A kind of non-ferrous metal inhibiter
Technical field
The present invention relates to a kind of for metal inhibitor.
Background technology
The metal of produced worldwide has 1/10 can not reclaim because of corrosion.According to the Center Francais De La Corrosion report, within 80 years, France's loss 1,150 hundred million French Francs, Britain lose 10,000,000,000 pounds, account for 3~4% of various countries' national economy output value.Industrial development is faster, and the metal loss amount is larger.U.S.'s loss 5,500,000,000 in 1949, be 100~20,000,000,000 the sixties, rises to 70,000,000,000, average ten years the seventies and almost quadruple.China estimates approximately to lose Renminbi 30,000,000,000 every year, account for 3.5% of the national economy output value.World War II end nitrous diisopropyl glue and the utilization of nitrous acid bicyclohexylamine on weapon, promoted the development of inhibiter, but be limited to the iron and steel aspect more.Nineteen fifty, the U.S. was developed into benzotriazole (BTA), and promoted in non-ferrous metal.The later stage sixties, the U.S. produced the BTA2700 ton per year.Within 1980, increase to 10,000 tons, increase more than 20% every year on average.
Non-ferrous metal, as copper, silver, gold etc., because it is rare valuable, obtained the favor in a lot of fields.Because, especially important to the corrosion-resistant treatments of non-ferrous metal.At present, in order to reach good effect, the inhibiter of non-ferrous metal mainly adopts benzotriazole, but this chemical substance has huge poison, and operator's health is had to very large infringement.
Summary of the invention
The technical problem to be solved in the present invention is to overcome existing defect, and a kind of non-ferrous metal inhibiter of green non-poisonous evil is provided.
Purpose of the present invention is carried out specific implementation by the following technical programs:
A kind of non-ferrous metal inhibiter, each component by weight, 100 parts of Sodium Tetraborate 10-13 parts, sodium-chlor 5-10 part, phytic acid ca 20-30 part, Sodium Fluoride 3-6 part, titanium dioxide 0.02-0.5 part, ribonucleoside triphosphote 0.01-0.05 part, water.
As preferred version, above-mentioned non-ferrous metal inhibiter, each component by weight, 13 parts of Sodium Tetraboratees, 6.5 parts, sodium-chlor, 22.5 parts of phytic acid ca, 4 parts of Sodium Fluorides, 0.25 part of titanium dioxide, 0.02 part of ribonucleoside triphosphote, 100 parts, water.
Beneficial effect of the present invention:
Non-ferrous metal inhibiter provided by the present invention, abandoned traditional BTA, basic nontoxicity, and to also effective than the inhibiter that adopts BTA on the corrosion mitigating effect of non-ferrous metal.
Embodiment
Below the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein, only for description and interpretation the present invention, is not intended to limit the present invention.
embodiment 1:
A kind of non-ferrous metal inhibiter, each component by weight, 13 parts of Sodium Tetraboratees, 6.5 parts, sodium-chlor, 22.5 parts of phytic acid ca, 4 parts of Sodium Fluorides, 0.25 part of titanium dioxide, 0.02 part of ribonucleoside triphosphote, 100 parts, water.
embodiment 2:
A kind of non-ferrous metal inhibiter, each component by weight, 10 parts of Sodium Tetraboratees, 10 parts, sodium-chlor, 20 parts of phytic acid ca, 6 parts of Sodium Fluorides, 0.02 part of titanium dioxide, 0.05 part of ribonucleoside triphosphote, 100 parts, water.
embodiment 3:
A kind of non-ferrous metal inhibiter, each component by weight, 13 parts of Sodium Tetraboratees, 5 parts, sodium-chlor, 30 parts of phytic acid ca, 3 parts of Sodium Fluorides, 0.5 part of titanium dioxide, 0.01 part of ribonucleoside triphosphote, 100 parts, water.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment, the present invention is had been described in detail, for a person skilled in the art, its technical scheme that still can put down in writing aforementioned each embodiment is modified, or part technical characterictic wherein is equal to replacement.Within the spirit and principles in the present invention all, any modification of doing, be equal to replacement, improvement etc., within all should being included in protection scope of the present invention.