staple, 22 parts of perlite, 12 parts of glass bead, 12 parts of ceramic powders, 10 parts of graphene, surplus are water and carbon cloth.
St applied fireproofings as described above, preparation method include the following steps:
It takes cement, cinder, rock wool silk, perlite, glass bead, ceramic powders, graphene after mixing, water is added to stir evenly
Add in die freeze molding afterwards, module after molding using flame-retardant glue in module table face paste multilayer carbon fiber sheet, after produced
Product.
Embodiment 4:A kind of st types applied fireproofing, raw material are calculated as by weight:48 parts of cement, 11 parts of cinder, rock
18 parts of staple, 21 parts of perlite, 9 parts of glass bead, 9 parts of ceramic powders, 7 parts of graphene, surplus are water and carbon cloth.
St applied fireproofings as described above, preparation method include the following steps:
It takes cement, cinder, rock wool silk, perlite, glass bead, ceramic powders, graphene after mixing, water is added to stir evenly
Add in die freeze molding afterwards, module after molding using flame-retardant glue in module table face paste multilayer carbon fiber sheet, after produced
Product.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, there can be various modifications and variations in the spirit and principles in the present invention, these equivalent modifications or replacement etc.,
It is all contained within protection scope of the present invention.
Claims (4)
1. a kind of st types applied fireproofing, which is characterized in that its raw material is calculated as by weight:45~55 parts of cement, cinder 8~
12 parts, rock wool silk 16~22 parts, 18~22 parts of perlite, 8~12 parts of glass bead, 8~12 parts of ceramic powders, graphene 6~
10 parts, surplus is water and carbon cloth.
2. a kind of st types applied fireproofing according to claim 1, which is characterized in that its raw material is calculated as by weight:
50 parts of cement, 10 parts of cinder, 20 parts of rock wool silk, 20 parts of perlite, 10 parts of glass bead, 10 parts of ceramic powders, 9 parts of graphene,
Surplus is water and carbon cloth.
3. a kind of st types applied fireproofing according to claim 1, it is characterised in that:By weight, cinder:Vitreous
Microballon:Ceramic powders=1:1:1.
4. a kind of st types applied fireproofing according to claim 1, which is characterized in that preparation method includes following step
Suddenly:It takes cement, cinder, rock wool silk, perlite, glass bead, ceramic powders, graphene after mixing, water is added to stir evenly
Add in die freeze molding afterwards, module after molding using flame-retardant glue in module table face paste multilayer carbon fiber sheet, after produced
Product.