CN108166000A - A kind of non-ferrous metal corrosion inhibiter - Google Patents
A kind of non-ferrous metal corrosion inhibiter Download PDFInfo
- Publication number
- CN108166000A CN108166000A CN201711448664.4A CN201711448664A CN108166000A CN 108166000 A CN108166000 A CN 108166000A CN 201711448664 A CN201711448664 A CN 201711448664A CN 108166000 A CN108166000 A CN 108166000A
- Authority
- CN
- China
- Prior art keywords
- parts
- ferrous metal
- corrosion inhibiter
- metal corrosion
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of non-ferrous metal corrosion inhibiter, each component and corresponding parts by weight are：8 10 parts of Boratex, 8 10 parts of sodium chloride, 10 12 parts of calcium carbonate, 25 parts of zinc sulfate, 35 parts of potassium nitrate, 80 100 parts of water.Non-ferrous metal corrosion inhibiter proposed by the present invention proportioning is reasonable, and dosage is few during use, and property is stablized, and environmentally protective, production cost is low.
Description
Technical field
The invention belongs to field of mechanical technique, more particularly to a kind of non-ferrous metal corrosion inhibiter.
Background technology
Most metals spontaneous can all chemically react under field conditions (factors) with air or water, its own is then rotten
Erosion, so nature is rarely free of the natural simple metal of other impurities.Metal is good conductor, thus most of metal water,
Under the conditions of electrolyte is existing, easily reacts and go bad or aoxidize or generate other compounds, here it is be not added with protecting
Under conditions of metal erosion the reason of.The harm that metal corrodes is huge, first by the chemical industry facility of metal casting, city
Political affairs pipe network cannot reach due to corrosion expected from service life, increase financial cost；Secondly the main machine made of metal component
Accident occurs for tool, manned tool, pressure vessel etc. or because security intensity is not achieved in metal erosion, increases safety cost；Last gold
The reserves of category are limited, the storage of metal mineral reserves on the consumption earth that uncontrolled corrosion can be too fast, at the same also cost of manufacture,
Technologic waste increases environmental resource protection cost.
Invention content
It is an object of the invention to propose a kind of nontoxic, environmentally protective and at low cost non-ferrous metal corrosion inhibiter.
The purpose of the present invention is realized using following technical scheme.A kind of non-ferrous metal inhibition proposed according to the present invention
Agent, each component and corresponding parts by weight are：8-10 parts of Boratex, 8-10 parts of sodium chloride, 10-12 parts of calcium carbonate, zinc sulfate 2-5
Part, 3-5 parts of potassium nitrate, 80-100 parts of water.
Non-ferrous metal corrosion inhibiter proposed by the present invention proportioning is reasonable, and dosage is few during use, and property is stablized, environmentally protective, raw
It produces at low cost.
Above description is only the general introduction of technical solution of the present invention, in order to better understand the technological means of the present invention, and
It can be implemented in accordance with the contents of the specification, and to allow the above and other objects, features and advantages of the present invention can be brighter
Aobvious understandable, special below to lift preferred embodiment, detailed description are as follows.
Specific embodiment
The technological means and effect taken further to illustrate the present invention to reach predetermined goal of the invention, below in conjunction with
Preferred embodiment, to non-ferrous metal corrosion inhibiter its specific embodiment, structure, feature and its effect proposed according to the present invention,
It is described in detail as after.
Embodiment 1
A kind of non-ferrous metal corrosion inhibiter of the present invention, each component and corresponding parts by weight are：8 parts of Boratex, sodium chloride 8
Part, 10 parts of calcium carbonate, 2 parts of zinc sulfate, 3 parts of potassium nitrate, 80 parts of water.
Embodiment 2
A kind of non-ferrous metal corrosion inhibiter of the present invention, each component and corresponding parts by weight are：9 parts of Boratex, sodium chloride 9
Part, 11 parts of calcium carbonate, 3 parts of zinc sulfate, 4 parts of potassium nitrate, 86 parts of water.
Embodiment 3
A kind of non-ferrous metal corrosion inhibiter of the present invention, each component and corresponding parts by weight are：10 parts of Boratex, sodium chloride 9
Part, 11 parts of calcium carbonate, 4 parts of zinc sulfate, 4 parts of potassium nitrate, 96 parts of water.
Embodiment 4
A kind of non-ferrous metal corrosion inhibiter of the present invention, each component and corresponding parts by weight are：10 parts of Boratex, sodium chloride 10
Part, 12 parts of calcium carbonate, 5 parts of zinc sulfate, 5 parts of potassium nitrate, 100 parts of water.
The above described is only a preferred embodiment of the present invention, not doing limitation in any form to the present invention, appoint
What those skilled in the art, without departing from the scope of the present invention, technical spirit according to the present invention to
Any simple modification, equivalent change and modification that upper embodiment is done, in the range of still falling within technical solution of the present invention.
Claims (1)
1. a kind of non-ferrous metal corrosion inhibiter, it is characterised in that each component and corresponding parts by weight are：8-10 parts of Boratex, chlorination
8-10 parts of sodium, 10-12 parts of calcium carbonate, 2-5 parts of zinc sulfate, 3-5 parts of potassium nitrate, 80-100 parts of water.